CN110218506A - High-temperature-resistant multicolor metal powder coating and preparation method thereof - Google Patents
High-temperature-resistant multicolor metal powder coating and preparation method thereof Download PDFInfo
- Publication number
- CN110218506A CN110218506A CN201910583793.7A CN201910583793A CN110218506A CN 110218506 A CN110218506 A CN 110218506A CN 201910583793 A CN201910583793 A CN 201910583793A CN 110218506 A CN110218506 A CN 110218506A
- Authority
- CN
- China
- Prior art keywords
- parts
- pigment
- powder
- powdery paints
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a high-temperature-resistant multicolor metal powder coating and a preparation method thereof, wherein the high-temperature-resistant multicolor metal powder coating comprises the following components in parts by weight: 45-65 parts of organic silicon modified epoxy resin, 45-60 parts of polyester resin, 3-8 parts of curing agent, 2-6 parts of pigment, 2-4 parts of filler, 1-4 parts of metal powder, 10-16 parts of high-temperature resistant pigment red, 3-8 parts of wear-resistant additive, 3-8 parts of antioxidant and 0.2-1 part of accelerator. The invention adds the functional pigment and filler with high melting point, titanium dioxide, talcum powder, mica powder and aluminum powder according to the weight proportion, thereby not only endowing the coating with the color required by appearance, but also enhancing other comprehensive properties of the coating, such as wear resistance and high temperature resistance, thereby prolonging the service life and saving the cost.
Description
Technical field
The present invention relates to metal powder coating fields, and in particular to a kind of high temperature resistant multi-colour metal powdery paints and its preparation
Method.
Background technique
Metal powder coating refers to the various types powder containing metallic pigments (such as: pearlescent pigment, aluminium silver powder, Cu-Zn alloy powder)
Last coating.With the development of powdery paints and the raising of technical level, powdery paints kind becomes increasingly abundant and perfect, metal powder
The high-end powdery paints such as coating has also obtained developing on a large scale very much.Because it not only has defencive function outstanding, but also have magnificent gorgeous
Decorative appearance beautiful, flashing is charming, is received by the market very much.With the growth of metal powder coating dosage, people are to product
Quality requirement is also higher and higher.
But currently, the generally existing heat-resisting quantity of metallic paint in the market is insufficient, wearability is poor, after temperature increases
Coating surface is easily caused to damage, therefore, using also affecting service life indirectly.
Summary of the invention
In view of the above existing problems in the prior art, the present invention provides a kind of high temperature resistant multi-colour metal powdery paints and its systems
Dystectic functional pigments and fillers, titanium dioxide, talcum powder, mica powder, aluminium powder, thus not is added in Preparation Method according to the weight ratio
Color needed for appearance of coat only can be assigned, and other comprehensive performances of coating, such as wearability, heat-resisting quantity can be enhanced
Can, thus prolong the service life, save the cost.
To achieve the goals above, the technical solution adopted by the present invention is that: a kind of high temperature resistant multi-colour metal powdery paints, packet
Component containing following parts by weight: 45-65 parts of modifying epoxy resin by organosilicon, 45-60 parts of polyester resin, 3-8 parts of curing agent, pigment
2-6 parts, 2-4 parts of filler, 1-4 parts of metal powder, high-temperature resisting pigment be 10-16 parts red, 3-8 parts of antiwear assistant, 3-8 parts of antioxidant,
0.2-1 parts of promotor.
Preferably, the component comprising following parts by weight: 48-62 parts of modifying epoxy resin by organosilicon, polyester resin 48-62
Part, 4-7 parts of curing agent, 3-5 parts of pigment, 2.5-4 parts of filler, 2-3 parts of metal powder, high-temperature resisting pigment be 12-15 parts red, wear-resisting helps
4-7 parts of agent, 4-7 parts of antioxidant, 0.5-0.8 parts of promotor.
Any of the above-described scheme is preferably, the component comprising following parts by weight: 45 parts of modifying epoxy resin by organosilicon, polyester
45 parts of resin, 3 parts of curing agent, 2 parts of pigment, 2 parts of filler, 1 part of metal powder, high-temperature resisting pigment be 10 parts red, 3 parts of antiwear assistant,
3 parts of antioxidant, 0.2 part of promotor.
Any of the above-described scheme is preferably, the component comprising following parts by weight: 50 parts of modifying epoxy resin by organosilicon, polyester
55 parts of resin, 5 parts of curing agent, 4 parts of pigment, 3 parts of filler, 2.5 parts of metal powder, high-temperature resisting pigment be 14 parts red, antiwear assistant 5
Part, 5 parts of antioxidant, 0.5 part of promotor.
Any of the above-described scheme is preferably, the component comprising following parts by weight: 65 parts of modifying epoxy resin by organosilicon, polyester
60 parts of resin, 8 parts of curing agent, 6 parts of pigment, 4 parts of filler, 4 parts of metal powder, high-temperature resisting pigment be 16 parts red, 8 parts of antiwear assistant,
8 parts of antioxidant, 1 part of promotor.
Any of the above-described scheme is preferably, and the metal powder is zinc powder and/or copper powder.
Any of the above-described scheme is preferably, and the pigment is cinnabar and/or laterite.
Any of the above-described scheme is preferably, and the promotor is aluminium oxide C.
Any of the above-described scheme is preferably, the filler be barium carbonate, titanium dioxide, talcum powder, mica powder, in aluminium powder extremely
Few one kind.
Color needed for titanium dioxide, talcum powder, mica powder, aluminium powder etc. both can assign appearance of coat, and painting can be enhanced
Other comprehensive performances of layer, such as wearability.
Any of the above-described scheme is preferably, the barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder amount ratio be 1-
4:2-3:2-4:3-5:2-4.
Any of the above-described scheme is preferably, the barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder amount ratio be 1:
2:2:3:2.
Any of the above-described scheme is preferably, the barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder amount ratio be 2:
2.5:3:4:3.
Any of the above-described scheme is preferably, the barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder amount ratio be 4:
3:4:5:4.
Any of the above-described scheme is preferably, and the antiwear assistant is at least one of aluminium oxide, silicon nitride.
Any of the above-described scheme is preferably, and the curing agent is epoxy curing agent.
The present invention also provides a kind of preparation methods of high temperature resistant multi-colour metal powdery paints comprising the steps of:
Step (1), by weight ratio by modifying epoxy resin by organosilicon, polyester resin, metal powder high-speed stirred mix;
Step (2), by mixture obtained above through melting extrusion, broken, screening, extracting screen underflow;
Step (3), red, antiwear assistant, antioxidant, promotor high-speed stirred by screenings and curing agent, pigment, high-temperature resisting pigment
It mixes, obtains high temperature resistant multi-colour metal powdery paints.
Any of the above-described scheme is preferably, and the mixing speed in the step (1) is 120-160r/min.
Any of the above-described scheme is preferably, and melting extrusion temperature is 240-290 DEG C in the step (2).
Any of the above-described scheme is preferably, and screenings is 80-140 mesh in the step (2).
The beneficial effects of the present invention are: the present invention provides a kind of high temperature resistant multi-colour metal powdery paints and preparation method thereof,
Component comprising following parts by weight: 45-65 parts of modifying epoxy resin by organosilicon, 45-60 parts of polyester resin, 3-8 parts of curing agent, face
2-6 parts of material, 2-4 parts of filler, 1-4 parts of metal powder, high-temperature resisting pigment be 10-16 parts red, 3-8 parts of antiwear assistant, antioxidant 3-8
Part, 0.2-1 parts of promotor.Dystectic functional pigments and fillers, titanium dioxide, talcum powder, cloud is added in the present invention according to the weight ratio
Female powder, aluminium powder, thus color needed for appearance of coat can not only be assigned, and other comprehensive performances of coating can be enhanced, it is such as resistance to
Mill property, high temperature resistance, thus prolong the service life, save the cost.
Specific embodiment
Embodiment 1:
A kind of high temperature resistant multi-colour metal powdery paints, the component comprising following parts by weight: 45 parts of modifying epoxy resin by organosilicon gathers
45 parts of ester resin, 3 parts of curing agent, 2 parts of pigment, 2 parts of filler, 1 part of metal powder, high-temperature resisting pigment be 10 parts red, antiwear assistant 3
Part, 3 parts of antioxidant, 0.2 part of promotor.
Metal powder is zinc powder and/or copper powder.
Pigment is cinnabar and/or laterite.Promotor is aluminium oxide C.Filler is barium carbonate, titanium dioxide, talcum powder, mica
At least one of powder, aluminium powder.Barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder amount ratio be 1:2:2:3:2.
Antiwear assistant is aluminium oxide.Curing agent is epoxy curing agent.
The present invention also provides a kind of preparation methods of high temperature resistant multi-colour metal powdery paints comprising the steps of:
Step (1), by weight ratio by modifying epoxy resin by organosilicon, polyester resin, metal powder high-speed stirred mix, stirring
Speed is 120-160r/min.
Step (2), by mixture obtained above through melting extrusion, broken, screening, extracting screen underflow, melting extrusion temperature
It is 240-290 DEG C, screenings is 80-140 mesh.
Step (3), red, antiwear assistant, antioxidant, promotor high speed by screenings and curing agent, pigment, high-temperature resisting pigment
It stirs and evenly mixs, obtains high temperature resistant multi-colour metal powdery paints.
Embodiment 2:
A kind of high temperature resistant multi-colour metal powdery paints, the component comprising following parts by weight: 50 parts of modifying epoxy resin by organosilicon gathers
55 parts of ester resin, 5 parts of curing agent, 4 parts of pigment, 3 parts of filler, 2.5 parts of metal powder, high-temperature resisting pigment be 14 parts red, antiwear assistant 5
Part, 5 parts of antioxidant, 0.5 part of promotor.
Barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder amount ratio be 2:2.5:3:4:3.
Embodiment 3:
A kind of high temperature resistant multi-colour metal powdery paints, the component comprising following parts by weight: 65 parts of modifying epoxy resin by organosilicon gathers
60 parts of ester resin, 8 parts of curing agent, 6 parts of pigment, 4 parts of filler, 4 parts of metal powder, high-temperature resisting pigment be 16 parts red, antiwear assistant 8
Part, 8 parts of antioxidant, 1 part of promotor.
Barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder amount ratio be 4:3:4:5:4.
Embodiment 4:
A kind of high temperature resistant multi-colour metal powdery paints and embodiment 3 are different, the component comprising following parts by weight: comprising following
The component of parts by weight: 45 parts of modifying epoxy resin by organosilicon, 45 parts of polyester resin, 3 parts of curing agent, 2 parts of pigment, 2 parts of filler, gold
Belong to 1 part of powder, 3 parts of antiwear assistant, 3 parts of antioxidant, 0.2 part of promotor.
Embodiment 5:
A kind of high temperature resistant multi-colour metal powdery paints and embodiment 3 are different, and the component comprising following parts by weight: organosilicon changes
45 parts of epoxy resin of property, 45 parts of polyester resin, 3 parts of curing agent, 2 parts of pigment, 1 part of metal powder, high-temperature resisting pigment are 10 parts red, resistance to
3 parts of milling aid, 3 parts of antioxidant, 0.2 part of promotor.
High temperature resistant multi-colour metal powdery paints prepared by embodiment 1- embodiment 5 is tested for the property, test result is such as
Shown in the following table 1.
The test result of 1 high temperature resistant multi-colour metal powdery paints of table
Impact | Folding test | Weatherability | |
Reference standard | GB/T1732-1993 | GB/T6743-2007 | GB/T1865-2009 |
Embodiment 1 | 47cm.kg | 2mm | > 1000h |
Embodiment 2 | 48cm.kg | 2mm | > 1000h |
Embodiment 3 | 48cm.kg | 2mm | > 1000h |
Embodiment 4 | 47cm.kg | 2mm | > 500h |
Embodiment 5 | 44cm.kg | 1.8mm | > 600h |
It is weather-proof to can be seen that high temperature resistant multi-colour metal powdery paints prepared by embodiment 1- embodiment 3 from the test result of table 1
The performances such as property, bending are preferable.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
In the technical scope disclosed by the present invention, any changes or substitutions that can be easily thought of by anyone skilled in the art,
It should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of high temperature resistant multi-colour metal powdery paints, which is characterized in that the component comprising following parts by weight: organic silicon modified epoxy
45-65 parts of oxygen resin, 45-60 parts of polyester resin, 3-8 parts of curing agent, 2-6 parts of pigment, 2-4 parts of filler, 1-4 parts of metal powder,
High-temperature resisting pigment is 10-16 parts red, 3-8 parts of antiwear assistant, 3-8 parts of antioxidant, 0.2-1 parts of promotor.
2. a kind of high temperature resistant multi-colour metal powdery paints according to claim 1, which is characterized in that include following parts by weight
Component: 48-62 parts of modifying epoxy resin by organosilicon, 48-62 parts of polyester resin, 4-7 parts of curing agent, 3-5 parts of pigment, filler
2.5-4 parts, 2-3 parts of metal powder, high-temperature resisting pigment be 12-15 parts red, 4-7 parts of antiwear assistant, 4-7 parts of antioxidant, promotor
0.5-0.8 parts.
3. a kind of high temperature resistant multi-colour metal powdery paints according to claim 1, which is characterized in that include following parts by weight
Component: 45 parts of modifying epoxy resin by organosilicon, 45 parts of polyester resin, 3 parts of curing agent, 2 parts of pigment, 2 parts of filler, metal powder
1 part, high-temperature resisting pigment is 10 parts red, 3 parts of antiwear assistant, 3 parts of antioxidant, 0.2 part of promotor.
4. a kind of high temperature resistant multi-colour metal powdery paints according to claim 1, which is characterized in that include following parts by weight
Component: 50 parts of modifying epoxy resin by organosilicon, 55 parts of polyester resin, 5 parts of curing agent, 4 parts of pigment, 3 parts of filler, metal powder
2.5 parts, high-temperature resisting pigment is 14 parts red, 5 parts of antiwear assistant, 5 parts of antioxidant, 0.5 part of promotor.
5. a kind of high temperature resistant multi-colour metal powdery paints according to claim 1, which is characterized in that include following parts by weight
Component: 65 parts of modifying epoxy resin by organosilicon, 60 parts of polyester resin, 8 parts of curing agent, 6 parts of pigment, 4 parts of filler, metal powder
4 parts, high-temperature resisting pigment is 16 parts red, 8 parts of antiwear assistant, 8 parts of antioxidant, 1 part of promotor.
6. a kind of high temperature resistant multi-colour metal powdery paints according to any one of claims 1-5, which is characterized in that described
Promotor is aluminium oxide C.
7. a kind of high temperature resistant multi-colour metal powdery paints according to any one of claims 1-5, which is characterized in that described
Filler is at least one of barium carbonate, titanium dioxide, talcum powder, mica powder, aluminium powder.
8. a kind of high temperature resistant multi-colour metal powdery paints according to any one of claims 1-5, which is characterized in that described
Antiwear assistant is at least one of aluminium oxide, silicon nitride.
9. a kind of high temperature resistant multi-colour metal powdery paints according to any one of claims 1-5, which is characterized in that described
Curing agent is epoxy curing agent.
10. a kind of preparation method using high temperature resistant multi-colour metal powdery paints of any of claims 1-9, special
Sign is comprising the steps of:
Step (1), by weight ratio by modifying epoxy resin by organosilicon, polyester resin, metal powder high-speed stirred mix;
Step (2), by mixture obtained above through melting extrusion, broken, screening, extracting screen underflow;
Step (3), red, antiwear assistant, antioxidant, promotor high-speed stirred by screenings and curing agent, pigment, high-temperature resisting pigment
It mixes, obtains high temperature resistant multi-colour metal powdery paints.