CN106467376A - 免烧砖制备工艺方法 - Google Patents

免烧砖制备工艺方法 Download PDF

Info

Publication number
CN106467376A
CN106467376A CN201510498262.XA CN201510498262A CN106467376A CN 106467376 A CN106467376 A CN 106467376A CN 201510498262 A CN201510498262 A CN 201510498262A CN 106467376 A CN106467376 A CN 106467376A
Authority
CN
China
Prior art keywords
degrees celsius
hours
kiln
temperature
cement
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510498262.XA
Other languages
English (en)
Inventor
魏召召
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Baoji Huide Sanfei Development And Utilization Co Ltd
Original Assignee
Baoji Huide Sanfei Development And Utilization Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Baoji Huide Sanfei Development And Utilization Co Ltd filed Critical Baoji Huide Sanfei Development And Utilization Co Ltd
Priority to CN201510498262.XA priority Critical patent/CN106467376A/zh
Publication of CN106467376A publication Critical patent/CN106467376A/zh
Pending legal-status Critical Current

Abstract

本发明一种免烧砖制备工艺方法，包括将三种原料水泥、煤气化渣，水泥，豆沙石分别装入料仓，其中水泥20％：豆沙石30％：气化粗渣50％；通过上料机把配好的原料送入搅拌机，加水搅拌，其中1立方原料加4公斤的水；搅拌好的料通过皮带输送机送到制砖机口进行砖坯加工；码垛机将生产好的砖坯进行打堆；将打堆好的砖坯通过链板机送入养护窑；在蒸汽养护窑内养护15个小时，其中，蒸汽养护中将前置时间控制在3个小时，窑内温度25摄氏度；升温时间控制在2个小时，窑内温度从25摄氏度提升到70摄氏度；恒温时间控制在8个小时，窑内温度70摄氏度；降温时间控制在2小时，温度从70摄氏度降至25摄氏度的蒸汽养护流程；出窑。

Description

免烧砖制备工艺方法
技术领域
本发明涉及一种免烧砖制备工艺方法。
背景技术
国家发展和改革委员会40号令《产业结构调整指导目录(2005年本)》要求对以煤为燃料的倒烟窑进行彻底取缔，坚决淘汰高能耗、高排放、低效益的落后生产能力。而此项目是固体废渣的二次利用，建设符合《产业结构调整指导目录(2011年本)》第三类煤炭中第7项煤矸石、煤泥、洗中煤等低热值燃料综合利用；第17项建材中非烧结、非蒸压粉煤灰砖生产线。属于国家推广使用新材料，以新型墙体材料替代实心粘土砖，支持废弃资料的利用，是新的产业导向。
以前的免烧砖是利用粉煤灰、煤渣、煤矸石、尾矿渣、化工渣或天然砂等作为主料。
发明内容
针对上述问题，本发明提供一种免烧砖制备工艺方法。
为达到上述发明目的，本发明免烧砖制备工艺方法，所述工艺具体包括将三种原料水泥、煤气化渣，水泥，豆沙石分别装入料仓，通过计量器对料进行配比，其中水泥20％：豆沙石30％：气化粗渣50％；
通过上料机把配好的原料送入搅拌机，加水搅拌，其中1立方原料加4公斤的水；
搅拌好的料通过皮带输送机送到制砖机口进行砖坯加工；
码垛机将生产好的砖坯进行打堆；
将打堆好的砖坯通过链板机送入养护窑；
在蒸汽养护窑内养护15个小时，其中，蒸汽养护中将前置时间控制在3个小时，窑内温度25摄氏度；升温时间控制在2个小时，窑内温度从25摄氏度提升到70摄氏度；恒温时间控制在8个小时，窑内温度70摄氏度；降温时间控制在2小时，温度从70摄氏度降至25摄氏度的蒸汽养护流程；
出窑。
进一步地，所述豆沙石的直径为5-10mm。
有益效果：
与现有相关技术相比，本发明具有以下有益效果：
本发明可减轻气化渣对环境的影响，保护植被、地下水耕地及环境，减轻了环境污染问题，大大减轻了自然的负担，满足城市建设和房地产行业对透水砖、行道砖、马路道沿砖、砌块、标砖、护坡砖、盲道砖的需求，具备良好的社会效益。
具体实施方式
下面对本发明做进一步的描述。
本发明用煤气化渣作为主料，生产了第一批透水砖，经宝鸡建筑材料检测中心检测，该透水砖质量完全符合国家最新检验标准MU15，且比用其他废料做的砖强度高、重量轻、密实度好、耐久性强、尺寸标准、外形完整、色泽均匀，具有古朴自然的外观，可做清水墙，也可以做任何外饰。在工艺上：以前的免烧砖最少由四种原料组成，而我们研制的免烧建材，由气化渣、水泥、石销三种原料生产而成，从成本上就节约了设备、人工、维修费用。
本实施例本发明免烧砖制备工艺方法，所述工艺具体包括将三种原料分别装入料仓，通过计量器对料进行配比，其中水泥20％：豆沙石30％：气化粗渣50％；
通过上料机把配好的料送入搅拌机，加水搅拌，其中1立方材料加4公斤的水，容量1吨原料1分钟搅拌29.6圈内温10度到30度；
根据原料的内水的含量进行加水，比如：可以选取一些物料握一下，假如手心泛起的了水分说明水分已经超过，这时停止供水，适当的加一些原料；假如没有出水，但是原料之间也比较紧凑的话，说明刚恰好；假如不成团说明还得加点水。这样大致多少原料配比多少水；
搅拌好的料通过皮带输送机送到制砖机口进行砖坯加工；
码垛机将生产好的砖坯进行打堆；
将打堆好的砖坯通过链板机送入养护窑；
在蒸汽养护窑内养护15个小时，其中，蒸汽养护中将前置时间控制在3个小时，窑内温度25摄氏度；升温时间控制在2个小时，窑内温度从25摄氏度提升到70摄氏度；恒温时间控制在8个小时，窑内温度70摄氏度；降温时间控制在2小时，温度从70摄氏度降至25摄氏度的蒸汽养护流程；
出窑。
煤气化渣(不需要粉碎)，水泥，(增加强度)豆沙石(大小直5-10mm)，水。
上述配比的好处：1.固废利用2整体质量变轻3透水，保温4增加强度5色泽好6密实度高7粘合度超过国家标准。
煤气化渣也即气化渣是指煤在特定的设备内，在一定温度及压力下使煤中有机质与气化剂(如蒸汽/空气或氧气等)发生一系列化学反应，将固体煤转化为含有CO、H2、CH4等可燃气体和CO2、N2等非可燃气体的过程后产生的固体废渣。
气化渣的主要由：SiO2、Al2O3、Fe2O3、CaO、MgO、Na2O、K2O、TiO2等构成。
对本发明应当理解的是，以上所述的实施例，对本发明的目的、技术方案和有益效果进行了进一步详细的说明，以上仅为本发明的实施例而已，并不用于限定本发明，凡是在本发明的精神原则之内，所作出的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内，本发明的保护范围应该以权利要求所界定的保护范围为准。

Claims (2)

1.一种免烧砖制备工艺方法，其特征在于，所述工艺具体包括将三种原料水泥、煤气化渣，水泥，豆沙石分别装入料仓，通过计量器对料进行配比，其中水泥20％：豆沙石30％：气化粗渣50％；
通过上料机把配好的原料送入搅拌机，加水搅拌，其中1立方原料加4公斤的水；
搅拌好的料通过皮带输送机送到制砖机口进行砖坯加工；
码垛机将生产好的砖坯进行打堆；
将打堆好的砖坯通过链板机送入养护窑；
在蒸汽养护窑内养护15个小时，其中，蒸汽养护中将前置时间控制在3个小时，窑内温度25摄氏度；升温时间控制在2个小时，窑内温度从25摄氏度提升到70摄氏度；恒温时间控制在8个小时，窑内温度70摄氏度；降温时间控制在2小时，温度从70摄氏度降至25摄氏度的蒸汽养护流程；
出窑。
2.根据权利要求1所述的免烧砖制备工艺方法，其特征在于，所述豆沙石的直径为5-10mm。
CN201510498262.XA 2015-08-14 2015-08-14 免烧砖制备工艺方法 Pending CN106467376A (zh)