CN106390602A - Filtering material used for air/liquid filter, and preparation method thereof - Google Patents
Filtering material used for air/liquid filter, and preparation method thereof Download PDFInfo
- Publication number
- CN106390602A CN106390602A CN201611090395.4A CN201611090395A CN106390602A CN 106390602 A CN106390602 A CN 106390602A CN 201611090395 A CN201611090395 A CN 201611090395A CN 106390602 A CN106390602 A CN 106390602A
- Authority
- CN
- China
- Prior art keywords
- layer
- fiber layer
- glass micro
- air
- filtering material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a filtering material used for an air/liquid filter, and a preparation method thereof. The filtering material used for an air/liquid filter comprises a first glass microfiber layer and an auxiliary fiber layer, and a hot melt adhesive layer is bonded between the first glass microfiber layer and the auxiliary fiber layer, wherein the auxiliary fiber layer is a second glass microfiber layer or a PP fusing spray fiber layer. The first glass microfiber layer is the skeleton structure of the filtering material used for an air/liquid filter, and plays a role in supporting, and the first glass microfiber layer has a filtering effect; and the first glass microfiber layer and the auxiliary fiber layer are bonded, so the air filtering material with high filtering efficiency, low resistance and long service life is obtained, the replacement cycle of the air filtering material is reduced, and the use cost is reduced.
Description
Technical field
The present invention relates to filtering material field., more particularly to a kind of air/liquid filtering material for filter and its system
Preparation Method.
Background technology
With communications and transportation, industrial boom, pollution also produces therewith, and especially to be listed in the world three big for air pollution
One of pollution, harm and impact are very big.Suck low quality air damage healthy, induce various diseases etc., especially recently
The inferior health that haze focus brings receives much concern.Filtering material has become industry, the product of life indispensability.The preparation commonly used at present
Air filting material is used mostly conventional polypropylene (PP) meltblown fibers, but the filter material that PP meltblown fibers are prepared for raw material
Material, filter efficiency is general, and filtration resistance is larger, and service life is shorter, and production cost is higher.
In addition, in real life, the liquid such as water or oil is required for carrying out filtration treatment, but the filtering material commonly used at present
Filter effect is general, and there is presently no a kind of filtering material and can be used in liquid filter, can be used for air filtration again
In device.
Content of the invention
Based on this it is necessary to provide a kind of high efficiency filter, filtration resistance relatively low air/liquid filtering material for filter
And preparation method thereof.
A kind of air/liquid filtering material for filter, including the first glass micro-fiber layer and auxiliary fiber layer, described
It is bonded with hot melt adhesive layer, wherein, described auxiliary fiber layer is the second glass between one glass micro-fiber layer and described auxiliary fiber layer
Glass microfibril layer or PP layer of meltblown fibers.
Wherein in an embodiment, the raw material of described hot melt adhesive layer is vistanex or polyamide.
Wherein in an embodiment, the one side of the not glued described hot melt adhesive layer of described PP layer of meltblown fibers is provided with the 3rd glass
Glass microfibril layer, is bonded with described hot melt adhesive layer between described PP layer of meltblown fibers and described 3rd glass micro-fiber layer.
Wherein in an embodiment, the outer surface of described first glass micro-fiber layer and described 3rd glass micro-fiber layer
It is designed with PET filament nonwoven layer of cloth, between described first glass micro-fiber layer and described PET filament nonwoven layer of cloth, the described 3rd
All it is bonded with described hot melt adhesive layer between glass micro-fiber layer and described PET filament nonwoven layer of cloth.
Wherein in an embodiment, described first glass micro-fiber layer, described second glass micro-fiber layer and described
The thickness of three glass micro-fiber layer is all 0.15~0.25mm, and the thickness of described auxiliary fiber layer is 0.10~0.15mm.
Wherein in an embodiment, described first glass micro-fiber layer, described second glass micro-fiber layer and described
The grammes per square metre of three glass micro-fiber layer is all 30~40g/m2;The grammes per square metre of described PP layer of meltblown fibers is 20~25g/m2.
Wherein in an embodiment, the glue-spread of described hot melt adhesive layer is 1~2g/m2.
A kind of preparation method of air/liquid filtering material for filter, comprises the following steps:
1) on hot melt adhesive machine, the PUR of spraying molten in continuous first glass micro-fiber layer;
2) continuously it is coated with the first glass micro-fiber layer of PUR and continuous auxiliary fiber layer is heated through a pair
Pressure roller heat seal, forms hot melt adhesive layer between described glass micro-fiber layer and described auxiliary fiber layer, by cooling, winds, that is,
Can get air/liquid filtering material for filter;
Wherein, described auxiliary fiber layer is the second glass micro-fiber layer or PP layer of meltblown fibers.
Wherein in an embodiment, the raw material of described hot melt adhesive layer is vistanex or polyamide.
Wherein in an embodiment, described first glass micro-fiber layer, described second glass micro-fiber layer thickness all
For 0.15~0.25mm, the thickness of described PP layer of meltblown fibers is 0.10~0.15mm.
Above-mentioned air/liquid filtering material for filter, due to being filtered for air/liquid using the first glass micro-fiber layer
The skeleton structure of device filtering material, plays a supporting role, and the first glass micro-fiber layer has filter effect;And by the first glass
Glass microfibril layer is bonded with auxiliary fiber layer, can obtain the air/liquid of high efficiency filter, lower resistance and long service life
Filtering material, reduces the replacement cycle of air/liquid filtering material, reduces use cost;Above-mentioned air/liquid filter is used
Filter material material, both can serve as air filting material, can serve as liquid filtration material again.
Brief description
Fig. 1 is the structural representation of the air/liquid filtering material for filter of embodiments of the invention 1;
Fig. 2 is the process chart of the preparation method of air/liquid filtering material for filter of the present invention;
Fig. 3 is the structural representation of the air/liquid filtering material for filter of embodiments of the invention 2;
Fig. 4 is the structural representation of the air/liquid filtering material for filter of embodiments of the invention 3;
Fig. 5 is the structural representation of the air/liquid filtering material for filter of embodiments of the invention 4.
Specific embodiment
For making the present invention become apparent, select preferred embodiment, and coordinate accompanying drawing to be described in detail below.
Refer to Fig. 1 and Fig. 3, a kind of air/liquid filtering material for filter, including the first glass micro-fiber layer 1 He
Auxiliary fiber layer 2, is bonded with hot melt adhesive layer 3 between the first glass micro-fiber layer 1 and auxiliary fiber layer 2, wherein, auxiliary fiber layer
2 is the second glass micro-fiber layer 21 or PP layer of meltblown fibers 22.
Preferably, the raw material of hot melt adhesive layer 3 is vistanex or polyamide.The glue-spread of hot melt adhesive layer 3 be 1~
2g/m2.
Refer to Fig. 4, the one side of the not glued hot melt adhesive layer 3 of PP layer of meltblown fibers 22 is provided with the 3rd glass micro-fiber layer 4, PP
It is bonded with hot melt adhesive layer 3 between layer of meltblown fibers 22 and the 3rd glass micro-fiber layer 4.
Refer to Fig. 5, the outer surface of the first glass micro-fiber layer 1 and the 3rd glass micro-fiber layer 4 is designed with PET long filament no
Spin layer of cloth 5, between the first glass micro-fiber layer 1 and PET filament nonwoven layer of cloth 5, the 3rd glass micro-fiber layer 4 and PET long filament no
Spin and be all bonded with hot melt adhesive layer 3 between layer of cloth 5.
Wherein, the thickness of the first glass micro-fiber layer 1, the second glass micro-fiber layer 21 and the 3rd glass micro-fiber layer 4 is all
For 0.15~0.25mm, the thickness of PP layer of meltblown fibers 22 is 0.10~0.15mm, and the thickness of PET filament nonwoven layer of cloth 5 is
0.10~0.15mm.
The grammes per square metre of the first glass micro-fiber layer 1, the second glass micro-fiber layer 21 and the 3rd glass micro-fiber layer 4 is all 30~
40g/m2;The grammes per square metre of PP layer of meltblown fibers 22 is 20~25g/m2, the grammes per square metre of PET filament nonwoven layer of cloth 5 is 20~25g/m2.
Above-mentioned air/liquid filtering material for filter, due to being filtered for air/liquid using the first glass micro-fiber layer
The skeleton structure of device filtering material, plays a supporting role, and the first glass micro-fiber layer has filter effect;And by the first glass
Glass microfibril layer is bonded with auxiliary fiber layer, can obtain the air/liquid of high efficiency filter, lower resistance and long service life
Filtering material, reduces the replacement cycle of air/liquid filtering material, reduces use cost;Above-mentioned air/liquid filter is used
Filter material material, both can serve as air filting material, can serve as liquid filtration material again.
Refer to Fig. 2, a kind of preparation method of air/liquid filtering material for filter, comprise the following steps:
1) on hot melt adhesive machine, the PUR of spraying molten in continuous first glass micro-fiber layer 1;
2) continuously it is coated with the first glass micro-fiber layer 1 of PUR and continuous auxiliary fiber layer 2 is added through a pair
Hot-pressing roller heat seal, forms hot melt adhesive layer 3 between glass micro-fiber layer 1 and auxiliary fiber layer 2, by cooling, winds, you can
To air/liquid filtering material for filter;
Wherein, auxiliary fiber layer 2 is the second glass micro-fiber layer 21 or PP layer of meltblown fibers 22.
The preparation method of above-mentioned air/liquid filtering material for filter, due to using in the first glass micro-fiber layer and
Spraying hot-melt adhesive layer between auxiliary fiber layer, and Heating roll heat seal, make the first glass micro-fiber layer and auxiliary fiber layer gluing
Uniformly, sound construction, stable.
With reference to specific embodiment, the air/liquid filtering material for filter of the present invention is further elaborated.
Embodiment 1
Refer to Fig. 1~2, a kind of preparation method of air/liquid filtering material for filter, comprise the following steps:
1) on hot melt adhesive machine, the PUR of spraying molten in continuous first glass micro-fiber layer 1;
2) continuously it is coated with the first glass micro-fiber layer 1 of PUR and continuous second glass micro-fiber layer 21 warp
A pair of Heating roll heat seal, forms hot melt adhesive layer 3 between the first glass micro-fiber layer 1 and the second glass micro-fiber layer 21, after
Cooled, winding, you can obtain first glass micro-fiber layer the-the second glass micro-fiber layer air/liquid filter filter material
Material.
Wherein, the first glass micro-fiber layer, the thickness of the second glass micro-fiber layer are respectively 0.15,0.20mm, the first glass
Glass microfibril layer, the grammes per square metre of the second glass micro-fiber layer are respectively 30,35g/m2.
The raw material of hot melt adhesive layer 3 is vistanex, and glue-spread is 2g/m2.
The air/liquid filtering material for filter of the present embodiment, thickness is 0.35mm, with Technical Sourcing Internation of the U.S. 8130 type
Automatically filtrate tester is tested, and test result is as follows:Filter efficiency reaches 99.8%, and filtration resistance is 38Pa, very
Spend for 780mg.
Embodiment 2
Refer to Fig. 2~3, a kind of preparation method of air/liquid filtering material for filter, comprise the following steps:
1) on hot melt adhesive machine, the PUR of spraying molten in continuous first glass micro-fiber layer 1;
2) continuously it is coated with the first glass micro-fiber layer 1 of PUR and continuous PP layer of meltblown fibers 22 through a pair
Heating roll heat seal, forms hot melt adhesive layer 3 between the first glass micro-fiber layer 1 and PP layer of meltblown fibers 22, by cooling, receives
Volume, you can obtain the air/liquid filtering material for filter of the first glass micro-fiber layer-PP layer of meltblown fibers.
Wherein, the thickness of the first glass micro-fiber layer is 0.15mm, and the grammes per square metre of the first glass micro-fiber layer is 30g/m2.PP
The thickness of layer of meltblown fibers is 0.15mm.The grammes per square metre of PP layer of meltblown fibers is 25g/m2.
The raw material of hot melt adhesive layer 3 is vistanex, and glue-spread is 1g/m2.
The air/liquid filtering material for filter of the present embodiment, thickness is 0.3mm, with Technical Sourcing Internation of the U.S. 8130 type certainly
Dynamic filtrate tester is tested, and test result is as follows:Filter efficiency reaches 99.7%, and filtration resistance is 35Pa, deflection
For 750mg.
Embodiment 3
Refer to Fig. 2 and Fig. 4, a kind of preparation method of air/liquid filtering material for filter, comprise the following steps:
1) on hot melt adhesive machine, the PUR of spraying molten in continuous first glass micro-fiber layer 1;
2) continuously it is coated with the first glass micro-fiber layer 1 of PUR and continuous PP layer of meltblown fibers 22 through a pair
Heating roll heat seal, forms hot melt adhesive layer 3 between the first glass micro-fiber layer 1 and PP layer of meltblown fibers 22, by cooling, receives
Volume, obtains first compound semi-finished product the first glass layer-hot melt adhesive layer-PP layer of meltblown fibers;
3) using and step 2) identical method passes through the PUR of melting by step 2) the first compound semi-finished product of obtaining
Firmly engage with the 3rd glass micro-fiber layer 4, and make PP layer of meltblown fibers 22, by cooling, wind, you can obtain the first glass
The air/liquid filter filter material of fibrage-hot melt adhesive layer-PP layer of meltblown fibers-hot melt adhesive layer-the second glass layer
Material.
Wherein, the first glass micro-fiber layer, the thickness of the 3rd glass micro-fiber layer are respectively 0.15,0.20mm, the first glass
Glass microfibril layer, the grammes per square metre of the 3rd glass micro-fiber layer are respectively 30,35g/m2.The thickness of PP layer of meltblown fibers is 0.10mm.
The grammes per square metre of PP layer of meltblown fibers is 20g/m2.
The raw material of hot melt adhesive layer 3 is polyamide, and glue-spread is 1.5g/m2.
The air/liquid filtering material for filter of the present embodiment, thickness is 0.41mm, with Technical Sourcing Internation of the U.S. 8130 type
Automatically filtrate tester is tested, and test result is as follows:Filter efficiency reaches 99.9%, and filtration resistance is 50Pa, very
Spend for 800mg.
Embodiment 4
Refer to Fig. 2 and Fig. 5, a kind of preparation method of air/liquid filtering material for filter, comprise the following steps:
1) on hot melt adhesive machine, the PUR of spraying molten in continuous first glass micro-fiber layer 1;
2) continuously it is coated with the first glass micro-fiber layer 1 of PUR and continuous PET filament nonwoven layer of cloth 5 through one
To Heating roll heat seal, form hot melt adhesive layer 3 between the first glass micro-fiber layer 1 and PET filament nonwoven layer of cloth 5, by cold
But, wind, obtain second compound semi-finished product PET filament nonwoven layer of cloth-hot melt adhesive layer-the first glass micro-fiber layer;
3) using and step 2) identical method passes through the PUR of melting by step 2) the second compound semi-finished product of obtaining
Firmly engage with PP layer of meltblown fibers 22, by cooling, wind, obtain the 3rd compound semi-finished product PET filament nonwoven layer of cloth-
Hot melt adhesive layer the-the first glass micro-fiber layer-hot melt adhesive layer-PP layer of meltblown fibers;
4) using and step 2) identical method passes through the PUR of melting by step 3) the 3rd compound semi-finished product that obtain
Firmly engage with the 3rd glass micro-fiber layer, by cooling, wind, obtain the 4th compound semi-finished product PET continuous yarn non-woven fabrics
Layer-hot melt adhesive layer the-the first glass micro-fiber layer-hot melt adhesive layer-PP layer of meltblown fibers-hot melt adhesive layer-the three glass micro-fiber layer;
5) using and step 2) identical method passes through the PUR of melting by step 4) the 4th compound semi-finished product that obtain
Firmly engage with PET filament nonwoven layer of cloth, by cooling, wind, you can obtain ET filament nonwoven layer of cloth-hot melt adhesive layer-the first
Glass micro-fiber layer-hot melt adhesive layer-PP layer of meltblown fibers-hot melt adhesive layer-the three glass micro-fiber layer-hot melt adhesive layer-PET long filament
The air/liquid filtering material for filter of nonwoven layer.
The raw material of hot melt adhesive layer 3 is polyamide, and glue-spread is 2g/m2.
Wherein, the first glass micro-fiber layer, the thickness of the 3rd glass micro-fiber layer are all 0.20mm, the first glass microfiber
Layer, the grammes per square metre of the 3rd glass micro-fiber layer are respectively 30,35g/m2.The thickness of PP layer of meltblown fibers is 0.10mm.The melt-blown fibre of PP
The grammes per square metre of dimension layer is 20g/m2.The thickness of PET filament nonwoven layer of cloth is 0.10mm, and grammes per square metre is 20g/m2.
The air/liquid filtering material for filter of the present embodiment, thickness is 0.72mm, with Technical Sourcing Internation of the U.S. 8130 type
Automatically filtrate tester is tested, and test result is as follows:Filter efficiency reaches 99.99%, and filtration resistance is 60Pa, very
Spend for 860mg.
Embodiment described above only have expressed the several embodiments of the present invention, and its description is more concrete and detailed, but simultaneously
Therefore the restriction to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for those of ordinary skill in the art
For, without departing from the inventive concept of the premise, some deformation can also be made and improve, these broadly fall into the guarantor of the present invention
Shield scope.Therefore, the protection domain of patent of the present invention should be defined by claims.
Claims (10)
1. a kind of air/liquid filtering material for filter is it is characterised in that include the first glass micro-fiber layer and auxiliary fiber
Layer, is bonded with hot melt adhesive layer between described first glass micro-fiber layer and described auxiliary fiber layer, wherein, described auxiliary fiber layer
For the second glass micro-fiber layer or PP layer of meltblown fibers.
2. air/liquid filtering material for filter according to claim 1 is it is characterised in that described hot melt adhesive layer
Raw material is vistanex or polyamide.
3. air/liquid filtering material for filter according to claim 1 is it is characterised in that described PP meltblown fibers
The one side of the not glued described hot melt adhesive layer of layer is provided with the 3rd glass micro-fiber layer, described PP layer of meltblown fibers and described 3rd glass
It is bonded with described hot melt adhesive layer between microfibril layer.
4. air/liquid filtering material for filter according to claim 3 is it is characterised in that described first glass is micro-
The outer surface of fibrage and described 3rd glass micro-fiber layer is designed with PET filament nonwoven layer of cloth, described first glass microfiber
Between layer and described PET filament nonwoven layer of cloth, all viscous between described 3rd glass micro-fiber layer and described PET filament nonwoven layer of cloth
Have described hot melt adhesive layer.
5. the air/liquid filtering material for filter according to claim 1 or 3 is it is characterised in that described first glass
The thickness of microfibril layer, described second glass micro-fiber layer and described 3rd glass micro-fiber layer is all 0.15~0.25mm, institute
The thickness stating auxiliary fiber layer is 0.10~0.15mm.
6. the air/liquid filtering material for filter according to claim 1 or 3 is it is characterised in that described first glass
The grammes per square metre of microfibril layer, described second glass micro-fiber layer and described 3rd glass micro-fiber layer is all 30~40g/m2;Described
The grammes per square metre of PP layer of meltblown fibers is 20~25g/m2.
7. the air/liquid filtering material for filter according to Claims 1 to 4 any one is it is characterised in that described
The glue-spread of hot melt adhesive layer is 1~2g/m2.
8. a kind of preparation method of air/liquid filtering material for filter is it is characterised in that comprise the following steps:
1) on hot melt adhesive machine, the PUR of spraying molten in continuous first glass micro-fiber layer;
2) continuously it is coated with the first glass micro-fiber layer of PUR and continuous auxiliary fiber layer through a pair of Heating roll
Heat seal, forms hot melt adhesive layer between described glass micro-fiber layer and described auxiliary fiber layer, by cooling, winds, you can
To air/liquid filtering material for filter;
Wherein, described auxiliary fiber layer is the second glass micro-fiber layer or PP layer of meltblown fibers.
9. the preparation method of the air/liquid filtering material for filter stated according to Claim 8 is it is characterised in that described heat
The raw material of melt layer is vistanex or polyamide.
10. the preparation method of air/liquid filtering material for filter according to claim 8 is it is characterised in that described
First glass micro-fiber layer, the thickness of described second glass micro-fiber layer are all 0.15~0.25mm, described PP layer of meltblown fibers
Thickness be 0.10~0.15mm.