CN106592379B - A kind of baking-free water-permeable brick and preparation method thereof that epitaxial layer is set - Google Patents
A kind of baking-free water-permeable brick and preparation method thereof that epitaxial layer is set Download PDFInfo
- Publication number
- CN106592379B CN106592379B CN201710002643.3A CN201710002643A CN106592379B CN 106592379 B CN106592379 B CN 106592379B CN 201710002643 A CN201710002643 A CN 201710002643A CN 106592379 B CN106592379 B CN 106592379B
- Authority
- CN
- China
- Prior art keywords
- extension
- layer
- baking
- free water
- protective layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of baking-free water-permeable brick and preparation method thereof that epitaxial layer is arranged, baking-free water-permeable brick include successively from top to bottom base and superficial layer, and the side of brick body is provided with extension protective layer in one week.The present invention proposes a kind of baking-free water-permeable brick that epitaxial layer is arranged; in the extension of brick body, one week extension protective layer is set; brick body is protected; it is avoided to collapse foot or delamination because of collision in carrying or paving; in addition the preparation method of the baking-free water-permeable brick of two kinds of above-mentioned setting epitaxial layers is also proposed; two methods are each advantageous, all have operability.
Description
Technical field
The present invention relates to water-permeable brick technical field more particularly to a kind of baking-free water-permeable brick that epitaxial layer is arranged and its preparation sides
Method.
Background technique
It is generally required in city at present in municipal works such as the bottom surfaces on pavement, cell road surface, shopping mall and building periphery
Middle laying pavement brick, common pavement brick have marble, ceramic tile, glazed tile, cement brick etc..But due to the road surface of mentioned kind
Brick permeability rate is too low, and the use of large area makes rainwater be difficult to infiltrate into underground, destroys underground microenvironment, often results in underground
The problems such as water level decreasing, land subsidence, vegetation survive difficulty, and in rain and snow, ground is easy ponding, influences to pass through.So
Develop water-permeable brick again in recent years, application increases year by year.
Existing water-permeable brick when actually carrying or paving, often collide with by side, is easy to appear after colliding with and collapses foot or de-
Layer defects cause water-permeable brick unusable, cause largely to waste, and not environmentally.
Summary of the invention
It is an object of the invention to propose a kind of baking-free water-permeable brick that epitaxial layer is arranged, it is arranged outside one week in the extension of brick body
Prolong protective layer, brick body is protected, it is avoided to collapse foot or delamination because of collision in carrying or paving.
Another object of the present invention also proposed the preparation method of the baking-free water-permeable brick of two kinds of above-mentioned setting epitaxial layers, and two kinds
Method is each advantageous, all has operability.
To achieve this purpose, the present invention adopts the following technical scheme:
A kind of baking-free water-permeable brick that epitaxial layer is arranged successively includes base and superficial layer, the side of brick body from top to bottom
Bian Yizhou is provided with extension protective layer.
Further description, the extension protective layer are mixed with acquisition by aggregate, Nutrition Soil and fiber clava.
Further description, the component of the extension protective layer by mass percentage, including 30-40% aggregate, 20-
30% Nutrition Soil and 30-50% fiber clava.
Further description, the extension protective layer are tabletted by the mixing of aggregate, Nutrition Soil and fiber clava
What back wall group was formed.
Further description, the component of the extension protective layer by mass percentage, including 5-10 cement, 20-30%
Aggregate, 20-30% Nutrition Soil and 30-50% fiber clava.
Further description, the extension protective layer are equipped with natural fiber silk, the day towards the one side of brick body
Right fiber filament is embedded in brick body.
Further description, a kind of preparation method of the baking-free water-permeable brick of above-mentioned setting epitaxial layer, including following step
It is rapid:
A, it prepares extension protective layer: weighing aggregate, Nutrition Soil and fiber clava by formula rate, be stirred mixing,
Its mixture is suppressed, extension screening glass is obtained；
B, by conventional base mixture injection moulding mold, be placed on shake table and vibrate, make base mixture at
Type mold bottom is paved, and binder layer is obtained；
C, in conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table, in 20-
Compression moulding under the pressure of 30Mpa, obtains adobe；
D, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick；
E, binder is coated in the side of brick body, and extension screening glass is bonded along its side, had after consolidation
There is the baking-free water-permeable brick of epitaxial layer.
Further description, a kind of preparation method of the baking-free water-permeable brick of above-mentioned setting epitaxial layer, including following step
It is rapid:
A, it prepares extension protective layer: weighing aggregate, Nutrition Soil and fiber clava by formula rate, be stirred mixing,
Its mixture is suppressed, extension screening glass is obtained；
B, extension screening glass is disposed around in molding die；
C, by conventional base mixture injection moulding mold, be placed on shake table and vibrate, make base mixture at
Type mold bottom is paved, and binder layer is obtained；
D, in conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table, in 20-
Compression moulding under the pressure of 30Mpa, obtains adobe；
E, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick.
Further description, it is natural in the surface spreading of extension screening glass after compacting obtains extension screening glass in step A
Fiber filament, and it is pressed using silk screen, obtain the extension screening glass that surface is equipped with swingable natural fiber silk.
Further description, a kind of preparation method of the baking-free water-permeable brick of above-mentioned setting epitaxial layer, including following step
It is rapid:
A, it prepares extension protective layer base-material: weighing cement, aggregate, Nutrition Soil and fiber clava by formula rate, add water
It is stirred mixing and obtains extension protective layer base-material, be injected into the outer rim of molding die, obtain extension protective layer；
B, it by the inside casing of conventional base mixture injection moulding mold, is placed on shake table and vibrates, mix base
Material is paved in molding die bottom, obtains binder layer；
C, in the inside casing of conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table；
D, while vibration, the bulkhead in molding die is taken out, makes extension protective layer and binder layer and superficial layer
Side portion blends, and the compression moulding under the pressure of 20-30Mpa, obtains adobe；
E, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick.
Beneficial effects of the present invention:
1, brick body is protected, it is avoided to collapse foot or delamination because of collision in carrying or paving, reduce carrying or paving
When waste；
2, extension screening glass is bonded in the periphery of brick body using binder by a kind of preparation method, without to existing equipment
Or process carries out excessive improvement；
3, extension protective layer and brick body consolidation are structure as a whole by another preparation method, extension screening glass and brick body side
The adhesive strength in face is higher, and when carrying, extension protective layer is not easy to fall off.
Detailed description of the invention
Fig. 1 is the structural schematic diagram of baking-free water-permeable brick of the invention；
Fig. 2 is the schematic diagram of the section structure of baking-free water-permeable brick of the invention.
Wherein: base 1, superficial layer 2, extension protective layer 3, natural fiber silk 31.
Specific embodiment
To further illustrate the technical scheme of the present invention below with reference to the accompanying drawings and specific embodiments.
As shown in Figs. 1-2, it is a kind of be arranged epitaxial layer baking-free water-permeable brick, from top to bottom successively include base and superficial layer,
The side of brick body is provided with extension protective layer 3 in one week.Water-permeable brick in carrying or paving, often collide with by side, is easy
Foot or delamination defect are collapsed in appearance, therefore one week extension protective layer 3 is arranged in the side of brick body in the application, protects to brick body,
It is avoided to collapse foot or delamination because of collision in carrying or paving.
Further description, the extension protective layer 3 are mixed with acquisition by aggregate, Nutrition Soil and fiber clava.
Extension protective layer 3 is prepared by the component for being suitable for plant growth plantation, is after planting protected by extension by the external world
Layer provides nutrient, grow vegetation can along the periphery of superficial layer, makes the baking-free water-permeable brick of the application can be effective when carrying
It avoids collapsing except foot, when in use, nutrient effect can be supplied to by extension protective layer 3, enclose and plant in the side of brick body one
Plant, gap when for blocking brick and brick splicing are given people's naked eyes a kind of illusion in no brick body splicing gap, while being planted in plantation
After object, be conducive to the draining on road surface.
Further description is easy to fall off since the mixture of aggregate and Nutrition Soil sizing intensity is not high, therefore to mixed
It closes and fiber clava is added in material, for enhancing the sizing intensity of extension protective layer, it is avoided to provide aggregate, the Nutrition Soil of nutrition
It is easy to fall off.
Further description, the component of the extension protective layer 3 by mass percentage, including 30-40% aggregate, 20-
30% Nutrition Soil and 30-50% fiber clava.
It should be noted that the Nutrition Soil is powder, mixed using aggregate and Nutrition Soil, can avoid Nutrition Soil and inhale
It is wet blocking, it is unfavorable for plant establishment germination, in addition can provide different nutriment, and it is extension protection that fiber clava, which is added, on the one hand
Layer can have certain fixed form, increase intensity, on the other hand for lockking aggregate and Nutrition Soil, avoid it in brick body incipient species
The aggregate of extension protective layer or Nutrition Soil are influenced by the external world and are lost when son is not grown.Further, natural fiber stick is selected
Shape body, the natural fiber later period is decomposed into organic matter, for providing nutrient.
Further description, the extension protective layer 3 are tabletted by the mixing of aggregate, Nutrition Soil and fiber clava
What back wall group was formed.
Another preferred embodiment, the component of the extension protective layer by mass percentage, including 5-10 cement, 20-30% bone
Material, 20-30% Nutrition Soil and 30-50% fiber clava.
Further description, the extension protective layer is equipped with natural fiber silk 31 towards the one side of brick body, described
Natural fiber silk 31 is embedded in brick body.Extension protective layer 3 is provided with the natural fiber silk 31 embedded in brick body, for enhancing
The close connection of its extension protective layer and brick body avoids extension protective layer from being easy to fall off when carrying.
Further description, a kind of preparation method of the baking-free water-permeable brick of above-mentioned setting epitaxial layer, including following step
It is rapid:
A, it prepares extension protective layer: weighing aggregate, Nutrition Soil and fiber clava by formula rate, be stirred mixing,
Its mixture is suppressed, extension screening glass is obtained；
B, by conventional base mixture injection moulding mold, be placed on shake table and vibrate, make base mixture at
Type mold bottom is paved, and binder layer is obtained；
C, in conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table, in 20-
Compression moulding under the pressure of 30Mpa, obtains adobe；
D, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick；
E, binder is coated in the side of brick body, and extension screening glass is bonded along its side, had after consolidation
There is the baking-free water-permeable brick of epitaxial layer.
Extension screening glass is bonded in the periphery of brick body using binder, without carrying out excessively to existing equipment or process
Improve, only finally factory front wall paste extension screening glass, and can by cutting by the extra extension screening glass of protrusion into
Row segmentation, further instruction, the extension screening glass after segmentation can continue to make when for example size may continue to be used in another brick body
With if when clout undersize, can recycle clout, compacting be can be used again for broken rear progress of shaking.
Another embodiment, a kind of preparation method of the baking-free water-permeable brick of above-mentioned setting epitaxial layer, comprising the following steps:
A, it prepares extension protective layer: weighing aggregate, Nutrition Soil and fiber clava by formula rate, be stirred mixing,
Its mixture is suppressed, extension screening glass is obtained；
B, extension screening glass is disposed around in molding die；
C, by conventional base mixture injection moulding mold, be placed on shake table and vibrate, make base mixture at
Type mold bottom is paved, and binder layer is obtained；
D, in conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table, in 20-
Compression moulding under the pressure of 30Mpa, obtains adobe；
E, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick.
Above-mentioned preparation method is that first extension screening glass is disposed around in molding die and carries out cloth again in cloth, is made outer
Prolonging screening glass can just be combined before not consolidating with base mixture and surface layer mixture, and common compacting consolidation, consolidating is one
Body structure, extension screening glass and the adhesive strength of brick body side are higher, the extension when carrying.
Further description, it is natural in the surface spreading of extension screening glass after compacting obtains extension screening glass in step A
Fiber filament, and it is pressed using silk screen, obtain the extension screening glass that surface is equipped with swingable natural fiber silk.
Usable silk screen is pressed, and the head of natural fiber silk or tail portion are pressed in extension screening glass, makes its portion
It is exceptionally exposed to the surface of extension screening glass, is formed on its surface swingable strand, swingable natural fiber silk is embedding after cloth
Enter in base or superficial layer, keeps extension protective layer closer to the connection of brick body.
Another embodiment, a kind of preparation method of the baking-free water-permeable brick of above-mentioned setting epitaxial layer, comprising the following steps:
A, it prepares extension protective layer base-material: weighing cement, aggregate, Nutrition Soil and fiber clava by formula rate, add water
It is stirred mixing and obtains extension protective layer base-material, be injected into the outer rim of molding die, obtain extension protective layer；
B, it by the inside casing of conventional base mixture injection moulding mold, is placed on shake table and vibrates, mix base
Material is paved in molding die bottom, obtains binder layer 1；
C, in the inside casing of conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table, obtain
Obtain superficial layer 2；
D, while vibration, the bulkhead in molding die is taken out, extension protective layer and binder layer 1 and superficial layer 2 are made
Side portion blend, and the compression moulding under the pressure of 20-30Mpa obtains adobe；
E, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick.
The component of the extension protective layer by mass percentage, including 5-10 cement, 20-30% aggregate, 20-30% nutrition
Soil and 30-50% fiber clava, the addition of cement, which makes extension protect layer, can form mud, and characteristic and base mixture or surface layer are mixed
It is similar to close material, boundary can be re-started after being separated by cloth and blended, its spaced slot is made to disappear.Extension protective layer base-material exists
Extension protecting frame is formed by the bulkhead in molding die when cloth, and carries out cloth layer mixture and surface mixing inside it
Expect, after the completion of cloth, take out bulkhead, its boundary is made to carry out fusion contact, realization extension protecting frame is mutually combined closely with brick body.
Preferably, the water content of extension protective layer base-material is 20%.
The technical principle of the invention is described above in combination with a specific embodiment.These descriptions are intended merely to explain of the invention
Principle, and shall not be construed in any way as a limitation of the scope of protection of the invention.Based on the explanation herein, the technology of this field
Personnel can associate with other specific embodiments of the invention without creative labor, these modes are fallen within
Within protection scope of the present invention.
Claims (7)
1. a kind of baking-free water-permeable brick that epitaxial layer is arranged, it is characterised in that: described from top to bottom successively including base and superficial layer
The side of brick body is provided with extension protective layer in one week；The component of the extension protective layer by mass percentage, including 30-40% bone
Material, 20-30% Nutrition Soil and 30-50% fiber clava；The extension protective layer is by aggregate, Nutrition Soil and fiber clava
Mix what tabletted back wall group was formed.
2. a kind of baking-free water-permeable brick that epitaxial layer is arranged according to claim 1, it is characterised in that: the extension protective layer
Component by mass percentage, including 5-10% cement, 20-30% aggregate, 20-30% Nutrition Soil and 30-50% fiber are rodlike
Body.
3. a kind of baking-free water-permeable brick that epitaxial layer is arranged according to claim 1, it is characterised in that: the extension protective layer
One side towards brick body is equipped with natural fiber silk, and the natural fiber silk is embedded in brick body.
4. a kind of preparation method of baking-free water-permeable brick that epitaxial layer is arranged as described in claim 1, it is characterised in that: including with
Lower step:
A, it prepares extension protective layer: weighing aggregate, Nutrition Soil and fiber clava by formula rate, mixing is stirred, to it
Mixture is suppressed, and extension screening glass is obtained；
B, it by conventional base mixture injection moulding mold, is placed on shake table and vibrates, make base mixture in shaping mould
Tool bottom is paved, and binder layer is obtained；
C, in conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table, 20-30Mpa's
Compression moulding under pressure, obtains adobe；
D, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick；
E, binder is coated in the side of brick body, and extension screening glass is bonded along its side, obtained after consolidation outside having
Prolong the baking-free water-permeable brick of layer.
5. a kind of preparation method of baking-free water-permeable brick that epitaxial layer is arranged as described in claim 1, it is characterised in that: including with
Lower step:
A, it prepares extension protective layer: weighing aggregate, Nutrition Soil and fiber clava by formula rate, mixing is stirred, to it
Mixture is suppressed, and extension screening glass is obtained；
B, extension screening glass is disposed around in molding die；
C, it by conventional base mixture injection moulding mold, is placed on shake table and vibrates, make base mixture in shaping mould
Tool bottom is paved, and binder layer is obtained；
D, in conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table, 20-30Mpa's
Compression moulding under pressure, obtains adobe；
E, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick.
6. a kind of preparation method of baking-free water-permeable brick that epitaxial layer is arranged as claimed in claim 5, it is characterised in that: step A
After middle compacting obtains extension screening glass, in the surface spreading natural fiber silk of extension screening glass, and using silk screen it is carried out by
Pressure obtains the extension screening glass that surface is equipped with swingable natural fiber silk.
7. a kind of preparation method of baking-free water-permeable brick that epitaxial layer is arranged as claimed in claim 2, it is characterised in that: including with
Lower step:
A, it prepares extension protective layer base-material: weighing cement, aggregate, Nutrition Soil and fiber clava by formula rate, water is added to carry out
It is stirred and obtains extension protective layer base-material, be injected into the outer rim of molding die, obtain extension protective layer；
B, it by the inside casing of conventional base mixture injection moulding mold, is placed on shake table and vibrates, base mixture is made to exist
Molding die bottom is paved, and binder layer is obtained；
C, in the inside casing of conventional surface layer mixture injection moulding mold and it will put and vibrate 10-15min on a vibration table；
D, while vibration, the bulkhead in molding die is taken out, the side of extension protective layer Yu binder layer and superficial layer is made
Portion blends, and the compression moulding under the pressure of 20-30Mpa, obtains adobe；
E, by adobe at normal temperature natural consolidation, maintenance, obtain baking-free water-permeable brick.