CN106554732A - 一种人造板用胶粘剂的制备方法 - Google Patents
一种人造板用胶粘剂的制备方法 Download PDFInfo
- Publication number
- CN106554732A CN106554732A CN201510630915.5A CN201510630915A CN106554732A CN 106554732 A CN106554732 A CN 106554732A CN 201510630915 A CN201510630915 A CN 201510630915A CN 106554732 A CN106554732 A CN 106554732A
- Authority
- CN
- China
- Prior art keywords
- added
- resulting solution
- stirring
- preparation
- artificial board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了人造板用胶粘剂的制备方法,包括以下步骤:将滑石粉加入一定量的水中,搅拌至充分溶解;将步骤一所得溶液加热,调节PH,再先后加入淀粉和聚醚多元醇,边加热边搅拌;向步骤二所得溶液加入偏硼酸钠和苯甲酸钠,调节PH,再加入尿素搅拌;向步骤三所得溶液加入高分子量热塑性树脂,加热搅拌,待自然冷却即得。本发明的有益效果:不释放有毒有害气体,具有良好的环境协调性,解决人造板带来的室内空气中的甲醛污染问题;该胶粘剂相对于现有粘剂,挥发性有机物更低,环保性能更优。
Description
技术领域
本发明涉及一种板材胶粘剂,特别涉及一种人造板用胶粘剂的制备方法。
背景技术
随着人民生活水平的提高和建筑、装饰装修、包装等行业的持续稳定发展,我国人造板产量迅速增长,人造板生产中普遍采用的胶粘剂是甲醛系合成树脂,主要是脲醛树脂及其改性产品。经过多年的努力,我国人造板胶粘剂生产水平有了很大提高,人造板及其制品环保特性有了很大改善,但是不能完全消除其制品甲醛释放,并且不少企业生产的人造板及其制品(家具、木地板、室内木质装饰材料等)仍然存在着较为严重的甲醛释放问题,是室内空气污染中甲醛污染的主要来源。
发明内容
本发明的目的在于克服现有技术中所存在的上述不足,提供一种人造板用胶粘剂的制备方法。
为了实现上述发明目的,本发明提供了以下技术方案:
一种人造板用胶粘剂的制备方法,包括以下步骤:
步骤一、将滑石粉加入一定量的水中,搅拌至充分溶解;
步骤二、将步骤一所得溶液加热到60-70℃,调节PH至6-6.5,再先后加入淀粉和聚醚多元醇,边加热边搅拌20-50分钟;
步骤三、向步骤二所得溶液加入偏硼酸钠和苯甲酸钠,调节PH至7-7.5,再加入尿素搅拌30-40分钟;
步骤四、向步骤三所得溶液加入高分子量热塑性树脂,加热搅拌30-50分钟,待自然冷却即得。
与现有技术相比,本发明的有益效果:不释放有毒有害气体,具有良好的环境协调性,解决人造板带来的室内空气中的甲醛污染问题;该胶粘剂相对于现有粘剂,挥发性有机物更低,环保性能更优。
具体实施方式
下面结合试验例及具体实施方式对本发明作进一步的详细描述。但不应将此理解为本发明上述主题的范围仅限于以下的实施例,凡基于本发明内容所实现的技术均属于本发明的范围。
实施例1:
一种人造板用胶粘剂的制备方法,包括以下步骤:
步骤一、将滑石粉加入一定量的水中,搅拌至充分溶解;
步骤二、将步骤一所得溶液加热到65℃,调节PH至6,再先后加入淀粉和聚醚多元醇,边加热边搅拌35分钟;
步骤三、向步骤二所得溶液加入偏硼酸钠和苯甲酸钠,调节PH至7,再加入尿素搅拌30分钟;
步骤四、向步骤三所得溶液加入高分子量热塑性树脂,加热搅拌30分钟,待自然冷却即得。
Claims (1)
1.一种人造板用胶粘剂的制备方法,其特征在于,包括以下步骤:
步骤一、将滑石粉加入一定量的水中,搅拌至充分溶解;
步骤二、将步骤一所得溶液加热到60-70℃,调节PH至6-6.5,再先后加入淀粉和聚醚多元醇,边加热边搅拌20-50分钟;
步骤三、向步骤二所得溶液加入偏硼酸钠和苯甲酸钠,调节PH至7-7.5,再加入尿素搅拌30-40分钟;
步骤四、向步骤三所得溶液加入高分子量热塑性树脂,加热搅拌30-50分钟,待自然冷却即得。