CN106380222A - 一种环保建筑材料 - Google Patents

一种环保建筑材料 Download PDF

Info

Publication number
CN106380222A
CN106380222A CN201610747091.4A CN201610747091A CN106380222A CN 106380222 A CN106380222 A CN 106380222A CN 201610747091 A CN201610747091 A CN 201610747091A CN 106380222 A CN106380222 A CN 106380222A
Authority
CN
China
Prior art keywords
weight portion
weight
environmental
construction material
straw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610747091.4A
Other languages
English (en)
Inventor
梁乔保
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610747091.4A priority Critical patent/CN106380222A/zh
Publication of CN106380222A publication Critical patent/CN106380222A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种环保建筑材料，包括如下组分：污泥废弃物60‑120重量份、秸秆碎30‑50重量份、活性炭50‑80重量份、硅藻土30‑50重量份、碳纤维10‑15重量份、氧化镁1‑2重量份、硬脂酸锌1.5‑4重量份、无机铝盐0.5‑1重量份、碳黑3‑5重量份、过氧化二异丙苯0.2‑0.8重量份。本发明的环保建筑材料使用了污泥废弃物、秸秆碎作为基体材料，实现了废弃物的回收利用、具有环保节能的优点。

Description

一种环保建筑材料
技术领域
本发明涉及建筑新材料领域，具体的，涉及一种环保建筑材料。
背景技术
一般来说，净水场或下水最终处理场、工厂或焚烧厂等产生的污泥及非有机物的所有残留物被分类为废弃物，通过回收过程以指定的方法被废弃。但是，为了回收并废弃如上所述的废污泥，需要具备有大型的回收设施及回收装置，其并非以回收时的状态被掩埋废弃，而是为了得到环境方面上的自然再生作用，在将采取的粘土和废污泥混合的状态下进行掩埋。由此，粘土的消耗量多的同时，基于混合粘土的体积及掩埋量过多增加，在废弃场的指定及设立上存在有较多困难。着工业社会的发达，处于天然材料相当不足的情况，鉴于此，提示出将污泥废弃物与无机物混合加工而成型后，经由干燥、烧制制步骤而制造建材的方法。由此制造出的轻量骨料具有减少所使用的混凝土的比重，同时，由于骨料内部的无数个气孔，还能够同时得到绝热及隔音的效果。但是单一使用此物质做成的建筑材料往往韧度不够，需要添加一些能够使其增加韧度的东西。农作物秸秆是取之不尽的自然资源，农作物秸秆的资源化利用符合可持续发展的社会需求，故而发明人尝试将污泥废弃物与秸秆碎料相结合配合多中添加及制成一种新型的建筑材料。
发明内容
本发明所要解决的技术问题是提供一种节能环保的环保建筑材料。
本发明解决上述技术问题的技术方案如下：一种环保建筑材料，包括如下组分：
污泥废弃物60-120重量份、秸秆碎30-50重量份、活性炭50-80重量份、硅藻土30-50重量份、碳纤维10-15重量份、氧化镁1-2重量份、硬脂酸锌1.5-4重量份、无机铝盐0.5-1重量份、碳黑3-5重量份、过氧化二异丙苯0.2-0.8重量份。
进一步,包括如下组分：
污泥废弃物60重量份、秸秆碎30重量份、活性炭50重量份、硅藻土30重量份、碳纤维10重量份、氧化镁1重量份、硬脂酸锌1.5重量份、无机铝盐0.5重量份、碳黑3重量份、过氧化二异丙苯0.2重量份。
进一步,包括如下组分：
污泥废弃物120重量份、秸秆碎50重量份、活性炭80重量份、硅藻土50重量份、碳纤维15重量份、氧化镁2重量份、硬脂酸锌4重量份、无机铝盐1重量份、碳黑5重量份、过氧化二异丙苯0.8重量份。
进一步,包括如下组分：
污泥废弃物88重量份、秸秆碎43重量份、活性炭62重量份、硅藻土37重量份、碳纤维13重量份、氧化镁1.6重量份、硬脂酸锌1.8重量份、无机铝盐0.7重量份、碳黑4重量份、过氧化二异丙苯0.6重量份。
一种环保建筑材料的制造方法，包括如下步骤：
(a)将污泥废弃物60-120重量份、秸秆碎30-50重量份、活性炭50-80重量份、硅藻土30-50重量份、碳纤维10-15重量份、氧化镁1-2重量份、硬脂酸锌1.5-4重量份、无机铝盐0.5-1重量份、碳黑3-5重量份、过氧化二异丙苯0.2-0.8重量份进行混合得到均匀的混合物；
(b)将所述混合物放入模具中晾晒成型；
(c)将所述成型的建筑材料进行烧制。
进一步，所述步骤(c)的烧制温度为1180-1260℃，烧制时间为5-7小时。
本发明的有益效果是：本发明的环保建筑材料使用了污泥废弃物、秸秆碎作为基体材料，实现了废弃物的回收利用、具有环保节能的优点。
具体实施方式
以下对本发明的原理和特征进行描述，所举实例只用于解释本发明，并非用于限定本发明的范围。
实施例1
一种环保建筑材料，包括如下组分：
污泥废弃物60重量份、秸秆碎30重量份、活性炭50重量份、硅藻土30重量份、碳纤维10重量份、氧化镁1重量份、硬脂酸锌1.5重量份、无机铝盐0.5重量份、碳黑3重量份、过氧化二异丙苯0.2重量份。
一种环保建筑材料的制造方法，包括如下步骤：
(a)将污泥废弃物60重量份、秸秆碎30重量份、活性炭50重量份、硅藻土30重量份、碳纤维10重量份、氧化镁1重量份、硬脂酸锌1.5重量份、无机铝盐0.5重量份、碳黑3重量份、过氧化二异丙苯0.2重量份进行混合得到均匀的混合物；
(b)将所述混合物放入模具中晾晒成型；
(c)将所述成型的建筑材料进行烧制。
所述步骤(c)的烧制温度为1260℃，烧制时间为5小时。
实施例2
一种环保建筑材料，包括如下组分：
污泥废弃物120重量份、秸秆碎50重量份、活性炭80重量份、硅藻土50重量份、碳纤维15重量份、氧化镁2重量份、硬脂酸锌4重量份、无机铝盐1重量份、碳黑5重量份、过氧化二异丙苯0.8重量份。
一种环保建筑材料的制造方法，包括如下步骤：
(a)将污泥废弃物120重量份、秸秆碎50重量份、活性炭80重量份、硅藻土50重量份、碳纤维15重量份、氧化镁2重量份、硬脂酸锌4重量份、无机铝盐1重量份、碳黑5重量份、过氧化二异丙苯0.8重量份进行混合得到均匀的混合物；
(b)将所述混合物放入模具中晾晒成型；
(c)将所述成型的建筑材料进行烧制。
所述步骤(c)的烧制温度为1180℃，烧制时间为7小时。
实施例3
一种环保建筑材料，包括如下组分：
污泥废弃物88重量份、秸秆碎43重量份、活性炭62重量份、硅藻土37重量份、碳纤维13重量份、氧化镁1.6重量份、硬脂酸锌1.8重量份、无机铝盐0.7重量份、碳黑4重量份、过氧化二异丙苯0.6重量份。
一种环保建筑材料的制造方法，包括如下步骤：
(a)将污泥废弃物88重量份、秸秆碎43重量份、活性炭62重量份、硅藻土37重量份、碳纤维13重量份、氧化镁1.6重量份、硬脂酸锌1.8重量份、无机铝盐0.7重量份、碳黑4重量份、过氧化二异丙苯0.6重量份进行混合得到均匀的混合物；
(b)将所述混合物放入模具中晾晒成型；
(c)将所述成型的建筑材料进行烧制。
所述步骤(c)的烧制温度为1220℃，烧制时间为6小时。
对比例1
市售普通建筑材料。
分别将实施例1-3中得到的样品1-3进行性能的测试，其数据见下表：
隔音效果 保温效果 质量比(样品/对比样品)
样品1 良好 良好 0.76
样品2 良好 良好 0.80
样品3 良好 良好 0.77
对比样品1 一般 一般 1
以上所述仅为本发明的较佳实施例，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。

Claims (6)

1.一种环保建筑材料，其特征在于，包括如下组分：
污泥废弃物60-120重量份、秸秆碎30-50重量份、活性炭50-80重量份、硅藻土30-50重量份、碳纤维10-15重量份、氧化镁1-2重量份、硬脂酸锌1.5-4重量份、无机铝盐0.5-1重量份、碳黑3-5重量份、过氧化二异丙苯0.2-0.8重量份。
2.根据权利要求1所述环保建筑材料，其特征在于,包括如下组分：
污泥废弃物60重量份、秸秆碎30重量份、活性炭50重量份、硅藻土30重量份、碳纤维10重量份、氧化镁1重量份、硬脂酸锌1.5重量份、无机铝盐0.5重量份、碳黑3重量份、过氧化二异丙苯0.2重量份。
3.根据权利要求1所述环保建筑材料，其特征在于,包括如下组分：
污泥废弃物120重量份、秸秆碎50重量份、活性炭80重量份、硅藻土50重量份、碳纤维15重量份、氧化镁2重量份、硬脂酸锌4重量份、无机铝盐1重量份、碳黑5重量份、过氧化二异丙苯0.8重量份。
4.根据权利要求1所述环保建筑材料，其特征在于,包括如下组分：
污泥废弃物88重量份、秸秆碎43重量份、活性炭62重量份、硅藻土37重量份、碳纤维13重量份、氧化镁1.6重量份、硬脂酸锌1.8重量份、无机铝盐0.7重量份、碳黑4重量份、过氧化二异丙苯0.6重量份。
5.一种环保建筑材料的制造方法，其特征在于，包括如下步骤：
(a)将污泥废弃物60-120重量份、秸秆碎30-50重量份、活性炭50-80重量份、硅藻土30-50重量份、碳纤维10-15重量份、氧化镁1-2重量份、硬脂酸锌1.5-4重量份、无机铝盐0.5-1重量份、碳黑3-5重量份、过氧化二异丙苯0.2-0.8重量份进行混合得到均匀的混合物；
(b)将所述混合物放入模具中晾晒成型；
(c)将所述成型的建筑材料进行烧制。
6.根据权利要求5所述一种环保建筑材料的制造方法，其特征在于，所述步骤(c)的烧制温度为1180-1260℃，烧制时间为5-7小时。
CN201610747091.4A 2016-08-28 2016-08-28 一种环保建筑材料 Pending CN106380222A (zh)