CN104763119B - A kind of radioprotective heat insulation decoration integrated plate - Google Patents
A kind of radioprotective heat insulation decoration integrated plate Download PDFInfo
- Publication number
- CN104763119B CN104763119B CN201510114811.9A CN201510114811A CN104763119B CN 104763119 B CN104763119 B CN 104763119B CN 201510114811 A CN201510114811 A CN 201510114811A CN 104763119 B CN104763119 B CN 104763119B
- Authority
- CN
- China
- Prior art keywords
- fiber
- heat insulation
- integrated plate
- radioprotective
- decoration integrated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to a kind of radioprotective heat insulation decoration integrated plate, its manufacture method is：First plates are become required version type as base material, choose one or more of nano level silver fiber, copper fiber or nickel fiber and put in container, by above-mentioned metallic fiber and binding agent according to 3：1 ratio mixes and uses high-speed stirred injection apparatus quickly to stir, stirred in 10 seconds, from high-speed jets in 28 45 degree of temperature, under conditions of pressure 2 2.5Mpa, the mixture of metallic fiber and binding agent is uniformly ejected on base material, coating thickness is 0.02 0.08mm, then rapidly cool to form radiation protective layer in 30 seconds, then polyurathamc is sprayed in radiation protective layer under the pressure of 2 2.5Mpa, radioprotective heat insulation decoration integrated plate after solidification, can be formed.The present invention not only has insulation, decoration function, is also coated with layer of metal sealing coat on base material, can be effectively isolated electromagnetic radiation, reduces the radiation receiving amount of human body in building, is conducive to human body health.
Description
Technical field
The present invention relates to building material field, more particularly to a kind of radioprotective heat insulation decoration integrated plate.
Background technology
Heat preservation decoration integrative production board, is to be prefabricated in the factory the sheet material with exterior-wall heat insulation function of molding.Existing
Heat insulation decoration integrated plate is composited with ornament materials by insulation material, hangs over building exterior wall face for patch, has insulation and fills
Decorations function.However, with the raising of Modern Live level, the application of electrical equipment, radio, network etc. is more and more extensive, outdoor
High-tension line, high pressure facility, various radiation source are seen everywhere, the special equipment such as Hi-Tech equipment, various naval vessel, and high-quality is prevented
Radiate being in great demand of heat insulating decorative board.Therefore, electromagnetic radiation is also increasingly subject to people's attention, existing building system
In typically only insulation material and strength structure, building do not have special radiation proof function in itself, how to found one kind and have
Radiation proof function, the radioprotective heat insulation decoration integrated plate of insulation, decoration, radioprotective can be integrated, there is highly important valency
Value.
Content of the invention
The invention aims to providing a kind of radioprotective heat insulation decoration integrated plate so as to existing insulation and decoration function, and
The effect of radioprotective can be played, be conducive to the health of human body.
For solving the above problems, the present invention provides a kind of radioprotective heat insulation decoration integrated plate, and its manufacture method is：First will
The required version type of plates one-tenth, as base material, chooses one of nano level silver fiber, copper fiber or nickel fiber or several
Kind put in container, by above-mentioned metallic fiber and binding agent according to 3：1 ratio mixes and uses high-speed stirred injection apparatus quick
Stirring, stirred in 10 seconds, from high-speed jets under conditions of temperature 28-45 degree, pressure 2-2.5Mpa by metal
Fiber is uniformly ejected on base material with the mixture of binding agent, and coating thickness is 0.02-0.08mm, then fast in 30 seconds
Speed is cooled into radiation protective layer, then polyurathamc is sprayed in radiation protective layer under the pressure of 2-2.5Mpa, after solidification i.e.
Radioprotective heat insulation decoration integrated plate can be formed.
Further, the mixing speed of described high-speed stirred injection apparatus is more than 3000 revs/min.
Further, described metal powder is that silver fiber, copper fiber and nickel fiber press 2：1：The mixture of 1 ratio mixing.
After such design, the present invention at least has advantages below：
Not only there is insulation, the decoration function of traditional heat insulating decorative board, layer of metal fiber is also coated with base material
Sealing coat, can be effectively isolated electromagnetic radiation, reduce the radiation receiving amount of human body in building, be conducive to human body health, can be same
When possess insulation, decoration and radioprotective multi-functional.
The application adopts high pressure painting technology by the metal bisque of polyurathamc direct spraying, solves conventional vacuum
In plate, metal level and layer of polyurethane are difficult the difficult problem combining, and the two conjugation is good, stable performance.
Specific embodiment
The present invention provides a kind of radioprotective heat insulation decoration integrated plate, and its manufacture method is：First plates are become institute
The version type needing, as base material, is chosen one or more of nano level silver fiber, copper fiber or nickel fiber and is put in container, will
Above-mentioned metallic fiber and binding agent are according to 3：1 ratio mixes and uses high-speed stirred injection apparatus quickly to stir, and stirs in 10 seconds
Mix uniformly, under conditions of temperature 28-45 degree, pressure 2-2.5Mpa, metallic fiber and binding agent is mixed from high-speed jets
Compound is uniformly ejected on base material, and coating thickness is 0.02-0.08mm, then rapidly cools to form radioprotective in 30 seconds
Layer, then polyurathamc is sprayed in radiation protective layer under the pressure of 2-2.5Mpa, radioprotective insulation can be formed after solidification
Decorative integrated plate.
More preferably, the mixing speed of described high-speed stirred injection apparatus is more than 3000 revs/min.Metallic fiber and bonding
The quantity for spray of the mixture of agent is in 30 80g/m2.
Described metallic fiber is that nanometer-level silver fiber, copper fiber and nickel fiber press 2：1：The mixture of 1 ratio mixing.
The above, be only presently preferred embodiments of the present invention, and not the present invention is made with any pro forma restriction, this
Skilled person makes a little simple modification, equivalent variations or modification using the technology contents of the disclosure above, all falls within this
In bright protection domain.
Claims (2)
1. a kind of radioprotective heat insulation decoration integrated plate is it is characterised in that its manufacture method is：First plates are become required
Version type as base material, choose nano level silver fiber, copper fiber and nickel fiber and press 2：1：Put in container after 1 ratio mixing,
By above-mentioned metallic fiber and binding agent according to 3：1 ratio mixes and uses high-speed stirred injection apparatus quickly to stir, in 10 seconds
Stir, from high-speed jets under conditions of temperature 28-45 degree, pressure 2-2.5MPa by metallic fiber and binding agent
Mixture be uniformly ejected on base material, coating thickness be 0.02-0.08mm, then rapidly cooled to form anti-in 30 seconds
Radiating layer, then polyurathamc is sprayed in radiation protective layer under the pressure of 2-2.5MPa, radioprotective can be formed after solidification
Heat insulation decoration integrated plate.
2. radioprotective heat insulation decoration integrated plate according to claim 1 is it is characterised in that described high-speed stirred injection fills
The mixing speed put is more than 3000 revs/min.