CN106519858A - Spray paint and preparation method thereof - Google Patents
Spray paint and preparation method thereof Download PDFInfo
- Publication number
- CN106519858A CN106519858A CN201610945238.0A CN201610945238A CN106519858A CN 106519858 A CN106519858 A CN 106519858A CN 201610945238 A CN201610945238 A CN 201610945238A CN 106519858 A CN106519858 A CN 106519858A
- Authority
- CN
- China
- Prior art keywords
- powder
- paint
- parts
- preparation
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses spray paint. The spray paint comprises, by weight, 20.0-25.0 parts of conducting resin, 15.0-20.0 parts of conductive powder, 5.0-10.0 parts of pigment and filler, 0.2-0.5 part of dispersing agents, 0.2-0.5 part of antioxidants and 44.0-60.0 parts of solvent. The spray paint has the following beneficial effects that 1, construction operation is flexible, easy and convenient, and the product safety is high; 2, the spray paint does not contain resin and the solvent containing triphenyl phosphine, the content of triphenyl phosphine is controlled from the source, and the requirements for low toxicity and environmental friendliness can be met; 3, the wrapping property of the agents is good, and the storage stability is good; and 4, the conductivity is good. The invention further discloses a preparation method of the spray paint.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of spray painting and preparation method thereof.
Background technology
Aerosol paint(Also referred to as paint)Generally by inhalator jar, aerosol valve, content(Paint)Constitute with propellant, in addition with
Load and in inhalator jar, play the stirring ball for helping stirring action(Bead).Aerosol paint, with construction flexible operating flexible and convenient,
Spraying effect is excellent, and with fabulous defencive function, is widely used in various bottoms such as metal, timber, glass, ABS plastic
The application of material.Common spray painting is mainly based on color, metallic surface effect on the market, it is impossible to meet particular customer to product
Can demand, in order to meet his particular requirement of client, we need the spray painting of development function type badly.
With developing rapidly for information technology, computer network, message processing device, electronic communication equipment and various electrical equipment
Equipment is extensively applied in industry-by-industry as the carrier of information technology, electromagnetic signal, as which is easily by outside electromagnetic interference
Appearance is botched routines, so as to have serious consequences, it is therefore necessary to take various effective safeguard procedures, could ensure which is interference-free
And paralysis.Electromagenetic wave radiation is increased considerably in addition, has directly threatened health, is that shielding electromagnetic pollution makes which be limited to one
Determine region, people coat as efficient, simple and direct means to avoid letting out for electromagnetic radiation frequently with anti-EMI shield
Leakage.
Anti- EMI shielding coating is made an addition in specific resin raw material with conductive metal powder, shape after spraying is dry
Into paint film that can be conductive, so as to the function of shielding electromagnetic interference.It is widely used in integrated circuit, keyboard switch, photoconduction
The fields such as material, but the anti-EMI shielding coating existence and stability of general category is poor, and construction is complicated, it is impossible to the aspect such as long-term preservation
It is not enough.Anti- electromagnetic interference shield spray painting can meet the requirement of conductive effect;Its encapsulation is good, is difficult to be oxidized;Carry, apply simultaneously
Work is convenient, without the need for spray gun spraying after latting drown, can preserve for a long time, be difficult precipitation.
At present, at home and abroad disclosed anti-EMI shielding coating technology has a lot.
As Chinese patent of the number of patent application for CN104497656A discloses a kind of anti-shielding conductive coating, mainly pass through
Acrylic resin, glass fibre, auxiliary agent and mixed solvent, solve fire resisting, the adhesive force of existing anti-EMI shielding coating
Performance, containing toxic solvents such as styrene, acetaldehyde in formula, and the defect that complicated, stability difference of constructing cannot be preserved for a long time.
As can be seen here, develop it is a kind of have anti-electromagnetic interference shield, can preserve for a long time, antioxygenic property is good, low toxicity, use
Facilitate the spray painting of feature imperative.
The content of the invention
It is an object of the present invention to provide it is a kind of have anti-electromagnetic interference shield, can preserve for a long time, antioxygenic property is good,
The spray painting of low toxicity, feature easy to use, to overcome techniques as described above defect.It is a further object to provide above-mentioned
The preparation method of spray painting.
According to an aspect of the invention, there is provided a kind of paint, its weight includes:
Described electroconductive resin is organosilicon modified crylic acid resin, acetal resin, in rosin modified phenolic resin
It is at least one.
Preferably, described electroconductive resin is organosilicon modified crylic acid resin, and its viscosity is 1800~2200mPa s.
Described conducting powder is copper powder, white carbon black, nikel powder, aluminium powder, argentum powder, at least one in silver-coated copper powder.
Preferably, described conducting powder is silver-coated copper powder, and 1.5~10um of particle diameter conducts electricity very well, and specific insulation is low.
Described color stuffing is glass dust, at least one in polyethylene wax powder.
Described dispersant is at least one in BYK-P104S, SRE-4044.
Described antioxidant is at least one in BHT, SRE-701.
Described solvent is dimethyl carbonate, dibutyl carbonate, DBE(Mixed dibasic acid ester), isopropanol, sec-Butyl Acetate
In at least one, from the low poison solvent of different volatilization gradients, without toxic solvents such as " triphen " and halogenated hydrocarbons, preferably
Meet low toxicity, environmental requirement.
The spray painting that the present invention is provided and the anti-electromagnetic interference shield type coating products contrast in market, have the advantages that:
1. filling aerosol mode is adopted, and constructing operation is flexible, simple, safe;
2., using the resin without " triphen " and low poison solvent, " triphen " content is controlled from source, low toxicity, ring is met
Guaranteed request;
3. combined by electroconductive resin, color stuffing, conducting powder, auxiliary agent and solvent, make that agent material encapsulation is good, stability
It is good, while conductive effect can be met;
4th, electric conductivity is excellent, and with outstanding anti-electromagnetic interference shield effectiveness.
According to another aspect of the present invention, there is provided a kind of preparation method of spray painting, comprise the following steps:
1) pretreatment of conducting powder:By weight ratio, 10~20 parts of mixed solvents are added in container, are slowly added to
Conducting powder, is stirred after 1~2h with the rotating speed of 600~800r/min, stops stirring immersion 12h, using front again with 1200r/min's
Rotating speed dispersed with stirring 5min;
2) preparation of paint vehicle:In having electroconductive resin, dispersant to add dispersion cylinder by weight ratio, start stirring is equal
It is even, pretreated conducting powder, antioxidant, color stuffing and balance solvent are slowly added to into dispersion cylinder with 600~800r/min
Dispersion 30min, makes paint vehicle;
3) fill:Paint vehicle is filtered, agitation beads is added in inhalator jar, by certain pack completeness by paint vehicle fill to inhalator jar
In, carry out sealing, filling propellant after adding valve, after crossing water-bath, load onto head, that is, anti-electromagnetic interference shield spray painting is obtained.
Described paint vehicle and propellant, by weight ratio, paint vehicle:Propellant=1.8~3:1.
Described pack completeness is preferably 76%~82%, big tank can be avoided to fill less, loading amount foot, it is ensured that under the conditions of 50 ± 2 DEG C
Interior pressure≤the 0.8MPa of product after 0.5h is placed, and product falls without damaged, No leakage under 1.8m height, it is ensured that product
It is safe
Specific embodiment
The composition for painting, preparation method are illustrated below by way of specific embodiment and substrate surface construction work are carried out using spray painting
Skill etc., to be better understood from the present invention.
Embodiment 1
1) conducting powder pretreatment:By weight ratio, 10 parts of DBE, 5 parts of dimethyl carbonate are added in container, slowly
5 parts of 10 parts of argentum powder and white carbon black are added, is stirred after 1~2h with the rotating speed of 600~800r/min, stop stirring immersion 12h, using front
Again with rotating speed dispersed with stirring 5min of 1200r/min;
2) preparation of paint vehicle:By weight ratio by organosilicon modified crylic acid resin(Viscosity is 1800~2200mPa
s)12 parts, during 8 parts of acetal resin, 0.2 part of SRE-4044 add dispersion cylinder, start stirs, by 5 parts of glass dust, SRE-
701 0.2 parts, 10 parts of dimethyl carbonate, 6 parts of dibutyl carbonate, DBE10 parts, 18.6 parts of isopropanol be slowly added to dispersion cylinder, stir
Mix to range estimation without obvious granule;Pretreated conductive slurry is added, 30min is disperseed with 600~800r/min, paint vehicle is made;
3) fill:Paint vehicle is filtered, agitation beads is put into in inhalator jar, be 76% and weight paint vehicle by pack completeness:
Propellant=2.5:1 carries out fill, adds valve to carry out sealing, filling propellant, loads onto head, that is, painted after crossing water-bath
A。
Embodiment 2
1) conducting powder pretreatment:By weight ratio, 10 parts of DBE, 5 parts of dimethyl carbonate are added in container, slowly
Add silver-coated copper powder(1.5~10um of particle diameter)17 parts, stirred after 1~2h with the rotating speed of 600~800r/min, stop stirring immersion
12h, using front again with rotating speed dispersed with stirring 5min of 1200r/min;
2) preparation of paint vehicle:By weight ratio by organosilicon modified crylic acid resin(Viscosity is 1800~2200mPa
s)23 parts, during 0.3 part of SRE-4044 adds dispersion cylinder, start stirs, by 7 parts of polyethylene wax powder, 0.3 part of BHT, carbonic acid
8.1 parts of dimethyl ester, 5.2 parts of dibutyl carbonate, DBE7.5 parts, 16.6 parts of isopropanol are slowly added to dispersion cylinder, stir to range estimation nothing
Obvious granule;Pretreated conductive slurry is added, 30min is disperseed with 600~800r/min, paint vehicle is made;
3) fill:Paint vehicle is filtered, agitation beads is put into in inhalator jar, be 79% and weight paint vehicle by pack completeness:
Propellant=1.8:1 carries out fill, adds valve to carry out sealing, filling throwing propellant, loads onto head, that is, sprayed after crossing water-bath
Paint B.
Embodiment 3
1) conducting powder pretreatment:By weight ratio, 10 parts of DBE, 5 parts of dimethyl carbonate are added in container, slowly
5 parts of 15 parts of aluminium powder and nikel powder are added, is stirred after 1~2h with the rotating speed of 600~800r/min, stop stirring immersion 12h, using front
Again with rotating speed dispersed with stirring 5min of 1200r/min;
2) preparation of paint vehicle:By weight ratio by 12 parts of organosilicon modified crylic acid resin, 5 parts of acetal resin, pine
During 0.5 part of 8 parts of fragrant phenol-formaldehyde resin modified and BYK-P104S add dispersion cylinders, start stirs, by 10 parts of polyethylene wax powder,
0.5 part of SRE-701,6 parts of dimethyl carbonate, 4.4 parts of dibutyl carbonate, DBE4.7 parts, 13.9 parts of isopropanol are slowly added to dispersion
Cylinder, stirs to range estimation without obvious granule;Pretreated conductive slurry is added, 30min is disperseed with 600~800r/min, is made
Paint vehicle;
3) fill:Paint vehicle is filtered, agitation beads is put into in inhalator jar, be 82% and weight paint vehicle by pack completeness:
Propellant=2:1 carries out fill, adds valve to carry out sealing, filling throwing propellant, loads onto head, that is, painted after crossing water-bath
C。
Embodiment 4
1) conducting powder pretreatment:By weight ratio, 10 parts of DBE, 5 parts of dimethyl carbonate are added in container, slowly
Add 18 parts of copper powder, stirred after 1~2h with the rotating speed of 600~800r/min, stop stirring immersion 12h, using it is front again with
Rotating speed dispersed with stirring 5min of 1200r/min;
2) preparation of paint vehicle:By weight ratio 22 parts of organosilicon modified crylic acid resin, SRE-40440.2 parts are added
In dispersion cylinder, start stirs, by 4 parts of polyethylene wax powder, 2 parts of glass dust, SRE-7010.3 parts, 8.4 parts of dimethyl carbonate,
5.4 parts of dibutyl carbonate, DBE7.8 parts, 16.9 parts of isopropanol are slowly added to reaction cylinder, stir to range estimation without obvious granule;Add
Pretreated conductive slurry, disperses 30min with 600~800r/min, makes paint vehicle;
3) fill:Paint vehicle is filtered, agitation beads is put into in inhalator jar, be 78% and weight paint vehicle by pack completeness:
Propellant=3:1 carries out fill, adds valve to carry out sealing, filling propellant, loads onto head, that is, obtain the D that paints after crossing water-bath.
Comparative example 5
1) preparation of paint vehicle:40 parts of acrylic resin, 20 parts of styrene, 35 parts of acetaldehyde are added into dispersion by weight ratio
In cylinder, start stirs, and 5 parts of polyethylene wax powder, 15 parts of addition dispersion cylinders of glass fibre are stirred to range estimation without obvious
Grain, makes paint vehicle E;
2) application:To filter after paint vehicle latting drown, in adding pneumatic spray gun and as requested object surface is sprayed.
The correlated performance method of testing of spray painting A~E that embodiment 1~4, comparative example 5 are provided is as follows:
1. workability:Embodiment 1~4 uses aerosol form fill, constructs simple and convenient, without the need for paint;Comparative example 5
For spray gun in construction, filter after paint vehicle latting drown, in adding pneumatic spray gun and as requested object surface is sprayed.
2. surface drying time:Using chronometry, coating surface is touched with finger, calculate stickiness and disappear, the tack-free time.
3. film thickness:Coating thickness detector EM2271.
4. specific insulation:Specific insulation is determined using ZST-121 volumetric surfaces resistivity tester.
5. pressure in:By GB/T 14449-2008《Aerosol products method of testing》The regulation of " 5.1 intrinsic pressure test " is entered
OK, the product tested after 50 DEG C of water bath with thermostatic control 1h successively with 0~1.6MPa pressure gauges is intrinsic pressure.
6. pack completeness:By BB/T 0047《Aerosol paint》The regulation of " measure of 5.11 pack completeness " is carried out.
7. fall-down test:By SN/T 1180-2003《Import and export aerosol can safety verification code》" 6.3.5 fall-down tests "
Regulation carry out, deformation rate refers to that the inhalator jar quantity deformed Jing after fall-down test accounts for the percentage ratio of total quantity, sampling observation 10
Prop up sample.
The performance test results of spray painting A~E that embodiment 1~4 and comparative example 5 are provided are as shown in table 1 below.
1 impact of performance of table is contrasted
As can be seen from Table 1, the present invention is provided anti-electromagnetic interference shield spray painting and prior art(Comparative example 5)Compare,
Constructing operation is more flexible, easy, safe, and meet environmental requirement, shelf characteric it is excellent and meanwhile meet electric conductivity will
The product asked.
Above-described is only some embodiments of the present invention.For the person of ordinary skill of the art, not
On the premise of departing from the invention design, some deformations and improvement can also be made, these belong to the protection model of the present invention
Enclose.
Claims (10)
1. a kind of spray painting, it is characterised in that each component includes by weight ratio:
2. it is as claimed in claim 1 to paint, it is characterised in that the electroconductive resin is organosilicon modified crylic acid resin, gathers
At least one in formaldehyde resin, rosin modified phenolic resin, the conducting powder are copper powder, white carbon black, nikel powder, aluminium powder, argentum powder, silver
At least one in copper-clad powder.
3. it is as claimed in claim 2 to paint, it is characterised in that the electroconductive resin is 1800~2200mPa s for viscosity
Organosilicon modified crylic acid resin, the conducting powder are silver-coated copper powder that particle diameter is 1.5~10um.
4. it is as claimed in claim 1 to paint, it is characterised in that described color stuffing is glass dust, in polyethylene wax powder extremely
Few one kind.
5. it is as claimed in claim 1 to paint, it is characterised in that the dispersant be in BYK-P104S, SRE-4044 at least
It is a kind of.
6. it is as claimed in claim 1 to paint, it is characterised in that described antioxidant is at least in BHT, SRE-701
Kind.
7. it is as claimed in claim 1 to paint, it is characterised in that described solvent be dimethyl carbonate, dibutyl carbonate, DBE,
At least one in isopropanol, sec-Butyl Acetate.
8. the preparation method painted as claimed in claim 1, it is characterised in that comprise the following steps:
1) pretreatment of conducting powder:By weight ratio, 10~20 parts of mixed solvents are added in container, are slowly added to conduction
Powder, is stirred after 1~2h with the rotating speed of 600~800r/min, stops stirring immersion 12h, using front again with the rotating speed of 1200r/min
Dispersed with stirring 5min;
2) preparation of paint vehicle:In having electroconductive resin, dispersant to add dispersion cylinder by weight ratio, start stirs, will
Pretreated conducting powder, antioxidant, color stuffing and balance solvent are slowly added to dispersion cylinder, are disperseed with 600~800r/min
30min, makes paint vehicle;
3) fill:Paint vehicle is filtered, and agitation beads is added in inhalator jar, by certain pack completeness by paint vehicle fill to inhalator jar,
Carry out sealing, filling propellant after adding valve, after crossing water-bath, load onto head, that is, spray painting is obtained.
9. the preparation method painted as claimed in claim 8, it is characterised in that by weight ratio, the paint vehicle:Propellant
=1.8~3:1.
10. the preparation method painted as claimed in claim 8, it is characterised in that described pack completeness is 76%~82%.