CN106478070A - 一种吸水率低的烧结砖 - Google Patents

一种吸水率低的烧结砖 Download PDF

Info

Publication number
CN106478070A
CN106478070A CN201510550188.1A CN201510550188A CN106478070A CN 106478070 A CN106478070 A CN 106478070A CN 201510550188 A CN201510550188 A CN 201510550188A CN 106478070 A CN106478070 A CN 106478070A
Authority
CN
China
Prior art keywords
fired brick
water absorption
absorption rate
sulfonic acid
acid calcium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510550188.1A
Other languages
English (en)
Inventor
刘和超
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510550188.1A priority Critical patent/CN106478070A/zh
Publication of CN106478070A publication Critical patent/CN106478070A/zh
Pending legal-status Critical Current

Abstract

本发明所采用的技术解决方案是一种吸水率低的烧结砖，主要成分为粉煤灰和砂质粘土，其特征在于：还加入了河道淤泥15-20份、木质素磺酸钙粉5-15份，烧结球15-20份、玻璃粉5-10份。与现有技术相比，本发明所具有的有益效果为：本发明通过加入河道淤泥、木质素磺酸钙粉，烧结球、玻璃粉，使得该烧结砖具有很好的效果。

Description

一种吸水率低的烧结砖
技术领域
本发明涉及烧结砖技术领域，尤其涉及一种吸水率低的烧结砖。
背景技术
凡以粘土、页岩、煤矸石或粉煤灰为原料，经成型和高温焙烧而制得的用于砌筑承重和非承重墙体的砖统称为烧结砖。烧结砖在我国已经有两千多年的历史，仍是当今一种很广泛的墙体材料。
发明内容
所要解决的技术问题是克服现有技术存在的缺陷，提供一种吸水率低的烧结砖。
本发明所采用的技术解决方案是一种吸水率低的烧结砖，主要成分为粉煤灰和砂质粘土，其特征在于：还加入了河道淤泥15-20份、木质素磺酸钙粉5-15份，烧结球15-20份、玻璃粉5-10份。
与现有技术相比，本发明所具有的有益效果为：本发明通过加入河道淤泥、木质素磺酸钙粉，烧结球、玻璃粉，使得该烧结砖具有很好的效果。
具体实施方式
本发明详细内容结合实施例加以说明：
实施例1：一种吸水率低的烧结砖，主要成分为粉煤灰和砂质粘土，其特征在于：还加入了河道淤泥15-20份、木质素磺酸钙粉5-15份，烧结球15-20份、玻璃粉5-10份。
实施例2：一种吸水率低的烧结砖，主要成分为粉煤灰和砂质粘土，其特征在于：还加入了河道淤泥15-18份、木质素磺酸钙粉5-15份，烧结球15-20份、玻璃粉5-10份。

Claims (2)

1.一种吸水率低的烧结砖，主要成分为粉煤灰和砂质粘土，其特征在于：还加入了河道淤泥15-20份、木质素磺酸钙粉5-15份，烧结球15-20份、玻璃粉5-10份。
2.根据权利要求1所述的一种吸水率低的烧结砖，主要成分为粉煤灰和砂质粘土，其特征在于：所述的河道淤泥15-18份、木质素磺酸钙粉5-15份，烧结球15-20份、玻璃粉5-10份。
CN201510550188.1A 2015-09-01 2015-09-01 一种吸水率低的烧结砖 Pending CN106478070A (zh)