CN102993863A - Amino-acrylic conducting paint - Google Patents
Amino-acrylic conducting paint Download PDFInfo
- Publication number
- CN102993863A CN102993863A CN 201210407402 CN201210407402A CN102993863A CN 102993863 A CN102993863 A CN 102993863A CN 201210407402 CN201210407402 CN 201210407402 CN 201210407402 A CN201210407402 A CN 201210407402A CN 102993863 A CN102993863 A CN 102993863A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- parts
- aminoacrylic acid
- sprayed paint
- amino
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an amino-acrylic conducting paint. The amino acrylic conducting paint comprises the following ingredients in parts by mass: 40 to 50 parts of acrylic resin, 10 to 20 parts of amino resin, 1 to 5 parts of aluminum tripolyphosphate, 1 to 5 parts of china clay, 1 to 3 parts of high-pigment carbon black, 1 to 3 parts of precipitated barium sulphate, 0.1 to 1 part of strontium yellow, 25 to 35 parts of distilled water and 2 to 6 parts of diluent. The amino-acrylic conducting paint can be used for coating outer walls of electronic products, is high in stability of electric conduction and has a good antistatic construction effect.
Description
Technical field
The present invention relates to a kind of spraying paint, relate in particular to a kind of aminoacrylic acid conduction and spray paint.
Background technology
At present China's electrical apparatus industry development is very fast, and output also constantly raises, and this has just driven the development of coating industry.Paint for domestic electric appliance has a variety of, such as waterborne dip paint, powder coating, sprays paint etc., these coating each own own a bit, still seldom have coating to possess the function of conduction.The function of electric conduction paint is exactly to play the effect of conduction behind the formation paint film, and the interference of shielding electromagnetic wave can guarantee the safety that household electrical appliances use like this.
Summary of the invention
The object of the invention is to overcome the deficiency of above-mentioned prior art, provide a kind of aminoacrylic acid conduction to spray paint, can be used for the application of household electrical appliance, shield the hertzian wave of its generation.
Technical scheme: a kind of aminoacrylic acid conduction is sprayed paint, contain following composition in mass parts: acrylic resin 40～50 mass parts, aminoresin 10～20 mass parts, aluminium triphosphate 1～5 mass parts, china clay 1～5 mass parts, high-carbon black pigment 1～3 mass parts, process white 1～3 mass parts, strontium yellow 0.1～1 mass parts, distilled water 25～35 mass parts, thinner 2～6 mass parts.
Aminoresin described above is under 25 ℃, and its viscosity is 2500～4500mPas.
Aluminium triphosphate density described above is 2～3g/cm
3, moisture≤1.5%, the pH value is 5.5～7.
The particle size range of high-carbon black pigment described above is 10～16.
Process white pH value described above is 6.5～8.0, moisture≤0.2%, sulfide≤0.003%.
Thinner described above contains following composition in mass parts: dimethylbenzene 30 mass parts, heavy aromatic hydrocarbon 24 mass parts, propyl carbinol 13 mass parts, static inhibitor 0.6 mass parts.
Static inhibitor described above is the butyl dimethyl benzyl ammonium chloride.
Beneficial effect: aminoacrylic acid conduction provided by the invention is sprayed paint, and cost is lower, has good conductive stability and static construction effect, can be used for the application of household electrical appliance outer wall.
Embodiment
Embodiment 1
1. the aminoacrylic acid of the present invention conduction preparation of described thinner of spraying paint: dimethylbenzene 30 mass parts and heavy aromatic hydrocarbon 24 mass parts are incorporated in the propyl carbinol of 13 mass parts, after stirring, add static inhibitor 0.6 mass parts mixing and get final product.
2. the aminoacrylic acid of the present invention conduction preparation of spraying paint: with acrylic resin 46 mass parts, strontium yellow 0.56 mass parts, aluminium triphosphate 4 mass parts, china clay 1.28 mass parts, high-carbon black pigment 1.3 mass parts, process white 2 mass parts and distilled water 25 mass parts one reinstate homogenizer pre-dispersed evenly after, be ground to fineness＜40 μ m with sand mill again, then add aminoresin 11.46 mass parts, again grind one time, through silk screen filter, add again thinner 4.5 mass parts mass parts and fully mix, get finished product.
Aminoacrylic acid conduction provided by the invention is sprayed paint, and the resistivity of thinner is 10M Ω cm, and the shielding electromagnetic wave ability reaches 1.7T, has good conductive stability and static construction effect.
The above is the preferred embodiments of the present invention, but the present invention also is not limited to above only embodiment, slightly does improvement and also will be considered as protection scope of the present invention on embodiment.
Claims (7)
1. an aminoacrylic acid conduction is sprayed paint, it is characterized in that containing following composition in mass parts: acrylic resin 40～50 mass parts, aminoresin 10～20 mass parts, aluminium triphosphate 1～5 mass parts, china clay 1～5 mass parts, high-carbon black pigment 1～3 mass parts, process white 1～3 mass parts, strontium yellow 0.1～1 mass parts, distilled water 25～35 mass parts, thinner 2～6 mass parts.
2. aminoacrylic acid conduction according to claim 1 is sprayed paint, and it is characterized in that described aminoresin under 25 ℃, and its viscosity is 2500～4500mPas.
3. aminoacrylic acid conduction according to claim 1 is sprayed paint, and it is characterized in that described aluminium triphosphate density is 2～3g/cm
3, moisture≤1.5%, the pH value is 5.5～7.
4. aminoacrylic acid conduction according to claim 1 is sprayed paint, and the particle size range that it is characterized in that described high-carbon black pigment is 10～16.
5. aminoacrylic acid conduction according to claim 1 is sprayed paint, and it is characterized in that described process white pH value is 6.5～8.0, moisture≤0.2%, sulfide≤0.003%.
6. aminoacrylic acid conduction according to claim 1 is sprayed paint, and it is characterized in that described thinner contains following composition in mass parts: dimethylbenzene 30 mass parts, heavy aromatic hydrocarbon 24 mass parts, propyl carbinol 13 mass parts, static inhibitor 0.6 mass parts.
7. aminoacrylic acid conduction according to claim 6 is sprayed paint, and it is characterized in that described static inhibitor is the butyl dimethyl benzyl ammonium chloride.