CN106520030A - 一种汽车密封胶及其制备方法 - Google Patents
一种汽车密封胶及其制备方法 Download PDFInfo
- Publication number
- CN106520030A CN106520030A CN201510568950.9A CN201510568950A CN106520030A CN 106520030 A CN106520030 A CN 106520030A CN 201510568950 A CN201510568950 A CN 201510568950A CN 106520030 A CN106520030 A CN 106520030A
- Authority
- CN
- China
- Prior art keywords
- rubber
- automobile sealant
- solvent
- sealant according
- automobile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种汽车密封胶，主要由橡胶、热塑性弹性体、增塑剂、增粘树脂、抗老化剂、增稠剂、填料、溶剂组成。制备方法为：将橡胶在两辊机中塑料薄通，薄通10遍后待用。将薄通后的橡胶、SBS、增塑剂和增粘树脂浸泡在溶剂中1-2天，至完全溶解后搅拌均匀。在浸泡后的混合溶剂中加入填料、抗老化剂和增稠剂，使用三辊机碾压3-5次至物料均匀为止。将碾压均匀的胶放至脱泡机中，脱泡20分钟至胶表面光泽细腻为止至。成品包装。用本发明制作的密封胶环保无毒，而且刮涂性好，刮涂后表面平滑细腻且涂层厚度均匀；特别是耐热性能突出，在100℃烘烤条件下不开裂不起泡。
Description
技术领域
本发明涉及一种汽车用密封胶，具体用于汽车焊缝的密封。
背景技术
随着汽车产品向环保节能、安全舒适、轻量化、低成本除尘布、长寿命和无公害方向发展，新型高品质汽车胶粘剂/密封胶的开发和应用已经成为汽车制造业亟待重视的创新课题。
焊缝密封胶可以防止空气、雨水、尘土进入车内，起到密封、防锈、防漏的重要作用。目前汽车厂家使用的常温固化型密封胶均使用了大量的三苯、甲醛等毒性溶剂，对人体、环境有非常大的影响，不符合环保、可持续发展战略，而水性密封胶在许多性能上较溶剂型密封胶有明显差距，因此开发一种环保、无毒性的常温固化密封胶很有高的应用前景。
发明内容
本发明为解决上述问题，提供了一种环保、无毒的一种环保型常温固化的汽车密封胶及其制备方法。
本发明为实现上述目的，所采取的技术方案是：一种汽车密封胶，其特征在于：按重量百分比组成：橡胶15-25%、热塑性弹性体SBS
5-8%、增塑剂3-5%、增粘树脂5-10%、抗老化剂1-3%、增稠剂1-2%、填料20-30%、溶剂30-40%。
一种汽车密封胶的制备方法，具体步骤为：
a、将橡胶在两辊机中塑料薄通，薄通10遍后待用；
b、将薄通后的橡胶、SBS、增塑剂和增粘树脂浸泡在溶剂中1-2天，至完全溶解后搅拌均匀；
c、在浸泡后的混合溶剂中加入填料、抗老化剂和增稠剂，使用三辊机碾压3-5次至物料均匀为止；
d、将碾压均匀的胶放至脱泡机中，脱泡20 分钟至胶表面光泽细腻为止至；
e、成品包装。
本发明的有益效果是：1、环保无毒，传统的密封胶使用了大量的三苯、甲醛等毒性溶剂，对人体、环境有非常大的影响，本发明使用的溶剂均为环保无毒害型溶剂。2、刮涂性好，刮涂后表面平滑细腻且涂层厚度均匀。3、耐热性能突出，在100℃烘烤条件下不开裂不起泡。
具体实施方式
以下将结合实施例对本发明的构思、具体结构及产生的技术效果进行清楚、完整地描述，以充分地理解本发明的目的、特征和效果。显然，所描述的实施例只是本发明的一部分实施例，而不是全部实施例，基于本发明的实施例，本领域的技术人员在不付出创造性劳动的前提下所获得的其他实施例，均属于本发明保护的范围。本发明创造中的各个技术特征，在不互相矛盾冲突的前提下可以交互组合。
一种汽车密封胶，其特征在于：按重量百分比组成：橡胶15-25%、热塑性弹性体SBS
5-8%、增塑剂3-5%、增粘树脂5-10%、抗老化剂1-3%、增稠剂1-2%、填料20-30%、溶剂30-40%。
一种汽车密封胶的制备方法，具体步骤为：
a、将橡胶在两辊机中塑料薄通，薄通10遍后待用；
b、将薄通后的橡胶、SBS、增塑剂和增粘树脂浸泡在溶剂中1-2天，至完全溶解后搅拌均匀；
c、在浸泡后的混合溶剂中加入填料、抗老化剂和增稠剂，使用三辊机碾压3-5次至物料均匀为止；
d、将碾压均匀的胶放至脱泡机中，脱泡20 分钟至胶表面光泽细腻为止至；
e、成品包装。
以上对本发明的较佳实施方式进行了具体说明，但本发明创造并不限于所述实施例，熟悉本领域的技术人员在不违背本发明精神的前提下还可作出种种的等同变型或替换，这些等同的变型或替换均包含在本申请权利要求所限定的范围内。
Claims (10)
1.一种汽车密封胶，其特征在于：按重量百分比组成：橡胶15-25%、热塑性弹性体SBS 5-8%、增塑剂3-5%、增粘树脂5-10%、抗老化剂1-3%、增稠剂1-2%、填料20-30%、溶剂30-40%。
2.根据权利要求1所述的汽车密封胶，其特征在于：所述的橡胶为丙烯酸酯橡胶。
3.根据权利要求1所述的汽车密封胶，其特征在于：所述的热塑性弹性体SBS为LG411型号。
4.根据权利要求1所述的汽车密封胶，其特征在于：所述的增粘树脂为萜烯树脂或C9石油树脂的任意一种或两种。
5.根据权利要求1所述的汽车密封胶，其特征在于：所述的增塑剂为油酸甲酯。
6.根据权利要求1所述的汽车密封胶，其特征在于：所述的抗老化剂为264防老剂。
7.根据权利要求1所述的汽车密封胶，其特征在于：所述的增稠剂为有机膨润土。
8.根据权利要求1所述的汽车密封胶，其特征在于：所述的填料为纳米碳酸钙和轻质碳酸钙二种。
9.根据权利要求1所述的汽车密封胶，其特征在于：所述的溶剂为环己烷或乙酸丁酯的任意一种或两种。
10.一种汽车密封胶的制备方法，具体步骤为：
a、将橡胶在两辊机中塑料薄通，薄通10遍后待用；
b、将薄通后的橡胶、SBS、增塑剂和增粘树脂浸泡在溶剂中1-2天，至完全溶解后搅拌均匀；
c、在浸泡后的混合溶剂中加入填料、抗老化剂和增稠剂，使用三辊机碾压3-5次至物料均匀为止；
d、将碾压均匀的胶放至脱泡机中，脱泡20 分钟至胶表面光泽细腻为止至；
e、成品包装。