CN106497328A - A kind of additional type electrosilvering powdery paints - Google Patents
A kind of additional type electrosilvering powdery paints Download PDFInfo
- Publication number
- CN106497328A CN106497328A CN201610962285.6A CN201610962285A CN106497328A CN 106497328 A CN106497328 A CN 106497328A CN 201610962285 A CN201610962285 A CN 201610962285A CN 106497328 A CN106497328 A CN 106497328A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- powdery paints
- electrosilvering
- bonding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of additional type electrosilvering powdery paints, and the powdery paints is formed by 13 parts of argentum powder in units of weight portion, 94 98 parts of bottom powder, 13 parts of bondings of fine stearic acid；Wherein bottom powder is made up of following raw material：20 40 parts of epoxy resin, 20 40 parts of polyester resin, 0.5 1.5 parts of levelling agent, 701 doses 0.8 1.5 parts, 10 30 parts of barium sulfate, 5 15 parts of colorant.The present invention combines epoxy resin and polyester resin as film forming matter, makes coating that there is good weatherability, and coating figure layer metal-like is strong, and good luster, mobility are good, smooth surface.
Description
Technical field
The invention belongs to art of powder coatings, and in particular to a kind of additional type electrosilvering powdery paints.
Background technology
Existing more than the 60 years development of powdery paints, as powdery paints belongs to environment-friendly type coating compared to solvent based coating,
Its various excellent performance is added, is compiled from interview one and is received extensively favor, wide market.But the production of powdery paints
It is faced with the challenge from aspects such as environmental protection, technology.
In decorative paint field, in addition to plain edition various luster, the powdery paints kind of flat surface, various texture powder
Last coating obtains kind and consumption also to be increased year by year.In these kinds, electrosilvering powdery paints is decorative powder coatings man
One important member of race.Silver has beautiful silvery white gloss, and silver is 91% to the reflectance of visible ray, with tempting white
Coloured light pool, therefore favored by consumers.But existing electrosilvering powdery paints cannot be met in terms of metallic luster texture
The increasingly harsh demand of consumer.Therefore the present invention is intended to provide a kind of additional type plating with desired metallic silver color pool texture
Silver powder coating.
Content of the invention
The present invention provides a kind of additional type electrosilvering powdery paints, improves the metallic luster texture of electrosilvering powdery paints.
For achieving the above object, the present invention is adopted the following technical scheme that：
A kind of additional type electrosilvering powdery paints, is formed by following weight portion raw material bonding：Argentum powder 1-3 parts, bottom powder 94-98
Part, fine stearic acid 1-3 parts.Wherein, the bottom powder is made up of following raw material：Epoxy resin 20-40 parts, polyester resin
20-40 parts, levelling agent 0.5-1.5 parts, 701 doses of 0.8-1.5 parts, barium sulfate 10-30 parts, colorant 5-15 parts.
Preferably, a kind of additional type electrosilvering powdery paints, is formed by following weight portion raw material bonding：2 parts of argentum powder, bottom
96 parts of powder, 2 parts of fine stearic acid.Wherein, the bottom powder is made up of following raw material：35 parts of epoxy resin, polyester resin
35 parts, 1 part of levelling agent, 701 doses 1 part, 20 parts of barium sulfate, 8 parts of colorant.
A kind of additional type electrosilvering powdery paints, its preparation process are as follows：
（1）Prepared by bottom powder：The bottom powder raw material of above-mentioned weight portion is weighed, melting extrusion, cooling are broken, cross 160 mesh sieves；
（2）Bonding mixes：Argentum powder, bottom powder and fine stearic acid are carried out bonding, bonding temperature is set as 50-55 DEG C, bonding
Time is 5-20min, crosses 100 mesh sieves and obtains finished product.
It is an advantage of the current invention that：The present invention combines epoxy resin and polyester resin as film forming matter, has coating
Good weatherability, coating figure layer metal-like are strong, and good luster, mobility are good, smooth surface.
Specific embodiment
Embodiment 1
A kind of additional type electrosilvering powdery paints, is formed by following weight portion raw material bonding：2 parts of argentum powder, 96 parts of bottom powder are fine
2 parts of stearic acid.Wherein, the bottom powder is made up of following raw material：35 parts of epoxy resin, 35 parts of polyester resin, levelling agent 1
Part, 701 doses 1 part, 20 parts of barium sulfate, 8 parts of colorant.
A kind of additional type electrosilvering powdery paints, its preparation process are as follows：
（1）Prepared by bottom powder：The bottom powder raw material of above-mentioned weight portion is weighed, melting extrusion, cooling are broken, cross 160 mesh sieves；
（2）Bonding mixes：Argentum powder, bottom powder and fine stearic acid are carried out bonding, bonding temperature is set as 53 DEG C, the bonding time
For 10min, cross 100 mesh sieves and obtain finished product.
Embodiment 2
A kind of additional type electrosilvering powdery paints, is formed by following weight portion raw material bonding：1 part of argentum powder, 98 parts of bottom powder are fine
1 part of stearic acid.Wherein, the bottom powder is made up of following raw material：20 parts of epoxy resin, 40 parts of polyester resin, levelling agent
0.5 part, 701 doses 1.5 parts, 30 parts of barium sulfate, 5 parts of colorant.
A kind of additional type electrosilvering powdery paints, its preparation process are as follows：
（1）Prepared by bottom powder：The bottom powder raw material of above-mentioned weight portion is weighed, melting extrusion, cooling are broken, cross 160 mesh sieves；
（2）Bonding mixes：Argentum powder, bottom powder and fine stearic acid are carried out bonding, bonding temperature is set as 50 DEG C, the bonding time
For 5min, cross 100 mesh sieves and obtain finished product.
Embodiment 3
A kind of additional type electrosilvering powdery paints, is formed by following weight portion raw material bonding：3 parts of argentum powder, 94 parts of bottom powder are fine
3 parts of stearic acid.Wherein, the bottom powder is made up of following raw material：40 parts of epoxy resin, 20 parts of polyester resin, levelling agent
1.5 parts, 701 doses 0.8 part, 10 parts of barium sulfate, 15 parts of colorant.
A kind of additional type electrosilvering powdery paints, its preparation process are as follows：
（1）Prepared by bottom powder：The bottom powder raw material of above-mentioned weight portion is weighed, melting extrusion, cooling are broken, cross 160 mesh sieves；
（2）Bonding mixes：Argentum powder, bottom powder and fine stearic acid are carried out bonding, bonding temperature is set as 55 DEG C, the bonding time
For 20min, cross 100 mesh sieves and obtain finished product.
The foregoing is only presently preferred embodiments of the present invention, all impartial changes that is done according to scope of the present invention patent with
Modification, should all belong to the covering scope of the present invention.
Claims (3)
1. a kind of additional type electrosilvering powdery paints, it is characterised in that formed by following weight portion raw material bonding：Argentum powder 1-3
Part, bottom powder 94-98 parts and fine stearic acid 1-3 parts.
2. a kind of additional type electrosilvering powdery paints as claimed in claim 1, it is characterised in that the bottom powder is by following weight
Part raw material is made：Epoxy resin 20-40 parts, polyester resin 20-40 parts, levelling agent 0.5-1.5 parts, 701 doses of 0.8-1.5 parts, sulfur
Sour barium 10-30 parts, colorant 5-15 parts.
3. a kind of additional as claimed in claim 1 type electrosilvering powdery paints, it is characterised in that its concrete preparation method is such as
Under：
（1）Prepared by bottom powder：The bottom powder raw material of above-mentioned weight portion is weighed, melting extrusion, cooling are broken, cross 160 mesh sieves；
（2）Bonding mixes：Argentum powder, bottom powder and fine stearic acid are carried out bonding, bonding temperature is set as 50-55 DEG C, bonding
Time is 5-20min, crosses 100 mesh sieves and obtains finished product.