CN106630915A - 一种室内装修抗渗透防火材料及其生产方法 - Google Patents
一种室内装修抗渗透防火材料及其生产方法 Download PDFInfo
- Publication number
- CN106630915A CN106630915A CN201710003641.6A CN201710003641A CN106630915A CN 106630915 A CN106630915 A CN 106630915A CN 201710003641 A CN201710003641 A CN 201710003641A CN 106630915 A CN106630915 A CN 106630915A
- Authority
- CN
- China
- Prior art keywords
- grain slag
- weight
- lightweight aggregate
- binding material
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种室内装修抗渗透防火材料及其生产方法,包括板体,所述板体内水渣轻骨料菱镁胶凝材料(1)、玻璃纤维网格布(2)、有色面层(3)、无纺布(4)、有机硅防水层(5)、有色面浆料(6)、抗污涂层(7)组成的饰面水渣轻骨料镁硅板。本发明采用经过特殊处理的轻骨料作为填充材料进行菱镁胶凝材料的制作,具有较好的防火防潮性能;本发明通过添加有机硅作为防水材料,具有了抗渗透功能;本发明通过在有色面层增加抗污层,具有了抗污的效果。
Description
技术领域
本发明涉及建筑板材领域,具体是指一种室内装修抗渗透防火材料及其生产方法。
背景技术
长期以来高炉炉渣都做为废物扔掉,这不仅是一项巨大的浪费、而且炉渣堆积如山、侵占良田、妨碍交通、甚至限制了高炉生产,目前我国高炉炉渣的利用率很低,只有60~70%。德国的蒂森克虏伯钢厂现在炉渣的综合回收率水平已接近95%,其中冶金渣的回收利用率尤为突出。在德国,高炉渣利用率达到了100%,同时炼钢渣的利用率也超过了90%。高炉炉渣的处理方法主要是干渣和水渣处理两种,其中水渣由高炉溶渣与铁水分离后,经渣沟进入溶渣粒化区水冲渣而成。水渣可以作为优质建筑原料,生产各种具有不同功能的建筑材料,水渣都是很好的建筑材料,
本发明探索一种能将水渣变废为宝的,加之利用陶粒、珍珠岩、玻化微珠、EPS泡沫珠等轻质的防火材料,同时加入对机械性能增强的纤维,上述原材料的使用使得本发明所涉及的防火板质量更轻,防火性能优,通过加入有机硅防水材料,制作出防火、防水防潮、机械性能好、装饰效果好的等多方面性能兼顾的一种室内装修抗渗透防火材料。
目前,按JC688-2006玻镁平板和JG/T414-2013建筑用菱镁装饰板标准生产的防火板,主要用于防火装修。该防火板以大量的锯末为填充料,产品吸水率>10%,软化系数0.85,抗压强度低。
发明内容
本发明要解决的技术问题是提供一种以菱镁材料为胶凝剂,加入大量高炉水渣和轻骨料为填充料,加入有机硅防水材料制作的且适用于室内装修的抗渗透防火材料。
本发明通过下述技术方案实现:一种室内装修抗渗透防火材料及其生产方法,包括板体,包括板体,所述板体由下往上依次设有抗污涂层7、有色面层3、有机硅防水层5以及玻璃纤维网格布2,所述有色面层3和玻璃纤维网格布2之间设有有色面浆料6;所述板体由上往下依次设有无纺布4、有机硅防水层5以及玻璃纤维网格布2,所述有无纺布4、和玻璃纤维网格布2之间的空隙填充有水渣轻骨料菱镁胶凝材料1,所述防水层5渗透到水渣轻骨料菱镁胶凝材料1中;所述上部玻璃纤维网格布2和下部玻璃纤维网格布2之间的板体空间填充有水渣轻骨料菱镁胶凝材料1。
为了更好的实现本发明,优选的,所述有色面层(3)的材质为水渣轻骨料菱镁胶凝材料1。
进一步地,在所述有色面层3上喷涂抗污剂、烘干固化、形成抗污涂层7。
进一步地,所述有色面层3内添加有颜料土。
进一步地,所述轻骨料是陶粒、珍珠岩、玻化微珠、之一或其组合。
进一步地,所述玻璃纤维网格布2用来加强抗折强度。
进一步地,所述玻璃纤维网格布2总层数为4~10层。
进一步地,所述无纺布4总层数为2~7层,所述板体总厚度为10-40mm。
进一步地,所述轻骨料是陶粒、珍珠岩、玻化微珠之一或其组合。其中陶粒(Φ1-3mm,密度600g/L,吸水率20%);珍珠岩(密度80g/L,吸水率>100%);玻化微珠(早期称闭孔珍珠岩,密度130g/L,吸水率30%-50%)。
进一步地,所述无纺布是9g~100g每平方米。无纺布是根据水渣轻骨料本防火板厚度不同选择9g至100g每平方米,其主要作用减少产品表面孔隙率,方便真空吸盘产品下线。
另外的,制备这种室内装修抗渗透防火材料及其生产方法的方法,包括一下步骤:
(1)首先制备好水渣轻骨料菱镁胶凝材料1:
A、制备29.4°Bé硫酸镁水:将一份重量的七水硫酸镁加入一份重量的水使硫酸镁溶解成29.4°Bé硫酸镁水;
B、制备有色面浆料6:取步骤A中一份重量的29.4°Bé硫酸镁水,并向其中加入一份重量的氧化镁轻烧粉、一份重量的白云石粉、一份重量的水渣粉、一份重量的改性剂,并将上述混合物搅拌均匀,得到有色面浆料6;
C、制备水渣轻骨料菱镁胶凝材料1的:取步骤A中一份重量的29.4°Bé硫酸镁水,再向其中加入一份重量的氧化镁轻烧粉、一份重量的白云石粉、一份重量的水渣粉、一份重量的水渣、一份重量陶粒或珍珠岩,以及一份重量的改性剂,搅拌均匀得到水渣轻骨料菱镁胶凝材料1,并将其按重量分成至少两份;或取步骤A中一份重量的29.4°Bé硫酸镁水,再向其中加入一份重量的氧化镁轻烧粉、一份重量的水渣粉、一份重量的水渣、一份玻化微珠,以及一份重量的改性剂,搅拌均匀得到水渣轻骨料菱镁胶凝材料1,并将其按重量分成至少两份;
(2)开始制作室内装修抗渗透防火材料:
A、所述的作用于室内防水装修的板材在防火板生产线上成型,将制作好的有色面浆料6铺平在PVC或ABS基板上;
B、将相应数量的玻璃纤维网格布2压入有色面浆料6中,在玻璃纤维网格布2上铺设水渣轻骨料菱镁胶凝材料1,水渣轻骨料菱镁胶凝材料1隔着玻璃纤维网格布2铺平在有色面浆料6上;
C、然后再在水渣轻骨料菱镁胶凝材料1上铺放有相应数量的玻璃纤维网格布(2),在此层水渣轻骨料菱镁胶凝材料1上铺有无纺布4;
D、经切割、整平、养护、固化、拆模、四边定尺切割、养护,喷涂有机硅防水剂、烘干固化,形成有机硅防水层5,喷涂界面剂、烘干固化,形成抗污涂层7。
F、形成由水渣轻骨料菱镁胶凝材料1、玻璃纤维网格布2、有色面层3、无纺布4、有机硅防水层5、有色面浆料6、抗污涂层7组成的饰面水渣轻骨料镁硅板。
其中要说明的是,所述的水渣为水淬矿渣,一种很好的活性混合料.但由于水渣硬度高且易磨性差,目前,仅有少量被水泥生产企业当作水泥掺合料使用,而大多数钢厂都将水渣作为废料堆放,不但占有大量耕地,且污染环境。而本发明所使用的水渣粉是把熔融状态的高炉渣置于水中急速冷却而形成的,用水淬将高温液态炉渣击碎,变成为松散的水渣;或者用蒸汽或压缩空气将高温液态炉渣击散,变成为蓬松的渣棉。高炉水渣是综合利用的好方法,先进的高炉水渣已经100%得到利用。目前,冲制水渣的工艺设备均能保证水渣的质量,玻璃化程度可以达到90%~95%,水渣平均粒度为0.2~3.0mm,水渣含水≤15%。
本发明与现有技术相比,具有以下优点及有益效果:
(1)本发明采用经过特殊处理的轻骨料作为填充材料进行菱镁胶凝材料的制作,从而能够将废弃且容易引起环境污染的高滤渣废料进行合理利用,不仅做到了废物回收二次利用,且具有较好的防火防潮性能;
(2)本发明通过使用有机硅防水材料,具有抗渗透的作用;
(3)本发明具有抗污层,能够抗污。
附图说明
通过阅读参照以下附图对非限制性实施例所作的详细描述,本发明的其他特征、目的和优点将会变得更为明显:
图1为本发明的结构示意图。
其中:1—水渣轻骨料菱镁胶凝材料、2—玻璃纤维网格布、3—有色面层、4—无纺布、5—有机硅防水层、6—有色面浆料、7—抗污涂层。
具体实施方式
下面详细描述本发明的实施例,所述实施例的示例在附图中示出,其中自始至终相同或类似的标号表示相同或类似的元件或具有相同或类似功能的元件。下面通过参考附图描述的实施例是示例性的,仅用于解释本发明,而不能理解为对本发明的限制。
实施例1:
本实施例当中的一种室内装修抗渗透防火材料及其生产方法,如图1所示,一种室内装修抗渗透防火材料及其生产方法,包括板体,包括板体,所述板体由下往上依次设有抗污涂层7、有色面层3、有机硅防水层5以及玻璃纤维网格布2,所述有色面层3和玻璃纤维网格布2之间设有有色面浆料6;所述板体由上往下依次设有无纺布4、有机硅防水层5以及玻璃纤维网格布2,所述有无纺布4、和玻璃纤维网格布2之间的空隙填充有水渣轻骨料菱镁胶凝材料1,所述防水层5渗透到水渣轻骨料菱镁胶凝材料1中;所述上部玻璃纤维网格布2和下部玻璃纤维网格布2之间的板体空间填充有水渣轻骨料菱镁胶凝材料1。
所述有色面层(3)的材质为水渣轻骨料菱镁胶凝材料(1)。在所述有色面层(3)上喷涂抗污剂、烘干固化、形成抗污涂层(7)。所述有色面层(3)内添加有颜料土。所述轻骨料是陶粒、珍珠岩、玻化微珠、之一或其组合。所述玻璃纤维网格布(2)用来加强抗折强度。所述玻璃纤维网格布(2)总层数为4~10层。所述无纺布(4)总层数为2~7层,所述板体总厚度为10-40mm。所述轻骨料是陶粒、珍珠岩、玻化微珠之一或其组合。其中陶粒(Φ1-3mm,密度600g/L,吸水率20%);珍珠岩(密度80g/L,吸水率>100%);玻化微珠(早期称闭孔珍珠岩,密度130g/L,吸水率30%-50%)。所述无纺布是9g~100g每平方米。无纺布是根据水渣轻骨料本防火板厚度不同选择9g至100g每平方米,其主要作用减少产品表面孔隙率,方便真空吸盘产品下线。
另外的,制备这种室内装修抗渗透防火材料及其生产方法的方法,包括一下步骤:
(1)首先制备好凝胶材料:
A、制备29.4°Bé硫酸镁水:将850kg的七水硫酸镁加入1000kg的水使硫酸镁溶解成29.4°Bé硫酸镁水;
B、制备有色面浆料6:取步骤A中125kg的29.4°Bé硫酸镁水,并向其中加入100kg的氧化镁轻烧粉、2kg氧化铁红、4kg的白云石粉、125kg的水渣粉、一份重量的改性剂,并将上述混合物搅拌均匀,得到有色面浆料6;
C、制备水渣轻骨料菱镁胶凝材料1的:取步骤A中130kg的29.4°Bé硫酸镁水,再向其中加入100kg的氧化镁轻烧粉、4kg的白云石粉、150kg的水渣粉、200kg的水渣、90kg陶粒以及一份重量的改性剂,得到水渣轻骨料菱镁胶凝材料1,并将其按重量分成至少两份;
(2)开始制作用于室内防水装修的板材:
A、所述的作用于室内防水装修的板材在防火板生产线上成型,将制作好的有色面浆料6铺平在PVC或ABS基板上;
B、将2层玻璃纤维网格布2压入有色面浆料6中,在玻璃纤维网格布2上铺设水渣轻骨料菱镁胶凝材料1,水渣轻骨料菱镁胶凝材料1隔着玻璃纤维网格布2铺平在有色面浆料6上;
C、然后再在水渣轻骨料菱镁胶凝材料1上铺放有2层玻璃纤维网格布(2),在此层水渣轻骨料菱镁胶凝材料1上铺有无纺布4;
D、经切割、整平、养护、固化、拆模、四边定尺切割、养护,喷涂有机硅防水剂、烘干固化,形成有机硅防水层5,喷涂界面剂、烘干固化,形成抗污涂层7。
F、形成由水渣轻骨料菱镁胶凝材料1、玻璃纤维网格布2、有色面层3、无纺布4、有机硅防水层5、有色面浆料6、抗污涂层7组成的饰面水渣轻骨料镁硅板,板厚10mm。
实施例2:
本实施例在上述实施例1的基础上,进一步说明。本实施例对所述步骤(1)中的水渣轻骨料菱镁胶凝材料的制作进行进一步地优选:
(1)首先制备好凝胶材料:
A、制备29.4°Bé硫酸镁水:将850kg的七水硫酸镁加入1000kg的水使硫酸镁溶解成29.4°Bé硫酸镁水;
B、制备有色面浆料6:取步骤A中125kg的29.4°Bé硫酸镁水,并向其中加入100kg的氧化镁轻烧粉、2kg氧化铁红、4kg的白云石粉、125kg的水渣粉、一份重量的改性剂,并将上述混合物搅拌均匀,得到有色面浆料6;
C、制备水渣轻骨料菱镁胶凝材料1的:取步骤A中150kg的29.4°Bé硫酸镁水,再向其中加入100kg的氧化镁轻烧粉、4kg的白云石粉、150kg的水渣粉、200kg的水渣、13kg珍珠岩以及一份重量的改性剂,得到水渣轻骨料菱镁胶凝材料1,并将其按重量分成至少两份;
实施例3:
本实施例在上述实施例1的基础上,进一步说明。本实施例对所述步骤(1)中的水渣轻骨料菱镁胶凝材料的制作进行进一步地优选:
(1)首先制备好凝胶材料:
A、制备29.4°Bé硫酸镁水:将850kg的七水硫酸镁加入1000kg的水使硫酸镁溶解成29.4°Bé硫酸镁水;
B、制备有色面浆料6:取步骤A中125kg的29.4°Bé硫酸镁水,并向其中加入100kg的氧化镁轻烧粉、2kg氧化铁红、4kg的白云石粉、125kg的水渣粉、一份重量的改性剂,并将上述混合物搅拌均匀,得到有色面浆料6;
C、制备水渣轻骨料菱镁胶凝材料1的:取步骤A中140kg的29.4°Bé硫酸镁水,再向其中加入100kg的氧化镁轻烧粉、150kg的水渣粉、200kg的水渣、13kg玻化微珠以及一份重量的改性剂,得到水渣轻骨料菱镁胶凝材料1,并将其按重量分成至少两份;
实施例4:
本实施例在上述实施例1的基础上,进一步说明。本实施例对所述步骤(1)中的有色面浆料6的制作进行进一步地优选:
(1)首先制备好凝胶材料:
A、制备29.4°Bé硫酸镁水:将850kg的七水硫酸镁加入1000kg的水使硫酸镁溶解成29.4°Bé硫酸镁水;
B、制备有色面浆料6:取步骤A中125kg的29.4°Bé硫酸镁水,并向其中加入100kg的氧化镁轻烧粉、2kg氧化铁红、4kg的白云石粉、125kg的水渣粉、一份重量的改性剂,并将上述混合物搅拌均匀,得到有色面浆料6;
C、制备水渣轻骨料菱镁胶凝材料1的:取步骤A中140kg的29.4°Bé硫酸镁水,再向其中加入100kg的氧化镁轻烧粉、150kg的水渣粉、200kg的水渣、13kg玻化微珠以及一份重量的改性剂,得到水渣轻骨料菱镁胶凝材料1,并将其按重量分成至少两份;
实施例5:
本实施例在上述实施例1的基础上,进一步说明。本实施例对所述步骤(1)中的有色面浆料6的制作进行进一步地优选:
(1)首先制备好凝胶材料:
A、制备29.4°Bé硫酸镁水:将850kg的七水硫酸镁加入1000kg的水使硫酸镁溶解成29.4°Bé硫酸镁水;
B、制备有色面浆料6:取步骤A中125kg的29.4°Bé硫酸镁水,并向其中加入100kg的氧化镁轻烧粉、4kg氧化铁红、4kg的白云石粉、125kg的水渣粉、一份重量的改性剂,并将上述混合物搅拌均匀,得到有色面浆料6;
C、制备水渣轻骨料菱镁胶凝材料1的:取步骤A中140kg的29.4°Bé硫酸镁水,再向其中加入100kg的氧化镁轻烧粉、150kg的水渣粉、200kg的水渣、13kg玻化微珠以及一份重量的改性剂,得到水渣轻骨料菱镁胶凝材料1,并将其按重量分成至少两份;
实施例6
本实施例是在实施例1的基础上就玻璃纤维网格布2的用量进行优选。
(2)开始制作用于室内防水装修的板材:
A、所述的作用于室内防水装修的板材在防火板生产线上成型,将制作好的有色面浆料6铺平在PVC或ABS基板上;
B、将3层玻璃纤维网格布2压入有色面浆料6中,在玻璃纤维网格布2上铺设水渣轻骨料菱镁胶凝材料1,水渣轻骨料菱镁胶凝材料1隔着玻璃纤维网格布2铺平在有色面浆料6上;
C、然后再在水渣轻骨料菱镁胶凝材料1上铺放有3层玻璃纤维网格布(2),在此层水渣轻骨料菱镁胶凝材料1上铺有无纺布4;
D、经切割、整平、养护、固化、拆模、四边定尺切割、养护,喷涂有机硅防水剂、烘干固化,形成有机硅防水层5,喷涂界面剂、烘干固化,形成抗污涂层7。
F、形成由水渣轻骨料菱镁胶凝材料1、玻璃纤维网格布2、有色面层3、无纺布4、有机硅防水层5、有色面浆料6、抗污涂层7组成的饰面水渣轻骨料镁硅板,板厚25mm。
实施例7
本实施例是在实施例1的基础上就玻璃纤维网格布2的用量进行优选。
(2)开始制作用于室内防水装修的板材:
A、所述的作用于室内防水装修的板材在防火板生产线上成型,将制作好的有色面浆料6铺平在PVC或ABS基板上;
B、将4层玻璃纤维网格布2压入有色面浆料6中,在玻璃纤维网格布2上铺设水渣轻骨料菱镁胶凝材料1,水渣轻骨料菱镁胶凝材料1隔着玻璃纤维网格布2铺平在有色面浆料6上;
C、然后再在水渣轻骨料菱镁胶凝材料1上铺放有4层玻璃纤维网格布(2),在此层水渣轻骨料菱镁胶凝材料1上铺有无纺布4;
D、经切割、整平、养护、固化、拆模、四边定尺切割、养护,喷涂有机硅防水剂、烘干固化,形成有机硅防水层5,喷涂界面剂、烘干固化,形成抗污涂层7。
F、形成由水渣轻骨料菱镁胶凝材料1、玻璃纤维网格布2、有色面层3、无纺布4、有机硅防水层5、有色面浆料6、抗污涂层7组成的饰面水渣轻骨料镁硅板,板厚40mm。
实施例7
本实施例是在实施例1的基础上就玻璃纤维网格布2的用量进行优选。
(2)开始制作用于室内防水装修的板材:
A、所述的作用于室内防水装修的板材在防火板生产线上成型,将制作好的有色面浆料6铺平在PVC或ABS基板上;
B、将5层玻璃纤维网格布2压入有色面浆料6中,在玻璃纤维网格布2上铺设水渣轻骨料菱镁胶凝材料1,水渣轻骨料菱镁胶凝材料1隔着玻璃纤维网格布2铺平在有色面浆料6上;
C、然后再在水渣轻骨料菱镁胶凝材料1上铺放有5层玻璃纤维网格布(2),在此层水渣轻骨料菱镁胶凝材料1上铺有无纺布4;
D、经切割、整平、养护、固化、拆模、四边定尺切割、养护,喷涂有机硅防水剂、烘干固化,形成有机硅防水层5,喷涂界面剂、烘干固化,形成抗污涂层7。
F、形成由水渣轻骨料菱镁胶凝材料1、玻璃纤维网格布2、有色面层3、无纺布4、有机硅防水层5、有色面浆料6、抗污涂层7组成的饰面水渣轻骨料镁硅板,板厚40mm。
根据以上实施例得知:当饰面水渣镁硅板厚度为10mm时四层玻璃纤维网格布,抗折强度>12Mpa,当饰面水渣镁硅板厚度为25mm时六层玻璃纤维网格布,抗折强度>30Mpa,当饰面水渣镁硅板厚度为40mm时八层玻璃纤维网格布,抗折强度>30Mpa,当饰面水渣镁硅板厚度为40mm时十层玻璃纤维网格布,抗折强度>30Mpa。饰面纤维水渣镁硅板厚度不同,可选择四至十层玻璃纤维网格布。
尽管已经示出和描述了本发明的实施例,本领域的普通技术人员可以理解:在不脱离本发明的原理和宗旨下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由权利要求及其等同物限定。
Claims (10)
1.一种室内装修抗渗透防火材料,其特征在于:包括板体,所述板体由下往上依次设有抗污涂层(7)、有色面层(3)、有机硅防水层(5)以及玻璃纤维网格布(2),所述有色面层(3)和玻璃纤维网格布(2)之间设有有色面浆料(6);所述板体由上往下依次设有无纺布(4)、有机硅防水层(5)以及玻璃纤维网格布(2),所述有无纺布(4)、和玻璃纤维网格布(2)之间的空隙填充有水渣轻骨料菱镁胶凝材料(1),所述防水层(5)渗透到水渣轻骨料菱镁胶凝材料(1)中;所述上部玻璃纤维网格布(2)和下部玻璃纤维网格布(2)之间的板体空间填充有水渣轻骨料菱镁胶凝材料(1)。
2.根据权利要求1所述的一种室内装修抗渗透防火材料,其特征在于,所述有色面层(3)的材质为水渣轻骨料菱镁胶凝材料(1)。
3.根据权利要求1或2所述的一种室内装修抗渗透防火材料,其特征在于,所述有色面层(3)内添加有颜料。
4.根据权利要求1或2所述的一种室内装修抗渗透防火材料,其特征在于,所述轻骨料是陶粒、珍珠岩、玻化微珠、之一或其组合。
5.根据权利要求1或2所述的一种室内装修抗渗透防火材料,其特征在于,所述玻璃纤维网格布(2)用来加强抗折强度。
6.根据权利要求5所述的一种室内装修抗渗透防火材料,其特征在于,所述玻璃纤维网格布(2)总层数为4~10层。
7.根据权利要求1或2所述的一种室内装修抗渗透防火材料,其特征在于,所述无纺布(4)总层数为2~7层。
8.根据权利要求1或2所述的一种室内装修抗渗透防火材料,其特征在于,所述无纺布(4)是9g~100g每平方米。
9.根据权利要求1或2所述的一种室内装修抗渗透防火材料,其特征在于,所述板体厚度为10-40mm。
10.一种制备如权利要求1~9所述的一种室内装修抗渗透防火材料的制备方法,其特征在于:所述的具体步骤如下:
(1)首先制备好水渣轻骨料菱镁胶凝材料(1):
A、制备29.4°Bé硫酸镁水:将一份重量的七水硫酸镁加入一份重量的水使硫酸镁溶解成29.4°Bé硫酸镁水;
B、制备有色面浆料(6):取步骤A中一份重量的29.4°Bé硫酸镁水,并向其中加入一份重量的氧化镁轻烧粉、一份重量的白云石粉、一份重量的水渣粉、一份重量的改性剂,并将上述混合物搅拌均匀,得到有色面浆料(6);
C、制备水渣轻骨料菱镁胶凝材料(1)的:取步骤A中一份重量的29.4°Bé硫酸镁水,再向其中加入一份重量的氧化镁轻烧粉、一份重量的白云石粉、一份重量的水渣粉、一份重量的水渣、一份重量陶粒或珍珠岩,以及一份重量的改性剂,搅拌均匀得到水渣轻骨料菱镁胶凝材料(1),并将其按重量分成至少两份;或取步骤A中一份重量的29.4°Bé硫酸镁水,再向其中加入一份重量的氧化镁轻烧粉、一份重量的水渣粉、一份重量的水渣、一份玻化微珠,以及一份重量的改性剂,搅拌均匀得到水渣轻骨料菱镁胶凝材料(1),并将其按重量分成至少两份;
(2)开始制作室内装修抗渗透防火材料:
A、所述的作用于室内防水装修的板材在防火板生产线上成型,将制作好的有色面浆料(6)铺平在PVC或ABS基板上;
B、将相应数量的玻璃纤维网格布(2)压入有色面浆料(6)中,在玻璃纤维网格布(2)上铺设水渣轻骨料菱镁胶凝材料(1),水渣轻骨料菱镁胶凝材料(1)隔着玻璃纤维网格布(2)铺平在有色面浆料(6)上;
C、然后再在水渣轻骨料菱镁胶凝材料(1)上铺放有相应数量的玻璃纤维网格布(2),在此层水渣轻骨料菱镁胶凝材料(1)上铺有无纺布(4);
D、经切割、整平、养护、固化、拆模、四边定尺切割、养护,喷涂有机硅防水剂、烘干固化,形成有机硅防水层(5),喷涂界面剂、烘干固化,形成污涂层(7)。
F、形成由水渣轻骨料菱镁胶凝材料(1)、玻璃纤维网格布(2)、有色面层(3)、无纺布(4)、有机硅防水层(5)、有色面浆料(6)、抗污涂层(7)组成的饰面水渣轻骨料镁硅板。