CN109703226A - A kind of water transfer construction method - Google Patents
A kind of water transfer construction method Download PDFInfo
- Publication number
- CN109703226A CN109703226A CN201910059487.3A CN201910059487A CN109703226A CN 109703226 A CN109703226 A CN 109703226A CN 201910059487 A CN201910059487 A CN 201910059487A CN 109703226 A CN109703226 A CN 109703226A
- Authority
- CN
- China
- Prior art keywords
- film
- vinal
- water
- layer
- text
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water to transfer construction method, it include: PET film, vinal, adhering coating, activator, using following steps: the surface of PET film S1: being carried out intaglio printing picture and text, so that there is picture and text ink layer in PET film surface, the film surface that PET film is then printed with to picture and text ink layer coats vinal by the means of showering, S2: the PET film that showering has vinal is laid on coater steel strip surface, the temperature difference is formed using the difference of cooling steel band and PET film paving temperature, to make vinal liquid moment form film layer, keep vinal Nian Jie with picture and text ink layer；In this method PTE film performance of ink it is good, without ductility, convenient for printing clear picture and text.Showering vinal price is reduced than existing polyvinyl alcohol film printing cost simultaneously, reduces requirement of the manufacturing process to environment.
Description
Technical field
The present invention relates to water to transfer field, transfers construction method more particularly, to a kind of water.
Background technique
Water transfer technique is referred to as more environmentally friendly technology, mainly transfers water using the pressure and activator of water
Peeling layer solution transfer on carrier thin film, basic procedure are as follows: printing, primer spray, the extension of film, activation, the transfer, water of film
It washes, dry, topcoating and drying etc..
But the process that current water transfer technique needs is relatively complicated, higher cost requires more production environment
It is harsh.
Summary of the invention
The present invention is to overcome above situation insufficient, it is desirable to provide a kind of technical solution that can solve the above problem.
A kind of water transfer construction method, comprising: PET film, vinal, adhering coating, activator, use are following
Step:
S1: carrying out intaglio printing picture and text for the surface of PET film, so that picture and text ink layer occurs in PET film surface, then will
The film surface that PET film is printed with picture and text ink layer coats vinal by the means of showering；
S2: the PET film that showering has vinal is laid on coater steel strip surface, utilizes cooling steel band
The temperature difference is formed with the difference of PET film paving temperature, so that vinal liquid moment be made to form film layer, keeps polyvinyl alcohol fine
It ties up Nian Jie with picture and text ink layer；
S3: the PET film as carrier being torn off, the film figure layer of vinal Yu printing image-text ink layer is left,
Then film coating is placed into roller coating equipment, adhering coating is applied in film figure layer by roller coating equipment, is then sent
Enter into drying equipment, carrying out 60-70 DEG C of drying can be at water transfer printing film；
S4: water transfer printing film is printed into tiling up, 25-30 DEG C of thermostatic water bath is put it into and impregnates 1-2 minutes, make
Water transfer printing film vinal is completely dissolved in the water surface, is left picture and text ink layer and floats the water surface, then in water transfer printing film ink
Spraying activator in attachment figure layer surface makes ink adhesive layer sufficiently dissolve activation；
S5: the workpiece for needing to shift picture and text is pushed from the water surface toward underwater, makes figure layer will be between workpiece using the pressure of water
Air discharge, make activate ink adhesive layer it is completely closely sealed with workpiece surface, reach the complete transfer effect of picture and text；
S6: the workpiece transferred is rinsed well with clear water, and surface sprays acrylic acid gloss oil/UV gloss oil protective layer.
As a further solution of the present invention: the ink in the S1 in ink layer is acrylic plastics ink.
As a further solution of the present invention: the ingredient of vinal in the S2 are as follows: polyvinyl alcohol resin 20-
30 parts, 20-30 parts of starch, 30-40 parts of modified polyvinylalcohol, 10-20 parts of water, 0.1-0.5 parts of plasticizer, coupling agent 0.1-0.5
Part, preparation method are as follows: polyvinyl alcohol resin, starch, modified polyvinylalcohol, water, plasticizer, coupling agent are added to mixing
It in device, is mixed evenly, while being heated to 110-130 DEG C and dissolve mixture sufficiently forming mixed liquor, static 2
Hour completely removes bubble inside mixture, so that vinal is formed, it is then logical by 95-100 DEG C of heat preservation again
Road enters coater.
As a further solution of the present invention: adhering coating precentagewise includes following composition in the S3: acrylic acid is soft
Property resin 20%-30%, nitrocotton 2%-5%, silica 1 %-2%, ethyl ester 35%-45%, levelling agent 0.1%-
0.2%, isopropanol 5%-10%, butyl ester 10%-20%.
As a further solution of the present invention: activator precentagewise includes following composition: dimethylbenzene in the S4
20%-30%, butyl ester 5%-10%, toluene 30%-40%, isopropanol 3%-5%, isophorone 20%-30%, ethyl ester
10%-20%.
As a further solution of the present invention: the thin film layer thickness that vinal liquid is formed in the S2 is 30-45
Micron.
Compared with prior art, the beneficial effects of the present invention are: in this method PTE film performance of ink it is good, do not extend
Property, convenient for printing clear picture and text.Showering vinal price is dropped than existing polyvinyl alcohol film printing cost simultaneously
It is low, reduce requirement of the manufacturing process to environment.
Additional aspect and advantage of the invention will be set forth in part in the description, partially will from the following description
Become obvious, or practice through the invention is recognized.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described reality
Applying example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field
Those of ordinary skill's every other embodiment obtained without making creative work, belongs to guarantor of the present invention
The range of shield.
In the embodiment of the present invention, a kind of water transfers construction method, comprising: PET film, vinal, adhering coating,
Activator, using following steps:
S1: carrying out intaglio printing picture and text for the surface of PET film, so that picture and text ink layer occurs in PET film surface, then will
The film surface that PET film is printed with picture and text ink layer coats vinal by the means of showering；
S2: the PET film that showering has vinal is laid on coater steel strip surface, utilizes cooling steel band
The temperature difference is formed with the difference of PET film paving temperature, so that vinal liquid moment be made to form film layer, keeps polyvinyl alcohol fine
It ties up Nian Jie with picture and text ink layer；
S3: the PET film as carrier being torn off, the film figure layer of vinal Yu printing image-text ink layer is left,
Then film coating is placed into roller coating equipment, adhering coating is applied in film figure layer by roller coating equipment, is then sent
Enter into drying equipment, carrying out 60-70 DEG C of drying can be at water transfer printing film；
S4: water transfer printing film is printed into tiling up, 25-30 DEG C of thermostatic water bath is put it into and impregnates 1-2 minutes, make
Water transfer printing film vinal is completely dissolved in the water surface, is left picture and text ink layer and floats the water surface, then in water transfer printing film ink
Spraying activator in attachment figure layer surface makes ink adhesive layer sufficiently dissolve activation；
S5: the workpiece for needing to shift picture and text is pushed from the water surface toward underwater, makes figure layer will be between workpiece using the pressure of water
Air discharge, make activate ink adhesive layer it is completely closely sealed with workpiece surface, reach the complete transfer effect of picture and text；
S6: the workpiece transferred is rinsed well with clear water, and surface sprays acrylic acid gloss oil/UV gloss oil protective layer.
Ink in the S1 in ink layer is acrylic plastics ink.
The ingredient of vinal in the S2 are as follows: 20-30 parts of polyvinyl alcohol resin, 20-30 parts of starch are modified and gather
30-40 parts of vinyl alcohol, 10-20 parts of water, 0.1-0.5 parts of plasticizer, 0.1-0.5 parts of coupling agent, preparation method are as follows: by poly- second
Enol resin, starch, modified polyvinylalcohol, water, plasticizer, coupling agent are added in mixing arrangement, be mixed
It is even, while being heated to 110-130 DEG C and dissolve mixture sufficiently forming mixed liquor, make within static 2 hours bubble inside mixture thorough
Bottom removal, to form vinal, then enters coater by 95-100 DEG C of heat preservation channel again.
Adhering coating precentagewise includes following composition in the S3: acrylic acid flexible resin 20%-30%, nitrocotton
2%-5%, silica 1 %-2%, ethyl ester 35%-45%, levelling agent 0.1%-0.2%, isopropanol 5%-10%, butyl ester
10%-20%.
Activator precentagewise includes following composition in the S4: dimethylbenzene 20%-30%, butyl ester 5%-10%, toluene
30%-40%, isopropanol 3%-5%, isophorone 20%-30%, ethyl ester 10%-20%.
The thin film layer thickness that vinal liquid is formed in the S2 is 30-45 microns.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case where without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, nothing
By from the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by institute
Attached claim rather than above description limit, it is intended that will fall within the meaning and scope of the equivalent elements of the claims
All changes be included within the present invention.
Claims (6)
1. a kind of water transfers construction method characterized by comprising PET film, vinal, adhering coating, activator,
Using following steps:
S1: the surface of PET film is subjected to intaglio printing picture and text, so that picture and text ink layer occurs in PET film surface, then by PET film
The film surface for being printed with picture and text ink layer coats vinal by the means of showering；
S2: being laid on coater steel strip surface for the PET film that showering has vinal, utilizes cooling steel band and PET
The difference that film spreads temperature forms the temperature difference, so that vinal liquid moment be made to form film layer, makes vinal and figure
Literary ink layer bonding；
S3: the PET film as carrier is torn off, leaves the film figure layer of vinal Yu printing image-text ink layer, then
Film coating is placed into roller coating equipment, adhering coating is applied in film figure layer by roller coating equipment, is then sent to
In drying equipment, carrying out 60-70 DEG C of drying can be at water transfer printing film；
S4: water transfer printing film is printed into tiling up, 25-30 DEG C of thermostatic water bath is put it into and impregnates 1-2 minutes, transfer water
Film vinal is completely dissolved in the water surface, is left picture and text ink layer and floats the water surface, then adheres in water transfer printing film ink and scheme
Layer surface spraying activator makes ink adhesive layer sufficiently dissolve activation；
S5: the workpiece for needing to shift picture and text is pushed from the water surface toward underwater, makes figure layer by the sky between workpiece using the pressure of water
Gas discharge keeps activation ink adhesive layer completely closely sealed with workpiece surface, reaches the complete transfer effect of picture and text；
S6: the workpiece transferred is rinsed well with clear water, and surface sprays acrylic acid gloss oil/UV gloss oil protective layer.
2. a kind of water according to claim 1 transfers construction method, which is characterized in that the ink in the S1 in ink layer
For acrylic plastics ink.
3. a kind of water according to claim 1 transfers construction method, which is characterized in that vinal in the S2
Ingredient are as follows: 20-30 parts of polyvinyl alcohol resin, 20-30 parts of starch, 30-40 parts of modified polyvinylalcohol, 10-20 parts of water, plasticizer
0.1-0.5 parts, 0.1-0.5 parts of coupling agent, preparation method are as follows: by polyvinyl alcohol resin, starch, modified polyvinylalcohol, water, increasing
Modeling agent, coupling agent are added in mixing arrangement, are mixed evenly, while being heated to 110-130 DEG C keeps mixture abundant
Dissolution forms mixed liquor, completely removes bubble inside mixture, to form vinal, then again
Enter coater by 95-100 DEG C of heat preservation channel.
4. a kind of water according to claim 1 transfers construction method, which is characterized in that adhering coating presses percentage in the S3
Than including following composition: acrylic acid flexible resin 20%-30%, nitrocotton 2%-5%, silica 1 %-2%, ethyl ester
35%-45%, levelling agent 0.1%-0.2%, isopropanol 5%-10%, butyl ester 10%-20%.
5. a kind of water according to claim 1 transfers construction method, which is characterized in that activator precentagewise in the S4
Including following composition: dimethylbenzene 20%-30%, butyl ester 5%-10%, toluene 30%-40%, isopropanol 3%-5%, different Fo Er
Ketone 20%-30%, ethyl ester 10%-20%.
6. a kind of water according to claim 1 transfers construction method, which is characterized in that vinal liquid in the S2
The thin film layer thickness of formation is 30-45 microns.