CN104403517A - High imitation electroplating silver powder paint and preparation method thereof - Google Patents
High imitation electroplating silver powder paint and preparation method thereof Download PDFInfo
- Publication number
- CN104403517A CN104403517A CN201410633548.XA CN201410633548A CN104403517A CN 104403517 A CN104403517 A CN 104403517A CN 201410633548 A CN201410633548 A CN 201410633548A CN 104403517 A CN104403517 A CN 104403517A
- Authority
- CN
- China
- Prior art keywords
- powder
- powder coating
- electrosilvering
- silver powder
- imitates
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high imitation electroplating silver powder paint. The paint comprises transparent paint basic powder and silver powder, and the transparent paint basic powder contains a silver powder directional arranging agent. The invention also discloses a binding preparation method of the powdery paint. The silver powder directional arranging agent is added into the transparent paint basic powder, then under the binding assistance of a binding machine, the silver powder migrates to the surface of melt powdery paint with high viscosity, the silver powder is well arranged under the effect of the directional arranging agent, and a reflective chromium-coated mirror metal-liked effect can be achieved on the surface of the coating.
Description
Technical field
The present invention relates to a kind of powder coating, particularly relate to a kind of high imitative electrosilvering powder coating.Meanwhile, the invention still further relates to the preparation method of the imitative electrosilvering powder coating of this height.
Background technology
Powder coating has the characteristic such as performance, good decorative property, use safety that is energy-conservation, VOC free discharge, and domestic powder coating technology development in recent years rapidly.Powder coating is as decorative material, and plentiful along with what live, people are no longer limited to the requirement of powder coating coating single color.There is the binding powder coating of metal appearance, generally acknowledged it is art of powder coatings medium and high-grade goods by people, be subject to the favorable comment of the market segments such as household electrical appliances, furniture and automobile, slowly promote in every field and come.The coating that height wherein imitates electrosilvering powder coating has excellent mirror effect and beautiful outward appearance, extremely the pursuing of people.But current height imitates the coating gloss partially dark (< 100GU) of electrosilvering powder coating, and coating has dim spot pockety and shrinkage cavity, the metallic membrane effect of coatingsurface reflective chromium plating minute surface is unsatisfactory.
Summary of the invention
The object of this invention is to provide a kind of high imitative electrosilvering powder coating, this powder coating coating gloss > 100GU, create the metal effect of reflective picture chromium plating minute surface and beautiful appearance effect.
Another object of the present invention is to provide above-mentioned height to imitate the binding method of electrosilvering powder coating.
First object of the present invention is achieved through the following technical solutions: a kind of high imitative electrosilvering powder coating, comprises powder at the bottom of Clear paint and silver powder, wherein, align agent in powder at the bottom of described Clear paint containing silver powder.
Agent is aligned containing appropriate silver powder in powder at the bottom of Clear paint of the present invention, after at the bottom of Clear paint, powder and silver powder are bound, when hot setting, silver powder aligns agent and promotes that silver powder is to melting high viscosity powder coating surface transport, aligning under agent effect, obtaining good aligning, producing the metallic membrane of reflective picture chromium plating minute surface at coatingsurface, make coatingsurface gloss at more than 100GU, increase coating whiteness and metal sense.
Particularly, powder at the bottom of Clear paint of the present invention aligns agent by clear coat binder and silver powder and forms.Wherein, described clear coat binder is convention transparent powder coating, and its component comprises resin and auxiliary agent etc.
In the present invention, with powder coating total mass for Calculation Basis, the mass parts that described silver powder aligns agent is 0.5 ~ 1.5 part, preferably 0.8 ~ 1.2 part.Particularly, it is aldehyde ketone condensation resin that described silver powder aligns agent.Aldehyde ketone condensation resin can guarantee metal-powder mirror effect, can keep enough mechanical propertys and aesthetic appearance simultaneously.As one embodiment of the present of invention, described aldehyde ketone condensation resin is white odorless particle, fusing point 127 ~ 169 DEG C, fugitive constituent≤0.5%, the such as CATB-250 of the various trade mark, CTB-280 and K-100 etc., wherein preferred CATB-250, K-100.
In the present invention, with the total mass of clear coat binder for Calculation Basis, the mass parts of the resin in described clear coat binder is 50 ~ 95 parts, and it comprises the conventional resin of all kinds powder coating such as epoxy resin, vibrin, urethane resin and acrylic resin.Described auxiliary agent is conven-tional adjuvants used for powder coating, and its mass parts is 1 ~ 10 part, and it comprises one or more the mixing in flow agent, defoamer, st-yrax and ventilating agent etc.
Also solidifying agent can be comprised in clear coat binder of the present invention, this solidifying agent mass parts is 1 ~ 50 part, and it comprises the corresponding solidifying agent of all kinds powder coating such as epoxy resin, isocyanuric acid three-glycidyl ester (TGIC), amine curing agent and beta-hydroxy alkylamide (HAA).
In the present invention, the part by weight 100:0.003-100:0.015 of powder and silver powder at the bottom of described Clear paint, preferred 100:0.008.
Described silver powder is metallic leafing pigments.Particularly, described metallic leafing pigments is metallic aluminium pigment.Described metallic aluminium pigment is the floating type aluminium pigment of particle diameter 4-20 μm, comprises SCHLENK company Powdal 170XB, Powdal 130; Benda-Lutz company 2091,7080,2081 and ECKART company PC100, Chromal IV etc.
Second object of the present invention is achieved through the following technical solutions: the binding method of high imitative electrosilvering powder coating, comprises the following steps:
(1) take powder at the bottom of Clear paint in proportion and silver powder mixes, be placed in binding machine;
(2) in room temperature environment, pass into shielding gas in bonding machines and bind;
(3) powder completing nation fixed sieves, and obtains high imitative electrosilvering metal powder coating.
Rotating speed 400 ~ the 1000n/min of bonding machines in step of the present invention (2), rotation time arranges 3 ~ 7min.Preferred rotating speed 7000 ~ 8000n/min, rotation time arranges 4 ~ 6min, to guarantee that powder at the bottom of Clear paint fully mixes with silver powder in bonding machines equipment, silver powder is produced and aligns effect.
Embodiment
The present invention will be described to enumerate a part of specific examples below, be necessary to herein means out be following specific embodiment only for the invention will be further described, do not represent limiting the scope of the invention.Some nonessential amendments that other people make according to the present invention and adjustment still belong to protection scope of the present invention.
In following examples, bonding machines adopts German HENSCHEL company MB350 model bonding machines group.Rotating speed 400 ~ the 1000n/min of bonding machines in step of the present invention (2), rotation time arranges 3 ~ 7min.Preferred rotating speed 7000 ~ 8000n/min, rotation time arranges 4 ~ 6min, to guarantee that powder at the bottom of powder fully mixes with silver powder in bonding machines equipment, silver powder is produced and aligns effect.
It is aldehyde ketone condensation resin that silver powder aligns agent.Aldehyde ketone condensation resin can guarantee metal-powder mirror effect, can keep enough mechanical propertys and aesthetic appearance simultaneously.As one embodiment of the present of invention, described aldehyde ketone condensation resin is white odorless particle, fusing point 127 ~ 169 DEG C, fugitive constituent≤0.5%, the such as CATB-250 of the various trade mark, CTB-280 and K-100 etc., wherein preferred CATB-250, K-100.
Auxiliary agent is conven-tional adjuvants used for powder coating, comprises one or more the mixing in flow agent, st-yrax, ventilating agent etc.
Silver powder is metallic leafing pigments.Particularly, described metallic leafing pigments is metallic aluminium pigment.Described metallic aluminium pigment is the floating type aluminium pigment of particle diameter 4-20 μm, comprises SCHLENK company Powdal 170XB, Powdal 130; Benda-Lutz company 2091,7080,2081 and ECKART company PC100, Chromal IV etc.
Vibrin NH3307, Guangzhou Qing Tian Resins Corporation produces.
Vibrin SJ4B, Anhui Shenjian New Material Co., Ltd. produces.
Vibrin P5086, Hangzhou Zhong Fa Industrial Co., Ltd. produces.
Epoxy resin R304 mitsui petrochemical industry is produced
The kind floating Chemical Manufacture in epoxy resin E-12 (604) Mount Huang
embodiment 1
Component and weight:
Vibrin P5086 50 parts
Epoxy resin E-12 (604) 50 parts
Flow agent 1.3 parts
St-yrax 0.6 part
K-100 0.8 part
Powder preparation at the bottom of Clear paint:
A () takes vibrin P5086, epoxy resin E-12 (604), flow agent, st-yrax and K-100 in proportion, be placed in compounding jar, fully mixing also broken 1 ~ 10 minute.
B the material after () fragmentation enters twin screw extruder and extrudes; Forcing machine heating and temperature control is at 80 ~ 120 DEG C.
(c) extrude after material be ground into through compressing tablet, cooling, pulverizer the powder that particle diameter (equivalent grain size D50) is 30 ~ 45 um, then screening after namely obtain powder at the bottom of Clear paint.
binding method:
(1) by powder at the bottom of Clear paint and the pre-mixing of metallic leafing pigments Benda-Lutz company 2091, part by weight 100:0.003 ~ 100:0.015, preferred 100:0.008.Take and mix, add in bonding machines.
(2) in room temperature environment, pass into shielding gas in bonding machines and bind.Arrange bonding machines parameter, rotating speed arranges 400-1000n/min, preferably 700 ~ 800 n/min, set of time 5min.
(3) after nation completes surely, gained powder sieves, and obtains high imitative electrosilvering powder coating.
Take out high imitative electrosilvering powder coating, spray plate with electrostatic gun, after baking, both obtain the metal effect that film coated surface produces reflective picture chromium plating minute surface.
embodiment 2
Component and weight:
Vibrin NH3307 93 parts
TGIC 7 parts
Flow agent 1.3 parts
St-yrax 0.6 part
CATB-250 0.8 part
Powder preparation at the bottom of Clear paint:
A () takes vibrin NH3307, TGIC, flow agent, st-yrax and CATB-250 in proportion, be placed in compounding jar, fully mixing also broken 1 ~ 10 minute.
B the material after () fragmentation enters twin screw extruder and extrudes; Forcing machine heating and temperature control is at 80 ~ 120 DEG C.
(c) extrude after material be ground into through compressing tablet, cooling, pulverizer the powder that particle diameter (equivalent grain size D50) is 30 ~ 45 um, then screening after namely obtain powder at the bottom of Clear paint.
nation determines method:
(1) by powder at the bottom of Clear paint and metallic leafing pigments ECKART company Chromal IV pre-mixing, part by weight 100:0.003 ~ 100:0.015, preferred 100:0.008.Take and mix, add in bonding machines.
(2) in room temperature environment, pass into shielding gas in bonding machines and bind.Arrange bonding machines parameter, rotating speed arranges 400-1000n/min, preferably 700 ~ 800 n/min, set of time 5min.
(3) after nation completes surely, gained powder sieves, and obtains high imitative electrosilvering powder coating.
Take out high imitative electrosilvering powder coating, spray plate with electrostatic gun, after baking, both obtain the metal effect that film coated surface produces reflective picture chromium plating minute surface.
embodiment 3
Component and weight are:
Vibrin SJ4B 95 parts
Hydroxyalkyl amide (Primid) 5 parts
Flow agent 1.3 parts
St-yrax 0.6 part
CATB-250 0.8 part
Powder preparation at the bottom of Clear paint:
A () takes vibrin SJ4B, hydroxyalkyl amide, flow agent, st-yrax and CATB-250 in proportion, be placed in compounding jar, fully mixing also broken 1 ~ 10 minute.
B the material after () fragmentation enters twin screw extruder and extrudes; Forcing machine heating and temperature control is at 80 ~ 120 DEG C.
(c) extrude after material be ground into through compressing tablet, cooling, pulverizer the powder that particle diameter (equivalent grain size D50) is 30 ~ 45 um, then screening after namely obtain powder at the bottom of Clear paint.
nation determines method:
(1) by powder at the bottom of Clear paint and metallic leafing pigments SCHLENK company Powdal 170XB pre-mixing, part by weight 100:0.003 ~ 100:0.015, preferred 100:0.008.Take and mix, add in bonding machines.
(2) in room temperature environment, pass into shielding gas in bonding machines and bind.Arrange bonding machines parameter, rotating speed arranges 400-1000n/min, preferably 700 ~ 800 n/min, set of time 5min.
(3) after nation completes surely, gained powder sieves, and obtains high imitative electrosilvering powder coating.
Take out high imitative electrosilvering powder coating, spray plate with electrostatic gun, after baking, both obtain the metal effect that film coated surface produces reflective picture chromium plating minute surface.
embodiment 4
Component and weight are:
Vibrin P5086 50 parts
Epoxy resin R304 50 parts
Flow agent 1.3 parts
St-yrax 0.6 part
CTB-280 0.9 part
Powder preparation at the bottom of Clear paint:
A () takes vibrin P5086, epoxy resin R304, flow agent, st-yrax and CTB-280 in proportion, be placed in compounding jar, fully mixing also broken 1 ~ 10 minute.
B the material after () fragmentation enters twin screw extruder and extrudes; Forcing machine heating and temperature control is at 80 ~ 120 DEG C.
(c) extrude after material be ground into through compressing tablet, cooling, pulverizer the powder that particle diameter (equivalent grain size D50) is 30 ~ 45 um, then screening after namely obtain powder at the bottom of Clear paint.
nation determines method:
(1) by powder at the bottom of Clear paint and the pre-mixing of metallic leafing pigments Benda-Lutz company 2091, part by weight 100:0.003 ~ 100:0.015, preferred 100:0.008.Take and mix, add in bonding machines.
(2) in room temperature environment, pass into shielding gas in bonding machines and bind.Arrange bonding machines parameter, rotating speed arranges 400-1000n/min, preferably 700 ~ 800 n/min, set of time 5min.
(3) after nation completes surely, gained powder sieves, and obtains high imitative electrosilvering powder coating.
Take out high imitative electrosilvering powder coating, spray plate with electrostatic gun, after baking, both obtain the metal effect that film coated surface produces reflective picture chromium plating minute surface.
test item:
| Test item | Inspecting standard or method | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
| Gloss (60 DEG C) | GB/T 9754 | ≥100GU | ≥100GU | ≥100GU | ≥100GU |
| Outward appearance | / | Mirror effect | Mirror effect | Mirror effect | Mirror effect |
| Sticking power | GB/T 9286 | 0 grade | 0 grade | 0 grade | 0 grade |
| Powder utilization | / | 82% | 82% | 82% | 82% |
| Shock resistance (50kgcm) | GB/T 1732 | Positive and negatively to pass through | Positive and negatively to pass through | Positive and negatively to pass through | Positive and negatively to pass through |
| Bending | GB/T 1731 | 2mm | 2mm | 2mm | 2mm |
In above-described embodiment 1 to 4, silver powder also can adopt the metal of different company to float Silver pigments, can add the mixture of one or more when testing, and produces the mirror metal effect of different-effect.
Claims (10)
1. a high imitative electrosilvering powder coating, comprises powder at the bottom of Clear paint and silver powder, it is characterized in that, aligns agent in powder at the bottom of described Clear paint containing silver powder.
2. height according to claim 1 imitates electrosilvering powder coating, it is characterized in that, powder at the bottom of described Clear paint aligns agent by clear coat binder and silver powder and forms.
3. height according to claim 1 imitates electrosilvering powder coating, it is characterized in that, described clear coat binder is convention transparent powder coating, and its component comprises resin, auxiliary agent and solidifying agent.
4. height according to claim 3 imitates electrosilvering powder coating, it is characterized in that, with the total mass of clear coat binder for Calculation Basis, described resin is usual resins used for powder coating, and its mass parts is 50 ~ 95 parts; Described auxiliary agent is conven-tional adjuvants used for powder coating, and its mass parts is 1 ~ 10 part; The mass parts of described solidifying agent is 1 ~ 50 part.
5. the height according to any one of claim 1 ~ 4 imitates electrosilvering powder coating, it is characterized in that, with powder coating total mass for Calculation Basis, it is 0.5 ~ 1.5 part that described silver powder aligns the mass parts of agent in powder coating.
6. height according to claim 5 imitates electrosilvering powder coating, it is characterized in that, it is aldehyde ketone condensation resin that described silver powder aligns agent.
7. height according to claim 6 imitates electrosilvering powder coating, it is characterized in that, the fusing point of described aldehyde ketone condensation resin 127 ~ 169 DEG C, fugitive constituent≤0.5%.
8. height according to claim 5 imitates electrosilvering powder coating, it is characterized in that, the part by weight 100:0.003-100:0.015 of powder and silver powder at the bottom of described Clear paint; Described silver powder is metallic leafing pigments; Described metallic leafing pigments is metallic aluminium pigment; Described metallic aluminium pigment is the floating type aluminium pigment of particle diameter 4 ~ 20 μm.
9. the height described in any one of claim 1 ~ 8 imitates the binding method of electrosilvering powder coating, it is characterized in that, comprises the following steps:
(1) take powder at the bottom of Clear paint in proportion and silver powder mixes, be placed in binding machine;
(2) in room temperature environment, pass into shielding gas in bonding machines and bind;
(3) powder completing nation fixed sieves, and obtains high imitative electrosilvering metal powder coating.
10. height according to claim 9 imitates the binding method of electrosilvering powder coating, it is characterized in that, rotating speed 400 ~ the 1000n/min of bonding machines in described step (2), rotation time arranges 3 ~ 7min, to guarantee that powder at the bottom of Clear paint fully mixes with silver powder in bonding machines equipment, silver powder is produced and aligns effect.