CN106542797B - Method for repairing marble table crack - Google Patents
Method for repairing marble table crack Download PDFInfo
- Publication number
- CN106542797B CN106542797B CN201610999130.XA CN201610999130A CN106542797B CN 106542797 B CN106542797 B CN 106542797B CN 201610999130 A CN201610999130 A CN 201610999130A CN 106542797 B CN106542797 B CN 106542797B
- Authority
- CN
- China
- Prior art keywords
- marble
- natural marble
- powder
- natural
- slurry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a method for repairing cracks on a marble table top, which comprises the following specific steps: 1) washing the broken stone chips and impurities at the cracks of the natural marble by using a high-pressure water gun; 2) injecting the base layer slurry into cracks of the natural marble, and scraping the redundant base layer slurry until the surface of the base layer slurry is 1-2mm lower than that of the natural marble; the base layer slurry is prepared by mixing the following raw materials in percentage by weight: 2-5% of lignin, 1-3% of zeolite powder, 23-26% of silicon carbide powder, 45-48% of sulphoaluminate cement and 25-28% of water; the area repaired by the method is not easy to crack and can recover the natural texture of the marble.
Description
Technical field
The present invention relates to a kind of restorative procedures of marble countertop crackle.
Background technology
For natural marble due to bright and clean exquisiteness after polishing, texture is natural and tripping, has very high dicoration and is widely used as house
Have the important materials of table top, but natural marble threshold stoneshot is insufficient, is easy embrittlement and grows bacterium, after cracking
It is difficult to restore natural texture by conventional joint filling repairing, influences beauty, and the region after reparation is easy to crack again.
Invention content
The technical problem to be solved by the present invention is to the shortcomings that overcoming the above prior art：A kind of area after reparation is provided
Domain is not easy to crack, can restore marble natural texture marble countertop crackle restorative procedure.
Technical solution of the invention is as follows：A kind of restorative procedure of marble countertop crackle, including walk in detail below
Suddenly：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Base's slurry is injected into natural marble cracks, then strikes off extra base's slurry to base's pulp surface
Less than natural marble surface 1-2mm；Base's slurry by weight percentage, is mixed by following raw material：Lignin 2
~ 5%, zeolite powder 1 ~ 3%, carborundum powder 23 ~ 26%, sulphate aluminium cement 45 ~ 48%, water 25 ~ 28%；
3）Then natural marble cracks are filled to higher than natural marble surface 0.5-1mm with surface layer slurry, is put
It sets 24-48 hours；The surface layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2 ~ 5%, gas phase two
Silica 20 ~ 22%, carborundum powder 3 ~ 8%, natural marble original powder 15 ~ 20%, sulphate aluminium cement 30 ~ 35%, water 20 ~ 25%；
4）Polishing, polishing step 3）Surface layer slurry after middle filling is then whole to throw to being flushed with natural marble surface
Light processing.
Preferably, the average grain diameter of the carborundum powder is 200-500 nanometers.
As an optimization, the natural marble original powder for the natural marble to be repaired is of the same race or marble with block
The stone material powder that average grain diameter made of clast or fragment crushing grinding in process is 150-200 nanometers.
The beneficial effects of the invention are as follows：The present invention is by the different formulations of surface layer and base in conjunction with repairing natural marble
Threshold stony fracture line so that restoring area is not easy to crack again, and the former stone material powder by the way that special ratios are added can effectively restore
Marble natural texture.
Specific implementation mode
The present invention is described in further details with specific embodiment below, but the present invention is not only limited in detail below in fact
Apply example.
Embodiment one
A kind of restorative procedure of marble countertop crackle, including step in detail below：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Base's slurry is injected into natural marble cracks, then strikes off extra base's slurry to base's pulp surface
Less than natural marble surface 1-2mm；Base's slurry by weight percentage, is mixed by following raw material：Lignin 2
~ 5%, zeolite powder 1 ~ 3%, carborundum powder 23 ~ 26%, sulphate aluminium cement 45 ~ 48%, water 25 ~ 28%；
3）Then natural marble cracks are filled to higher than natural marble surface 0.5-1mm with surface layer slurry, is put
It sets 24-48 hours；The surface layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2 ~ 5%, gas phase two
Silica 20 ~ 22%, carborundum powder 3 ~ 8%, natural marble original powder 15 ~ 20%, sulphate aluminium cement 30 ~ 35%, water 20 ~ 25%；Institute
State natural marble original powder for during the Marble processing of the same race or with block with the natural marble to be repaired clast or
The stone material powder that average grain diameter made of fragment crushing grinding is 150-200 nanometers.
4）Polishing, polishing step 3）Surface layer slurry after middle filling is then whole to throw to being flushed with natural marble surface
Light processing
Embodiment two
A kind of restorative procedure of marble countertop crackle, including step in detail below：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Base's slurry is injected into natural marble cracks, then strikes off extra base's slurry to base's pulp surface
Less than natural marble surface 1mm；Base's slurry by weight percentage, is mixed by following raw material：Lignin 2%,
Zeolite powder 2%, the carborundum powder 26% that average grain diameter is 200-500 nanometers, sulphate aluminium cement 45%, water 25%；
3）Then natural marble cracks are filled to higher than natural marble surface 0.5mm with surface layer slurry, is placed
24-48 hours；The surface layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2%, gas phase titanium dioxide
Silicon 22%, carborundum powder 8%, natural marble original powder 15%, sulphate aluminium cement 30%, water 23%；The natural marble original powder is
Made of clast or fragment crushing grinding with the natural marble to be repaired during Marble processing of the same race or with block
The stone material powder that average grain diameter is 150-200 nanometers.
4）Polishing, polishing step 3）Surface layer slurry after middle filling is then whole to throw to being flushed with natural marble surface
Light processing
Embodiment three
A kind of restorative procedure of marble countertop crackle, including step in detail below：
1）The stone fragment of natural marble cracks, impurity are rinsed well with giant；
2）Base's slurry is injected into natural marble cracks, then strikes off extra base's slurry to base's pulp surface
Less than natural marble surface 2mm；Base's slurry by weight percentage, is mixed by following raw material：Lignin 2%,
Zeolite powder 1%, carborundum powder 26%, sulphate aluminium cement 45%, water 26%；
3）Then natural marble cracks are filled to higher than natural marble surface 1mm with surface layer slurry, places 48
Hour；The surface layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 5%, aerosil
20%, carborundum powder 5%, natural marble original powder 20%, sulphate aluminium cement 30%, water 20%；
4）Polishing, polishing step 3）Surface layer slurry after middle filling is then whole to throw to being flushed with natural marble surface
Light processing.The natural marble original powder is the Marble processing mistake of the same race or with block with the natural marble to be repaired
The stone material powder that average grain diameter made of clast or fragment crushing grinding in journey is 150-200 nanometers.
The feature implementation example that the above is only the present invention, is not limited in any way the scope of the present invention.It is all to use together
The technical solution formed Deng exchange or equivalence replacement, all falls within rights protection scope of the present invention.
Claims (2)
1. a kind of restorative procedure of marble countertop crackle, it is characterised in that：Including step in detail below：
1) stone fragment of natural marble cracks, impurity are rinsed well with giant；
2) base's slurry is injected into natural marble cracks, then strikes off extra base's slurry to base's pulp surface and is less than
Natural marble surface 1-2mm；Base's slurry by weight percentage, is mixed by following raw material：Lignin 2~
5%, zeolite powder 1~3%, carborundum powder 23~26%, sulphate aluminium cement 45~48%, water 25~28%；
3) it and then with surface layer slurry by natural marble cracks fills to higher than natural marble surface 0.5-1mm, places 24-
48 hours；The surface layer slurry by weight percentage, is mixed by following raw material：Montmorillonite powder 2~5%, gas phase dioxy
SiClx 20~22%, carborundum powder 3~8%, natural marble original powder 15~20%, sulphate aluminium cement 30~35%, water 20
~25%；
4) polishing, polishing step 3) in surface layer slurry after filling to being flushed with natural marble surface, then at whole polishing
Reason；
During the natural marble original powder is the Marble processing of the same race or with block with the natural marble to be repaired
The stone material powder that average grain diameter made of clast or fragment crushing grinding is 150-200 nanometers.
2. the restorative procedure of marble countertop crackle according to claim 1, it is characterised in that：The carborundum powder is put down
Equal grain size is 200-500 nanometers.