CN106434034A - Glass cleaning agent suitable for spray cleaning and preparation method thereof - Google Patents
Glass cleaning agent suitable for spray cleaning and preparation method thereof Download PDFInfo
- Publication number
- CN106434034A CN106434034A CN201610543154.4A CN201610543154A CN106434034A CN 106434034 A CN106434034 A CN 106434034A CN 201610543154 A CN201610543154 A CN 201610543154A CN 106434034 A CN106434034 A CN 106434034A
- Authority
- CN
- China
- Prior art keywords
- parts
- film forming
- brightener
- solvent
- spray cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass cleaning agent suitable for spray cleaning and a preparation method thereof. The glass cleaning agent is prepared from the following raw materials in parts by weight: 2-10 parts of isomeric C10 fatty alcohol ether, 2-10 parts of a low foaming type fatty alcohol alkoxy compound, 0.5-2 parts of an ampholytic surfactant, 3-10 parts of a brightening agent, 2-10 parts of acrylic homopolymer sodium salt, 3-15 parts of a hard surface film forming agent, 0.2-1 part of a chelating agent, 10-20 parts of a solvent and 50-70 parts of softened water. The glass cleaning agent disclosed by the invention has the advantages of being low in foaming, easy to rinse and free from water droplet hung on the glass surface after the glass is cleaned; a layer of hydrophilic thin film can be formed on the glass surface, and after being dried, the glass surface is smooth, clean and bright, is suitable for a spray cleaning manner and is naturally dried without being dried in a scraping or wiping manner after being cleaned.
Description
Technical field
Present invention relates particularly to a kind of glass cleaner, the glass cleaner of more particularly to a kind of suitable spray cleaning and
Its preparation method.
Background technology
, based on neutral cleaners, after this kind of cleaning agent cleaning glass, glass surface is easy for glass cleaner on the market at present
Hang the globule and can be only achieved transparent, bright effect it is necessary to scrape to do or dry；If not scraping dry or drying the globule, glass surface is just
The outward appearance of water stain impact glass can be left；This kind of glass cleaner is not suitable for spray cleaning glass in sum.
Content of the invention
It is an object of the invention to overcoming the shortcoming of prior art, provide a kind of glass cleaner of suitable spray cleaning and
Its preparation method, to solve the shortcoming that existing glass cleaner cleans the glass surface globule easy to hang after glass.
For achieving the above object, the technical solution used in the present invention is：
On the one hand, a kind of glass cleaner of suitable spray cleaning, is made up of the raw material of following weight：Isomery
2～10 parts of C10 fatty alcohol ether, 2～10 parts of low alveolitoid fat alcohol alkoxy compound, 0.5～2 part of amphoteric surfactant, light
Bright dose 3～10 parts, 2～10 parts of acrylate homopolymer sodium salt, 3～15 parts of crust film forming agent, 0.2～1 part of chelating agent, solvent 10
～20 parts, 50～70 parts of softened water.
Preferably, described amphoteric surfactant is selected from：Dodecyldimethylammonium hydroxide inner salt, cocamidopropyl propyl amide beet
Alkali or its mixture.
Preferably, described brightener is selected from：Acid and alkali-resistance surfactant, borax or its mixture.
Preferably, described crust film forming agent is hydrophilic high molecular polymer.
Preferably, described chelating agent is selected from：Sodium citrate, disodium ethylene diamine tetraacetate, sodium nitrilo triacetate or it is mixed
Compound.
Preferably, described solvent is to be selected from：Ethanol, isopropanol, ethylene glycol monobutyl ether or its mixture.
Preferably, being made up of the raw material of following weight：
6 parts of isomery C10 fatty alcohol ether, 3 parts of low alveolitoid fat alcohol alkoxy compound, 0.5 part of amphoteric surfactant, light
Bright dose 5 parts, 5 parts of acrylate homopolymer sodium salt, 10 parts of crust film forming agent, 0.5 part of chelating agent, 10 parts of solvent, 60 parts of softened water；
Described amphoteric surfactant is dodecyldimethylammonium hydroxide inner salt, and described brightener is acid and alkali-resistance surface-active
Agent, described crust film forming agent is hydrophilic high molecular polymer, and described chelating agent is disodium ethylene diamine tetraacetate, described solvent
For isopropanol.
Preferably, being made up of the raw material of following weight：
3 parts of isomery C10 fatty alcohol ether, 2 parts of low alveolitoid fat alcohol alkoxy compound, 1 part of amphoteric surfactant, light
3 parts of agent, 3 parts of acrylate homopolymer sodium salt, 8 parts of crust film forming agent, 0.5 part of chelating agent, 15 parts of solvent, 64.5 parts of softened water；
Described amphoteric surfactant is dodecyldimethylammonium hydroxide inner salt, and described brightener is acid and alkali-resistance surface-active
Agent, described crust film forming agent is hydrophilic high molecular polymer, and described chelating agent is disodium ethylene diamine tetraacetate, described solvent
For ethanol.
Preferably, being made up of the raw material of following weight：
7 parts of isomery C10 fatty alcohol ether, 3 parts of low alveolitoid fat alcohol alkoxy compound, 0.5 part of amphoteric surfactant, light
Bright dose 6 parts, 3 parts of acrylate homopolymer sodium salt, 7 parts of crust film forming agent, 0.5 part of chelating agent, 15 parts of solvent, 58 parts of softened water；
Described amphoteric surfactant is dodecyldimethylammonium hydroxide inner salt, and described brightener is acid and alkali-resistance surface-active
Agent, described crust film forming agent is hydrophilic high molecular polymer, and described chelating agent is disodium ethylene diamine tetraacetate, described solvent
For ethanol.
On the other hand, the preparation method of the glass cleaner of suitable spray cleaning, comprises the following steps：
Step 1, adds 10～40 DEG C of softened water in container, starts agitator and is stirred in container, to softening
Add chelating agent in water and stir to being completely dissolved, sequentially add isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxylates close
Thing and amphoteric surfactant simultaneously stir to being completely dissolved, and obtain solution a；
Step 2, brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, hard table
Face film forming agent stirs to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b；
Step 3, solution b standing is made contamination precipitation, through filtering impurity.
Beneficial effects of the present invention are
1st, isomery C10 fatty alcohol ether of the present invention and low alveolitoid fat alcohol alkoxy compound are washing decontamination composition, have
Good low bubble performance, can meet the requirement of spray cleaning well；Amphoteric surfactant is auxiliary decontamination composition, also simultaneously
There is sterilized, anlistatig effect；
Crust film forming agent and acrylate homopolymer sodium salt are film forming matter, can be hydrophilic thin in one layer of glass surface formation
Film, hydrophilic film can stop dirt and glass directly contact, rainwater just can the very molten dirt easily rinsing out glass surface, allow glass
The glass surface dirty cycle greatly prolongs, and hydrophilic film can be easy to be cleaned out with dirt in cleaning next time；Light
Agent has suds and increases the effect washing rear glass surface gloss, and can increase the adhesive force in glass surface for the film forming matter, prevents
Only film forming matter is flush with water in rinse cycle；
In sum, the low bubble of this glass cleaner, easily rinse, wash rear glass surface and do not hang the globule, can be in glass surface
Leave one layer of hydrophilic film, after being dried, glass surface is bright and clean, beautiful, the mode of suitable spray cleaning, do not need after cleaning to scrape
Do or dry and spontaneously dry.
Specific embodiment
For making the object, technical solutions and advantages of the present invention clearer, below in conjunction with the specific embodiment of the invention pair
Technical solution of the present invention is clearly and completely described.
Raw material introduction in following examples：
Embodiment 1：Take 6 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
3 parts of (Plurafac LF221), 0.5 part of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acid and alkali-resistance
5 parts of surfactant (SIMULSOL SL4) is as brightener, 5 parts of acrylate homopolymer sodium salt (445N), hydrophilic macromolecule
, as crust film forming agent, 0.5 part of disodium ethylene diamine tetraacetate (EDTA-2Na) is as chelating for 10 parts of polymer (Surf-S210)
Agent, 10 parts of isopropanol as solvent, 60 parts of softened water, standby.
Add 30 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 2：Take 3 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
2 parts of (Plurafac LF221), 1 part of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acid and alkali-resistance table
As brightener, 3 parts of acrylate homopolymer sodium salt (445N), hydrophilic macromolecule gathers 3 parts of face activating agent (SIMULSOL SL4)
8 parts of compound (Surf-S210) as crust film forming agent, 0.5 part of disodium ethylene diamine tetraacetate (EDTA-2Na) as chelating agent,
15 parts of ethanol as solvent, 64.5 parts of softened water, standby.
Add 10 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 3：7 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
3 parts of (Plurafac LF221), 0.5 part of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acid and alkali-resistance
6 parts of surfactant (SIMULSOL SL4) is as brightener, 3 parts of acrylate homopolymer sodium salt (445N), hydrophilic macromolecule
, as crust film forming agent, 0.5 part of disodium ethylene diamine tetraacetate (EDTA-2Na) is as chelating for 7 parts of polymer (Surf-S210)
Agent, 15 parts of ethanol as solvent, 58 parts of softened water, standby.
Add 40 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 4：Take 7 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
3.5 parts of (Plurafac LF221), 0.7 part of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acidproof
5.5 parts of alkali surfactant (SIMULSOL SL4) is as brightener, 5.5 parts of acrylate homopolymer sodium salt (445N), hydrophily
11 parts of high molecular polymer (Surf-S210) is as crust film forming agent, 0.7 part of work of disodium ethylene diamine tetraacetate (EDTA-2Na)
For chelating agent, 11 parts of isopropanol as solvent, 65 parts of softened water, standby.
Add 35 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 5：Take 4 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
2.5 parts of (Plurafac LF221), 1.2 parts of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acidproof
, as brightener, 3.5 parts of acrylate homopolymer sodium salt (445N), hydrophily is high for 4 parts of alkali surfactant (SIMULSOL SL4)
9 parts of Molecularly Imprinted Polymer (Surf-S210) is as crust film forming agent, 0.7 part of conduct of disodium ethylene diamine tetraacetate (EDTA-2Na)
Chelating agent, 18 parts of ethanol as solvent, 68 parts of softened water, standby.
Add 15 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 6：8 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
3.5 parts of (Plurafac LF221), 0.8 part of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acidproof
6.5 parts of alkali surfactant (SIMULSOL SL4) is as brightener, 3.5 parts of acrylate homopolymer sodium salt (445N), hydrophily
8 parts of high molecular polymer (Surf-S210) is as crust film forming agent, 0.8 part of work of disodium ethylene diamine tetraacetate (EDTA-2Na)
For chelating agent, 18 parts of ethanol as solvent, 55 parts of softened water, standby.
Add 35 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 7：Take 8 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
3.8 parts of (Plurafac LF221), 0.9 part of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acidproof
5.8 parts of alkali surfactant (SIMULSOL SL4) is as brightener, 5.5 parts of acrylate homopolymer sodium salt (445N), hydrophily
12 parts of high molecular polymer (Surf-S210) is as crust film forming agent, 0.9 part of work of disodium ethylene diamine tetraacetate (EDTA-2Na)
For chelating agent, 12 parts of isopropanol as solvent, 68 parts of softened water, standby.
Add 37 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 8：Take 5 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
2.8 parts of (Plurafac LF221), 1.5 parts of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acidproof
4.5 parts of alkali surfactant (SIMULSOL SL4) is as brightener, 3.8 parts of acrylate homopolymer sodium salt (445N), hydrophily
10 parts of high molecular polymer (Surf-S210) is as crust film forming agent, 0.9 part of work of disodium ethylene diamine tetraacetate (EDTA-2Na)
For chelating agent, 19 parts of ethanol as solvent, 69 parts of softened water, standby.
Add 13 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Embodiment 9：9 parts of isomery C10 fatty alcohol ether (Lutensol XL70), low alveolitoid fat alcohol alkoxy compound
3.8 parts of (Plurafac LF221), 0.9 part of dodecyldimethylammonium hydroxide inner salt (BS-12) is as amphoteric surfactant, acidproof
6.8 parts of alkali surfactant (SIMULSOL SL4) is as brightener, 3.8 parts of acrylate homopolymer sodium salt (445N), hydrophily
9 parts of high molecular polymer (Surf-S210) is as crust film forming agent, 0.9 part of work of disodium ethylene diamine tetraacetate (EDTA-2Na)
For chelating agent, 19 parts of ethanol as solvent, 58 parts of softened water, standby.
Add 38 DEG C of softened water in container, start agitator and be stirred in container, add chela in softened water
Mixture simultaneously stirs to being completely dissolved, and sequentially adds isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and both sexes table
Face activating agent simultaneously stirs to being completely dissolved, and obtains solution a.
Brightener is added in solution a and stirs to being completely dissolved, sequentially add acrylate homopolymer sodium salt, crust film forming
Agent is stirred to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b.
Solution b standing is made contamination precipitation, through filtering impurity.
Above-mentioned embodiment is used for illustrating the present invention, rather than limits the invention, in the spirit of the present invention
In scope of the claims, any modifications and changes that the present invention is made, both fall within protection scope of the present invention.
Claims (10)
1. a kind of glass cleaner of suitable spray cleaning is it is characterised in that be made up of the raw material of following weight：
2～10 parts of isomery C10 fatty alcohol ether, 2～10 parts of low alveolitoid fat alcohol alkoxy compound, amphoteric surfactant 0.5
～2 parts, 3～10 parts of brightener, 2～10 parts of acrylate homopolymer sodium salt, 3～15 parts of crust film forming agent, chelating agent 0.2～1
Part, 10～20 parts of solvent, 50～70 parts of softened water.
2. the glass cleaner of suitable spray cleaning according to claim 1 is it is characterised in that described amphoteric surfactant selects
From：Dodecyldimethylammonium hydroxide inner salt, Cocoamidopropyl betaine or its mixture.
3. the glass cleaner of suitable spray cleaning according to claim 1 is it is characterised in that described brightener is selected from：Acidproof
Alkali surfactant, borax or its mixture.
4. the glass cleaner of suitable spray cleaning according to claim 1 is it is characterised in that described crust film forming agent is parent
Aqueous polymer.
5. the glass cleaner of suitable spray cleaning according to claim 1 is it is characterised in that described chelating agent is selected from：Lemon
Sour sodium, disodium ethylene diamine tetraacetate, sodium nitrilo triacetate or its mixture.
6. the glass cleaner of suitable spray cleaning according to claim 1 is it is characterised in that described solvent is to be selected from：Ethanol,
Isopropanol, ethylene glycol monobutyl ether or its mixture.
7. the glass cleaner of the suitable spray cleaning according to claim 1～6 is it is characterised in that by following weight
Raw material make：
6 parts of isomery C10 fatty alcohol ether, 3 parts of low alveolitoid fat alcohol alkoxy compound, 0.5 part of amphoteric surfactant, brightener
5 parts, 5 parts of acrylate homopolymer sodium salt, 10 parts of crust film forming agent, 0.5 part of chelating agent, 10 parts of solvent, 60 parts of softened water；
Described amphoteric surfactant is dodecyldimethylammonium hydroxide inner salt, and described brightener is acid and alkali-resistance surfactant, institute
Stating crust film forming agent is hydrophilic high molecular polymer, and described chelating agent is disodium ethylene diamine tetraacetate, and described solvent is different
Propyl alcohol.
8. the glass cleaner of the suitable spray cleaning according to claim 1～6 is it is characterised in that by following weight
Raw material make：
3 parts of isomery C10 fatty alcohol ether, 2 parts of low alveolitoid fat alcohol alkoxy compound, 1 part of amphoteric surfactant, brightener 3
Part, 3 parts of acrylate homopolymer sodium salt, 8 parts of crust film forming agent, 0.5 part of chelating agent, 15 parts of solvent, 64.5 parts of softened water；
Described amphoteric surfactant is dodecyldimethylammonium hydroxide inner salt, and described brightener is acid and alkali-resistance surfactant, institute
Stating crust film forming agent is hydrophilic high molecular polymer, and described chelating agent is disodium ethylene diamine tetraacetate, and described solvent is second
Alcohol.
9. the glass cleaner of the suitable spray cleaning according to claim 1～6 is it is characterised in that by following weight
Raw material make：
7 parts of isomery C10 fatty alcohol ether, 3 parts of low alveolitoid fat alcohol alkoxy compound, 0.5 part of amphoteric surfactant, brightener
6 parts, 3 parts of acrylate homopolymer sodium salt, 7 parts of crust film forming agent, 0.5 part of chelating agent, 15 parts of solvent, 58 parts of softened water；
Described amphoteric surfactant is dodecyldimethylammonium hydroxide inner salt, and described brightener is acid and alkali-resistance surfactant, institute
Stating crust film forming agent is hydrophilic high molecular polymer, and described chelating agent is disodium ethylene diamine tetraacetate, and described solvent is second
Alcohol.
10. the preparation method of the glass cleaner of suitable spray cleaning according to claims 1 to 9 is it is characterised in that wrap
Include following steps：
Step 1, adds 10～40 DEG C of softened water in container, starts agitator and is stirred in container, in softened water
Add chelating agent simultaneously to stir to being completely dissolved, sequentially add isomery C10 fatty alcohol ether, low alveolitoid fat alcohol alkoxy compound and
Amphoteric surfactant simultaneously stirs to being completely dissolved, and obtains solution a；
Step 2, brightener is added in solution a and stirs to being completely dissolved, and sequentially adds acrylate homopolymer sodium salt, crust becomes
Film stirs to dissolving completely, adds solvent and stirs to solution homogeneous transparent, obtains solution b；
Step 3, solution b standing is made contamination precipitation, through filtering impurity.