CN107235696A - A kind of concrete building brick and preparation method thereof - Google Patents
A kind of concrete building brick and preparation method thereof Download PDFInfo
- Publication number
- CN107235696A CN107235696A CN201710444392.4A CN201710444392A CN107235696A CN 107235696 A CN107235696 A CN 107235696A CN 201710444392 A CN201710444392 A CN 201710444392A CN 107235696 A CN107235696 A CN 107235696A
- Authority
- CN
- China
- Prior art keywords
- parts
- concrete building
- building brick
- steam
- cinder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of concrete building brick and preparation method thereof, the concrete building brick is made up of the component of following parts by weight：45 80 parts of cinder, 20 40 parts of waste gypsum, 8 20 parts of zeolite powder, 20 30 parts of cement, 36 parts of naphthalene water reducer, 36 parts of antifreezing agent, 15 parts of tricalcium aluminate, 3 10 parts of redispersable latex powder, 25 parts of cellulose ether, 13 parts of salt resistance retarder, 5 12 parts of emulsified asphalt, 40 55 parts of water.Compared with prior art, the concrete building brick in the present invention can be recycled to cinder, waste gypsum, both environmentally friendly, be saved material again.
Description
Technical field
The present invention relates to building material technical field, more particularly to a kind of concrete building brick and preparation method thereof.
Background technology
A large amount of waste residues, waste material can be produced in industrial production, for example, the cinder that coal works is produced, the barren rock of job site throughout the year
Cream etc., these solid refuses are not often processed in time, a large amount of to stack meeting land occupation and pollute surrounding environment, if
Being discharged into water system can cause river to silt up, and toxic chemical substance therein can also cause harm to human body and biology.At present, solid
The treatment measures of rubbish are limited, for example, fill, burn, this kind of mode can both expend substantial contribution, while can also be caused to environment
Pollution.
The content of the invention
It is an object of the invention to provide a kind of concrete building brick and preparation method thereof, it both can be to cinder, waste gypsum etc.
Waste material is recycled, while saving production cost.
To achieve the above object, the present invention provides following technical scheme：
A kind of concrete building brick, it is made up of the component of following parts by weight：45-80 parts of cinder, waste gypsum 20-40
Part, 8-20 parts of zeolite powder, 20-30 parts of cement, 3-6 parts of naphthalene water reducer, 3-6 parts of antifreezing agent, 1-5 parts of tricalcium aluminate can divide again
Dissipate 3-10 parts of latex powder, 2-5 parts of cellulose ether, 1-3 parts of salt resistance retarder, 5-12 parts of emulsified asphalt, 40-55 parts of water.
Preferably, the concrete building brick is made up of the component of following parts by weight：66 parts of cinder, 25 parts of waste gypsum, boiling
14 parts of stone flour, 22 parts of cement, 3.5 parts of naphthalene water reducer, 5 parts of antifreezing agent, 3 parts of tricalcium aluminate, 6 parts of redispersable latex powder is fine
Plain 3 parts of the ether of dimension, 1.8 parts of salt resistance retarder, 8 parts of emulsified asphalt, 45 parts of water.
Preferably, the concrete building brick is made up of the component of following parts by weight：70 parts of cinder, 35 parts of waste gypsum, boiling
15 parts of stone flour, 22 parts of cement, 4 parts of naphthalene water reducer, 4 parts of antifreezing agent, 3 parts of tricalcium aluminate, 8 parts of redispersable latex powder, fiber
Plain 2 parts of ether, 1 part of salt resistance retarder, 10 parts of emulsified asphalt, 50 parts of water.
Preferably, the preparation method of described concrete building brick, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) cinder, waste gypsum and zeolite powder are added in ball crusher the grinding that adds water, until solid particle crosses 220-250
Mesh sieve, obtains preparing batch mixing；
(3) the preparation batch mixing in step (2), cement are added into mixer, mixer uniform stirring is added after 2-4 minutes
Redispersable latex powder, emulsified asphalt, continue stir 2-6 minutes, sequentially add naphthalene water reducer, antifreezing agent, tricalcium aluminate,
Cellulose ether and salt resistance retarder, after stirring 3-5 minutes, slurry of laying bricks；
(4) slurry of laying bricks in step (3) is cast in stock mould, slurry of laying bricks is cooled and shaped in stock mould by normal temperature
After obtain adobe body；
(5) that adobe body is put into steam-cured room is steam-cured, and temperature is 48-58 degree, steam-cured time 3-5 hours, steam-cured good adobe
The fragment of brick of all size is machined to by cutting, then fragment of brick is put into still kettle carries out high-pressure steaming and cultivating, steam curing temperature 200-
215 degree, most recession pressure, cooling went out still kettle and obtained product at 5-7 hours the high-pressure steaming and cultivating time.
Preferably, in high-pressure steaming and cultivating, by the Stress control of still kettle in 1.2-1.5Mpa, 210 degree of steam curing temperature, high pressure
The steam-cured time was at 6 hours.
Compared with prior art, the beneficial effects of the invention are as follows：
Concrete building brick in the present invention to cinder, waste gypsum consume and profit using cinder, waste gypsum as primary raw material
Laying bricks required for being prepared into social production with it, thus it is both environmentally friendly, cost of material is saved again；At the same time, also added with naphthalene
The raw materials such as based water reducer, antifreezing agent, redispersable latex powder, cellulose ether and salt resistance retarder so that the coagulation in the present invention
Soil is laid bricks, and mechanical property is good, and compression strength is high.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one：
A kind of concrete building brick, it is made up of the component of following parts by weight：66 parts of cinder, 25 parts of waste gypsum, zeolite
14 parts of powder, 22 parts of cement, 3.5 parts of naphthalene water reducer, 5 parts of antifreezing agent, 3 parts of tricalcium aluminate, 6 parts of redispersable latex powder, fiber
Plain 3 parts of ether, 1.8 parts of salt resistance retarder, 8 parts of emulsified asphalt, 45 parts of water.
The preparation method of described concrete building brick, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) cinder, waste gypsum and zeolite powder are added in ball crusher the grinding that adds water, until solid particle crosses 220-250
Mesh sieve, obtains preparing batch mixing；
(3) the preparation batch mixing in step (2), cement are added into mixer, mixer uniform stirring is added after 2-4 minutes
Redispersable latex powder, emulsified asphalt, continue stir 2-6 minutes, sequentially add naphthalene water reducer, antifreezing agent, tricalcium aluminate,
Cellulose ether and salt resistance retarder, after stirring 3-5 minutes, slurry of laying bricks；
(4) slurry of laying bricks in step (3) is cast in stock mould, slurry of laying bricks is cooled and shaped in stock mould by normal temperature
After obtain adobe body；
(5) that adobe body is put into steam-cured room is steam-cured, and temperature is 48-58 degree, steam-cured time 3-5 hours, steam-cured good adobe
The fragment of brick of all size is machined to by cutting, then fragment of brick is put into still kettle carries out high-pressure steaming and cultivating, steam curing temperature 200-
215 degree, most recession pressure, cooling went out still kettle and obtained product at 5-7 hours the high-pressure steaming and cultivating time.
Embodiment two：
A kind of concrete building brick, it is made up of the component of following parts by weight：70 parts of cinder, 35 parts of waste gypsum, zeolite
15 parts of powder, 22 parts of cement, 4 parts of naphthalene water reducer, 4 parts of antifreezing agent, 3 parts of tricalcium aluminate, 8 parts of redispersable latex powder, cellulose
2 parts of ether, 1 part of salt resistance retarder, 10 parts of emulsified asphalt, 50 parts of water.
The preparation method of described concrete building brick, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) cinder, waste gypsum and zeolite powder are added in ball crusher the grinding that adds water, until solid particle crosses 220-250
Mesh sieve, obtains preparing batch mixing；
(3) the preparation batch mixing in step (2), cement are added into mixer, mixer uniform stirring is added after 2-4 minutes
Redispersable latex powder, emulsified asphalt, continue stir 2-6 minutes, sequentially add naphthalene water reducer, antifreezing agent, tricalcium aluminate,
Cellulose ether and salt resistance retarder, after stirring 3-5 minutes, slurry of laying bricks；
(4) slurry of laying bricks in step (3) is cast in stock mould, slurry of laying bricks is cooled and shaped in stock mould by normal temperature
After obtain adobe body；
(5) that adobe body is put into steam-cured room is steam-cured, and temperature is 48-58 degree, steam-cured time 3-5 hours, steam-cured good adobe
The fragment of brick of all size is machined to by cutting, then fragment of brick is put into still kettle carries out high-pressure steaming and cultivating, steam curing temperature 200-
215 degree, most recession pressure, cooling went out still kettle and obtained product at 5-7 hours the high-pressure steaming and cultivating time.
Embodiment three：
A kind of concrete building brick, it is made up of the component of following parts by weight：45 parts of cinder, 20 parts of waste gypsum, zeolite
8 parts of powder, 20 parts of cement, 3 parts of naphthalene water reducer, 3 parts of antifreezing agent, 1 part of tricalcium aluminate, 3 parts of redispersable latex powder, cellulose ether
2 parts, 1 part of salt resistance retarder, 5 parts of emulsified asphalt, 40 parts of water.
The preparation method of described concrete building brick, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) cinder, waste gypsum and zeolite powder are added in ball crusher the grinding that adds water, until solid particle crosses 220-250
Mesh sieve, obtains preparing batch mixing；
(3) the preparation batch mixing in step (2), cement are added into mixer, mixer uniform stirring is added after 2-4 minutes
Redispersable latex powder, emulsified asphalt, continue stir 2-6 minutes, sequentially add naphthalene water reducer, antifreezing agent, tricalcium aluminate,
Cellulose ether and salt resistance retarder, after stirring 3-5 minutes, slurry of laying bricks；
(4) slurry of laying bricks in step (3) is cast in stock mould, slurry of laying bricks is cooled and shaped in stock mould by normal temperature
After obtain adobe body；
(5) that adobe body is put into steam-cured room is steam-cured, and temperature is 48-58 degree, steam-cured time 3-5 hours, steam-cured good adobe
The fragment of brick of all size is machined to by cutting, then fragment of brick is put into still kettle carries out high-pressure steaming and cultivating, steam curing temperature 200-
215 degree, most recession pressure, cooling went out still kettle and obtained product at 5-7 hours the high-pressure steaming and cultivating time.
Example IV：
A kind of concrete building brick, it is made up of the component of following parts by weight：80 parts of cinder, 40 parts of waste gypsum, zeolite
20 parts of powder, 30 parts of cement, 6 parts of naphthalene water reducer, 6 parts of antifreezing agent, 5 parts of tricalcium aluminate, 10 parts of redispersable latex powder, cellulose
5 parts of ether, 3 parts of salt resistance retarder, 12 parts of emulsified asphalt, 55 parts of water.
The preparation method of described concrete building brick, it comprises the following steps：
(1) each raw material components are weighed according to ratio of weight and number；
(2) cinder, waste gypsum and zeolite powder are added in ball crusher the grinding that adds water, until solid particle crosses 220-250
Mesh sieve, obtains preparing batch mixing；
(3) the preparation batch mixing in step (2), cement are added into mixer, mixer uniform stirring is added after 2-4 minutes
Redispersable latex powder, emulsified asphalt, continue stir 2-6 minutes, sequentially add naphthalene water reducer, antifreezing agent, tricalcium aluminate,
Cellulose ether and salt resistance retarder, after stirring 3-5 minutes, slurry of laying bricks；
(4) slurry of laying bricks in step (3) is cast in stock mould, slurry of laying bricks is cooled and shaped in stock mould by normal temperature
After obtain adobe body；
(5) that adobe body is put into steam-cured room is steam-cured, and temperature is 48-58 degree, steam-cured time 3-5 hours, steam-cured good adobe
The fragment of brick of all size is machined to by cutting, then fragment of brick is put into still kettle carries out high-pressure steaming and cultivating, steam curing temperature 200-
215 degree, most recession pressure, cooling went out still kettle and obtained product at 5-7 hours the high-pressure steaming and cultivating time.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to skill of the invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (5)
1. a kind of concrete building brick, it is characterised in that it is made up of the component of following parts by weight：45-80 parts of cinder, barren rock
20-40 parts of cream, 8-20 parts of zeolite powder, 20-30 parts of cement, 3-6 parts of naphthalene water reducer, 3-6 parts of antifreezing agent, 1-5 parts of tricalcium aluminate,
3-10 parts of redispersable latex powder, 2-5 parts of cellulose ether, 1-3 parts of salt resistance retarder, 5-12 parts of emulsified asphalt, 40-55 parts of water.
2. a kind of concrete building brick according to claim 1, it is characterised in that：The concrete building brick is by following parts by weight
Several components are made：66 parts of cinder, 25 parts of waste gypsum, 14 parts of zeolite powder, 22 parts of cement, 3.5 parts of naphthalene water reducer, antifreezing agent 5
Part, 3 parts of tricalcium aluminate, 6 parts of redispersable latex powder, 3 parts of cellulose ether, 1.8 parts of salt resistance retarder, 8 parts of emulsified asphalt, water 45
Part.
3. a kind of concrete building brick according to claim 1, it is characterised in that：The concrete building brick is by following parts by weight
Several components are made：70 parts of cinder, 35 parts of waste gypsum, 15 parts of zeolite powder, 22 parts of cement, 4 parts of naphthalene water reducer, 4 parts of antifreezing agent,
3 parts of tricalcium aluminate, 8 parts of redispersable latex powder, 2 parts of cellulose ether, 1 part of salt resistance retarder, 10 parts of emulsified asphalt, 50 parts of water.
4. the preparation method of the concrete building brick according to any one of claim 1-3, it is characterised in that including following
Step：
(1) each raw material components are weighed according to ratio of weight and number；
(2) cinder, waste gypsum and zeolite powder are added in ball crusher the grinding that adds water, until solid particle crosses 220-250 mesh sieves,
Obtain preparing batch mixing；
(3) the preparation batch mixing in step (2), cement are added into mixer, mixer uniform stirring is after 2-4 minutes, and addition can be again
Dispersed latex powder, emulsified asphalt, continue to stir 2-6 minutes, sequentially add naphthalene water reducer, antifreezing agent, tricalcium aluminate, fiber
Plain ether and salt resistance retarder, after stirring 3-5 minutes, slurry of laying bricks；
(4) slurry of laying bricks in step (3) is cast in stock mould, slurry of laying bricks is obtained in stock mould after normal temperature is cooled and shaped
To adobe body；
(5) that adobe body is put into steam-cured room is steam-cured, and temperature is 48-58 degree, steam-cured time 3-5 hour, steam-cured good adobe process
Cutting is machined to the fragment of brick of all size, then fragment of brick is put into still kettle carries out high-pressure steaming and cultivating, steam curing temperature 200-215
Degree, most recession pressure, cooling went out still kettle and obtained product at 5-7 hours the high-pressure steaming and cultivating time.
5. the preparation method of concrete building brick according to claim 5, it is characterised in that in high-pressure steaming and cultivating, by steam pressure
The Stress control of kettle is in 1.2-1.5Mpa, 210 degree of steam curing temperature, and the high-pressure steaming and cultivating time was at 6 hours.