CN106422645A

CN106422645A - Formaldehyde removing material

Info

Publication number: CN106422645A
Application number: CN201610907316.8A
Authority: CN
Inventors: 林映霞
Original assignee: Individual
Current assignee: Individual
Priority date: 2016-10-19
Filing date: 2016-10-19
Publication date: 2017-02-22

Abstract

The invention relates to the field of chemical materials, and particularly relates to a formaldehyde removing material. The formaldehyde removing material is prepared from the following components in parts by weight: 3 to 5 parts of tea leaf extract, 2 to 4 parts of chitin, 7 to 9 parts of calcium chloride, 2 to 3.5 parts of iron sesquioxide, 9 to 11 parts of starch adhesive, 1 to 2 parts of potassium hypermanganate, 0.5 to 0.8 part of sodium hydroxide, 2 to 4 parts of sodium chloride, 22 to 25 parts of attapulgite clay, 6 to 8 parts of bentonite, 8 to 12 parts of diatomite, 10 to 13 parts of activated carbon, 8 to 11 parts of titanium pigment, 8 to 9 parts of folium artemisiae argyi extract, 5 to 6 parts of shaddock peel extract, 9 to 10 parts of orange peel extract, 2 to 3 parts of herba portulacae extract, 6 to 8 parts of fructus gleditsiae extract, 11 to 14 parts of hydroxymethyl cellulose, 6 to 9 parts of alkaline earth metal chloride and 45 to 50 parts of water. The formaldehyde removing material is low in cost, is healthy and environment-friendly, can be also used for effectively eliminating formaldehyde in daily life, removing dampness, sterilizing and getting rid of a peculiar smell, can be used for purifying air, further will not form secondary pollution, is high in formaldehyde removal rate, long in acting time, further, is nontoxic, and has no any side effects on a human body.

Description

A kind of formaldehyde drives away material

Technical field

The present invention relates to chemical field, more particularly, to a kind of formaldehyde expeling material.

Background technology

Formaldehyde is a kind of important Organic Ingredients, be mainly used in plastics industry phenolic resin such as processed, urea-formaldehyde plastics electricity beautiful, Synthetic fibers are as synthesized vinylon polyvinyl formal, leather industry, medicine, dyestuff etc..Use formaldehyde printing and dyeing assistant at present Relatively more is textile textile, because textile textile is easily wrinkling, can improve the stiffening of cotton using the auxiliary agent containing formaldehyde Degree.Textile containing formaldehyde, during people's dress and using, can gradually disengage free formaldehyde, by human respiratory tract And skin contact causes respiratory inflammation and scytitis, also eyes can be produced stimulates.Formaldehyde can cause allergy, also can induce Cancer.Producer is reduces cost using dyeing assistant containing formaldehyde, particularly some factories, using high honest and clean of content of formaldehyde Valency auxiliary agent, extremely harmful to human body.Preservative is done with formaldehyde, financial cost is too high, and smell is to operator in liquid detergent Member has stimulation, poisonous.It is different that the impact to health for the formaldehyde includes allotriosmia, stimulation, allergy, abnormal pulmonary function, liver function Often, immunologic dysfunction, nervous centralis impacted, also can inhereditary material in damaging cells, be suspect carcinogen.Wherein quick Sense is sense of smell and stimulation, and therefore its main harm shows as the stimulation to mucous membrane.Formaldehyde is easy to absorb through respiratory tract, but Little through skin absorption.Formaldehyde through nasal inhalation 93% is trapped in nasal cavity tissue, and high concentration occurs that respiratory tract is serious when sucking Stimulation and oedema, resistance of respiratory tract are increased, respiratory rate declines, Eye irritation, headache.Formaldehyde can be with NH in protein₂Base junction Symphysis becomes formylated albumen, initially stimulates eye mucous membrane at low concentrations, stimulates the upper respiratory tract, cause cough, chest when concentration is slightly higher Vexed, forehead feels there is special constriction simultaneously, and intense stimulus mucous membrane simultaneously makes it fester, and then cause inflammation in lung.Suck Cause after formaldehyde anorexia, apocleisis, lose weight, weak, insomnia；If often in contact with possible generation sensitization phenomenon. And skin histology can be caused to fester.Formaldehyde Central nervous also have anesthetic effect.

Content of the invention

It is an object of the invention to provide a kind of formaldehyde drives away material, solve the problems, such as prior art.

In order to realize above-mentioned purpose, adopt the following technical scheme that：A kind of formaldehyde drives away material, including following components and Weight portion：Tea extraction thing 3-5, chitin 2-4, calcium chloride 7-9, di-iron trioxide 2-3.5, starch adhesive 9-11, Gao Meng Sour potassium 1-2, NaOH 0.5-0.8, sodium chloride 2-4, attapulgite 22-25, bentonite 6-8, diatomite 8-12, live Property charcoal 10-13, titanium dioxide 8-11, tarragon extract 8-9, pomelo peel extract 5-6, orange peel extract 9-10, purslane extract Thing 2-3, Chinese honey locust extract 6-8, hydroxymethyl cellulose 11-14, alkaline earth metal chloride 6-9, water 45-50.

Further, including following components and weight portion：Tea extraction thing 4, chitin 3, calcium chloride 8, di-iron trioxide 3, starch adhesive 10, potassium permanganate 1.5, NaOH 0.7, sodium chloride 3.5, attapulgite 24, bentonite 7, diatom Soil 11, activated carbon 12, titanium dioxide 9, tarragon extract 8.5, pomelo peel extract 5.5, orange peel extract 9.5, purslane extracts Thing 2.5, Chinese honey locust extract 7, hydroxymethyl cellulose 13, alkaline earth metal chloride 8, water 47.

Further, the particle diameter of described calcium chloride and described di-iron trioxide is 250-320nm.

Further, described attapulgite and described diatomite are 80-100 mesh.

Compared with prior art, low cost of the present invention, health environment-friendly moreover it is possible to effectively eliminate the formaldehyde in daily life, Dehumidifying, sterilized, remove peculiar smell, can purify air and will not form that secondary pollution, formaldehyde removal efficiency be high, long action time, and no Poison, does not have any side effect to human body.

Specific embodiment

The invention will be further described below.

Embodiment 1

A kind of formaldehyde drives away material, including following components and weight portion：Tea extraction thing 3, chitin 2, calcium chloride 7, three oxidations Two iron 2, starch adhesive 9, potassium permanganate 1, NaOH 0.5, sodium chloride 2, attapulgite 22, bentonite 6, diatom Soil 8, activated carbon 10, titanium dioxide 8, tarragon extract 8, pomelo peel extract 5, orange peel extract 9, purslane extract 2, soap Angle extract 6, hydroxymethyl cellulose 11, alkaline earth metal chloride 6, water 45.

The particle diameter of wherein calcium chloride and di-iron trioxide is 250nm.Attapulgite and diatomite are 80 mesh.

Embodiment 2

A kind of formaldehyde drives away material, including following components and weight portion：Tea extraction thing 5, chitin 4, calcium chloride 9, three oxidations Two iron 3.5, starch adhesive 11, potassium permanganate 2, NaOH 0.8, sodium chloride 4, attapulgite 25, bentonite 8, silicon Diatomaceous earth 12, activated carbon 13, titanium dioxide 11, tarragon extract 9, pomelo peel extract 6, orange peel extract 10, purslane extract 3, Chinese honey locust extract 8, hydroxymethyl cellulose 14, alkaline earth metal chloride 9, water 50.Wherein calcium chloride and di-iron trioxide Particle diameter is 320nm.Attapulgite and diatomite are 100 mesh.

Embodiment 3

A kind of formaldehyde drives away material, including following components and weight portion：Tea extraction thing 4, chitin 3, calcium chloride 8, three oxidations Two iron 3, starch adhesive 10, potassium permanganate 1.5, NaOH 0.7, sodium chloride 3.5, attapulgite 24, bentonite 7, Diatomite 11, activated carbon 12, titanium dioxide 9, tarragon extract 8.5, pomelo peel extract 5.5, orange peel extract 9.5, purslane Extract 2.5, Chinese honey locust extract 7, hydroxymethyl cellulose 13, alkaline earth metal chloride 8, water 47.Wherein calcium chloride and three oxygen The particle diameter changing two iron is 280nm.Attapulgite and diatomite are 90 mesh.

The above is only the preferred embodiment of the present invention.It should be understood that for member of ordinary skill in the art, at this Invent under provided technology enlightenment, other equivalent modifications or improvement can also be made it should also be considered as the protection model of the present invention Enclose.

Claims

1. a kind of formaldehyde drives away material it is characterised in that including following components and weight portion：Tea extraction thing 3-5, chitin 2- 4, calcium chloride 7-9, di-iron trioxide 2-3.5, starch adhesive 9-11, potassium permanganate 1-2, NaOH 0.5-0.8, chlorine Change sodium 2-4, attapulgite 22-25, bentonite 6-8, diatomite 8-12, activated carbon 10-13, titanium dioxide 8-11, tarragon extracts Take thing 8-9, pomelo peel extract 5-6, orange peel extract 9-10, purslane extract 2-3, Chinese honey locust extract 6-8, methylol is fine Dimension plain 11-14, alkaline earth metal chloride 6-9, water 45-50.

2. formaldehyde according to claim 1 drives away material it is characterised in that including following components and weight portion：Tealeaves extracts Take thing 4, chitin 3, calcium chloride 8, di-iron trioxide 3, starch adhesive 10, potassium permanganate 1.5, NaOH 0.7, chlorine Change sodium 3.5, attapulgite 24, bentonite 7, diatomite 11, activated carbon 12, titanium dioxide 9, tarragon extract 8.5, pomelo peel Extract 5.5, orange peel extract 9.5, purslane extract 2.5, Chinese honey locust extract 7, hydroxymethyl cellulose 13, alkaline-earth metal chlorine Compound 8, water 47.

3. formaldehyde according to claim 1 and 2 drives away material it is characterised in that described calcium chloride and described three aoxidizes two The particle diameter of iron is 250-320nm.

4. formaldehyde according to claim 1 and 2 drives away material it is characterised in that described attapulgite and described diatomite For 80-100 mesh.