CN106435950A - Elastic shirt raw material containing heat generating fibers and weaving method - Google Patents

Elastic shirt raw material containing heat generating fibers and weaving method Download PDF

Info

Publication number
CN106435950A
CN106435950A CN201611080399.4A CN201611080399A CN106435950A CN 106435950 A CN106435950 A CN 106435950A CN 201611080399 A CN201611080399 A CN 201611080399A CN 106435950 A CN106435950 A CN 106435950A
Authority
CN
China
Prior art keywords
mixed yarn
raw
spandex
heat generating
stretch shirt
Prior art date
Application number
CN201611080399.4A
Other languages
Chinese (zh)
Inventor
蔡飞达
Original Assignee
杭州飞虹针织服饰有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 杭州飞虹针织服饰有限公司 filed Critical 杭州飞虹针织服饰有限公司
Priority to CN201611080399.4A priority Critical patent/CN106435950A/en
Publication of CN106435950A publication Critical patent/CN106435950A/en

Abstract

The invention discloses an elastic shirt raw material containing heat generating fibers and a weaving method. The raw material comprises a thread structure interlaced from blended yarns A, blended yarns B and spandex C, wherein in terms of yarn numbers, the yarn number ratio of the blended yarns A to the blended yarns B and the spandex C in the thread structure is 2:8:5; and in terms of fiber numbers, the blended yarns A are obtained by blending 65-75% of heat generating fibers and 25-35% of Modal, and the blended yarns B are obtained by blending 25-35% of heat generating fibers and 65-75% of Modal. The elastic shirt raw material has the characteristics of generating heat, preserving heat, guiding perspiration quickly, generating comfortable feeling and refreshing.

Description

Stretch shirt raw material and method for weaving containing heat generating fiber
Technical field
The present invention relates to textile raw material and textile technology technical field, especially relate to a kind of stretch shirt containing heat generating fiber Raw material and method for weaving.
Background technology
Warming is the important indicator of water clothes comfortableness, traditional heating method be typically to control heat conduction, Convection current, caused heat leakage is radiated, i.e., using thick fabric or the heat insulating material formed being incubated of cotton-wool class is added, had also adopts Metal coating raw material.But modern people are to the comfortableness of clothing, feature and cosmetic requirements more and more higher, traditional guarantor The general volume ratio of warm material is more too fat to move, is not easy to motion and lacks aesthetic feeling again;For the people of operation under extreme low temperature environment, The passive warming Functional Requirement that can not meet clothing well, therefore actively the heat insulating material formed exploitation of heat production formula has weight Want meaning.
For meeting these demands, people developed successfully active heat production formula heat insulating material formed-heat generating fiber, including moisture absorption Heat generating fiber, electric energy heat generating fiber, luminous energy heat generating fiber, chemical heat generating fiber etc..Wherein, the skill of hygroscopic heating fibers is produced Art relative maturity, has had product to appear on the market at present, such as Toray Warmsensor fiber, Softwarm fiber, Japanese Japan Spinning company N38 fiber, eks fiber, Japanese Asahi Chemical Industry Zhu Shi commercial firm Thermogear fiber, MIT's Renaiss α fibre Dimension etc..Though the mechanism of heat generating fiber is had nothing in common with each other, a basic physical phenomenon is all based on:Moisture evaporation is absorbed heat, on the contrary Vaporous water is converted into liquid and can also produce coagulation heat.The antiperspirant gas that body is produced exactly is turned by hygroscopic heating fibers using the vaporization of water Produced heat during aqueous water is turned to for warming.
Heat generating fiber is the dampness for being produced using the dermal respiration for absorbing human body reaching the effect of heating, fiber pars intermedia Divide containing static air, good thermal insulation effect is produced, not only allow fabric weight itself reduce, and the insulation of still air Property is also splendid, using the capillarity produced by the trickle groove of fiber surface and special spinning process, makes unnecessary moisture warp The effects such as stamen is inhaled, diffusion, transmission absorb rapidly and distribute, and make body keep dry and comfortable, and the natural fiber in natural imitation ecology is assigned The countless respirable micropores of fiber surface are given, softness and the comfort of natural fiber is reached, using special spinning technique, is reached Improve than similar yarn anti-pilling a lot.
Therefore research and development heat generating fiber and its correlation function product have good prospect.In the prior art containing heating The raw material of fiber is not yet exploited as stretch shirt product mainly based on Weft knitting product, therefore, by heat generating fiber Stretch shirt is applied to, its functionalization is realized, be that those skilled in the art have a to be solved problem.
Content of the invention
It is an object of the invention to provide a kind of stretch shirt raw material containing heat generating fiber, is given with stretch shirt prepared by the raw material Feeling for people is not only dry and comfortable but also warm.
It is a further object to provide the method for weaving of above-mentioned stretch shirt raw material.
For solving above-mentioned technical problem, the present invention adopts following technical proposals.
A kind of stretch shirt raw material containing heat generating fiber, the stretch shirt raw material includes that A mixed yarn, B mixed yarn and C spandex are handed over The helicitic texture that knits, in terms of radical, in the helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;
With fiber count gauge, the A mixed yarn is formed by the heat generating fiber of 65-75% and the Modal blending of 25-35%, The B mixed yarn is formed with the Modal blending of 65-75% by the heat generating fiber of 25-35%.
Preferably, the heat generating fiber is the Mei Yabi acrylon of Japanese Rhizoma Sparganii company, and the fineness of the heat generating fiber is 0.9D, a diameter of 38mm, density is 1.10-1.20g/cm3.
Preferably, the Modal is Lenzin Modal, and the fineness of the Lenzin Modal is 1.2D, a diameter of 38mm.
Preferably, the C spandex is Yantai Niu Shida spandex, and the fineness of the C spandex is 40D;The C spandex is described The one side of stretch shirt raw material adds.
Preferably, the warp count of the stretch shirt raw material:122/10cm, weft count:126/10cm.
Preferably, the grammes per square metre of the stretch shirt raw material is 220-230g/m2.
Preferably, the color fastness of the stretch shirt raw material is:Water-fast, soap, antiperspirant, more than 4 grades of unlubricated friction color fastness, wet color jail of rubbing More than 3 grades of degree.
Preferably, the stretch shirt raw material straight to washing shrinkage be -5~0%.
The method for weaving of above-mentioned stretch shirt raw material, the method includes to add 5 by 2 A mixed yarns and 8 B mixed yarns and one side The feeding method helicitic texture weaving of going the same way of root C spandex and AB yarn is formed.
Preferably, described 2 A mixed yarns and 8 B mixed yarns and one side are added 5 C spandexs and meanwhile feed method helicitic texture Weaving refers to one side per root A mixed yarn and per root B mixed yarn when braider is fed all with a C spandex while feeding, another Face is not added with C spandex;The A mixed yarn and B mixed yarn are formed by matching network compact spinning blending.
Beneficial effects of the present invention are as follows:
The rib-loop structure fabric that the present invention is made using heat generating fiber is different from traditional being escaped by prevention heat and reaches Warming fabric, it is voluntarily to be given off heat using heat generating fiber under certain condition, and prevents heat losses, so as to reach guarantor Warm effect, as heat generating fiber also has good moisture absorbing while giving off heat, thus the stretch shirt of the present invention is former What material gave people feels not only dry and comfortable but also warm.
Specific embodiment
In order to be illustrated more clearly that the present invention, with reference to preferred embodiment, the present invention is described further.Ability Field technique personnel should be appreciated that following specifically described content is illustrative and be not restrictive, and should not limit this with this The protection domain of invention.
Traditional insulation is that heat generating fiber is then self-heating and warm to prevent based on the thermal runaway sent by body A kind of brand-new material of body, its water absorption strong considerably beyond other kind fibers.
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes to add C Niu Shida in the middle of A mixed yarn and B mixed yarn High-elastic solid interlacement weave structure, AB mixed yarn is new with pilling fluffing resistant with Lenzin Modal by the heat generating fiber of different blending ratios Type match network compact spinning blending is formed, the smooth good permeability of Modal, and the Moisture converting of absorption can be dissipated by heat generating fiber for heat Issue.
Using the underwear that heat generating fiber is made have heat preservation persistently, lead antiperspirant become dry rapidly, be comfortable on, drive away vexed Heat, feel salubrious performance;The present invention using heat generating fiber be by hydrophobic acrylon and two kinds of compositions of hydrophilic acetic acid Composition, there is micropore on the surface of fiber, when dampness is by micropore, is just absorbed by acetate component and gives off heat, and acrylon composition is permissible The heat for generating is kept for the long period, simultaneously as water droplet can not be extruded return by the micropore of fiber, so dress Sultry humidity will not be felt.
The rib-loop structure fabric that the present invention is made using heat generating fiber is different from traditional being escaped by prevention heat and reaches Warming fabric, it is voluntarily to be given off heat using heat generating fiber under certain condition, and prevents heat losses, so as to reach guarantor Warm effect.Heat generating fiber also has good moisture absorbing while giving off heat, and its heating principle is gasified reverse The backward reaction principle of amount of heat, the i.e. antiperspirant that absorption human body is distributed and dampness can be absorbed when should utilize liquid evaporation to be carried out Physical reactions generate heat.While deriving the moisture for reducing after heat release, skin is made not have vexed wet sense, feeling for giving people is not only dry and comfortable but also warm Warm.Heat generating fiber thermal fabric has the characteristics that light, thin, soft, warm.
In A mixed yarn in the stretch shirt raw material containing heat generating fiber of the present invention, 65-75% containing heat generating fiber contains Modal The 65-75% containing Modal of 25-35% containing heat generating fiber in 25-35%, B mixed yarn.
The technological process of production of stretch shirt raw material of the present invention:
Openpore yarn → weave cotton cloth → dye → cutting → sewing → whole boiling hot → packaging → warehouse-in
Spinning equipment is:Match network compact spinning apparatus spin in two 187 spinning frames of frame of Shanghai+Jiangyin China;
Braider used is:The 34 cun of 18 pin rib knitting machine in big Chongqing, Taiwan;
A mixed yarn 2 and B mixed yarn 8 on the 34 cun of 18 pin rib-loop structure Imported Precision large circle machine in big Chongqing, Taiwan, adopt One side adds 5 C spandexs and forms while feeding the weaving of method rib-loop structure.
Heat generating fiber in following embodiments is 0.9D, a diameter of 38mm using fineness, and density is 1.1-1.2g/cm3's The Mei Yabi acrylon of Japanese Rhizoma Sparganii company;
Modal is the Lenzin Modal of 1.2D, a diameter of 38mm using fineness;
C spandex is Yantai Niu Shida spandex, and the fineness of the C spandex is 40D.
Embodiment 1
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 70% heat generating fiber and 30% Modal, and the B mixed yarn is by 30% Heat generating fiber with 70% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
122/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 126/10cm;Gram Weight is 225g/m2;Color fastness be 4 grades, directly to washing shrinkage be 0%.
Embodiment 2
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 65% heat generating fiber and 35% Modal, and the B mixed yarn is by 35% Heat generating fiber with 65% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
120/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 127/10cm;Gram Weight is 220g/m2;Color fastness be 4 grades, directly to washing shrinkage be -2%.
Embodiment 3
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 75% heat generating fiber and 25% Modal, and the B mixed yarn is by 25% Heat generating fiber with 75% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
125/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 130/10cm;Gram Weight is 230g/m2;Color fastness be 4 grades, directly to washing shrinkage be -3%.
Embodiment 4
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 68% heat generating fiber and 32% Modal, and the B mixed yarn is by 30% Heat generating fiber with 70% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
123/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 127/10cm;Gram Weight is 222g/m2;Color fastness be 4 grades, directly to washing shrinkage be -4%.
Embodiment 5
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 70% heat generating fiber and 30% Modal, and the B mixed yarn is by 25% Heat generating fiber with 75% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
125/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 128/10cm;Gram Weight is 226g/m2;Color fastness be 4 grades, directly to washing shrinkage be -2%.
Embodiment 6
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 72% heat generating fiber and 28% Modal, and the B mixed yarn is by 35% Heat generating fiber with 65% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
123/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 127/10cm;Gram Weight is 224g/m2;Color fastness be 4 grades, directly to washing shrinkage be -1%.
Embodiment 7
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 66% heat generating fiber and 34% Modal, and the B mixed yarn is by 28% Heat generating fiber with 72% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
124/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 127/10cm;Gram Weight is 223g/m2;Color fastness be 4 grades, directly to washing shrinkage be -3%.
Embodiment 8
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 73% heat generating fiber and 27% Modal, and the B mixed yarn is by 32% Heat generating fiber with 68% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
121/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 129/10cm;Gram Weight is 224g/m2;Color fastness be 4 grades, directly to washing shrinkage be -1%.
Embodiment 9
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 68% heat generating fiber and 32% Modal, and the B mixed yarn is by 27% Heat generating fiber with 73% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
121/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 127/10cm;Gram Weight is 223g/m2;Color fastness be 4 grades, directly to washing shrinkage be -3%.
Embodiment 10
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 69% heat generating fiber and 31% Modal, and the B mixed yarn is by 26% Heat generating fiber with 74% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
123/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 128/10cm;Gram Weight is 227g/m2;Color fastness be 4 grades, directly to washing shrinkage be -4%.
Embodiment 11
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 74% heat generating fiber and 26% Modal, and the B mixed yarn is by 33% Heat generating fiber with 67% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
124/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 127/10cm;Gram Weight is 228g/m2;Color fastness be 4 grades, directly to washing shrinkage be -5%.
Embodiment 12
A kind of stretch shirt raw material containing heat generating fiber, the raw material includes the screw thread that A mixed yarn, B mixed yarn and C spandex interweave Structure, in terms of radical, in helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;With fiber count gauge, A mixed yarn is formed using match network compact spinning blending by 73% heat generating fiber and 27% Modal, and the B mixed yarn is by 32% Heat generating fiber with 68% Modal using match network compact spinning blending form.
A mixed yarn 2 and B mixed yarn 8 on Imported Precision large circle machine, using one side per root with C spandex while feed Method another side is not added with the weaving of spandex rib-loop structure and forms the raw material for stretch shirt.
124/the 10cm of warp count of stretch shirt raw material obtained in the present embodiment, weft count is 129/10cm;Gram Weight is 229g/m2;Color fastness is 4 grades, to washing shrinkage is directly -- 3%.
Finally it should be noted that:Various embodiments above only in order to technical scheme to be described, rather than a limitation;To the greatest extent Pipe has been described in detail to the present invention with reference to foregoing embodiments, it will be understood by those within the art that:Its according to So the technical scheme described in foregoing embodiments can be modified, or which part or all technical characteristic are entered Row equivalent;And these modifications or replacement, do not make the essence of appropriate technical solution depart from various embodiments of the present invention technology The scope of scheme.

Claims (10)

1. a kind of stretch shirt raw material containing heat generating fiber, it is characterised in that:The stretch shirt raw material includes A mixed yarn, B mixed yarn The helicitic texture for interweaving with C spandex, in terms of radical, in the helicitic texture, the radical ratio of A mixed yarn, B mixed yarn and C spandex is 2:8:5;
With fiber count gauge, the A mixed yarn is formed by the heat generating fiber of 65-75% and the Modal blending of 25-35%, described B mixed yarn is formed with the Modal blending of 65-75% by the heat generating fiber of 25-35%.
2. stretch shirt raw material according to claim 1, it is characterised in that:The heat generating fiber is U.S. of Japanese Rhizoma Sparganii company Refined green acrylon, the fineness of the heat generating fiber is 0.9D, a diameter of 38mm, and density is 1.10-1.20g/cm3.
3. stretch shirt raw material according to claim 1, it is characterised in that:The Modal is Lenzin Modal, the orchid The fineness of smart Modal is 1.2D, a diameter of 38mm.
4. stretch shirt raw material according to claim 1, it is characterised in that:The C spandex is Yantai Niu Shida spandex, described The fineness of C spandex is 40D;The C spandex adds in the one side of the stretch shirt raw material.
5. stretch shirt raw material according to claim 1, it is characterised in that:The warp count of the stretch shirt raw material:120- 125/10cm, weft count:125-130 root/10cm.
6. stretch shirt raw material according to claim 1, it is characterised in that:The grammes per square metre of the stretch shirt raw material is 220- 230g/m2.
7. stretch shirt raw material according to claim 1, it is characterised in that:The color fastness of the stretch shirt raw material is:Water-fast, Soap, antiperspirant, more than 4 grades of unlubricated friction color fastness, wet more than 3 grades of the color fastness of rubbing.
8. stretch shirt raw material according to claim 1, it is characterised in that:The stretch shirt raw material straight to washing shrinkage be -5 ~0%.
9. a kind of method for weaving of the stretch shirt raw material containing described in any one of claim 1 to 8, it is characterised in that:2 A are mixed Spinning and 8 B mixed yarns and one side add the feeding method helicitic texture weaving of going the same way of 5 C spandexs and AB yarn to form.
10. method for weaving according to claim 9, it is characterised in that:Described by 2 A mixed yarns and 8 B mixed yarns and One side adds 5 C spandexs while the helicitic texture weaving of the method for feeding refers to one side per root A mixed yarn and per root B mixed yarn in feeding braiding All with a C spandex while feeding, another side is not added with C spandex during machine;The A mixed yarn and B mixed yarn are tight by matching network Spin blending to form.
CN201611080399.4A 2016-11-30 2016-11-30 Elastic shirt raw material containing heat generating fibers and weaving method CN106435950A (en)