CN106542797A - Method for repairing marble table crack - Google Patents
Method for repairing marble table crack Download PDFInfo
- Publication number
- CN106542797A CN106542797A CN201610999130.XA CN201610999130A CN106542797A CN 106542797 A CN106542797 A CN 106542797A CN 201610999130 A CN201610999130 A CN 201610999130A CN 106542797 A CN106542797 A CN 106542797A
- Authority
- CN
- China
- Prior art keywords
- marble
- natural marble
- powder
- natural
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method for repairing cracks on a marble table top, which comprises the following specific steps: 1) washing the broken stone chips and impurities at the cracks of the natural marble by using a high-pressure water gun; 2) injecting the base layer slurry into cracks of the natural marble, and scraping the redundant base layer slurry until the surface of the base layer slurry is 1-2mm lower than that of the natural marble; the base layer slurry is prepared by mixing the following raw materials in percentage by weight: 2-5% of lignin, 1-3% of zeolite powder, 23-26% of silicon carbide powder, 45-48% of sulphoaluminate cement and 25-28% of water; the area repaired by the method is not easy to crack and can recover the natural texture of the marble.
Description
Technical field
The present invention relates to a kind of restorative procedure of marble countertop crackle.
Background technology
Natural marble is natural and tripping due to bright and clean exquisiteness after polishing, texture, has very high dicoration and is widely used as house
The important materials of tool table top, but natural marble threshold stoneshot is not enough, easy embrittlement and breed bacteria, after cracking
Repaired by conventional joint filling and be difficult to recover natural texture, affect attractive in appearance, and the region after repairing easily is ftractureed again.
The content of the invention
The technical problem to be solved is the shortcoming for overcoming above prior art：A kind of area after reparation is provided
Domain is not easy to crack, can recover marble natural texture marble countertop crackle restorative procedure.
The technical solution of the present invention is as follows：A kind of restorative procedure of marble countertop crackle, including walking in detail below
Suddenly：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Basic unit's slurry is injected into into natural marble cracks, unnecessary basic unit's slurry is then struck off and is less than to basic unit's pulp surface
Natural marble surface 1-2mm；Basic unit's slurry by weight percentage, is mixed by following raw material：Lignin 2 ~ 5%,
Zeolite powder 1 ~ 3%, carborundum powder 23 ~ 26%, sulphate aluminium cement 45 ~ 48%, water 25 ~ 28%；
3）Then natural marble cracks are filled to higher than natural marble surface 0.5-1mm with top layer slurry, places 24-
48 hours；The top layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2 ~ 5%, gas phase titanium dioxide
Silicon 20 ~ 22%, carborundum powder 3 ~ 8%, natural marble original powder 15 ~ 20%, sulphate aluminium cement 30 ~ 35%, water 20 ~ 25%；
4）Polishing, polishing step 3）Top layer slurry after middle filling is extremely flushed with natural marble surface, then at overall polishing
Reason.
Preferably, the mean diameter of the carborundum powder is 200-500 nanometers.
Used as optimization, the natural marble original powder is of the same race with natural marble to be repaired or with the marble of block
Stone material powder of the mean diameter of chip or fragment crushing grinding in the course of processing for 150-200 nanometers.
The invention has the beneficial effects as follows：The present invention combines to repair natural marble threshold by the different formulations of top layer and basic unit
Stony fracture stricture of vagina so that restoring area is difficult to ftracture again, can effectively recover Dali by adding the former stone material powder of special ratios
Stone natural texture.
Specific embodiment
The present invention is described in further details with specific embodiment below, but the present invention is not only limited in detail below in fact
Apply example.
Embodiment one
A kind of restorative procedure of marble countertop crackle, including step in detail below：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Basic unit's slurry is injected into into natural marble cracks, unnecessary basic unit's slurry is then struck off and is less than to basic unit's pulp surface
Natural marble surface 1-2mm；Basic unit's slurry by weight percentage, is mixed by following raw material：Lignin 2 ~ 5%,
Zeolite powder 1 ~ 3%, carborundum powder 23 ~ 26%, sulphate aluminium cement 45 ~ 48%, water 25 ~ 28%；
3）Then natural marble cracks are filled to higher than natural marble surface 0.5-1mm with top layer slurry, places 24-
48 hours；The top layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2 ~ 5%, gas phase titanium dioxide
Silicon 20 ~ 22%, carborundum powder 3 ~ 8%, natural marble original powder 15 ~ 20%, sulphate aluminium cement 30 ~ 35%, water 20 ~ 25%；The day
So marble original powder be of the same race with natural marble to be repaired or the Marble processing with block during chip or fragment
Stone material powder of the mean diameter of crushing grinding for 150-200 nanometers.
4）Polishing, polishing step 3）Top layer slurry after middle filling is to flushing with natural marble surface, then overall to throw
Optical processing
Embodiment two
A kind of restorative procedure of marble countertop crackle, including step in detail below：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Basic unit's slurry is injected into into natural marble cracks, unnecessary basic unit's slurry is then struck off and is less than to basic unit's pulp surface
Natural marble surface 1mm；Basic unit's slurry by weight percentage, is mixed by following raw material：Lignin 2%, zeolite
Powder 2%, carborundum powder 26% of the mean diameter for 200-500 nanometers, sulphate aluminium cement 45%, water 25%；
3）Then natural marble cracks are filled to higher than natural marble surface 0.5mm with top layer slurry, places 24-48
Hour；The top layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2%, aerosil
22%, carborundum powder 8%, natural marble original powder 15%, sulphate aluminium cement 30%, water 23%；Natural marble original powder be with
Natural marble to be repaired is of the same race or Marble processing with block during chip or fragment crushing grinding it is flat
Particle diameter is the stone material powder of 150-200 nanometers.
4）Polishing, polishing step 3）Top layer slurry after middle filling is to flushing with natural marble surface, then overall to throw
Optical processing
Embodiment three
A kind of restorative procedure of marble countertop crackle, including step in detail below：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Basic unit's slurry is injected into into natural marble cracks, unnecessary basic unit's slurry is then struck off and is less than to basic unit's pulp surface
Natural marble surface 2mm；Basic unit's slurry by weight percentage, is mixed by following raw material：Lignin 2%, zeolite
Powder 1%, carborundum powder 26%, sulphate aluminium cement 45%, water 26%；
3）Then natural marble cracks are filled to higher than natural marble surface 1mm with top layer slurry, is placed 48 hours；
The top layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 5%, aerosil 20%, carbonization
Silica flour 5%, natural marble original powder 20%, sulphate aluminium cement 30%, water 20%；
4）Polishing, polishing step 3）Top layer slurry after middle filling is extremely flushed with natural marble surface, then at overall polishing
Reason.Natural marble original powder be of the same race with natural marble to be repaired or the Marble processing with block during
Chip or fragment crushing grinding mean diameter for 150-200 nanometers stone material powder.
The above is only the feature implementation example of the present invention, the scope of the present invention is not limited in any way.It is all to adopt same
The technical scheme formed Deng exchange or equivalence replacement, all falls within rights protection scope of the present invention.
Claims (3)
1. a kind of restorative procedure of marble countertop crackle, it is characterised in that：Including step in detail below：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Basic unit's slurry is injected into into natural marble cracks, unnecessary basic unit's slurry is then struck off and is less than to basic unit's pulp surface
Natural marble surface 1-2mm；Basic unit's slurry by weight percentage, is mixed by following raw material：Lignin 2 ~ 5%,
Zeolite powder 1 ~ 3%, carborundum powder 23 ~ 26%, sulphate aluminium cement 45 ~ 48%, water 25 ~ 28%；
3）Then natural marble cracks are filled to higher than natural marble surface 0.5-1mm with top layer slurry, places 24-
48 hours；The top layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2 ~ 5%, gas phase titanium dioxide
Silicon 20 ~ 22%, carborundum powder 3 ~ 8%, natural marble original powder 15 ~ 20%, sulphate aluminium cement 30 ~ 35%, water 20 ~ 25%；
4）Polishing, polishing step 3）Top layer slurry after middle filling is extremely flushed with natural marble surface, then at overall polishing
Reason.
2. the restorative procedure of marble countertop crackle according to claim 1, it is characterised in that：The carborundum powder it is flat
Particle diameter is 200-500 nanometers.
3. the restorative procedure of marble countertop crackle according to claim 1, it is characterised in that：The natural marble is former
Powder be of the same race with natural marble to be repaired or the Marble processing with block during chip or fragment crushing grinding and
Into mean diameter for 150-200 nanometers stone material powder.