CN106433393A - Matting powder coating - Google Patents
Matting powder coating Download PDFInfo
- Publication number
- CN106433393A CN106433393A CN201610777472.7A CN201610777472A CN106433393A CN 106433393 A CN106433393 A CN 106433393A CN 201610777472 A CN201610777472 A CN 201610777472A CN 106433393 A CN106433393 A CN 106433393A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- powder coating
- extinction
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a matting powder coating. The matting powder coating is prepared from the following raw materials in parts by weight: 10-50 parts of organosilicon-modified epoxy resin, 10-50 parts of polyester resin, 4-15 parts of acrylic resin, 8-30 parts of titanium dioxide, 15-45 parts of matting barium sulfate, 3-15 parts of filler, 2-6 parts of an aid and 0.1-1.2 parts of masterbatches. The powder coating has outstanding high-temperature and low-temperature resistance, also has good mechanical performance, high impact resistance, good matting property, high attractiveness and good decoration effect, and is green and environment-friendly.
Description
Technical field
The present invention relates to powder coating technology field is and in particular to a kind of extinction powder coating.
Background technology
The application of thermosetting powder coating is quite varied, mainly by household electrical appliance, office furniture, automobile component, friendship
Logical facility, electric equipment, various tubing, construction material etc..The powdery paints that fast development is got up in recent years is a kind of new
Not solvent-laden solid powdery coating, it has and is easy at normal temperatures store, and utilization rate is high and easy the advantages of construct.From
Since powdery paints comes out, obtain being widely recognized as and developing rapidly of consumer.The preparation of this new powdery paints
Technique is typically mixed in certain proportion by specific resin, pigment, filler, curing agent and other auxiliary agent, then by extruding,
The techniques such as pulverizing are prepared from.
With social development, the working environment of various instruments becomes more complicated, basement, harbour, shaft bottom, depth
Water, tunnel, chemical plant etc., this instrument of the strong influence such as high/low temperature change, high pressure, HI high impact, high corrosion
Normal use, and coated by efficient powdery paints, good protected effect can be played, reduce the damage of instrument
Rate.
Content of the invention
It is an object of the invention to provide a kind of high temperature resistant, shock resistance, corrosion-resistant, there is the flatting silica of good decorative effect
Last coating.
The present invention is achieved through the following technical solutions:
A kind of extinction powder coating, including the raw material composition of following parts by weight:
10 ~ 50 parts of modifying epoxy resin by organosilicon;
10 ~ 50 parts of polyester resin;
4 ~ 15 parts of acrylic resin;
8 ~ 30 parts of titanium dioxide;
15 ~ 45 parts of extinction barium;
3 ~ 15 parts of filler;
2 ~ 6 parts of auxiliary agent;
0.1 ~ 1.2 part of color masterbatch.
Further, described a kind of extinction powder coating, including the raw material composition of following parts by weight:
15 ~ 35 parts of modifying epoxy resin by organosilicon;
15 ~ 35 parts of polyester resin;
5 ~ 12 parts of acrylic resin;
10 ~ 25 parts of titanium dioxide;
15 ~ 30 parts of extinction barium;
3 ~ 15 parts of filler;
2 ~ 6 parts of auxiliary agent;
0.1 ~ 1.2 part of color masterbatch.
Further, described filler includes activated carbon powder, carbon black, wax powder, zinc oxide and aluminum-spinel powder.
Further, described activated carbon powder, carbon black, the mass ratio of wax powder, zinc oxide and aluminum-spinel powder are 3:
0.05~0.1:0.2~0.5:0.5~1.2:1~2.
Further, described auxiliary agent includes 0.5 ~ 3 part of levelling agent, 0.5 ~ 1.5 part of optical brightener, 0.5 ~ 1.5 part disappear
The antioxidant of photo etching and 0.05 ~ 0.25 part.
The invention has the beneficial effects as follows:Powdery paints proposed by the present invention has excellent high- and low-temperature resistance performance, meanwhile,
Mechanical property is good, and shock resistance is strong, and extinction is good, and meanwhile, aesthetics is high, has good decorative effect, and, green ring
Protect.
Specific embodiment
With reference to embodiment, the present invention is described further.
Embodiment 1
A kind of extinction powder coating, including the raw material composition of following parts by weight:
15 parts of modifying epoxy resin by organosilicon;
15 parts of polyester resin;
5 parts of acrylic resin;
10 parts of titanium dioxide;
15 parts of extinction barium;
3 parts of filler;
3.32 parts of auxiliary agent;
0.5 part of color masterbatch.
In the present embodiment, filler includes activated carbon powder, carbon black, wax powder, zinc oxide and aluminum-spinel powder, activated carbon
Powder, carbon black, the mass ratio of wax powder, zinc oxide and aluminum-spinel powder are 3:0.08:0.3:1:1.5, auxiliary agent includes 1.5 parts
Levelling agent, 0.8 part of optical brightener, the antioxidant of 0.8 part of delustering agent and 0.12 part.
Embodiment 2
A kind of extinction powder coating, including the raw material composition of following parts by weight:
28 parts of modifying epoxy resin by organosilicon;
28 parts of polyester resin;
8 parts of acrylic resin;
20 parts of titanium dioxide;
28 parts of extinction barium;
10 parts of filler;
3.32 parts of auxiliary agent;
0.6 part of color masterbatch.
In the present embodiment, filler includes activated carbon powder, carbon black, wax powder, zinc oxide and aluminum-spinel powder, activated carbon
Powder, carbon black, the mass ratio of wax powder, zinc oxide and aluminum-spinel powder are 3:0.08:0.3:1:1.5, auxiliary agent includes 1.5 parts
Levelling agent, 0.8 part of optical brightener, the antioxidant of 0.8 part of delustering agent and 0.12 part.
Embodiment 3
A kind of extinction powder coating, including the raw material composition of following parts by weight:
35 parts of modifying epoxy resin by organosilicon;
35 parts of polyester resin;
12 parts of acrylic resin;
25 parts of titanium dioxide;
30 parts of extinction barium;
15 parts of filler;
3.32 parts of auxiliary agent;
1.2 parts of color masterbatch.
In the present embodiment, filler includes activated carbon powder, carbon black, wax powder, zinc oxide and aluminum-spinel powder, activated carbon
Powder, carbon black, the mass ratio of wax powder, zinc oxide and aluminum-spinel powder are 3:0.08:0.3:1:1.5, auxiliary agent includes 1.5 parts
Levelling agent, 0.8 part of optical brightener, the antioxidant of 0.8 part of delustering agent and 0.12 part.
The above, be only embodiments of the invention, is not the restriction that the present invention is made with any other form, and
Any modification made according to the technical spirit of the present invention or equivalent variations, still fall within scope of the present invention.
Claims (5)
1. a kind of extinction powder coating it is characterised in that:Raw material composition including following parts by weight:
10 ~ 50 parts of modifying epoxy resin by organosilicon;
10 ~ 50 parts of polyester resin;
4 ~ 15 parts of acrylic resin;
8 ~ 30 parts of titanium dioxide;
15 ~ 45 parts of extinction barium;
3 ~ 15 parts of filler;
2 ~ 6 parts of auxiliary agent;
0.1 ~ 1.2 part of color masterbatch.
2. according to claim 1 a kind of extinction powder coating it is characterised in that:Raw material group including following parts by weight
Become:
15 ~ 35 parts of modifying epoxy resin by organosilicon;
15 ~ 35 parts of polyester resin;
5 ~ 12 parts of acrylic resin;
10 ~ 25 parts of titanium dioxide;
15 ~ 30 parts of extinction barium;
3 ~ 15 parts of filler;
2 ~ 6 parts of auxiliary agent;
0.1 ~ 1.2 part of color masterbatch.
3. according to claim 1 a kind of extinction powder coating it is characterised in that:Described filler include activated carbon powder, carbon black,
Wax powder, zinc oxide and aluminum-spinel powder.
4. according to claim 3 a kind of extinction powder coating it is characterised in that:Described activated carbon powder, carbon black, wax powder, oxygen
Changing zinc and the mass ratio of aluminum-spinel powder is 3:0.05~0.1:0.2~0.5:0.5~1.2:1~2.
5. according to claim 1 a kind of extinction powder coating it is characterised in that:Described auxiliary agent includes 0.5 ~ 3 part of levelling
Agent, 0.5 ~ 1.5 part of optical brightener, the antioxidant of 0.5 ~ 1.5 part of delustering agent and 0.05 ~ 0.25 part.