CN106394047A - Water transfer printing process - Google Patents
Water transfer printing process Download PDFInfo
- Publication number
- CN106394047A CN106394047A CN201610735713.1A CN201610735713A CN106394047A CN 106394047 A CN106394047 A CN 106394047A CN 201610735713 A CN201610735713 A CN 201610735713A CN 106394047 A CN106394047 A CN 106394047A
- Authority
- CN
- China
- Prior art keywords
- picture
- layer
- text layer
- water
- water transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a water transfer printing process. The water transfer printing process includes the following steps that S1, an image-text layer is printed, and specifically, UV ink without a photocuring agent is printed on a water transfer printing film to form the image-text layer; S2, the image-text layer is activated, and specifically, the water transfer printing film is flatly laid on the water surface of a transfer printing water channel, and an activating agent and a photocuring agent are evenly sprayed to the surface of the image-text layer; S3, water transfer printing is conducted, and specifically, a product needing water transfer printing is made to get close to the water transfer printing film gradually, and the image-text layer is slowly transferred to the surface of the product; S4, washing is conducted, and specifically, residual films on the product are removed and a floating layer on the surface is washed away with clear water; S5, drying is carried out, and specifically, ultraviolet rays irradiate on the product to dry the product in a curing mode; S6, paint is sprayed; and S7, drying is conducted. By means of the water transfer printing process provided by the invention, the UV ink can be transfer-printed to the product, various image-text patterns can be printed on the product, the environment is protected, and the image-text layer is not prone to falling.
Description
Technical field
The present invention relates to a kind of water transfer printing technique, belong to printing technology.
Background technology
With the increasingly raising of people's living standard, also increasingly stronger to beautiful pursuit, in some plastic cement or glass etc.
Carve on product or the phenomenon of printing and dyeing decorative pattern picture and text also gets more and more, in prior art, also have and realize moulding by hand spray
Printing and dyeing decorative pattern on glue product, but the decorative pattern so spraying out, less exquisite and uneven, and also it is impaired easily to come off.
Content of the invention
Based on deficiency above, the technical problem to be solved in the present invention is to provide a kind of water transfer printing technique, and it can be by various figures
Literary composition is transferred on product, can print out varied, riotous with colour exquisite picture and text on product, and difficult for drop-off, quality
Well, production efficiency is high.
In order to solve above technical problem, present invention employs technical scheme below：A kind of water transfer printing technique, its feature exists
In comprising the following steps：
S1：Picture and text layer prints, including：A, on the surface of the side of PET film (" on the surface of side " herein be by
PET film regards a plate product as, and thickness direction is ignored, but one of the upper surface of plate product or lower surface surface
On) setting one picture and text layer；B, on the picture and text layer of a side surface of PET film arrange one layer of PVA film layer；C, described PET film of tearing,
Obtain water transfer film；
S2：Picture and text layer activates, and water transfer film is laid on the transfer tank water surface, picture and text layer upward, by activator and
Light curing agent even application, in picture and text layer surface, makes picture and text layer activate；
S3：Water transfers, and the water temperature in water transfer printing pool is risen to 28 DEG C -32 DEG C it would be desirable to the product of water transfer is along its profile
Gradually press close to water transfer film, picture and text layer slowly transfers to product surface in the presence of hydraulic pressure；
S4：Washing, product is taken out from tank, removes the thin film remaining, then is washed away with clear water and anchor at product surface
Floating layer；
S5：It is dried, removes the moisture of product surface, and product is carried out solidifying drying according to ultraviolet；
S6：Spray painting, sprays UV gloss oil in picture and text layer surface；
S7：It is dried, the product after spray painting is dried according to ultraviolet.
Picture and text layer of the present invention is the ink layer of printing or the metal level of plating.
The first kind of way that the present invention realizes above-mentioned steps b is：By casting technology (the tape casting or flow casting molding technology)
One layer of PVA film is arranged on the picture and text layer on the surface of the side of PET film, specifically：First add micro helping by after PVA water dissolution
Agent, PVA solution is cast on the picture and text layer of PET film, described picture and text layer is transferred on PVA after cooling.
The second way that the present invention realizes above-mentioned steps b is：The picture and text layer on the surface of the side of PET film arranges one
Layer PVA film, specifically：First will after PVA water dissolution add trace assistant, through film head extrusion equably levelling in described PET
Picture and text layer on；Described picture and text layer is transferred on PVA after cooling.
Above two of the present invention is realized containing glycerol in the auxiliary agent described in the mode of step b；Described auxiliary agent composition includes：
Glycerol 1-10 part, Polyethylene Glycol 0.6-3 part, tributyl phosphate 0.2-2 part, modified starch 1.5-2 part, tween 0.3-0.5 part；Help
The effect of agent is to adjust the viscosity of PVA solution, and the addition of auxiliary agent is so that the viscosity of PVA solution reaches 10000-
20000cps is standard；Viscosity controls the thickness of thin film, and viscosity is too high to cause overweight coating, otherwise too thin；Glycerin components
Make PVA molecular chain rupture, allow PVA to mix homogeneously with other components, good film-forming property；The thickness of described PVA film is 5.5-6.5 μ
m.
Above two of the present invention is realized in the mode of step b, before cooling, is required to dry PVA, drying temperature 85
DEG C, time 20min；Cooling described in step b is and is cooled down drying the temperature producing.
In above-mentioned steps a of the present invention, by silk screen printing or intaglio printing figure message on a pet film.
In above-mentioned steps a of the present invention, it is printing one picture and text layer or plating one in the picture and text layer of a side surface setting of PET film
The picture and text layer of metal, before the picture and text layer of printing one picture and text layer or plating one metal, is first coated with a side surface of PET film
One layer of release layer, described picture and text layer is on release layer.
In above-mentioned steps a of the present invention, before printing or electroplating picture and text layer, on a side surface of PET film, first it is deposited with one
Metal level, then prints or plating picture and text layer on described metal level.
In above-mentioned steps a of the present invention, printing used ink is UV ink or PU ink.
Release layer of the present invention is a kind of resin, such as in modified epoxy, phenolic resin, alkyd resin etc.
Kind, release layer coating layer thickness is 5.5-6.5 μm.
The pH value of the water in step S2 of the present invention is between 6.5-7.5.
Activator in step S2 of the present invention is organic mixed solvent；It is specially each group packet of following weight ratio
Become：DBA (dibutyl adipate): BAC (n-butyl acetate): anti-plain boiled water (ethylene glycol monobutyl ether): HDDA (cyclohexanediacetic):
Light curing agent (commercial inks special curing agent)=50: 10: 15: 20: 5；The activator of the present invention is mixed solvent, mainly with
The solvent mixing of different boiling, evaporation rate is different, adds resin and light curing agent, it primarily serves the purpose of again by the print of solid-state
Brush ink is dissolved into liquid, and controls the degree of oil slick's pervasion, if diffusion is excessively serious, figure disintegrate, solution is low reduces.
The step that the stretching of picture and text layer is extended also is included in step S3 of the present invention.
In step S4 of the present invention, the speed of washing is 0.5m/min-1m/min, and temperature is 25 DEG C -37 DEG C.
Using above technical scheme, the present invention achieves following technique effect：
(1) water transfer printing technique that the present invention provides, UV ink or metal picture and text layer can be transferred on product for it, can produce
Various materials, riotous with colour exquisite picture and text are printed out on product, and difficult for drop-off；
(2) water temperature during water transfer controls at 28 DEG C -32 DEG C, prevents under the too low dissolubility that can make base film of water temperature
Fall, water temperature over-high easily causes damage to picture and text again, causes picture and text to deform；
(3) speed washed be 0.5m/min-1m/min, temperature be 25 DEG C -37 DEG C, prevent hydraulic pressure excessive and temperature not
Fit and picture and text are caused damage.
(4) spray painting process is carried out to the product after water transfer using UV gloss oil, more environmentally-friendly.
(5) manufacture method of water transfer printing film of the present invention, is used as intermediate medium by PET, so that patterned layer is transferred in
On PVA film.Directly need not be printed on PVA film, be reduced the difficulty of printing process and electroplating process, improve and produce speed
Degree, and the water transfer printing film produced is good, this is because：PVA is a kind of extraordinary material of hydrophilic, is characterized in hydrophilic
Not oleophylic, for example, typically will coat PVA inside the carton of dress food, the oil immersion inside decoction so can be avoided to have moistened paper
Box, when this is also why sometimes to clean cutlery box with water, can feel to wash more greasy and more greasy, that is because will be water miscible
PVA has washed out；Just because of PVA easily absorbs water very much, and thin film very flexible is easily stretchable, if directly printed on PVA, entirely
Environment must control in 25 DEG C of relative humidity 50～55, temperature, and thin film tension force on the printer is most difficult to control, and tension force is too little
Thin film slack and undisciplined cannot registering, overtension thin film is stretched at once, and the thin film of a km has printed and stretching may become 1,200
Rice, leads to the resolution of pattern also can be greatly affected；Therefore, current PVA film print speed printing speed only has 20～40m/min the soonest,
Relative production capacity is very low；And different by the water sucting degree of often a roll of PVA film, the printing ink concentration that it can absorb also can
Affected by relative, even using the oil film of same concentrations, the film of different volumes prints color and has drop；And review
PET or OPP film, water absorption only about 2%, and material do not have any elasticity, just can solve the institute of printing on direct PVA
Some shortcomings, whether printing speed on or color repeatability all considerably beyond the performance of PVA；It is additionally useful for electroplating
Thin film can not contain too many moisture content, and to can be tightened up fixation, the metal being otherwise deposited with cannot uniformly fall from the teeth outwards,
There is vapor also can affect the effect electroplated simultaneously；Therefore the present invention cleverly by pattern printing on a pet film, is then transferred to
On PVA, greatly improve speed of production, and the water transfer printing film produced is good.
Brief description
Fig. 1 is a kind of flow chart of water transfer printing technique of the present invention.
Specific embodiment
Embodiment 1
S1：Picture and text layer prints, including：A, a picture and text layer is arranged on the surface of the side of PET film；B, the one of PET film
One layer of PVA film is arranged on the picture and text layer on the surface of side；C, described PET film of tearing；
Further, in step a, before printing figure message layer on the surface of the side of PET film, in the side of PET film
One layer of release layer, about 6 μm of release layer coating layer thickness are first coated with surface, release composition of layer is phenolic resin, described picture and text layer sets
On release layer, described picture and text layer is the ink layer of printing or the metal level of plating, the printing of ink layer adopt silk screen printing or
Intaglio, printing used ink is UV ink；It is also possible to printing or electroplating picture and text layer in another specific embodiment
Before, first a metal level is deposited with the surface of the side of PET film, then prints on described metal level or plating picture and text layer；
Further, in step b, by one layer of PVA is arranged on the picture and text layer on the surface of the side in PET film for the casting technology
Film, specifically：First trace assistant (auxiliary component will be added after PVA water dissolution：5 parts of glycerol, 1 part of Polyethylene Glycol, tricresyl phosphate fourth
1 part of ester, 2 parts of modified starch, Tween 80) 0.4 part；The effect of auxiliary agent is to adjust the viscosity of PVA solution, the addition of auxiliary agent with
Make PVA solution viscosity reach 15000cps about be standard；Viscosity controls the thickness of thin film, and viscosity is too high to be caused to apply
Layer is blocked up, otherwise too thin；Glycerin components make PVA molecular chain rupture, allow PVA to mix homogeneously with other components, good film-forming property), will
PVA solution is cast on the picture and text layer of PET film, PVA is dried, described picture and text layer is transferred on PVA after cooling；In another tool
In body embodiment it is also possible to first will after PVA water dissolution add trace assistant, through film head extrusion equably levelling described
On the picture and text layer of PET, PVA is dried, described picture and text layer is transferred on PVA after cooling, and described trace assistant contains glycerol；
S2：Picture and text layer activates, and water transfer film is laid on the transfer tank water surface, picture and text layer upward, by activator and
Light curing agent even application, in picture and text layer surface, makes picture and text layer activate；Keep the water cleaning in tank, pH value is 6.5, activator
It is a kind of organic mixed solvent based on aromatic hydrocarbon, such as resin, can dissolve rapidly and destroy water transfer film, but will not damage
Bad picture and text layer, makes picture and text be in free state it is easy to separate with carrier thin film；
S3：Water transfers, and the water temperature in water transfer printing pool is risen to 28 DEG C it would be desirable to the product of water transfer gradually pastes along its profile
Nearly water transfer film, picture and text layer can slowly transfer to product surface in the presence of hydraulic pressure；Stick intrinsic with priming paint of ink layer
Effect can produce adhesive force, in transfer process, the neat and tidy of stock to be kept and working environment, stock and water coating film
Laminating speed to keep uniform, it is to avoid thin film gauffer and make picture and text unsightly, preferably suitable for picture and text stretching is extended, as far as possible
Avoid overlap, especially in conjunction with place, the product that transfer goes out can be made more aesthetically pleasing, quality is higher；Water temperature is also impact transfer matter
The important parameter of amount, water temperature is too low, may make the decreased solubility of base film, and water temperature over-high easily causes to picture and text to damage again
Evil, causes picture and text to deform, and transfer tank can adopt automatic temperature control apparatus, and water temperature is controlled in stable scope；
S4：Washing, product is taken out from tank, removes the thin film remaining, then is washed away with clear water and anchor at product surface
Floating layer；The speed about 0.5m/min of washing, temperature is 25 DEG C；
S5：It is dried, removes the moisture of product surface, and product is carried out solidifying drying according to ultraviolet；
S6：Spray painting, sprays UV gloss oil in picture and text layer surface, to strengthen the repellence to environment for the picture and text layer, UV gloss oil is more suitable
Answer environmental requirement,
S7：It is dried, the product after spray painting is carried out solidifying drying according to ultraviolet.
Embodiment 2
S1：Picture and text layer prints, including：A, a picture and text layer is arranged on the surface of the side of PET film；B, the one of PET film
One layer of PVA film is arranged on the picture and text layer on the surface of side；C, described PET film of tearing；
In step a, by silk screen printing or intaglio printing figure message layer on a pet film, on the surface of the side of PET film
Before upper printing figure message layer, one layer of release layer is first coated with the surface of the side of PET film, described release layer be alkyd resin,
Thickness is 6 μm, and on release layer, described picture and text layer is the ink layer of printing or the metal level of plating to described picture and text layer, printing
The ink being used is UV ink；In another specific embodiment it is also possible to before printing or electroplating picture and text layer, first in PET
One metal level is deposited with the surface of the side of film, then prints on described metal level or plating picture and text layer；
In step b, by one layer of PVA film is arranged on the picture and text layer on the surface of the side in PET film for the casting technology, specifically
Ground：First trace assistant will be added after PVA water dissolution, PVA solution is cast on the picture and text layer of PET film, PVA is dried, warp
After cooling, described picture and text layer is transferred on PVA；It is also possible to first micro- by adding after PVA water dissolution in another specific embodiment
Amount auxiliary agent, through film head extrusion, equably levelling, on the picture and text layer of described PET, PVA is dried, after cooling described picture and text layer
Transfer on PVA, described auxiliary component is 8 parts of glycerol, 2 parts of Polyethylene Glycol, 1.5 parts of tributyl phosphate, 2 parts of modified starch, tells
80 0.5 parts of temperature；The effect of auxiliary agent is to adjust the viscosity of PVA solution, and the addition of auxiliary agent is so that the viscosity of PVA solution reaches
It is standard to 18000cps；Viscosity controls the thickness of thin film, and viscosity is too high to cause overweight coating, otherwise too thin；Glycerol becomes
Dividing makes PVA molecular chain rupture, allows PVA to mix homogeneously with other components, good film-forming property；The thickness of described PVA film is 6 μm；
S2：Picture and text layer activates, and water transfer film is laid on the transfer tank water surface, picture and text layer upward, by activator and
Light curing agent even application, in picture and text layer surface, makes picture and text layer activate；Keep the water cleaning in tank, pH value is 6.5, activator
It is a kind of organic mixed solvent based on aromatic hydrocarbon, such as resin, can dissolve rapidly and destroy water transfer film, but will not damage
Bad picture and text layer, makes picture and text be in free state it is easy to separate with carrier thin film；
S3：Water transfers, and the water temperature in water transfer printing pool is risen to 30 DEG C it would be desirable to the product of water transfer gradually pastes along its profile
Nearly water transfer film, picture and text layer can slowly transfer to product surface in the presence of hydraulic pressure；Stick intrinsic with priming paint of ink layer
Effect can produce adhesive force, in transfer process, the neat and tidy of stock to be kept and working environment, stock and water coating film
Laminating speed to keep uniform, it is to avoid thin film gauffer and make picture and text unsightly, preferably suitable for picture and text stretching is extended, as far as possible
Avoid overlap, especially in conjunction with place, the product that transfer goes out can be made more aesthetically pleasing, quality is higher；Water temperature is also impact transfer matter
The important parameter of amount, water temperature is too low, may make the decreased solubility of base film, and water temperature over-high easily causes to picture and text to damage again
Evil, causes picture and text to deform, and transfer tank can adopt automatic temperature control apparatus, and water temperature is controlled in stable scope；
S4：Washing, product is taken out from tank, removes the thin film remaining, then is washed away with clear water and anchor at product surface
Floating layer；The speed about 0.8m/min of washing, temperature is 30 DEG C；
S5：It is dried, removes the moisture of product surface, and product is carried out solidifying drying according to ultraviolet；
S6：Spray painting, sprays UV gloss oil in picture and text layer surface, to strengthen the repellence to environment for the picture and text layer, UV gloss oil is more suitable
Answer environmental requirement,
S7：It is dried, the product after spray painting is carried out solidifying drying according to ultraviolet.
Embodiment 3
S1：Picture and text layer prints, including：A, a picture and text layer is arranged on the surface of the side of PET film；B, the one of PET film
One layer of PVA film is arranged on the picture and text layer on the surface of side；C, described PET film of tearing；
In step a, by silk screen printing or intaglio printing figure message layer on a pet film, on the surface of the side of PET film
Before upper printing figure message layer, one layer of release layer is first coated with the surface of the side of PET film, described release layer is a kind of resin,
On release layer, described picture and text layer is the ink layer of printing or the metal level of plating to described picture and text layer, prints used oil
Ink is UV ink；In another specific embodiment it is also possible to before printing or electroplating picture and text layer, first in the side of PET film
One metal level is deposited with surface, then prints on described metal level or plating picture and text layer；
In step b, by one layer of PVA film is arranged on the picture and text layer on the surface of the side in PET film for the casting technology, specifically
Ground：First trace assistant will be added after PVA water dissolution, PVA solution is cast on the picture and text layer of PET film, PVA is dried, warp
After cooling, described picture and text layer is transferred on PVA；It is also possible to first micro- by adding after PVA water dissolution in another specific embodiment
Amount auxiliary agent, through film head extrusion, equably levelling, on the picture and text layer of described PET, PVA is dried, after cooling described picture and text layer
Transfer on PVA, described trace assistant contains glycerol；
S2：Picture and text layer activates, and water transfer film is laid on the transfer tank water surface, picture and text layer upward, by activator and
Light curing agent even application, in picture and text layer surface, makes picture and text layer activate；Keep the water cleaning in tank, pH value is 6.5, activator
It is a kind of organic mixed solvent based on aromatic hydrocarbon, such as resin, can dissolve rapidly and destroy water transfer film, but will not damage
Bad picture and text layer, makes picture and text be in free state it is easy to separate with carrier thin film；
S3：Water transfers, and the water temperature in water transfer printing pool is risen to 32 DEG C it would be desirable to the product of water transfer gradually pastes along its profile
Nearly water transfer film, picture and text layer can slowly transfer to product surface in the presence of hydraulic pressure；Stick intrinsic with priming paint of ink layer
Effect can produce adhesive force, in transfer process, the neat and tidy of stock to be kept and working environment, stock and water coating film
Laminating speed to keep uniform, it is to avoid thin film gauffer and make picture and text unsightly, preferably suitable for picture and text stretching is extended, as far as possible
Avoid overlap, especially in conjunction with place, the product that transfer goes out can be made more aesthetically pleasing, quality is higher；Water temperature is also impact transfer matter
The important parameter of amount, water temperature is too low, may make the decreased solubility of base film, and water temperature over-high easily causes to picture and text to damage again
Evil, causes picture and text to deform, and transfer tank can adopt automatic temperature control apparatus, and water temperature is controlled in stable scope；
S7：Washing, product is taken out from tank, removes the thin film remaining, then is washed away with clear water and anchor at product surface
Floating layer；The speed about 1m/min of washing, temperature is 37 DEG C；
S5：It is dried, removes the moisture of product surface, and product is carried out solidifying drying according to ultraviolet；
S6：Spray painting, sprays UV gloss oil in picture and text layer surface, to strengthen the repellence to environment for the picture and text layer, UV gloss oil is more suitable
Answer environmental requirement,
S7：It is dried, the product after spray painting is carried out solidifying drying according to ultraviolet.
The auxiliary component of the present embodiment, release composition of layer are with embodiment 2.
The embodiment of the present invention preparation product, in 50 no white point, bite, scratch and dim design phenomenon occur,
High yield rate.
The manufacture method of water transfer printing film of the present invention, is used as intermediate medium by PET, makes patterned layer be transferred in PVA
On film.Directly need not be printed on PVA film, be reduced the difficulty of printing process and electroplating process, be improved speed of production, and
And the water transfer printing film produced is good.It is directly in conjunction with graph layer is imprinted on product for water transfer between PVA film and graph layer
Afterwards, PVA film can be washed off by washing completely, and figure layer surface does not just have other coherent substances, makes the printing effect that water transfers good
Good, the quality of product is good.
The water transfer printing technique that UV ink is transferred to plastic parts that the present invention provides, UV ink can be transferred to plastic parts by it
On, varied, riotous with colour exquisite pattern can be printed out on plastic parts, and difficult for drop-off.In addition, it is necessary to explanation
It is that the technique of the present invention is not limited to plastic parts, it can be used for the product of other materials, such as glass-ceramic product, stainless
Product made from steel etc..
Finally it should be noted that：These are only the preferred embodiments of the present invention and oneself, be not limited to the present invention, although
With reference to embodiment, the present invention is described in detail, for a person skilled in the art, it still can be to aforementioned
Technical scheme described in each embodiment is modified, or carries out equivalent to wherein some technical characteristics, but all
Within the spirit and principles in the present invention, any modification, equivalent substitution and improvement made etc., should be included in the protection of the present invention
Within the scope of.
Claims (13)
1. a kind of water transfer printing technique is it is characterised in that comprise the following steps：
S1：Picture and text layer prints, including：A, a picture and text layer is arranged on the surface of the side of PET film；B, in the side of PET film
One layer of PVA film is arranged on the picture and text layer on surface；C, described PET film of tearing；
S2：Picture and text layer activates, and water transfer film is laid on the transfer tank water surface, and picture and text layer upward, will be solid to activator and light
Agent even application, in picture and text layer surface, makes picture and text layer activate；
S3：Water transfer, by the water temperature in water transfer printing pool rise to 28 DEG C -32 DEG C it would be desirable to water transfer product along its profile gradually
Press close to water transfer film, picture and text layer slowly transfers to product surface in the presence of hydraulic pressure；
S4：Washing, product is taken out from tank, remove residual thin film, then washed away with clear water anchor at product surface float
Layer；
S5：It is dried, removes the moisture of product surface, and product is carried out solidifying drying according to ultraviolet；
S6：Spray painting, sprays UV gloss oil in picture and text layer surface；
S7：It is dried, the product after spray painting is dried according to ultraviolet.
2. water transfer printing technique according to claim 1 it is characterised in that：Described picture and text layer is ink layer or the plating of printing
Metal level.
3. water transfer printing technique according to claim 1 is it is characterised in that in step b, by casting technology in PET film
One layer of PVA film is arranged on the picture and text layer on the surface of side, specifically：First trace assistant will be added after PVA water dissolution, by PVA
Solution curtain coating on the picture and text layer of PET film, transfer on PVA after cooling by described picture and text layer.
4. water transfer printing technique according to claim 1 is it is characterised in that in step b, on the surface of the side of PET film
One layer of PVA film is arranged on picture and text layer, specifically：First trace assistant will be added after PVA water dissolution, through film head extrusion equably
Levelling on the picture and text layer of described PET, transfer on PVA after cooling by described picture and text layer.
5. the water transfer printing technique according to claim 3 or 4 is it is characterised in that described trace assistant composition includes：Glycerol 1-
10 parts, Polyethylene Glycol 0.6-3 part, tributyl phosphate 0.2-2 part, modified starch 1.5-2 part, tween 0.3-0.5 part.
6. the water transfer printing technique according to claim 3 or 4 is it is characterised in that in step b, before cooling, PVA is dried.
7. water transfer printing technique according to claim 2 is it is characterised in that in step a, printing used ink is UV oil
Ink or PU ink；In step a, by silk screen printing or intaglio printing figure message on a pet film；In step a, in PET film
Before one picture and text layer or the picture and text layer of plating one metal are printed on the surface of side, the surface of the side of PET film is first coated with
One layer of release layer；Described picture and text layer is on release layer.
8. water transfer printing technique according to claim 7 is it is characterised in that described release layer is modified epoxy, phenolic aldehyde
One of resin, alkyd resin are constituted, and the thickness of release layer is 5.5-6.5 μm.
9. water transfer printing technique according to claim 1 is it is characterised in that in step a, print or plating picture and text layer it
Before, first a metal level is deposited with the surface of the side of PET film, then prints on described metal level or plating picture and text layer.
10. water transfer printing technique according to claim 1 it is characterised in that：The pH value of the water in described step S2 is in 6.5-
7.5 between.
11. water transfer printing techniques according to claim 1 it is characterised in that：Activator in described step S2 is to weigh as follows
The each group of amount ratio is grouped into：DBA: BAC: anti-plain boiled water: HDDA: light curing agent=50: 10: 15: 20: 5.
12. water transfer printing techniques according to claim 1 it is characterised in that：Also include in described step S3 drawing picture and text layer
Stretch the step of exhibition.
13. water transfer printing techniques according to claim 1 it is characterised in that：In described step S4, the speed of washing is 0.5m/
Min-1m/min, temperature is 25 DEG C -37 DEG C.