CN106280609A - A kind of computer data wire wrapping priming paint - Google Patents
A kind of computer data wire wrapping priming paint Download PDFInfo
- Publication number
- CN106280609A CN106280609A CN201610708510.3A CN201610708510A CN106280609A CN 106280609 A CN106280609 A CN 106280609A CN 201610708510 A CN201610708510 A CN 201610708510A CN 106280609 A CN106280609 A CN 106280609A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- data wire
- priming paint
- computer data
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe present invention relates to a kind of computer data wire wrapping priming paint，It is made up of the component of following mass fraction: lead sulfate tribasic 16～20 parts、Chitosan 18～22 parts、Litsea cubeba oil 14～18 parts、Calcium carbonate 12～16 parts、Merlon 18～22 parts、Hexamethylene 14～18 parts、Polyvinylpyrrolidone 12～16 parts、Acetylspiramycin 18～22 parts、Triethanolamine 14～18 parts、Butanediol 12～16 parts、Reed fragrant plant glue 18～22 parts、Dichloroisocyanuric acid sodium 14～18 parts、Oleum Camphora 14～18 parts、Bravo 12～16 parts、Trimethyl benzyl ammonia chloride 18～22 parts、Tea polyphenols 14～18 parts、Sodium diacetate 12～16 parts、Kaolin powder 18～22 parts、Pentaerythritol acrylate 14～18 parts、Furane resins 12～16 parts、Zinc stearate 18～22 parts、Sodium laurylsulfate 14～18 parts、Stannum oxide 12～16 parts、Titanium dioxide 18～22 parts、Nano cupric oxide 14～18 parts.Product of the present invention improves properties of product.
Description
Technical field
The present invention relates to a kind of computer data wire wrapping priming paint, belong to computer technology field.
Background technology
Computer (computer) is commonly called as computer, is modern a kind of electronic computer device for supercomputing, Ke Yijin
Row numerical computations, can carry out again logical calculated, also have store-memory function.It is can to run according to program, automatically, at a high speed
Process the modernization intelligent electronic device of mass data.It is made up of hardware system and software system, is fitted without any software
Computer be referred to as bare machine.Supercomputer, industrial control computer, network computer, personal computer, embedded can be divided into
Computer five class, more advanced computer has biocomputer, photonic computer, quantum computer etc..Invention on computer person is about
Writing brush von Neumann.Computer is one of 20th century state-of-the-art science and technology invention, and the production to the mankind is movable and social
Activity creates extremely important impact, and develops rapidly with powerful vitality.Its application is from initial military section
Grind the application extension every field to society, defined huge computer industry, driven the technology of global range
Progressive, thus cause deep social change, computer, throughout general school, enterprises and institutions, enters common people house,
Become requisite instrument in information-intensive society.During computer is installed and used, it is necessary to use data wire, these data wires are necessary to adopt
Using effect is improved by suitable mode.
Summary of the invention
It is an object of the invention to provide a kind of computer data wire wrapping priming paint, in order to computer data line bag is better achieved
The function of dress priming paint.
To achieve these goals, technical scheme is as follows.
A kind of computer data wire wrapping priming paint, is made up of the component of following mass fraction: lead sulfate tribasic 16～20 parts,
Chitosan 18～22 parts, litsea cubeba oil 14～18 parts, calcium carbonate 12～16 parts, Merlon 18～22 parts, polyhexamethylene pair
Guanidine hydrochloride 14～18 parts, polyvinylpyrrolidone 12～16 parts, acetylspiramycin 18～22 parts, triethanolamine 14～18
Part, butanediol 12～16 parts, reed fragrant plant glue 18～22 parts, dichloroisocyanuric acid sodium 14～18 parts, Oleum Camphora 14～18 parts, Bravo
12～16 parts, trimethyl benzyl ammonia chloride 18～22 parts, tea polyphenols 14～18 parts, sodium diacetate 12～16 parts, kaolin powder 18
～22 parts, pentaerythritol acrylate 14～18 parts, furane resins 12～16 parts, zinc stearate 18～22 parts, lauryl alcohol sulphuric acid
Sodium 14～18 parts, stannum oxide 12～16 parts, titanium dioxide 18～22 parts, nano cupric oxide 14～18 parts.
Further, above-mentioned computer data wire wrapping priming paint, it is made up of the component of following mass fraction: lead sulfate tribasic
16 parts, chitosan 18 parts, litsea cubeba oil 14 parts, calcium carbonate 12 parts, Merlon 18 parts, hexamethylene 14
Part, polyvinylpyrrolidone 12 parts, acetylspiramycin 18 parts, triethanolamine 14 parts, butanediol 12 parts, 18 parts of reed fragrant plant glue, two
14 parts of chlorine isocyanuric acid sodium, Oleum Camphora 14 parts, Bravo 12 parts, trimethyl benzyl ammonia chloride 18 parts, tea polyphenols 14 parts, diacetic acid
12 parts of sodium, kaolin powder 18 parts, pentaerythritol acrylate 14 parts, furane resins 12 parts, zinc stearate 18 parts, lauryl alcohol sulphuric acid
14 parts of sodium, stannum oxide 12 parts, titanium dioxide 18 parts, nano cupric oxide 14 parts.
Further, above-mentioned computer data wire wrapping priming paint, it is made up of the component of following mass fraction: lead sulfate tribasic
18 parts, chitosan 20 parts, litsea cubeba oil 16 parts, calcium carbonate 14 parts, Merlon 20 parts, hexamethylene 16
Part, polyvinylpyrrolidone 14 parts, acetylspiramycin 20 parts, triethanolamine 16 parts, butanediol 14 parts, 20 parts of reed fragrant plant glue, two
16 parts of chlorine isocyanuric acid sodium, Oleum Camphora 16 parts, Bravo 14 parts, trimethyl benzyl ammonia chloride 20 parts, tea polyphenols 16 parts, diacetic acid
14 parts of sodium, kaolin powder 20 parts, pentaerythritol acrylate 16 parts, furane resins 14 parts, zinc stearate 20 parts, lauryl alcohol sulphuric acid
16 parts of sodium, stannum oxide 14 parts, titanium dioxide 20 parts, nano cupric oxide 16 parts.
Further, above-mentioned computer data wire wrapping priming paint, it is made up of the component of following mass fraction: lead sulfate tribasic
20 parts, chitosan 22 parts, litsea cubeba oil 18 parts, calcium carbonate 16 parts, Merlon 22 parts, hexamethylene 18
Part, polyvinylpyrrolidone 16 parts, acetylspiramycin 22 parts, triethanolamine 18 parts, butanediol 16 parts, 22 parts of reed fragrant plant glue, two
18 parts of chlorine isocyanuric acid sodium, Oleum Camphora 18 parts, Bravo 16 parts, trimethyl benzyl ammonia chloride 22 parts, tea polyphenols 18 parts, diacetic acid
16 parts of sodium, kaolin powder 22 parts, pentaerythritol acrylate 18 parts, furane resins 16 parts, zinc stearate 22 parts, lauryl alcohol sulphuric acid
18 parts of sodium, stannum oxide 16 parts, titanium dioxide 22 parts, nano cupric oxide 18 parts.
Further, above-mentioned computer data wire wrapping priming paint preparation method step is as follows:
(1) by the lead sulfate tribasic of described mass fraction, chitosan, litsea cubeba oil, calcium carbonate, Merlon, poly-six
Di-2-ethylhexylphosphine oxide guanidine hydrochloride, polyvinylpyrrolidone, acetylspiramycin, triethanolamine, butanediol, reed fragrant plant glue, dichloro isocyanide
Urea acid sodium, kaolin powder, stannum oxide, titanium dioxide, nano cupric oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is 20
～40KHz, rate of dispersion 5000～about 5400r/min, jitter time is 30～60min；
(2) Oleum Camphora of described mass fraction, Bravo, trimethyl benzyl ammonia chloride, tea polyphenols, sodium diacetate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 20～35KHz, rate of dispersion 4800～about 5200r/min, jitter time be 30～
50min；
(3) pentaerythritol acrylate of described mass fraction, furane resins, zinc stearate, sodium laurylsulfate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 20～30KHz, rate of dispersion 4600～about 4800r/min, jitter time be 20～
40min；This product is prepared after mix homogeneously.
This beneficial effect of the invention is: this computer data wire wrapping priming paint process of preparing is simple, prepared product
Product have the most superior fire-retardant, acid and alkali-resistance, anti-mildew anti-microbial property, improve properties of product.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is described, in order to be better understood from the present invention.
Embodiment 1
Computer data wire wrapping priming paint in the present embodiment, is made up of the component of following mass fraction: lead sulfate tribasic
16 parts, chitosan 18 parts, litsea cubeba oil 14 parts, calcium carbonate 12 parts, Merlon 18 parts, hexamethylene 14
Part, polyvinylpyrrolidone 12 parts, acetylspiramycin 18 parts, triethanolamine 14 parts, butanediol 12 parts, 18 parts of reed fragrant plant glue, two
14 parts of chlorine isocyanuric acid sodium, Oleum Camphora 14 parts, Bravo 12 parts, trimethyl benzyl ammonia chloride 18 parts, tea polyphenols 14 parts, diacetic acid
12 parts of sodium, kaolin powder 18 parts, pentaerythritol acrylate 14 parts, furane resins 12 parts, zinc stearate 18 parts, lauryl alcohol sulphuric acid
14 parts of sodium, stannum oxide 12 parts, titanium dioxide 18 parts, nano cupric oxide 14 parts.
Above-mentioned computer data wire wrapping priming paint preparation method step is as follows:
(1) by the lead sulfate tribasic of described mass fraction, chitosan, litsea cubeba oil, calcium carbonate, Merlon, poly-six
Di-2-ethylhexylphosphine oxide guanidine hydrochloride, polyvinylpyrrolidone, acetylspiramycin, triethanolamine, butanediol, reed fragrant plant glue, dichloro isocyanide
Urea acid sodium, kaolin powder, stannum oxide, titanium dioxide, nano cupric oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is
20kHz, rate of dispersion about 5400r/min, jitter time is 60min；
(2) Oleum Camphora of described mass fraction, Bravo, trimethyl benzyl ammonia chloride, tea polyphenols, sodium diacetate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min；
(3) pentaerythritol acrylate of described mass fraction, furane resins, zinc stearate, sodium laurylsulfate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min；Mix homogeneously
Rear prepared this product.
Embodiment 2
Computer data wire wrapping priming paint in the present embodiment, is made up of the component of following mass fraction: lead sulfate tribasic
18 parts, chitosan 20 parts, litsea cubeba oil 16 parts, calcium carbonate 14 parts, Merlon 20 parts, hexamethylene 16
Part, polyvinylpyrrolidone 14 parts, acetylspiramycin 20 parts, triethanolamine 16 parts, butanediol 14 parts, 20 parts of reed fragrant plant glue, two
16 parts of chlorine isocyanuric acid sodium, Oleum Camphora 16 parts, Bravo 14 parts, trimethyl benzyl ammonia chloride 20 parts, tea polyphenols 16 parts, diacetic acid
14 parts of sodium, kaolin powder 20 parts, pentaerythritol acrylate 16 parts, furane resins 14 parts, zinc stearate 20 parts, lauryl alcohol sulphuric acid
16 parts of sodium, stannum oxide 14 parts, titanium dioxide 20 parts, nano cupric oxide 16 parts.
Above-mentioned computer data wire wrapping priming paint preparation method step is as follows:
(1) by the lead sulfate tribasic of described mass fraction, chitosan, litsea cubeba oil, calcium carbonate, Merlon, poly-six
Di-2-ethylhexylphosphine oxide guanidine hydrochloride, polyvinylpyrrolidone, acetylspiramycin, triethanolamine, butanediol, reed fragrant plant glue, dichloro isocyanide
Urea acid sodium, kaolin powder, stannum oxide, titanium dioxide, nano cupric oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is
30kHz, rate of dispersion about 5200r/min, jitter time is 45min；
(2) Oleum Camphora of described mass fraction, Bravo, trimethyl benzyl ammonia chloride, tea polyphenols, sodium diacetate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min；
(3) pentaerythritol acrylate of described mass fraction, furane resins, zinc stearate, sodium laurylsulfate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min；Mix homogeneously
Rear prepared this product.
Embodiment 3
Computer data wire wrapping priming paint in the present embodiment, is made up of the component of following mass fraction: lead sulfate tribasic
20 parts, chitosan 22 parts, litsea cubeba oil 18 parts, calcium carbonate 16 parts, Merlon 22 parts, hexamethylene 18
Part, polyvinylpyrrolidone 16 parts, acetylspiramycin 22 parts, triethanolamine 18 parts, butanediol 16 parts, 22 parts of reed fragrant plant glue, two
18 parts of chlorine isocyanuric acid sodium, Oleum Camphora 18 parts, Bravo 16 parts, trimethyl benzyl ammonia chloride 22 parts, tea polyphenols 18 parts, diacetic acid
16 parts of sodium, kaolin powder 22 parts, pentaerythritol acrylate 18 parts, furane resins 16 parts, zinc stearate 22 parts, lauryl alcohol sulphuric acid
18 parts of sodium, stannum oxide 16 parts, titanium dioxide 22 parts, nano cupric oxide 18 parts.
Above-mentioned computer data wire wrapping priming paint preparation method step is as follows:
(1) by the lead sulfate tribasic of described mass fraction, chitosan, litsea cubeba oil, calcium carbonate, Merlon, poly-six
Di-2-ethylhexylphosphine oxide guanidine hydrochloride, polyvinylpyrrolidone, acetylspiramycin, triethanolamine, butanediol, reed fragrant plant glue, dichloro isocyanide
Urea acid sodium, kaolin powder, stannum oxide, titanium dioxide, nano cupric oxide are mixed, ultrasonic high speed dispersion, and ultrasonic frequency is
40kHz, rate of dispersion 5000r/min, jitter time is 30min；
(2) Oleum Camphora of described mass fraction, Bravo, trimethyl benzyl ammonia chloride, tea polyphenols, sodium diacetate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min；
(3) pentaerythritol acrylate of described mass fraction, furane resins, zinc stearate, sodium laurylsulfate are added,
Ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min；Mix homogeneously
Rear prepared this product.
Performance measurement is carried out for the product in embodiment 1, embodiment 2 and embodiment 3 and certain commercially available prod, measured
Data are as shown in table 1.Fire protection flame retarding level estimate uses UL94 standard.
Table 1 the performance test results
Visible, product of the present invention has the most corrosion-resistant, fire protection flame retarding, anti-mildew, anti-microbial property.
The above is the preferred embodiment of the present invention, it is noted that for those skilled in the art
For, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications are also considered as
Protection scope of the present invention.
Claims (5)
1. a computer data wire wrapping priming paint, it is characterised in that: it is made up of the component of following mass fraction: lead sulfate tribasic
16～20 parts, chitosan 18～22 parts, litsea cubeba oil 14～18 parts, calcium carbonate 12～16 parts, Merlon 18～22 parts, poly-six
Di-2-ethylhexylphosphine oxide guanidine hydrochloride 14～18 parts, polyvinylpyrrolidone 12～16 parts, acetylspiramycin 18～22 parts, triethanolamine
14～18 parts, butanediol 12～16 parts, reed fragrant plant glue 18～22 parts, dichloroisocyanuric acid sodium 14～18 parts, Oleum Camphora 14～18 parts,
Bravo 12～16 parts, trimethyl benzyl ammonia chloride 18～22 parts, tea polyphenols 14～18 parts, sodium diacetate 12～16 parts, kaolinite
Soil powder 18～22 parts, pentaerythritol acrylate 14～18 parts, furane resins 12～16 parts, zinc stearate 18～22 parts, Laurel
Alcohol sodium sulfate 14～18 parts, stannum oxide 12～16 parts, titanium dioxide 18～22 parts, nano cupric oxide 14～18 parts.
Computer data wire wrapping priming paint the most according to claim 1, it is characterised in that: described computer data wire wrapping priming paint
Be made up of the component of following mass fraction: lead sulfate tribasic 16 parts, chitosan 18 parts, litsea cubeba oil 14 parts, calcium carbonate 12 parts,
Merlon 18 parts, hexamethylene 14 parts, polyvinylpyrrolidone 12 parts, acetylspiramycin 18 parts, three
Ethanolamine 14 parts, butanediol 12 parts, 18 parts of reed fragrant plant glue, dichloroisocyanuric acid sodium 14 parts, Oleum Camphora 14 parts, Bravo 12 parts, three
Methyl-benzyl ammonium chloride 18 parts, tea polyphenols 14 parts, sodium diacetate 12 parts, kaolin powder 18 parts, pentaerythritol acrylate 14 parts,
Furane resins 12 parts, zinc stearate 18 parts, sodium laurylsulfate 14 parts, stannum oxide 12 parts, titanium dioxide 18 parts, nano cupric oxide 14
Part.
3. according to the computer data wire wrapping priming paint described in claim 1 to 2, it is characterised in that: described computer data wire wrapping
Priming paint is made up of the component of following mass fraction: lead sulfate tribasic 18 parts, chitosan 20 parts, litsea cubeba oil 16 parts, calcium carbonate
14 parts, Merlon 20 parts, hexamethylene 16 parts, polyvinylpyrrolidone 14 parts, acetylspiramycin 20
Part, triethanolamine 16 parts, butanediol 14 parts, 20 parts of reed fragrant plant glue, dichloroisocyanuric acid sodium 16 parts, Oleum Camphora 16 parts, Bravo 14
Part, trimethyl benzyl ammonia chloride 20 parts, tea polyphenols 16 parts, sodium diacetate 14 parts, kaolin powder 20 parts, pentaerythritol acrylate
16 parts, furane resins 14 parts, zinc stearate 20 parts, sodium laurylsulfate 16 parts, stannum oxide 14 parts, titanium dioxide 20 parts, nano oxygen
Change copper 16 parts.
4. according to the computer data wire wrapping priming paint described in claims 1 to 3, it is characterised in that: described computer data wire wrapping
Priming paint is made up of the component of following mass fraction: lead sulfate tribasic 20 parts, chitosan 22 parts, litsea cubeba oil 18 parts, calcium carbonate
16 parts, Merlon 22 parts, hexamethylene 18 parts, polyvinylpyrrolidone 16 parts, acetylspiramycin 22
Part, triethanolamine 18 parts, butanediol 16 parts, 22 parts of reed fragrant plant glue, dichloroisocyanuric acid sodium 18 parts, Oleum Camphora 18 parts, Bravo 16
Part, trimethyl benzyl ammonia chloride 22 parts, tea polyphenols 18 parts, sodium diacetate 16 parts, kaolin powder 22 parts, pentaerythritol acrylate
18 parts, furane resins 16 parts, zinc stearate 22 parts, sodium laurylsulfate 18 parts, stannum oxide 16 parts, titanium dioxide 22 parts, nano oxygen
Change copper 18 parts.
Computer data wire wrapping priming paint the most according to claim 1, it is characterised in that: described computer data wire wrapping priming paint
Preparation method step is as follows:
(1) by the lead sulfate tribasic of described mass fraction, chitosan, litsea cubeba oil, calcium carbonate, Merlon, poly-six methylenes
Base biguanide hydrochloride, polyvinylpyrrolidone, acetylspiramycin, triethanolamine, butanediol, reed fragrant plant glue, DCCA
Sodium, kaolin powder, stannum oxide, titanium dioxide, nano cupric oxide are mixed, ultrasonic high speed dispersion, ultrasonic frequency be 20～
40KHz, rate of dispersion about 5000～5400r/min, jitter time is 30～about 60min；
(2) Oleum Camphora of described mass fraction, Bravo, trimethyl benzyl ammonia chloride, tea polyphenols, sodium diacetate are added, ultrasonic
High speed dispersion, ultrasonic frequency is 20～35KHz, and rate of dispersion is about 4800～5200r/min, jitter time be 30～
About 50min；
(3) pentaerythritol acrylate of described mass fraction, furane resins, zinc stearate, sodium laurylsulfate are added, ultrasonic
High speed dispersion, ultrasonic frequency is 20～30KHz, and rate of dispersion is about 4600～4800r/min, jitter time be 20～
About 40min；This product is prepared after mix homogeneously.