CN106367966A - 腈棉混纺织物纱线的浆纱工艺 - Google Patents

腈棉混纺织物纱线的浆纱工艺 Download PDF

Info

Publication number
CN106367966A
CN106367966A CN201610779857.7A CN201610779857A CN106367966A CN 106367966 A CN106367966 A CN 106367966A CN 201610779857 A CN201610779857 A CN 201610779857A CN 106367966 A CN106367966 A CN 106367966A
Authority
CN
China
Prior art keywords
weight
parts
weight portion
yarn
blended fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610779857.7A
Other languages
English (en)
Inventor
王红丹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu Xinyu Apparel Products Co Ltd
Original Assignee
Changshu Xinyu Apparel Products Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu Xinyu Apparel Products Co Ltd filed Critical Changshu Xinyu Apparel Products Co Ltd
Priority to CN201610779857.7A priority Critical patent/CN106367966A/zh
Publication of CN106367966A publication Critical patent/CN106367966A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种腈棉混纺织物纱线的浆纱工艺，包括如下步骤：1)将1～2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N‑甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；3)将纱线浸入浆液上浆，压去余液，烘干。本发明上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。

Description

腈棉混纺织物纱线的浆纱工艺
技术领域
本发明涉及腈棉混纺织物纱线的浆纱工艺。
背景技术
棉、粘胶以及合成纤维等织物的经纱，在织造前大都先经过浆纱；而现有浆纱用浆液的性能有待改进。
发明内容
本发明的目的在于提供一种腈棉混纺织物纱线的浆纱工艺，其上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。
为实现上述目的，本发明的技术方案是设计一种腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将1～2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
优选的，腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将1重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
优选的，腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
优选的，腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将1.2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
本发明的优点和有益效果在于：提供一种腈棉混纺织物纱线的浆纱工艺，其上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。
“退浆液”的性能和用途是由其组分及配比所决定的，且“退浆液”中的不同组分会相互影响，组分及其配比会决定“退浆液”的最终性能，如果组分及其配比不相互协调，单个组分所带来的有益效果，会被其他组分消减甚至消除，严重的时候，不同组分相互抵触，起不到整体综合作用，产生负作用和次品。本发明通过大量创造性劳动、反复验证，得到“退浆液”的最优组分及配比，使得多个组分综合在一起、相互协调、并产生正向综合效应。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将1～2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
实施例2
腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将1重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
实施例3
腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
实施例4
腈棉混纺织物纱线的浆纱工艺，包括如下步骤：
1)将1.2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
上述各实施例上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (4)

1.腈棉混纺织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将1～2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
2.根据权利要求1所述的腈棉混纺织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将1重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
3.根据权利要求1所述的腈棉混纺织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
4.根据权利要求1所述的腈棉混纺织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将1.2重量份天丝、2.2重量份丙酮、0.6重量份碳酸钠、1.3重量份N-甲基吡咯烷酮、16重量份玉米改性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入2.2重量份聚氧乙烯失水山梨醇脂肪酸酯、1.6重量份异构醇聚氧乙烯醚、0.8重量份钼酸胺、1.8重量份水杨酸苯酯，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
CN201610779857.7A 2016-08-31 2016-08-31 腈棉混纺织物纱线的浆纱工艺 Pending CN106367966A (zh)