CN107447147A - A kind of black aluminium alloy and preparation method thereof - Google Patents
A kind of black aluminium alloy and preparation method thereof Download PDFInfo
- Publication number
- CN107447147A CN107447147A CN201710706357.5A CN201710706357A CN107447147A CN 107447147 A CN107447147 A CN 107447147A CN 201710706357 A CN201710706357 A CN 201710706357A CN 107447147 A CN107447147 A CN 107447147A
- Authority
- CN
- China
- Prior art keywords
- parts
- titanium
- aluminium
- powder
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of black aluminium alloy and preparation method thereof, contains following components in parts by weight：Aluminium：50 80 parts；Zinc：20 40 parts；Copper：58 parts；Titanium：47 parts, black pigment：5 10 parts.Comprise the following steps：Powder, the mesh of fineness of powder 300 500 is made in aluminium, zinc, copper, titanium and black pigment；Aluminium, zinc, copper powders are mixed and heated to 1000 DEG C；C, titanium powder is heated to its fusing；D, the melt titanium for obtaining step c is added in the fusion mixture obtained in b step and stirred, 1,000 1200 DEG C of keeping temperature, the 5min of mixing time 3；The beneficial effects of the invention are as follows：Manufacture craft is simple, and cost of manufacture is relatively low, need not meet requirement of the people to health in its surface spraying antirust or decorative paint, unharmful substance release after making finished product, easy to spread.
Description
Technical field
The present invention relates to alloying metal preparation method, especially a kind of black aluminium alloy and preparation method thereof.
Background technology
Non-ferrous alloy it is widely used, be mainly used in automobile, building materials, household electrical appliances, electric power, 3C, machine-building etc. row
Industry.In recent years, fast-developing situation is presented in the industry such as automobile, building materials, household electrical appliances, electric power, 3C, machine-building, and non-ferrous metal closes
The development of golden manufacturing relies on the pulling of downstream industry, with the development of downstream industry, non-ferrous alloy manufacturing
Also it is rapidly developed.Non-ferrous alloy it is widely used, be mainly used in automobile, building materials, household electrical appliances, electric power, 3C, machinery system
The industry such as make.In recent years, fast-developing situation is presented in the industry such as automobile, building materials, household electrical appliances, electric power, 3C, machine-building, and coloured
The development of metal alloy manufacturing relies on the pulling of downstream industry, with the development of downstream industry, non-ferrous alloy system
Industry is made also to be rapidly developed.
Traditional non-ferrous metal is that the color of metal in itself is determined, is typically needed after processing on its surface
The material such as varnish with lacquer is used for antirust and decoration, the production of paint and environment can be caused than more serious pollution using process,
And after use can also sustained release harmful substance, influence people physical and mental health, it is impossible to meet the life requirement of modern people,
Therefore it is badly in need of a kind of improved technology to solve above-mentioned technological deficiency.
The content of the invention
The invention provides a kind of black aluminium alloy and preparation method thereof.
The present invention is achieved by the following technical solutions.
A kind of black aluminium alloy and preparation method thereof, contains following components in parts by weight：Aluminium：50-80 parts；Zinc：20-
40 parts；Copper：5-8 parts；Titanium：4-7 parts, black pigment：5-10 parts.
The black pigment is copper-chrome black.
Comprise the following steps：
A, powder, fineness of powder 300-500 mesh is made in aluminium, zinc, copper, titanium and black pigment；
B, aluminium, zinc, copper powders are mixed and heated to 1000 DEG C；
C, titanium powder is heated to its fusing；
D, the melt titanium for obtaining step c is added in the fusion mixture obtained in b step and stirred, keeping temperature 1000-
1200 DEG C, mixing time 3-5min；
E, black pigment powder is added in the alloy mixed melting thing obtained in Step d, is kept stirring for 10-15min, stirred
When 900-1000 DEG C of keeping temperature；
F, mould, natural cooling are injected according to forming requirements.
The beneficial effects of the invention are as follows：Manufacture craft is simple, and cost of manufacture is relatively low, need not be sprayed after making finished product on its surface
Antirust or decorative paint are applied, unharmful substance release, meets requirement of the people to health, it is easy to spread.
Embodiment
In order to deepen the understanding of the present invention, below in conjunction with embodiment, the invention will be further described, the embodiment
It is only used for explaining the present invention, does not form the restriction to protection scope of the present invention.
Embodiment 1
A kind of black aluminium alloy and preparation method thereof, contains following components in parts by weight：Aluminium：50-80 parts；Zinc：20-40
Part；Copper：5-8 parts；Titanium：4-7 parts, black pigment：5-10 parts.
Black pigment is copper-chrome black.
Comprise the following steps：
A, powder, fineness of powder 300-500 mesh is made in aluminium, zinc, copper, titanium and black pigment；
B, aluminium, zinc, copper powders are mixed and heated to 1000 DEG C；
C, titanium powder is heated to its fusing；
D, the melt titanium for obtaining step c is added in the fusion mixture obtained in b step and stirred, keeping temperature 1000-
1200 DEG C, mixing time 3-5min；
E, black pigment powder is added in the alloy mixed melting thing obtained in Step d, is kept stirring for 10-15min, stirred
When 900-1000 DEG C of keeping temperature；
F, mould, natural cooling are injected according to forming requirements.
Embodiment 2
A kind of black aluminium alloy and preparation method thereof, contains following components in parts by weight：Aluminium：50-80 parts；Zinc：20-40
Part；Copper：5-8 parts；Titanium：4-7 parts, black pigment：5-10 parts.
Black pigment is copper-chrome black.
Comprise the following steps：
A, powder, fineness of powder 300-500 mesh is made in aluminium, zinc, copper, titanium and black pigment；
B, aluminium, zinc, copper powders are mixed and heated to 1000 DEG C；
C, titanium powder is heated to its fusing；
D, the melt titanium for obtaining step c is added in the fusion mixture obtained in b step and stirred, keeping temperature 1000-
1200 DEG C, mixing time 3-5min；
E, black pigment powder is added in the alloy mixed melting thing obtained in Step d, is kept stirring for 10-15min, stirred
When 900-1000 DEG C of keeping temperature；
F, mould, natural cooling are injected according to forming requirements.
Embodiment 3
A kind of black aluminium alloy and preparation method thereof, contains following components in parts by weight：Aluminium：50-80 parts；Zinc：20-40
Part；Copper：5-8 parts；Titanium：4-7 parts, black pigment：5-10 parts.
Black pigment is copper-chrome black.
Comprise the following steps：
A, powder, fineness of powder 300-500 mesh is made in aluminium, zinc, copper, titanium and black pigment；
B, aluminium, zinc, copper powders are mixed and heated to 1000 DEG C；
C, titanium powder is heated to its fusing；
D, the melt titanium for obtaining step c is added in the fusion mixture obtained in b step and stirred, keeping temperature 1000-
1200 DEG C, mixing time 3-5min；
E, black pigment powder is added in the alloy mixed melting thing obtained in Step d, is kept stirring for 10-15min, stirred
When 900-1000 DEG C of keeping temperature；
F, mould, natural cooling are injected according to forming requirements.
The beneficial effects of the invention are as follows：Manufacture craft is simple, and cost of manufacture is relatively low, need not be sprayed after making finished product on its surface
Antirust or decorative paint are applied, unharmful substance release, meets requirement of the people to health, it is easy to spread.
More than, only it is presently preferred embodiments of the present invention, is not the limitation for making any other form to the present invention, and
Any modification or equivalent variations that technical spirit according to the present invention is made, still fall within scope of the present invention.
Claims (3)
- A kind of 1. black aluminium alloy and preparation method thereof, it is characterised in that：Contain following components in parts by weight：Aluminium：50-80 Part；Zinc：20-40 parts；Copper：5-8 parts；Titanium：4-7 parts, black pigment：5-10 parts.
- A kind of 2. black aluminium alloy according to claim 1 and preparation method thereof, it is characterised in that：The black pigment is Copper-chrome black.
- A kind of 3. black aluminium alloy according to claim 1 and preparation method thereof, it is characterised in that：Comprise the following steps：A, powder, fineness of powder 300-500 mesh is made in aluminium, zinc, copper, titanium and black pigment；B, aluminium, zinc, copper powders are mixed and heated to 1000 DEG C；C, titanium powder is heated to its fusing；D, the melt titanium for obtaining step c is added in the fusion mixture obtained in b step and stirred, keeping temperature 1000- 1200 DEG C, mixing time 3-5min；E, black pigment powder is added in the alloy mixed melting thing obtained in Step d, is kept stirring for 10-15min, stirred When 900-1000 DEG C of keeping temperature；F, mould, natural cooling are injected according to forming requirements.