CN106431482A - Plum-blossom-shaped pyroclastic rock lightweight through-hole ceramsite with air purification function - Google Patents
Plum-blossom-shaped pyroclastic rock lightweight through-hole ceramsite with air purification function Download PDFInfo
- Publication number
- CN106431482A CN106431482A CN201610847305.5A CN201610847305A CN106431482A CN 106431482 A CN106431482 A CN 106431482A CN 201610847305 A CN201610847305 A CN 201610847305A CN 106431482 A CN106431482 A CN 106431482A
- Authority
- CN
- China
- Prior art keywords
- air purification
- pyroclastic rock
- purification function
- quincunx
- lightweight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a plum-blossom-shaped pyroclastic rock lightweight through-hole ceramsite with an air purification function. The technical scheme of the ceramsite is characterized in that ingredients comprise attapulgite pottery clay powder with the air purification function, pyroclastic rock, activated clay waste residues, white carbon black, activated alumina, sodium aluminate, scrubbing pyroclastic rock photocatalytic spraying liquid and the like; the plum-blossom-shaped pyroclastic rock lightweight through-hole ceramsite with the air purification function is prepared from the ingredients through stirring, extruding granulation, drying, roasting, heat preservation, sieving, soaking, drying, sieving and sealed packaging; the plum-blossom-shaped pyroclastic rock lightweight through-hole ceramsite with the air purification function has the characteristics of being large in effective specific surface area, low in stacking density, high in moisture absorption, excellent in adsorption performance and high in lightweight strength and integrating micropores and macropores and is suitable for being placed in rooms, furniture cabinets, vehicles, airplanes, ships or other buildings for adsorbing and degrading pollutants such as formaldehyde, ammonia, benzene, TVOC (total volatile organic compounds) and the like, thereby achieving the purpose of air purification.
Description
Technical field
The present invention relates to haydite is and in particular to a kind of quincunx pyroclastic rock lightweight through hole with air purification function
Haydite.
Background technology
The air purifying preparation supplied in the market has following several types：Absorbent-type air purifying preparation, covering type taste removal
Product and Breakdown type taste removal product.Absorbent-type air purifying preparation is using materials such as activated carbon, bamboo charcoal, molecular sieve, mineral
The performances such as physical absorption, chemisorbed, catalysis oxidation and reduction remove the purification product of pollutant；Covering type taste removal product is profit
Cover the various abnormal flavour of in the air with the fragrance of aromatic hydrocarbon, abnormal flavour is not in fact removed, simply by a lot of air fresheners
With a kind of odor type, abnormal flavour is covered；Breakdown type air clearing product is more rare on the market.
Chinese patent Authorization Notice No.：CN 103861421 B, authorized announcement date：On November 18th, 2015, entitled " one
Kind of air purifying preparation ", discloses that " a kind of air purifying preparation, its preparing raw material is contained by mass fraction：Diatomite in powder, zeolite powder,
Medical stone powder, tourmaline powder, activated carbon powder, sepiolite powder, titanium dioxide powder, and adopt and prepare with the following method：1) by kieselguhr
Powder, zeolite powder, medical stone powder, tourmaline powder, activated carbon powder, sepiolite powder, titanium dioxide powder mixing；2) by step 1) gained mix
Compound pelletize；3) baking step 2) gained mixture after pelletize.The air purifying preparation specific surface that the present invention is obtained is big and uniform,
Good to the adsorption-decomposition function effect of in the air harmful substance, it is for interior, the depollution of environment of the closing space such as in-car and various sky
The ideal chose material of gas purifier ".
The weak point of above-mentioned patent is：(1) diatomite in powder, zeolite powder, medical stone powder, tourmaline powder, activated carbon powder and sea
Afrodite powder, not through necessary modification, is difficult to really play the effect of its effective purify air.(2) gained mixed powder
Adopt granulating disc pelletize after the clear water stirring adding 20-30%, be a kind of circular granular of a diameter of 1.2-1.6mm.Should
Mixed powder itself normal moisture content of invention is more than 10%, and the circular granular moisture content after the pelletize that adds water will be greater than 30%, and
Drying temperature, in the case of less than 100 DEG C, is difficult to dry circular granular in 3 hours.Kieselguhr, zeolite, Maifanitum,
After tourmaline and meerschaum carry out heat treatment process at 250～450 DEG C, its absorption property is relatively good, and this is the technology of this area
Personnel know altogether；The circular granular of this invention is dried in the case of less than 100 DEG C, can not effectively improve the work of purify air
With, and the comprcssive strength of circular granular also very little, gently one pinched with handss, circular granular will be crumbed as powdered.
The spheroidal air purifying preparation of supply, molecular sieve, desiccant or other spherical granules on market, in pelletize
It is first powdery dispensing to be processed into the bead that a kind of diameter is less than 0.5 millimeter in journey, then by the vaporific aqueous solution preparing, spray
Spill in the bead in on-stream comminutor, then powdery dispensing is trickled down on the surface of moistening bead, through being repeated several times
Spray vaporific aqueous solution and trickle down on the surface of moistening bead by powdery dispensing, through the parcel of layer upon layer, bead
Volume constantly increase, be finally completed the overall process of pelletize, be prepared into a kind of spherical granules, due to spherical granules internal junction
Structure is very closely knit, greatly reduces the effective specific surface area of spherical granules, the proportion of spherical granules and bulk density all than
Larger, directly influence the absorption purifying effect of spherical granules.
Content of the invention
The purpose of the present invention is to overcome weak point in prior art, provides and a kind of quincunx has air purification function
Pyroclastic rock lightweight through hole haydite.
The dispensing of the quincunx pyroclastic rock lightweight through hole haydite with air purification function is by having purify air work(
The attapulgite potter's clay powder of energy, pyroclastic rock, active white clay waste slag, white carbon, precipitated calcium carbonate, light magnesium oxide, active oxygen
Change aluminum, sodium aluminate, cenosphere, gesso, expanded perlite, sodium lauryl sulphate and washable pyroclastic rock light to touch
Matchmaker's spray coating liquor forms.
The production method of the quincunx pyroclastic rock lightweight through hole haydite with air purification function：Have quincunx
The dispensing of the pyroclastic rock lightweight through hole semi-finished product of air purification function is stirred, extruder grain, drying, roasting,
It is incubated, sieves, soaking, drying, sieving, packing as the quincunx pyroclastic rock lightweight through hole with air purification function
Haydite.
The attapulgite potter's clay powder with air purification function is by high viscous Concave-convex clay rod, attapulite constant humidity amendment, sky
So mineral adsorption filtering agent, Cacumen Platycladi, aluminium silicate fiber peacekeeping polyacrylamide composition, has preferable caking property, plasticity, touches
Degeneration, fire resistance and heat stability, can effectively adsorb the harmful substances such as formaldehyde in air, ammonia and benzene, environmental protection and enhancement
People's is healthy, and the present invention is from fineness of the particles≤0.074 millimeter of the attapulgite potter's clay powder with air purification function.
Pyroclastic rock is the rock between the transitional type between magma lava and sedimentary rock, wherein more than 50% one-tenth
Point be the material composition being sprayed by pyroclastic flow, relevant with many useful mineral products, such as ferrum, manganese, potassium, boron, sulfur, uranium deposit and
The metal sulfide such as copper, lead, zinc mineral deposit, in terms of nonmetal depdosit, it and Zeolite mineral, bentonite ore, kaolin ore, pyrophillite
Ore deposit etc. is in close relations, and these tephres are mainly the lava of premature coagulation, channel circumference on volcano and are exploded in volcanic eruption
The rock formation splitting, pyroclastic rock is in cellular, and the present invention selects fineness of the particles≤0.074 millimeter of pyroclastic rock.
Active hargil is a kind of odorless, tasteless, nontoxic white or cream-coloured powder or granule, and the activity after decolouring is white
Soil loses activity and becomes active white clay waste slag, some oily factories all by these active white clay waste slags abandon, if cannot and
When process, produces after the organic fermentation of lipid in active white clay waste slag and goes mouldy and stench, the not only wasting of resources, pollute environment and
Groundwater quality, and fire hazardous, will cause certain loss to society and enterprise；The present invention selects active white clay waste slag
Fineness of the particles≤0.149 millimeter.
White carbon is a kind of ultra tiny inorganic porous property material, due to its particle diameter very little, has that specific surface area is big, surface is inhaled
Attached power is strong, chemical purity is high, dispersive property is good, superior stability, reinforcing, thickening property, adhesive force and thixotropy etc. are special
Performance.
Precipitated calcium carbonate fine particles, surface are rougher, and specific surface area is big, and precipitated calcium carbonate also has and do not settle, easily point
Dissipate, the characteristic such as good luster, the present invention selects fineness of the particles≤0.074 millimeter of precipitated calcium carbonate.
Light magnesium oxide is the white loose unformed powder of lightweight, odorless, tasteless, and nontoxic, volume shared by light magnesium oxide is about
About the three times of heavy-burned magnesia, there are extremely fireproof heat-insulating property, reinforcing agent, adhesive, the present invention selects light magnesium oxide
Fineness of the particles≤0.074 millimeter.
Activated alumina is the solid material of a kind of porous, high degree of dispersion, has very big surface area, and its micropore surface has
Standby characteristic required by catalytic action, such as absorption property, surface activity, excellent heat stability etc., so be widely used as
The catalyst of chemical reaction and catalyst carrier, the present invention selects fineness of the particles≤0.074 millimeter of activated alumina.
Sodium aluminate also known as sodium metaaluminate, are a kind of general chemical article, white, odorless, tasteless, in alkaline solid,
Easily absorb moisture content and carbon dioxide in atmosphere, the present invention selects fineness of the particles≤0.074 millimeter of sodium aluminate.
Natural dihydrate gypsum is also called Gypsum Fibrosum, through calcining, levigate obtain gesso, Gypsum Fibrosum preparata has more micropore
Structure, is allowed to have excellent sound insulation, heat-insulated and fire protecting performance, and the present invention selects fineness of the particles≤0.074 millimeter of gesso.
Cenosphere outward appearance is canescence, is a kind of loose, good fluidity powder body material, cenosphere proportion is little, table
Face is smooth, intensity is big, easily disperse, the present invention select the fineness of the particles of cenosphere≤≤ 0.149 millimeter.
Perlite is expanded and becomes a kind of lightweight, multifunctional novel shaped material, have that apparent density is light, heat conductivity is low,
The features such as chemical stability is good, the present invention selects fineness of the particles≤0.074 millimeter of expanded perlite.
Sodium lauryl sulphate is white or faint yellow powdery, is dissolved in water, insensitive to alkali and hard water, has decontamination, breast
Change and excellent foaming power, be a kind of nontoxic anion surfactant.
Washable pyroclastic rock photocatalytic spray liquid is sprayed on building or decorative material surface, under the irradiation of light,
Can continual absorption and the pollutant such as degradation of formaldehyde, ammonia, benzene,toluene,xylene, TVOC, and have extremely strong sterilization,
The function of deodorization, mould proof, anti-fouling and self-cleaning and purify air.
The technical scheme is that：
1st, the dispensing of the quincunx pyroclastic rock lightweight through hole haydite with air purification function is by weight percentage by following
Group is grouped into：Quincunx have the pyroclastic rock lightweight through hole semi-finished product 55～95% of air purification function and washable
Pyroclastic rock photocatalytic spray liquid 5～45%.
2nd, the production method of the quincunx pyroclastic rock lightweight through hole haydite with air purification function：(1) first will be erasable
Wash pyroclastic rock photocatalytic spray liquid to put in fermentation vat, then will be light for the quincunx pyroclastic rock with air purification function
Matter through hole semi-finished product is slowly added in the washable pyroclastic rock photocatalytic spray liquid in fermentation vat, and quincunx have only
Change the micropore inside and outside the pyroclastic rock lightweight through hole semi-finished product of air function, constantly suck washable pyroclastic rock
Photocatalytic spray liquid, until in saturation；(2) take out from fermentation vat and be filled washable pyroclastic rock photocatalytic spray liquid
The quincunx pyroclastic rock lightweight through hole haydite with air purification function, be transported in low temperature rotary drying oven and carry out
Dry, drying temperature controls at 150～180 DEG C, and drying time controlled at 1～3 hour；(3) by the quincunx tool after oven drying at low temperature
The pyroclastic rock lightweight through hole haydite having air purification function is transported in flat vibrating screen and is sieved, and weeds out broken
Grain and powder, pack the finished product for the quincunx pyroclastic rock lightweight through hole haydite with air purification function.
3rd, the dispensing by weight hundred of the quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function
Ratio is divided to be made up of following component：Have the attapulgite potter's clay powder 10～45% of air purification function, pyroclastic rock 5～25%,
Active white clay waste slag 2～10%, white carbon 1～8%, precipitated calcium carbonate 1～5%, light magnesium oxide 1～5%, activated alumina
1～5%, sodium aluminate 0.5～5%, cenosphere 0.5～5%, gesso 0.5～5%, expanded perlite 0.5～5%, ten
Sodium dialkyl sulfate 0.5～5% and water 10～40%.
4th, the production method of the quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function：(1) will
The stirring that the dispensing input of the quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function has operated
In mixer, stirring is mixed into the mixture of the quincunx pyroclastic rock lightweight through hole haydite with air purification function；⑵
The mixture of the quincunx pyroclastic rock lightweight through hole haydite with air purification function is transported in Squeezinggranulator, squeezes
Pressure pelletize is the quincunx pyroclastic rock lightweight through hole haydite blank material with air purification function, and quincunx have purification sky
The macropore at the pyroclastic rock lightweight through hole haydite blank material center of airway dysfunction is through hole；(3) by quincunx, there is purify air work(
The pyroclastic rock lightweight through hole haydite blank material of energy is transported in swinging drying oven is dried, and drying temperature controls
200～250 DEG C, drying time controlled at 1～4 hour；(4) the quincunx volcano with air purification function after drying is broken
Bits rock lightweight through hole haydite blank material be transported to swinging roasting kiln roasting, the temperature control of combustor at 900～950 DEG C,
Roasting time controlled at 1～3 hour；(5) by the quincunx pyroclastic rock lightweight through hole with air purification function after roasting
Haydite blank material, input is incubated in rustless steel cylinder storehouse, and temperature retention time controlled at 24～72 hours；(6) by the prunus mume (sieb.) sieb.et zucc. after insulation cooling
The pyroclastic rock lightweight through hole haydite blank material that flower-shape has air purification function is transported in roller vibrating screen and is sieved,
Weeding out broken granule and powder is the quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function.
The production method the 5th, with the attapulgite potter's clay powder of air purification function is：(1) will there is the recessed of air purification function
Pulverized in input pulverizer after the dispensing mixing of convex rod potter's clay powder, the compound particles fineness after pulverizing is less than 0.5 millimeter；
(2) pulverulent mixture is added and soak in old pond that to carry out soaking old process with water be semi-finished product, soak old time control and exist
7～30 days；(3) semi-finished product are inputted in vacuum-extruder and be squeezed into cylindrical bar, the diameter control of cylindrical bar exists
2～10 millimeters；(4) cylindrical bar is input to cement threshing ground and carries out dry in the sun, the cylindrical bar water content after dry in the sun is little
In 15%；(5) pulverizing will be carried out for powder in the cylindrical bar input grinding machine after dry in the sun, the fineness of the particles of powder is little
In 0.074 millimeter.
The dispensing with the attapulgite potter's clay powder of air purification function is made up of following component by weight percentage：High viscous recessed
Convex rod stone clay 35～60%, attapulite constant humidity amendment 10～35%, natural-minerals adsorptive filter medium 5～20%, Cacumen Platycladi 2
～15%, alumina silicate fibre 1～5% and polyacrylamide 0.1～3%.
The attapulgite potter's clay powder with air purification function is applied on 2 25th, 2011 using by the present inventor
" having the attapulgite potter's clay powder of air purification function ", Chinese patent Authorization Notice No. is：CN 102173743 B, Granted publication
Day：On July 25th, 2012.
High viscous Concave-convex clay rod is to be glued using the attapulgite that the processing technique improving viscosity of attapulgite clay produces
Soil, from the attapulgite clay of mining area exploitation, needs the weathering through 30～120 days；Modification processing method is：With weight
Percentage ratio calculates, and takes the attapulgite clay after weathering 94～98%, is uniformly added into 2～6% sodium carbonate, common input leaching
In bubble pond, clear water is added to carry out soaking ageing, soak time is 72～120 hours；Take the attapulgite clay after immersion, input
It is stirred in blender, and by the attapulgite clay after stirring, is extruded into thin slice through extruder, its THICKNESS CONTROL is 0.5～2
Millimeter, attapulgite clay thin slice carries out dry in the sun, the attapulgite clay thin slice after dry in the sun, its water content≤15%；Dispensing
Calculated in weight percent：Attapulgite clay 94～98% after dry in the sun, High hydrophilous resin 0.5～5% and cellulose 0.5～
3%, above-mentioned dispensing is stirred, after stirring, in input grinding machine, carries out pulverizing, fineness of the particles≤0.074 millimeter；
Above-mentioned production technology is " to improve viscosity of attapulgite clay using filed in 20 days June in 2005 of the present inventor
Processing technique ", Chinese patent Authorization Notice No. is：CN 1317067C, authorized announcement date：On May 23rd, 2007.
The detection method of high viscous Concave-convex clay rod：Take 28.0g attapulgite clay powder sample, add homogenizer
In suspension cup, add 372g water, suspension cup is placed on homogenizer, stir under 11000 revs/min of rotating speed
20 minutes, then by the beaker that high-speed stirred sample suspension pours 250mL into, tested using NDJ-1 type rotating cylinder viscometer
The viscosity of suspension, tested viscosity value >=2200 mPa s is high viscous Concave-convex clay rod.
6th, the dispensing of washable pyroclastic rock photocatalytic spray liquid is made up of following component by weight percentage：Volcano is broken
Bits rock 5～12%, attapulgite clay after the acidify 4～10%, high viscous Concave-convex clay rod 2～8%, nano titanium oxide 1
～5%, white carbon 1～5%, nano silver-supported antibacterial powder 0.5～5%, nano magnesia 0.5～5%, nano zirconium dioxide 0～
5%th, nano aluminium oxide 0～5%, nano zine oxide 0～5%, polyvinyl alcohol 0.5～5%, Polyethylene Glycol 0.1～3%, poly- two
Methylsiloxane 0.1～2% and deionized water 50～82%；
The production method of washable pyroclastic rock photocatalytic spray liquid：(1) by washable pyroclastic rock photocatalytic spray liquid
Carry out strong stirring, dispersion and emulsifying in the high speed dispersor that dispensing input has operated, then grind in input three-roll grinder
Grind the semi-finished product for washable pyroclastic rock photocatalytic spray liquid；(2) by the half of washable pyroclastic rock photocatalytic spray liquid
In finished product input colloid mill, carry out again disperseing, emulsifying, pulverizing, homogenizing, froth breaking and grinding；(3) the washable volcano after grinding
Granularity≤0.01 millimeter of solid particle in clastic rock photocatalytic spray liquid, canned for washable pyroclastic rock photocatalytic spray
Liquid.
Washable pyroclastic rock photocatalytic spray liquid is using " can filed on 07 29th, 2016 by the applicant
Clean pyroclastic rock photocatalytic spray liquid ", Chinese Patent Application No. is：201610612791.2.
Heretofore described PCm is weight percentage.
Having in the attapulgite potter's clay powder of air purification function in the present invention has substantial amounts of micropore and activated carbon, has relatively
Caking property well, plasticity, thixotropy, fire resistance and heat stability, can effectively adsorb formaldehyde in air, ammonia and benzene etc. and be harmful to
Material.
It is primary raw material using the attapulgite potter's clay powder with air purification function, production is quincunx to have purify air work(
The pyroclastic rock lightweight through hole haydite of energy, has given full play to the Effective power of the attapulgite potter's clay powder with air purification function
Energy.
Tephre is mainly the rock shape that on volcano, the lava of premature coagulation, channel circumference are burst in volcanic eruption
Become, pyroclastic rock is in cellular, can increase the quincunx pyroclastic rock lightweight through hole haydite with air purification function
Internal porosity.
In roasting process, the lipid in active white clay waste slag and organic matter participate in quincunx tool to active white clay waste slag jointly
There is the roasting of the pyroclastic rock lightweight through hole haydite of air purification function, improve the heat of combustion-gas flow, not only can save
The energy, the inside also helping the quincunx pyroclastic rock lightweight through hole haydite with air purification function can be grilled thoroughly completely,
Increase the quincunx porosity within pyroclastic rock lightweight through hole haydite with air purification function.
White carbon, light magnesium oxide, activated alumina and sodium aluminate can improve the quincunx fire with air purification function
The absorbability of mountain clastic rock lightweight through hole haydite and the quincunx pyroclastic rock lightweight with air purification function of increase are led to
The granule strength of hole haydite.
12 are adopted in the quincunx dispensing of pyroclastic rock lightweight through hole semi-finished product with air purification function
Alkyl sodium sulfate, is conducive to produce substantial amounts of foam in stirring mixed process, quincunx has purify air work(to increase
The micropore within pyroclastic rock lightweight through hole haydite of energy.
Precipitated calcium carbonate, gesso, cenosphere and expanded perlite can reduce and quincunx have air purification function
Pyroclastic rock lightweight through hole haydite bulk density, increase the quincunx pyroclastic rock lightweight with air purification function
Porosity within through hole haydite.
Suck the quincunx pyroclastic rock with air purification function of washable pyroclastic rock photocatalytic spray liquid
Lightweight through hole semi-finished product, is the quincunx pyroclastic rock lightweight through hole pottery with air purification function after drying
Grain, under the irradiation of light, the quincunx pyroclastic rock lightweight through hole haydite with air purification function can be continual
The pollutant such as absorption and degradation of formaldehyde, ammonia, benzene and TVOC, and there is extremely strong sterilization, deodorization, mould proof, anti-fouling and self-cleaning and purification
The function of air.
The pyroclastic rock lightweight through hole haydite blank material that quincunx after extruder grain has air purification function is aqueous
Rate is more than 30%, is delivered directly to swinging roaster high temperature roasting, in high-temperature calcination process, the surface of haydite blank material
First start sintering curing, and the water vapour of inside is difficult to rapid evaporation out, haydite blank material will produce explosion, nor
Can grill thoroughly inside haydite blank material.
The quincunx pyroclastic rock lightweight through hole haydite blank material with air purification function is first transported to by the present invention
Slowly carry out prebake, drying temperature controls at 150～250 DEG C in swinging drying oven, then quincunx having after drying
The pyroclastic rock lightweight through hole haydite blank material of air purification function is transported to swinging roasting kiln roasting, the temperature of combustor
Degree controls at 900～950 DEG C it can be ensured that will be light for the quincunx pyroclastic rock with air purification function in roasting process
Matter through hole haydite blank material is grilled thoroughly, and will not produce explosion.
Quincunx after roasting has in the pyroclastic rock lightweight through hole haydite blank material of air purification function in temperature
Still up to more than 700 DEG C, by the quincunx pyroclastic rock lightweight through hole haydite hair with air purification function after roasting
Blank input is incubated in rustless steel cylinder storehouse, it is possible to use the waste heat of itself, continues there is air purification function to quincunx
Pyroclastic rock lightweight through hole haydite blank material uniformly heats, and not only can ensure that the quincunx volcano with air purification function
Grill thoroughly moreover it is possible to play the effect of uniformly dispersing heat completely inside clastic rock lightweight through hole haydite blank material, quincunx to improve
There is the inherent quality of the pyroclastic rock lightweight through hole haydite blank material of air purification function.
The quincunx pyroclastic rock lightweight through hole haydite blank material surface with air purification function and inside have in a large number
Micropore, be a kind of open pore, open pore not only each other insertion also communicate with the external world, the quincunx fire with air purification function
The macropore at mountain clastic rock lightweight through hole haydite blank material center is a kind of through hole, is conducive in roasting process, can be by haydite
Inside is grilled thoroughly completely, and can increase effective ratio area, intensity and the reduction bulk density of haydite.
The quincunx pyroclastic rock lightweight through hole haydite with air purification function has that specific surface area is big, bulk density
The spy that low, hydroscopicity is high, absorption property is superior, appearance and modeling free from extraneous odour attractive in appearance, lightweight intensity are good, micropore and macropore are integrated
Point, the quincunx pyroclastic rock lightweight through hole haydite with air purification function does not have dust in the dry state, can inhale
The pollutant such as the substantial amounts of formaldehyde of attached in the air, ammonia, benzene and TVOC, are immersed in all the year round in water and also will not produce disintegrate.
Suck the quincunx pyroclastic rock with air purification function of washable pyroclastic rock photocatalytic spray liquid
Lightweight through hole haydite, is to be degraded on the basis of absorption, improves the quincunx volcano with air purification function comprehensively
The absorption of clastic rock lightweight through hole haydite and the ability of purify air.
The quincunx pyroclastic rock lightweight through hole haydite with air purification function uses through long, adsorbs one
After quantitative pollutant, pyroclastic rock photocatalyst degradation capability begins to decline, and can present saturation, using 90～100
DEG C hot water, the quincunx pyroclastic rock lightweight through hole haydite with air purification function that will already be at saturation enters
Row backwash, the volcano that cleaning sticks to inside and outside the quincunx pyroclastic rock lightweight through hole haydite with air purification function is broken
Bits rock photo-catalyst film or microgranule, after cleaning up, will the new washable pyroclastic rock photocatalytic spray liquid prepared, spraying or
It is dipped into inside and outside the quincunx pyroclastic rock lightweight through hole haydite with air purification function, and dried or dry, can
To continue to play the effect of the quincunx pyroclastic rock lightweight through hole haydite purify air with air purification function.
The microgranule waste residue washing down can be used for planting bracketplant, Aloe, Folium Sansevieriae Trifasclatae, pocket Cortex cocois radiciss, Caulis Hederae Sinensiies and Epipremnum aureum (Linde et Andre) (Bunting.)
In green plantss, the interior thing that stays not decomposed of microgranule waste residue slowly will be adsorbed by green plantss such as bracketplant, Aloe, Folium Sansevieriae Trifasclataes
Decompose, new pollution will not be produced.
The quincunx pyroclastic rock lightweight through hole haydite with air purification function be applied to placement indoors, furniture cupboard
Cabinet, vehicle, aircraft, ship, subway, tunnel, highway baffle, military installations, ornament materials, public place or other are built
Build in thing, carry out absorption and the pollutant such as degradation of formaldehyde, ammonia, benzene, TVOC, to reach the purpose of long-time purify air.
Brief description
Fig. 1 is the quincunx pyroclastic rock lightweight through hole haydite schematic diagram with air purification function, and Fig. 2 is quincunx
There is the pyroclastic rock lightweight through hole haydite A-A profile of air purification function.
As shown in the figure：1 is the quincunx pyroclastic rock lightweight through hole haydite with air purification function, and 2 is quincunx
There is the through hole of the pyroclastic rock lightweight through hole haydite of air purification function.
Specific embodiment
With reference to embodiment, the invention will be further described：
1st, the dispensing of the quincunx pyroclastic rock lightweight through hole haydite with air purification function is by weight percentage by following
Group is grouped into：The quincunx pyroclastic rock lightweight through hole semi-finished product 84% with air purification function and washable volcano
Clastic rock photocatalytic spray liquid 16%.
2nd, the production method of the quincunx pyroclastic rock lightweight through hole haydite with air purification function：(1) first will be erasable
Wash pyroclastic rock photocatalytic spray liquid to put in fermentation vat, the more quincunx pyroclastic rock lightweight with air purification function
Through hole semi-finished product is slowly added in the washable pyroclastic rock photocatalytic spray liquid in fermentation vat, and quincunx have purification
Micropore inside and outside the pyroclastic rock lightweight through hole semi-finished product of air function, constantly sucks washable pyroclastic rock light
Catalyzed spraying liquid, until in saturation；(2) take out from fermentation vat and be filled washable pyroclastic rock photocatalytic spray liquid
The quincunx pyroclastic rock lightweight through hole haydite with air purification function, is transported in low temperature rotary drying oven and is dried
Dry, drying temperature controls at 160～180 DEG C, and drying time controlled at 2 hours；(3) quincunx after oven drying at low temperature is had net
The pyroclastic rock lightweight through hole haydite changing air function is transported in flat vibrating screen and is sieved, weed out broken granule and
Powder, packs the finished product for the quincunx pyroclastic rock lightweight through hole haydite with air purification function.
3rd, the dispensing by weight hundred of the quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function
Ratio is divided to be made up of following component：There is the attapulgite potter's clay powder 38% of air purification function, pyroclastic rock 10%, active hargil
Waste residue 4%, white carbon 3%, precipitated calcium carbonate 3%, light magnesium oxide 3%, activated alumina 2%, sodium aluminate 2%, hollow micro-
Pearl 2%, gesso 2%, expanded perlite 1%, sodium lauryl sulphate 2% and water 28%.
4th, the production method of quincunx pyroclastic rock lightweight through hole haydite 1 semi-finished product with air purification function：⑴
By stirring that the dispensing input of quincunx pyroclastic rock lightweight through hole haydite 1 semi-finished product with air purification function has operated
Mix in mixer, stirring is mixed into the mixture of the quincunx pyroclastic rock lightweight through hole haydite 1 with air purification function；
(2) the mixture of the quincunx pyroclastic rock lightweight through hole haydite 1 with air purification function is transported to Squeezinggranulator
In, extruder grain is quincunx pyroclastic rock lightweight through hole haydite 1 blank material with air purification function, and quincunx have
The macropore at the pyroclastic rock lightweight through hole haydite 1 blank material center of air purification function is through hole 2；(3) have quincunx only
Pyroclastic rock lightweight through hole haydite 1 blank material of change air function is transported in swinging drying oven is dried, and dries temperature
Degree controls at 220～240 DEG C, and drying time controlled at 2 hours；(4) by the quincunx fire with air purification function after drying
Mountain clastic rock lightweight through hole haydite 1 blank material is transported to swinging roasting kiln roasting, the temperature control of combustor 900～
920 DEG C, roasting time controlled at 1 hour；(5) by the quincunx pyroclastic rock lightweight with air purification function after roasting
Through hole haydite 1 blank material, input is incubated in rustless steel cylinder storehouse, and temperature retention time controlled at 48 hours；(6) by after insulation cooling
Quincunx pyroclastic rock lightweight through hole haydite 1 blank material with air purification function is transported in roller vibrating screen is sieved
Point, weeding out broken granule and powder is the quincunx pyroclastic rock lightweight through hole haydite 1 half with air purification function
Finished product.
Claims (3)
1. a kind of quincunx pyroclastic rock lightweight through hole haydite with air purification function is it is characterised in that quincunx tool
It is made up of following component by weight percentage the dispensing of the pyroclastic rock lightweight through hole haydite of air purification function：Quincunx
There is the pyroclastic rock lightweight through hole semi-finished product 55～95% of air purification function and washable pyroclastic rock light touches
Matchmaker's spray coating liquor 5～45%；
The dispensing percentage by weight of the described quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function
Form than by following component：There is the attapulgite potter's clay powder 10～45% of air purification function, pyroclastic rock 5～25%, live
Property hargil waste residue 2～10%, white carbon 1～8%, precipitated calcium carbonate 1～5%, light magnesium oxide 1～5%, activated alumina 1
～5%, sodium aluminate 0.5～5%, cenosphere 0.5～5%, gesso 0.5～5%, expanded perlite 0.5～5%, ten
Sodium dialkyl sulfate 0.5～5% and water 10～40%；
The production method of the quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function：(1) will be quincunx
There is the stirring mixer that the dispensing input of the pyroclastic rock lightweight through hole semi-finished product of air purification function has operated
In, stirring is mixed into the mixture of the quincunx pyroclastic rock lightweight through hole haydite with air purification function；(2) by Flos Mume
The mixture that shape has the pyroclastic rock lightweight through hole haydite of air purification function is transported in Squeezinggranulator, extruder grain
For the quincunx pyroclastic rock lightweight through hole haydite blank material with air purification function, quincunx have air purification function
Pyroclastic rock lightweight through hole haydite blank material center macropore be through hole；(3) by the quincunx fire with air purification function
Mountain clastic rock lightweight through hole haydite blank material is transported in swinging drying oven is dried, and drying temperature controls 200～250
DEG C, drying time controlled at 1～4 hour；(4) by the quincunx pyroclastic rock lightweight with air purification function after drying
Through hole haydite blank material is transported to swinging roasting kiln roasting, the temperature control of combustor at 900～950 DEG C, roasting time
Control at 1～3 hour；(5) by the quincunx pyroclastic rock lightweight through hole haydite blank with air purification function after roasting
Material, input is incubated in rustless steel cylinder storehouse, and temperature retention time controlled at 24～72 hours；(6) by quincunx having after insulation cooling
The pyroclastic rock lightweight through hole haydite blank material of air purification function is transported in roller vibrating screen is sieved, and weeds out broken
Granule and powder be the quincunx pyroclastic rock lightweight through hole semi-finished product with air purification function；
The dispensing of described washable pyroclastic rock photocatalytic spray liquid is made up of following component by weight percentage：Tephre
Rock 5～12%, attapulgite clay after the acidify 4～10%, high viscous Concave-convex clay rod 2～8%, nano titanium oxide 1～
5%th, white carbon 1～5%, nano silver-supported antibacterial powder 0.5～5%, nano magnesia 0.5～5%, nano zirconium dioxide 0～
5%th, nano aluminium oxide 0～5%, nano zine oxide 0～5%, polyvinyl alcohol 0.5～5%, Polyethylene Glycol 0.1～3%, poly- two
Methylsiloxane 0.1～2% and deionized water 50～82%；
The production method of washable pyroclastic rock photocatalytic spray liquid：(1) by washable pyroclastic rock photocatalytic spray liquid
Carry out strong stirring, dispersion and emulsifying in the high speed dispersor that dispensing input has operated, then grind in input three-roll grinder
Grind the semi-finished product for washable pyroclastic rock photocatalytic spray liquid；(2) by the half of washable pyroclastic rock photocatalytic spray liquid
In finished product input colloid mill, carry out again disperseing, emulsifying, pulverizing, homogenizing, froth breaking and grinding；(3) the washable volcano after grinding
Granularity≤0.01 millimeter of solid particle in clastic rock photocatalytic spray liquid, canned for washable pyroclastic rock photocatalytic spray
Liquid.
2. the quincunx pyroclastic rock lightweight through hole haydite with air purification function according to claim 1, it is special
Levy and be, there is fineness of the particles≤0.074 millimeter of the attapulgite potter's clay powder of air purification function, the granule of pyroclastic rock is thin
≤ 0.074 millimeter of degree, fineness of the particles≤0.149 millimeter of active white clay waste slag, fineness of the particles≤0.074 milli of precipitated calcium carbonate
Rice, fineness of the particles≤0.074 millimeter of light magnesium oxide, fineness of the particles≤0.074 millimeter of activated alumina, sodium aluminate
Grain fineness≤0.074 millimeter, fineness of the particles≤0.149 millimeter of cenosphere, fineness of the particles≤0.074 milli of gesso
Rice, fineness of the particles≤0.074 millimeter of expanded perlite.
3. the quincunx pyroclastic rock lightweight through hole haydite with air purification function according to claim 1, it is special
Levy and be, the production method of the quincunx pyroclastic rock lightweight through hole haydite with air purification function：(1) first will be washable
Pyroclastic rock photocatalytic spray liquid is put in fermentation vat, then by the quincunx pyroclastic rock lightweight with air purification function
Through hole semi-finished product is slowly added in the washable pyroclastic rock photocatalytic spray liquid in fermentation vat, and quincunx have purification
Micropore inside and outside the pyroclastic rock lightweight through hole semi-finished product of air function, constantly sucks washable pyroclastic rock light
Catalyzed spraying liquid, until in saturation；(2) take out from fermentation vat and be filled washable pyroclastic rock photocatalytic spray liquid
The quincunx pyroclastic rock lightweight through hole haydite with air purification function, is transported in low temperature rotary drying oven and is dried
Dry, drying temperature controls at 150～180 DEG C, and drying time controlled at 1～3 hour；(3) quincunx after oven drying at low temperature is had
The pyroclastic rock lightweight through hole haydite of air purification function is transported in flat vibrating screen and is sieved, and weeds out broken granule
And powder, pack the finished product for the quincunx pyroclastic rock lightweight through hole haydite with air purification function.