CN106584927A - 一种阻燃性好的复合塑料制品 - Google Patents
一种阻燃性好的复合塑料制品 Download PDFInfo
- Publication number
- CN106584927A CN106584927A CN201611157437.1A CN201611157437A CN106584927A CN 106584927 A CN106584927 A CN 106584927A CN 201611157437 A CN201611157437 A CN 201611157437A CN 106584927 A CN106584927 A CN 106584927A
- Authority
- CN
- China
- Prior art keywords
- parts
- accounts
- tube layer
- compound tube
- plastic product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明揭示了一种阻燃性好的复合塑料制品，包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚丙烯塑料、阻燃剂、填充剂、分散剂以及增韧剂组成，所述阻燃剂为三氧化二锑，所述填充剂为玻璃粉，所述分散剂为聚乙二醇，所述增韧剂为氯丁橡胶，所述第二复合管层由聚丙烯塑料、阻燃剂、润滑剂、耦合剂以及补强剂组成，所述阻燃剂为磷酸三（2，3‑二氯丙基）酯，所述润滑剂为聚乙烯蜡，所述耦合剂为丙三醇，所述补强剂为硅藻土。本发明采用复合结构设置，具有极佳的阻燃性，安全性高，强度大，质量好。
Description
技术领域
本发明涉及一种阻燃性好的复合塑料制品。
背景技术
聚丙烯，是由丙烯聚合而制得的一种热塑性树脂。聚丙烯为无毒、无臭、无味的乳白色高结晶的聚合物，是目前所有塑料中最轻的品种之一。它对水特别稳定，成型性好，制品表面光泽好。聚丙烯制品存在以下优点：相对密度小，是塑料中最轻的品种之一；良好的力学性能，除耐冲击性外，其他力学性能均比聚乙烯好，成型加工性能好；具有较高的耐热性，连续使用温度可达110-120℃；化学性能好，几乎不吸水，与绝大多数化学药品不反应；质地纯净，无毒性；电绝缘性好；聚丙烯制品的透明性比高密度聚乙烯制品的透明性好。但是聚丙烯制品同样存在阻燃性不佳的缺点。
发明内容
本发明的目的在于提供一种采用复合结构设置，具有极佳的阻燃性，安全性高，强度大，质量好的阻燃性好的复合塑料制品。
本发明的技术方案是，一种阻燃性好的复合塑料制品，包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚丙烯塑料、阻燃剂、填充剂、分散剂以及增韧剂组成，所述阻燃剂为三氧化二锑，所述填充剂为玻璃粉，所述分散剂为聚乙二醇，所述增韧剂为氯丁橡胶，所述第一复合管层各成分所占重量份数分别为：所述聚丙烯塑料占90-98份，所述三氧化二锑占14-19份，所述玻璃粉占37-42份，所述聚乙二醇占6-11份，所述氯丁橡胶占15-20份，所述第二复合管层由聚丙烯塑料、阻燃剂、润滑剂、耦合剂以及补强剂组成，所述阻燃剂为磷酸三（2，3-二氯丙基）酯，所述润滑剂为聚乙烯蜡，所述耦合剂为丙三醇，所述补强剂为硅藻土，所述第二复合管层各成分所占重量份数分别为：所述聚丙烯塑料占84-89份，所述磷酸三（2，3-二氯丙基）酯占10-15份，所述聚乙烯蜡占4-9份，所述丙三醇占2-7份，所述硅藻土占29-33份。
在本发明一个较佳实施例中，所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占91份，所述三氧化二锑占15份，所述玻璃粉占38份，所述聚乙二醇占7份，所述氯丁橡胶占16份。
在本发明一个较佳实施例中，所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占93份，所述三氧化二锑占16份，所述玻璃粉占39份，所述聚乙二醇占8份，所述氯丁橡胶占17份。
在本发明一个较佳实施例中，所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占97份，所述三氧化二锑占18份，所述玻璃粉占41份，所述聚乙二醇占10份，所述氯丁橡胶占19份。
在本发明一个较佳实施例中，所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占85份，所述磷酸三（2，3-二氯丙基）酯占11份，所述聚乙烯蜡占5份，所述丙三醇占3份，所述硅藻土占30份。
在本发明一个较佳实施例中，所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占86份，所述磷酸三（2，3-二氯丙基）酯占12份，所述聚乙烯蜡占6份，所述丙三醇占4份，所述硅藻土占31份。
在本发明一个较佳实施例中，所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占88份，所述磷酸三（2，3-二氯丙基）酯占14份，所述聚乙烯蜡占8份，所述丙三醇占6份，所述硅藻土占32份。
本发明所述为一种阻燃性好的复合塑料制品，采用复合结构设置，具有极佳的阻燃性，安全性高，强度大，质量好。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种阻燃性好的复合塑料制品，包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚丙烯塑料、阻燃剂、填充剂、分散剂以及增韧剂组成，所述阻燃剂为三氧化二锑，所述填充剂为玻璃粉，所述分散剂为聚乙二醇，所述增韧剂为氯丁橡胶，所述第一复合管层各成分所占重量份数分别为：所述聚丙烯塑料占90-98份，所述三氧化二锑占14-19份，所述玻璃粉占37-42份，所述聚乙二醇占6-11份，所述氯丁橡胶占15-20份，所述第二复合管层由聚丙烯塑料、阻燃剂、润滑剂、耦合剂以及补强剂组成，所述阻燃剂为磷酸三（2，3-二氯丙基）酯，所述润滑剂为聚乙烯蜡，所述耦合剂为丙三醇，所述补强剂为硅藻土，所述第二复合管层各成分所占重量份数分别为：所述聚丙烯塑料占84-89份，所述磷酸三（2，3-二氯丙基）酯占10-15份，所述聚乙烯蜡占4-9份，所述丙三醇占2-7份，所述硅藻土占29-33份。
进一步地，所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占91份，所述三氧化二锑占15份，所述玻璃粉占38份，所述聚乙二醇占7份，所述氯丁橡胶占16份。
进一步地，所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占93份，所述三氧化二锑占16份，所述玻璃粉占39份，所述聚乙二醇占8份，所述氯丁橡胶占17份。
进一步地，所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占97份，所述三氧化二锑占18份，所述玻璃粉占41份，所述聚乙二醇占10份，所述氯丁橡胶占19份。
进一步地，所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占85份，所述磷酸三（2，3-二氯丙基）酯占11份，所述聚乙烯蜡占5份，所述丙三醇占3份，所述硅藻土占30份。
进一步地，所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占86份，所述磷酸三（2，3-二氯丙基）酯占12份，所述聚乙烯蜡占6份，所述丙三醇占4份，所述硅藻土占31份。
进一步地，所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占88份，所述磷酸三（2，3-二氯丙基）酯占14份，所述聚乙烯蜡占8份，所述丙三醇占6份，所述硅藻土占32份。
另外，可通过调节产品各成分的不同重量份数，使得得到的产品性能高低不一。
本发明所述为一种阻燃性好的复合塑料制品，采用复合结构设置，具有极佳的阻燃性，安全性高，强度大，质量好。
以上所述仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (7)
1.一种阻燃性好的复合塑料制品，其特征在于：包括外部的第一复合管层和内部的第二复合管层，所述第一复合管层由聚丙烯塑料、阻燃剂、填充剂、分散剂以及增韧剂组成，所述阻燃剂为三氧化二锑，所述填充剂为玻璃粉，所述分散剂为聚乙二醇，所述增韧剂为氯丁橡胶，所述第一复合管层各成分所占重量份数分别为：所述聚丙烯塑料占90-98份，所述三氧化二锑占14-19份，所述玻璃粉占37-42份，所述聚乙二醇占6-11份，所述氯丁橡胶占15-20份，所述第二复合管层由聚丙烯塑料、阻燃剂、润滑剂、耦合剂以及补强剂组成，所述阻燃剂为磷酸三（2，3-二氯丙基）酯，所述润滑剂为聚乙烯蜡，所述耦合剂为丙三醇，所述补强剂为硅藻土，所述第二复合管层各成分所占重量份数分别为：所述聚丙烯塑料占84-89份，所述磷酸三（2，3-二氯丙基）酯占10-15份，所述聚乙烯蜡占4-9份，所述丙三醇占2-7份，所述硅藻土占29-33份。
2.根据权利要求1所述的阻燃性好的复合塑料制品，其特征在于：所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占91份，所述三氧化二锑占15份，所述玻璃粉占38份，所述聚乙二醇占7份，所述氯丁橡胶占16份。
3.根据权利要求1所述的阻燃性好的复合塑料制品，其特征在于：所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占93份，所述三氧化二锑占16份，所述玻璃粉占39份，所述聚乙二醇占8份，所述氯丁橡胶占17份。
4.根据权利要求1所述的阻燃性好的复合塑料制品，其特征在于：所述第一复合管层各成分所占重量份数具体为：所述聚丙烯塑料占97份，所述三氧化二锑占18份，所述玻璃粉占41份，所述聚乙二醇占10份，所述氯丁橡胶占19份。
5.根据权利要求1所述的阻燃性好的复合塑料制品，其特征在于：所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占85份，所述磷酸三（2，3-二氯丙基）酯占11份，所述聚乙烯蜡占5份，所述丙三醇占3份，所述硅藻土占30份。
6.根据权利要求1所述的阻燃性好的复合塑料制品，其特征在于：所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占86份，所述磷酸三（2，3-二氯丙基）酯占12份，所述聚乙烯蜡占6份，所述丙三醇占4份，所述硅藻土占31份。
7.根据权利要求1所述的阻燃性好的复合塑料制品，其特征在于：所述第二复合管层各成分所占重量份数具体为：所述聚丙烯塑料占88份，所述磷酸三（2，3-二氯丙基）酯占14份，所述聚乙烯蜡占8份，所述丙三醇占6份，所述硅藻土占32份。