CN108191353A - The lightweight aggregate concrete prepared using discarded clay brick - Google Patents
The lightweight aggregate concrete prepared using discarded clay brick Download PDFInfo
- Publication number
- CN108191353A CN108191353A CN201810210149.0A CN201810210149A CN108191353A CN 108191353 A CN108191353 A CN 108191353A CN 201810210149 A CN201810210149 A CN 201810210149A CN 108191353 A CN108191353 A CN 108191353A
- Authority
- CN
- China
- Prior art keywords
- clay brick
- aggregate
- lightweight aggregate
- water
- discarded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the lightweight aggregate concretes prepared using discarded clay brick, including major ingredient, auxiliary material, it is characterized in that major ingredient includes clay brick coarse aggregate, clay brick fine aggregate, auxiliary material includes cement, flyash, silicon powder, water-reducing agent, water, the present invention can not only solve the problems, such as that building castoff is handled using discarded clay brick as regeneration lightweight aggregate to prepare lightweight aggregate concrete, and the gradual deficient situation of sand and stone resources can also be alleviated, and there is the effect of light thermal-insulation by crushing common brick as lightweight aggregate concrete prepared by aggregate, meet the policy of national energy-saving emission reduction.Meanwhile there is good mechanical performance, while anti-freezing property meets existing professional standard JGJ 51 2002 using the lightweight aggregate concrete of formula production of the present invention《Lightweight aggregate concrete technology regulation》Regulation.
Description
Technical field
The present invention relates to discarded construction material process fields, and in particular to a kind of light bone prepared using discarded clay brick
Expect concrete.
Technical background
According to reports, China produced 20,000,000,000 m in total in past 50 years3The clay brick of left and right, and these clay bricks
It will be discarded with removal, and account for about the 30%~50% of total amount of construction waste according to estimation.Meanwhile with domestic infrastructure
Development, sand and stone resources are also increasingly deficienter.How building castoff is being solved with finding a stationary point in resource recycling,
It is current urgent problem.
It can alleviate the sand and stone resources gradually political affairs of the situation of scarcity and national energy-saving emission reduction there is presently no a kind of
Plan, and not only there is the effect of light thermal-insulation, the lightweight aggregate coagulation of clay brick preparation is discarded in the utilization for also having both sound absorption effect
Soil.
Invention content
The present invention be exactly in view of the above-mentioned problems, provide it is a kind of can alleviate sand and stone resources gradually deficient situation and
The policy of national energy-saving emission reduction, and not only there is the effect of light thermal-insulation, clay brick is discarded in the utilization for also having both sound absorption effect
The lightweight aggregate concrete of preparation.
In order to achieve the above objectives, the present invention uses following technical scheme.
The lightweight aggregate concrete prepared using discarded clay brick, including major ingredient, auxiliary material, it is characterised in that major ingredient includes clay
Brick coarse aggregate, clay brick fine aggregate, auxiliary material include cement, flyash, silicon powder, water-reducing agent, water, and each component mass percent expires
Foot is claimed below:Clay brick coarse aggregate 35%~45%, clay brick fine aggregate 25%~35%, cement 15%~25%, flyash 1%~
2%th, silicon powder 0.3%~0.8%, water-reducing agent 0.5%~2%, water 5%~10%.The clay brick coarse aggregate is 10~20mm by grain size
Clay brick aggregate and grain size be 4.75~10mm clay brick aggregate in mass ratio 4:1 ratio is uniformly mixed, and makes gained grain
Diameter grading meets the requirement of 5~20mm continuous gradings.The clay brick fine aggregate grain size is 0.5~4.75mm.The cement is preferred
Density is the portland cement of 3.0g/cm3.The flyash preferred density is the Class F fly ash of 2.4g/cm3.The diminishing
Agent needs to meet:Solid content is 10.55%, water-reducing rate 26%.
The present invention also provides a kind of methods for preparing lightweight aggregate concrete using discarded clay brick, include the following steps:First,
Aggregate crushes, discarded clay brick is crushed by movable crusher, sieves, clean, dry after obtain particle size range point
It is not:10~20mm, 4.75~10mm, 0.5~4.75mm regeneration clay brick aggregate;2nd, prepared by major ingredient, will be in step 1
Particle size range for 10~20mm and 4.75~10mm regeneration clay brick aggregate by certain mass than mixing as the thick bone of clay brick
Expect it is spare, particle size range be 0.5~4.75mm regeneration clay brick aggregate it is spare as clay brick fine aggregate;3rd, it feeds intake, it will be glutinous
Cob brick coarse aggregate, clay brick fine aggregate, cement, flyash, silicon powder after metering system is weighed by bucket elevator are put into and stirred successively
It mixes and is stirred in advance in machine 60 seconds or more;4th, spice adds in a certain amount of water in the powder stirred in advance excessively in step 3 and subtracts
Aqua is stirred for 120 seconds or more.
The present invention can not only solve to build to give up using discarded clay brick as regeneration lightweight aggregate to prepare lightweight aggregate concrete
The problem of gurry processing, and the gradual deficient situation of sand and stone resources can also be alleviated, and prepared as aggregate by broken common brick
Lightweight aggregate concrete there is the effect of light thermal-insulation, meet the policy of national energy-saving emission reduction.Meanwhile matched using of the present invention
The lightweight aggregate concrete just produced has good mechanical performance, while anti-freezing property meets existing professional standard JGJ 51-2002
《Lightweight aggregate concrete technology regulation》Regulation.
Specific embodiment
The technical solution in the present invention is clearly and completely described with reference to specific embodiment, it is clear that described
Embodiment be only part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, ability
Domain those of ordinary skill all other embodiments obtained without making creative work, belong to guarantor of the present invention
The range of shield.
Embodiment one:
Weight calculation weighs clay brick coarse aggregate 770Kg, clay brick fine aggregate 600Kg, cement 400Kg, flyash 30Kg, silicon powder
It is put by bucket elevator and is stirred in advance in blender 60 seconds successively after 12Kg, then add in the 1.5% of 130Kg water and total quality of material
Water-reducing agent is stirred for 120 seconds or more.
Embodiment two:
Weight calculation weighs clay brick coarse aggregate 770Kg, clay brick fine aggregate 600Kg, cement 350Kg, flyash 30Kg, silicon powder
It is put into and is stirred in advance in blender 60 seconds successively by bucket elevator after 10.5Kg, then add in the 1.2% of 120Kg water and total quality of material
Water-reducing agent, be stirred for 120 seconds or more.
Embodiment three:
Weight calculation weighs clay brick coarse aggregate 770Kg, clay brick fine aggregate 600Kg, cement 320Kg, flyash 30Kg, silicon powder
It is put by bucket elevator and is stirred in advance in blender 60 seconds successively after 9.6Kg, then add in the 1.0% of 110Kg water and total quality of material
Water-reducing agent is stirred for 120 seconds or more.
Using the lightweight aggregate concrete of this formula production in non-heating region, anti-freezing property presses existing professional standard JGJ
51-2002《Lightweight aggregate concrete technology regulation》Reach F15, in heating districts, during relative humidity≤60%, anti-freezing property is by existing
Row professional standard JGJ 51-2002《Lightweight aggregate concrete technology regulation》Reach F25, during relative humidity > 60%, anti-freezing property is pressed
Existing professional standard JGJ 51-2002《Lightweight aggregate concrete technology regulation》Reach the position of F35, alternation of wetting and drying and SEA LEVEL VARIATION
When, anti-freezing property presses existing professional standard JGJ 51-2002《Lightweight aggregate concrete technology regulation》Meet or exceed F50.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in each embodiment can also be properly combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (7)
1. the lightweight aggregate concrete prepared using discarded clay brick, including major ingredient, auxiliary material, it is characterised in that major ingredient includes clay brick
Coarse aggregate, clay brick fine aggregate, auxiliary material include cement, flyash, silicon powder, water-reducing agent, water, and each component mass percent meets
It is claimed below:Clay brick coarse aggregate 35%~45%, clay brick fine aggregate 25%~35%, cement 15%~25%, flyash 1%~2%,
Silicon powder 0.3%~0.8%, water-reducing agent 0.5%~2%, water 5%~10%.
2. the lightweight aggregate concrete prepared according to claim 1 using discarded clay brick, it is characterised in that the clay brick
The clay brick aggregate in mass ratio 4 that the clay brick aggregate that coarse aggregate is 10~20mm by grain size is 4.75~10mm with grain size:1 ratio
Example is uniformly mixed, and gained size grading is made to meet the requirement of 5~20mm continuous gradings.
3. the lightweight aggregate concrete prepared according to claim 1 using discarded clay brick, it is characterised in that the clay brick
Fine aggregate grain size is 0.5~4.75mm.
4. the lightweight aggregate concrete prepared according to claim 1 using discarded clay brick, it is characterised in that the cement is excellent
Select the portland cement that density is 3.0g/cm3.
5. the lightweight aggregate concrete prepared according to claim 1 using discarded clay brick, it is characterised in that the flyash
Preferred density is the Class F fly ash of 2.4g/cm3.
6. the lightweight aggregate concrete prepared according to claim 1 using discarded clay brick, it is characterised in that the water-reducing agent
It needs to meet:Solid content is 10.55%, water-reducing rate 26%.
7. the method for preparing lightweight aggregate concrete using discarded clay brick, includes the following steps:First, aggregate crushes, will be discarded glutinous
Cob brick crushed by movable crusher, sieved, being cleaned, dry after obtain particle size range and be respectively:10~20mm, 4.75
The regeneration clay brick aggregate of~10mm, 0.5~4.75mm;2nd, prepared by major ingredient, is 10~20mm by the particle size range in step 1
More spare as clay brick coarse aggregate than mixing by certain mass with the regeneration clay brick aggregate of 4.75~10mm, particle size range is
The regeneration clay brick aggregate of 0.5~4.75mm is spare as clay brick fine aggregate;3rd, it feeds intake, by clay brick coarse aggregate, clay brick
Fine aggregate, cement, flyash, silicon powder put into successively by bucket elevator in blender after metering system is weighed stir in advance 60 seconds with
On;4th, spice adds in a certain amount of water and water-reducing agent in the powder stirred in advance excessively in step 3, be stirred for 120 seconds with
On.