CN106380875A - 一种耐老化高黏高弹改性沥青及其制法 - Google Patents

一种耐老化高黏高弹改性沥青及其制法 Download PDF

Info

Publication number
CN106380875A
CN106380875A CN201610778966.7A CN201610778966A CN106380875A CN 106380875 A CN106380875 A CN 106380875A CN 201610778966 A CN201610778966 A CN 201610778966A CN 106380875 A CN106380875 A CN 106380875A
Authority
CN
China
Prior art keywords
parts
modified asphalt
rubber
aging
ageing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610778966.7A
Other languages
English (en)
Inventor
崔若宾
孔超
李颖
朱洪志
刘清敬
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong High Speed Material Storage And Transportation Co Ltd
Original Assignee
Shandong High Speed Material Storage And Transportation Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong High Speed Material Storage And Transportation Co Ltd filed Critical Shandong High Speed Material Storage And Transportation Co Ltd
Priority to CN201610778966.7A priority Critical patent/CN106380875A/zh
Publication of CN106380875A publication Critical patent/CN106380875A/zh
Pending legal-status Critical Current

Abstract

一种耐老化高黏高弹改性沥青及其制法，属于沥青技术领域，其特征是，包括如下重量份的原料制成：70#基质沥青100份，热塑性聚氨酯弹性体橡胶3‑5份，复配热塑性丁苯橡胶2‑6份，石油树脂1‑3份，橡胶油1‑5份，稳定剂0.2‑2份，抗老化剂0.5‑2份，抗光老化剂0.2‑1.1份。与现有技术相比，本发明制备的沥青具有高孔隙率，且具有优秀的黏度、弹性、耐热老化性和耐光老化，可广泛应用于海绵道路等透水路面的修建。

Description

一种耐老化高黏高弹改性沥青及其制法
技术领域
本发明涉及一种耐老化高黏高弹改性沥青及其制法，属于沥青技术领域。
背景技术
我国虽然已有多年路建经验，但是由于传统建设路面大多为密集配路面，遇到大雨或者暴雨易发生城市渍涝。为解决此类问题，现在我国正在大力推行海绵城市海面道路。海绵道路是一种像海绵一样能将地面积水迅速吸收的新型路面，采用大空隙沥青混合料作表层，将降雨透入到排水功能层，并通过层内空隙将雨水横向排出，从而消除了带来诸多行车不利作用的路表积水。这类海绵道路透水路面主要就是采用这种高黏高弹改性沥青制备的，具申请人所知，目前国内没有厂家专业生产此类产品。
公开号为CN102433007A的中国专利公开了一种路桥嵌缝沥青，其含有以下质量百分含量的原料制成：基础沥青60-85％，聚合物A 5-15％，聚合物B 0-15％，相容剂3-10％，稳定剂0-3％，其中，聚合物A和聚合物B可以采用橡胶、热塑性弹性体、塑料或合成树脂类等。该专利虽然引入了TPU，但由于该产品为嵌缝沥青，一般要求不透水，因此，其聚合物添加量高，且对沥青的孔隙率没有要求。该专利作为现有技术，其全文在此引用。
发明内容
本发明旨在研制一种新型耐老化的高黏高弹改性沥青，不仅能够满足海绵道路透水路面的使用，而且可以减缓沥青的老化，延长使用寿命，提高了使用的性价比。
本发明具体采用的技术方案是：
一种耐老化高黏高弹改性沥青，其特征是，包括如下重量份的原料制成：
其中，所述复配热塑性丁苯橡胶是星型SBS、线性SBS和SBR按照重量比2：1：1混合而成。
其中，石油树脂为碳五碳九共聚石油树脂，其在市场上很容易获得。
其中，橡胶油为环烷基橡胶油；
其中，稳定剂为硫磺。
其中，抗老化剂为抗氧化剂BHT，抗光老化剂为紫外线吸收剂UV-9
一种耐老化高黏高弹改性沥青的制法，其特征是，包括如下步骤：按照重量份数将基质沥青预热至175-185℃，加入配料罐，持续搅拌状态下加入橡胶油和热塑性聚氨酯弹性体橡胶充分溶胀30分钟，再加入复配的热塑性丁苯橡胶改性剂充分均匀混合，溶胀10分钟，经胶体磨剪切2次，使改性剂颗粒细度达到5μm以下，输送至发育罐加入稳定剂，保持180℃搅拌发育2h，加入石油树脂、抗老化剂和抗光老化剂，继续保温保持180℃搅拌发育2h，制成耐老化高黏高弹改性沥青。
与现有技术相比，本发明的有益效果在于：
1)本发明的沥青具有高孔隙率，且具有优秀的黏度、弹性、耐热老化性和耐光老化，可广泛应用于海绵道路等透水路面的修建。
2)本发明由于加入的热塑性聚氨酯弹性体橡胶(TPU)，具有良好的耐油性、韧性、耐磨性、耐老化性和粘合性，不仅能够够减少丁苯橡胶的使用量，而且还能增加产品的性能。
3)在本发明中增加了抗老化剂和抗光老化剂的使用，抗老化剂能够抑制或者延缓高聚物和其他有机化合物在空气中热氧化，抗光老化剂具有吸收率高、无毒、无致畸作用，对光、热稳定性好等优点，能够有效的增加产品的使用寿命，增加发明产品的性价比。
具体实施方式
一、配方
表1：配方表(重量份)
实施例1 实施例2 实施例3
70#基质沥青 100 100 100
TPU 3 4 5
复配热塑性丁苯橡胶 5 2 6
石油树脂 1 2 3
橡胶油 2 5 1
稳定剂 0.2 1 2
抗老化剂 0.5 1 2
抗光老化剂 1.1 0.5 0.2
配方表中，所有原料均为市售商品，在市场上容易获取。
其中，所述复配热塑性丁苯橡胶是星型SBS、线性SBS和SBR按照重量比2：1：1混合而成。
二、制法，选取实施例1-3中任一配方
先将基质沥青预热至175-185℃，加入配料罐，持续搅拌状态下加入橡胶油和热塑性聚氨酯弹性体橡胶充分溶胀30分钟，再加入复配的热塑性丁苯橡胶改性剂充分均匀混合，溶胀10分钟，经胶体磨剪切2次，使改性剂颗粒细度达到5μm以下，输送至发育罐加入稳定剂，保持180℃搅拌发育2h，加入石油树脂、抗老化剂和抗光老化剂，继续保温保持180℃搅拌发育2h，制成耐老化高黏高弹改性沥青。
三、产品检验，根据GB/T30516-2014对实施例获得的产品进行检验，结果如下：
表2

Claims (4)

1.一种耐老化高黏高弹改性沥青，其特征是，包括如下重量份的原料制成：
2.根据权利要求1所述的耐老化高黏高弹改性沥青，其特征是，所述复配热塑性丁苯橡胶是星型SBS、线性SBS和SBR按照重量比2：1：1混合而成；石油树脂为碳五碳九共聚石油树脂，橡胶油为环烷基橡胶油；稳定剂为硫磺。
3.根据权利要求1所述的耐老化高黏高弹改性沥青，其特征是，抗老化剂为抗氧化剂BHT，抗光老化剂为紫外线吸收剂UV-9。
4.一种耐老化高黏高弹改性沥青的制法，其特征是，包括如下步骤：按照重量份数将基质沥青预热至175-185℃，加入配料罐，持续搅拌状态下加入橡胶油和热塑性聚氨酯弹性体橡胶充分溶胀30分钟，再加入复配的热塑性丁苯橡胶改性剂充分均匀混合，溶胀10分钟，经胶体磨剪切2次，使改性剂颗粒细度达到5μm以下，输送至发育罐加入稳定剂，保持180℃搅拌发育2h，加入石油树脂、抗老化剂和抗光老化剂，继续保温保持180℃搅拌发育2h，制成耐老化高黏高弹改性沥青。
CN201610778966.7A 2016-08-31 2016-08-31 一种耐老化高黏高弹改性沥青及其制法 Pending CN106380875A (zh)