CN106381681A - 珊瑚绒织物纱线的浆纱工艺 - Google Patents
珊瑚绒织物纱线的浆纱工艺 Download PDFInfo
- Publication number
- CN106381681A CN106381681A CN201610782591.1A CN201610782591A CN106381681A CN 106381681 A CN106381681 A CN 106381681A CN 201610782591 A CN201610782591 A CN 201610782591A CN 106381681 A CN106381681 A CN 106381681A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- weight portion
- yarn
- fleece fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种珊瑚绒织物纱线的浆纱工艺，包括如下步骤：1)将1～2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；2)再依次投入0.9重量份α‑烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；3)将纱线浸入浆液上浆，压去余液，烘干。本发明上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。
Description
技术领域
本发明涉及珊瑚绒织物纱线的浆纱工艺。
背景技术
棉、粘胶以及合成纤维等织物的经纱，在织造前大都先经过浆纱；而现有浆纱用浆液的性能有待改进。
发明内容
本发明的目的在于提供一种珊瑚绒织物纱线的浆纱工艺，其上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。
为实现上述目的，本发明的技术方案是设计一种珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将1～2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
优选的，珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将1重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
优选的，珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
优选的，珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将1.2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
本发明的优点和有益效果在于：提供一种珊瑚绒织物纱线的浆纱工艺，其上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。
“退浆液”的性能和用途是由其组分及配比所决定的，且“退浆液”中的不同组分会相互影响，组分及其配比会决定“退浆液”的最终性能，如果组分及其配比不相互协调，单个组分所带来的有益效果，会被其他组分消减甚至消除，严重的时候，不同组分相互抵触，起不到整体综合作用，产生负作用和次品。本发明通过大量创造性劳动、反复验证，得到“退浆液”的最优组分及配比，使得多个组分综合在一起、相互协调、并产生正向综合效应。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将1～2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
实施例2
珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将1重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
实施例3
珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
实施例4
珊瑚绒织物纱线的浆纱工艺，包括如下步骤：
1)将1.2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
上述各实施例上浆后纱线毛羽贴伏、强力显着提高，耐磨好，纱线的保伸性能好。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (4)
1.珊瑚绒织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将1～2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
2.根据权利要求1所述的珊瑚绒织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将1重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
3.根据权利要求1所述的珊瑚绒织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。
4.根据权利要求1所述的珊瑚绒织物纱线的浆纱工艺，其特征在于，包括如下步骤：
1)将1.2重量份氯化钠、1.8重量份聚氨酯树脂、1.9重量份酚醛树脂、0.9重量份泡花碱、18重量份磷酸酯变性淀粉依次投入35重量份去离子水中，搅拌均匀；
2)再依次投入0.9重量份α-烯烃磺酸钠、1.3重量份十二烷基磺酸钠、2.2重量份聚丙烯酸酯、1.2重量份十六烷基一甲基二乙羟基溴化铵，继续搅拌，至充分混合均匀，制得浆液；
3)将纱线浸入浆液上浆，压去余液，烘干。