CN103694840B - A kind of reactor high temperature-resistant wire lacquer and preparation method thereof - Google Patents
A kind of reactor high temperature-resistant wire lacquer and preparation method thereof Download PDFInfo
- Publication number
- CN103694840B CN103694840B CN201310640498.3A CN201310640498A CN103694840B CN 103694840 B CN103694840 B CN 103694840B CN 201310640498 A CN201310640498 A CN 201310640498A CN 103694840 B CN103694840 B CN 103694840B
- Authority
- CN
- China
- Prior art keywords
- add
- high temperature
- linking agent
- hour
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of reactor high temperature-resistant wire lacquer and preparation method thereof, it is characterized in that, be made up of the raw material of following weight part: resol 12-15, E-42 epoxy resin 12-15, aluminium nitride 3-5, pentaerythritol triacrylate 6-9, linking agent TAC? 1-2, nylon 11? 12-15, Zinc Stearate 1-2, nano aluminum alumina 14-20, hexamethylene diisocyanate 4-5, polyvinylpyrrolidone 2-3, phenyl glycidyl ether 5-7, silicon carbide 1-2, auxiliary agent 7-9, dimethylbenzene 100-120, M-and P-cresols 100-120; Reactor high temperature-resistant wire lacquer of the present invention has following beneficial effect: the performance of painting in copper cover aluminum insulated wire production process improves, meet more than 180 DEG C heat conditions requirements, this paint is used for the skin of high heat resistance coil wire rod, can solidify with furnace temperature with polyester-imide priming paint, solve copper cover aluminum insulated wire all the time withstand voltage not up to standard, the difficult problem that hot stamping is not up to standard, resistance to pressure is good, and pin hole is controlled well.
Description
Technical field
The present invention relates to a kind of wire enamel, especially a kind of reactor high temperature-resistant wire lacquer and preparation method thereof.
Background technology
Enameled wire is a kind of electrical material, and it is at the high-strength insulating layer of a circular copper line surface processing thin layer, plays the effect with external insulation.The lousiness line also thinner than hair can be processed into, cotton covered wire thick as thumb by specification.Enameled wire has good insulation effect and waterproof ability.In electrical equipment, application is very extensive, as electric motor, and generator, water pump, electro-magnet, welding machine, household electrical appliance, cableless communication, loud speaker, tg, transformer etc.Wire enamel is the necessary insulating material producing enameled wire, wire enamel requires to have good tack, physical strength, insulating property, resistance toheat, wear resisting property, salt spray resistance and adverse environment resistant performance etc., but there is thermotolerance, wear no resistance in common wire enamel, insufficient strength, resistance to thermal level lower than the problems such as 120 DEG C, be difficult to the requirement meeting varying environment.Need to improve the formula of wire enamel and production technique, improve the performance of enamel-cover paint further, reduce its production cost.
Summary of the invention
Object of the present invention is just to provide a kind of reactor high temperature-resistant wire lacquer and preparation method thereof, to overcome the deficiencies in the prior art.
The object of the present invention is achieved like this:
A kind of reactor high temperature-resistant wire lacquer, it is characterized in that, be made up of the raw material of following weight part (kilogram): resol 12-15, E-42 epoxy resin 12-15, aluminium nitride 3-5, pentaerythritol triacrylate 6-9, linking agent TAC1-2, nylon 11 12-15, Zinc Stearate 1-2, nano aluminum alumina 14-20, hexamethylene diisocyanate 4-5, polyvinylpyrrolidone 2-3, phenyl glycidyl ether 5-7, silicon carbide 1-2, auxiliary agent 7-9, dimethylbenzene 100-120, M-and P-cresols 100-120;
Described auxiliary agent is made up of following raw materials in part by weight: nano mica powder 0.2-0.3, trolamine 1.2-1.3, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 2-3, hexamethylenetetramine 1-2, polyester acrylate 3-5, Viscoat 295 12-15, triethyl citrate 3-6, linking agent TAC1-2, Tenox PG 2-3, coix seed oil 1-2; Its preparation method is by polyester acrylate, Viscoat 295, triethyl citrate mixing, be heated to 60-70 DEG C, add linking agent TAC, Tenox PG, coix seed oil, stirring reaction 30-40 minute, add other remaining component again, continue stirring reaction 1-2 hour, to obtain final product.
The preparation method of described reactor high temperature-resistant wire lacquer, is characterized in that comprising the following steps:
(1), take dimethylbenzene, M-and P-cresols drops into and is uniformly mixed with in the reactor of agitator, be heated to 60-70 DEG C, add nylon 11, stir and be heated to 160-200 DEG C, after dissolving completely to nylon 11, then add polyvinylpyrrolidone, phenyl glycidyl ether, Zinc Stearate insulation 5-6 hour;
(2), by step (1) reaction mass be cooled to 70-80 DEG C, add silicon carbide, pentaerythritol triacrylate, linking agent TAC, hexamethylene diisocyanate, auxiliary agent, keep temperature, stirring reaction 2-3 hour;
(3), again add leftover materials, be warming up to 110-145 DEG C, continue stirring reaction 2-3 hour;
(4), cool material to 50-60 DEG C, be ground to 20-40 μm of slurry, filter and get final product.
Reactor high temperature-resistant wire lacquer of the present invention has following beneficial effect: the performance of painting in copper cover aluminum insulated wire production process improves, meet more than 180 DEG C heat conditions requirements, this paint is used for the skin of high heat resistance coil wire rod, can solidify with furnace temperature with polyester-imide priming paint, solve copper cover aluminum insulated wire all the time withstand voltage not up to standard, the difficult problem that hot stamping is not up to standard, resistance to pressure is good, and pin hole is controlled well.
Embodiment
Described reactor high temperature-resistant wire lacquer is made up of the raw material of following weight part (kilogram): resol 12-15, E-42 epoxy resin 12, aluminium nitride 3, pentaerythritol triacrylate 6, linking agent TAC2, nylon 11 12, Zinc Stearate 1, nano aluminum alumina 14, hexamethylene diisocyanate 4, polyvinylpyrrolidone 3, phenyl glycidyl ether 5, silicon carbide 1, auxiliary agent 7, dimethylbenzene 100, M-and P-cresols 100;
Described auxiliary agent is made up of following weight part (kilogram) raw material: nano mica powder 0.2, trolamine 1.2, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 2, hexamethylenetetramine 2, polyester acrylate 5, Viscoat 295 12, triethyl citrate 3, linking agent TAC1, Tenox PG 2, coix seed oil 1; Its preparation method is by polyester acrylate, Viscoat 295, triethyl citrate mixing, be heated to 60-70 DEG C, add linking agent TAC, Tenox PG, coix seed oil, stirring reaction 30-40 minute, add other remaining component again, continue stirring reaction 1-2 hour, to obtain final product.。
Preparation method comprises the following steps:
(1), take dimethylbenzene, M-and P-cresols drops into and is uniformly mixed with in the reactor of agitator, be heated to 60-70 DEG C, add nylon 11, stir and be heated to 160-200 DEG C, after dissolving completely to nylon 11, then add polyvinylpyrrolidone, phenyl glycidyl ether, Zinc Stearate insulation 5-6 hour;
(2), by step (1) reaction mass be cooled to 70-80 DEG C, add silicon carbide, pentaerythritol triacrylate, linking agent TAC, hexamethylene diisocyanate, auxiliary agent, keep temperature, stirring reaction 2-3 hour;
(3), again add leftover materials, be warming up to 110-145 DEG C, continue stirring reaction 2-3 hour;
(4), cool material to 50-60 DEG C, be ground to 20-40 μm of slurry, filter and get final product.
Use paint wire rod main performance index of the present invention as follows:
1, tack is good;
2, temperature classification >=180 DEG C, thermal shocking reaches 200 DEG C of paint films and does not ftracture;
3, transformer oil resistant 1200 hours/105 DEG C, paint film is without damage.
Claims (2)
1. a reactor high temperature-resistant wire lacquer, it is characterized in that, be made up of the raw material of following weight part: resol 12-15, E-42 epoxy resin 12-15, aluminium nitride 3-5, pentaerythritol triacrylate 6-9, linking agent TAC1-2, nylon 11 12-15, Zinc Stearate 1-2, nano aluminum alumina 14-20, hexamethylene diisocyanate 4-5, polyvinylpyrrolidone 2-3, phenyl glycidyl ether 5-7, silicon carbide 1-2, auxiliary agent 7-9, dimethylbenzene 100-120, M-and P-cresols 100-120;
Described auxiliary agent is made up of following raw materials in part by weight: nano mica powder 0.2-0.3, trolamine 1.2-1.3, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 2-3, hexamethylenetetramine 1-2, polyester acrylate 3-5, Viscoat 295 12-15, triethyl citrate 3-6, linking agent TAC1-2, Tenox PG 2-3, coix seed oil 1-2; Its preparation method is by polyester acrylate, Viscoat 295, triethyl citrate mixing, be heated to 60-70 DEG C, add linking agent TAC, Tenox PG, coix seed oil, stirring reaction 30-40 minute, add other remaining component again, continue stirring reaction 1-2 hour, to obtain final product.
2. the preparation method of reactor high temperature-resistant wire lacquer according to claim 1, is characterized in that comprising the following steps:
(1), take dimethylbenzene, M-and P-cresols drops into and is uniformly mixed with in the reactor of agitator, be heated to 60-70 DEG C, add nylon 11, stir and be heated to 160-200 DEG C, after dissolving completely to nylon 11, then add polyvinylpyrrolidone, phenyl glycidyl ether, Zinc Stearate insulation 5-6 hour;
(2), by step (1) reaction mass be cooled to 70-80 DEG C, add silicon carbide, pentaerythritol triacrylate, linking agent TAC, hexamethylene diisocyanate, auxiliary agent, keep temperature, stirring reaction 2-3 hour;
(3), again add leftover materials, be warming up to 110-145 DEG C, continue stirring reaction 2-3 hour;
(4), cool material to 50-60 DEG C, be ground to 20-40 μm of slurry, filter and get final product.