CN106366686A - Plastic wood material for manufacturing flame retardant door plank and preparation method of plastic wood - Google Patents

Plastic wood material for manufacturing flame retardant door plank and preparation method of plastic wood Download PDF

Info

Publication number
CN106366686A
CN106366686A CN201610981244.1A CN201610981244A CN106366686A CN 106366686 A CN106366686 A CN 106366686A CN 201610981244 A CN201610981244 A CN 201610981244A CN 106366686 A CN106366686 A CN 106366686A
Authority
CN
China
Prior art keywords
plastic
wood material
making
door panel
inflaming retarding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610981244.1A
Other languages
Chinese (zh)
Inventor
戴炬枫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Foshan Juye Technology Co Ltd
Original Assignee
Foshan Juye Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Foshan Juye Technology Co Ltd filed Critical Foshan Juye Technology Co Ltd
Priority to CN201610981244.1A priority Critical patent/CN106366686A/en
Publication of CN106366686A publication Critical patent/CN106366686A/en
Pending legal-status Critical Current

Abstract

The embodiment of the invention discloses a plastic wood material for manufacturing a flame retardant door plank and a preparation method of the plastic wood material. The plastic wood material is prepared from the following components by mass: 20-25 parts of polyvinyl chloride, 30-40 parts of polyethylene, 50-60 parts of wood powder, 1-2 parts of paraffin, 40-45 parts of a filler, 3-4 parts of a flame retardant, 2-3 parts of a stabilizer and 0.5-1.5 parts of a plasticizer. According to the plastic wood material for manufacturing the flame retardant door plate and the preparation method of the plastic wood material, the manufactured door plank is excellent in flame retardancy, better in fire resistant function and low in cost and has better market potential.

Description

A kind of for making plastic-wood material of inflaming retarding door panel and preparation method thereof
Technical field
The present invention relates to Material Field, more particularly, to a kind of plastic-wood material for making inflaming retarding door panel and its preparation side Method.
Background technology
With social development, composite is widely used in industry-by-industry field.Wherein, plastic-wood material is compound One kind of material.Have two kinds of characteristics of texture of plastics and timber due to moulding wood concurrently so that it becomes a kind of function admirable very Durable outdoor building materials;Also replace the Wood member of the uses such as harbour, harbour, it may also be used for substitute timber and make various packagings Thing, pallet, warehouse pallet etc. are too numerous to enumerate, and purposes is extremely wide.Plastic wood sheet, combines Plant fiber and plastics macromolecule material The plurality of advantages of material, can substitute timber in a large number, can effectively alleviate the contradiction that China's Forest Resources are poor, wood supply is in short supply, be A kind of low-carbon (LC) of great development prospect, green, renewable ecology plastic-wood material capable of circulation.
But, with the requirement more and more higher to security performance for the people, the fire protecting performance moulding timber product is also improved Higher requirement, wherein, door-plate as the main body of door, well imagine by its fireproof importance.
Content of the invention
In view of this, the invention provides a kind of for making plastic-wood material of inflaming retarding door panel and preparation method thereof, permissible It is effectively improved the problem of the door-plate flame retardant effect difference that plastic-wood material is made.
A kind of for making plastic-wood material of inflaming retarding door panel and preparation method thereof, this plastic-wood material is included by mass component:
Preferably, described paraffin is 1.5-2 part.
Preferably, described filler is barium sulfate.
Preferably, described barium sulfate is 42-44 part.
Preferably, described stabilizer is organic antimony stabilizer.
Preferably, described organic antimony stabilizer is 2.2-2.8 part.
Preferably, described plasticizer is diethyl phthalate.
Preferably, described diethyl phthalate is 1-1.2 part.
Preferably, described fire retardant is at least one in magnesium hydroxide and aluminium hydroxide.
A kind of preparation method of the plastic-wood material for making inflaming retarding door panel, method includes:
Prepared by premix material: wood powder is added in high mixer, with 1,200 1400 revs/min of high-speed stirred 10 minutes, wood Powder humid control, below 0.5%, is then respectively adding each component of above-mentioned remaining, carries out batch mixing, batch mixing by above-mentioned batch mixing by Batch mixer hot mixing system discharging, to cold mixing system, is cooled to 60 DEG C, obtains premix material;
Prepared by semi-finished product pelletize pellet: by premix material through parallel double-screw extruder extruding pelletization, technological temperature is set in 170 190 DEG C, to be used as semi-finished product pelletize pellet etc.;
Prepared by extrusion molding: the particle after extruding pelletization is added to extrusion molding in conical double-screw, technological temperature sets It is scheduled on 205 210 DEG C, is extruded by door-plate mould, that is, obtain flame-resistant plastic-wood material door-plate.
The present invention a kind of for making plastic-wood material of inflaming retarding door panel and preparation method thereof, the door-plate of making, have excellent Good fire resistance, increased safety while the service life that improve door-plate.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, Obviously, described embodiment is a part of embodiment of the present invention, rather than whole embodiments.Based on the enforcement in the present invention Example, the every other embodiment that those of ordinary skill in the art are obtained under the premise of not making creative work, broadly fall into The scope of protection of the invention.
It should be appreciated that when using in this specification and in the appended claims, term " inclusion " and "comprising" indicate The presence of described feature, entirety, step, operation, element and/or assembly, but it is not precluded from one or more of the other feature, whole Body, step, operation, the presence of element, assembly and/or its set or interpolation.
It will be further appreciated that, used in description of the invention and appended claims, term "and/or" is Refer to any combinations of one or more of the associated item listed and be possible to combine, and include these combinations.
Embodiment 1
By weight, a kind of composition for making the plastic-wood material of inflaming retarding door panel and preparation method thereof of the present embodiment Component is as follows:
Embodiment 2
By weight, a kind of composition for making the plastic-wood material of inflaming retarding door panel and preparation method thereof of the present embodiment Component is as follows:
Embodiment 3
By weight, a kind of composition for making the plastic-wood material of inflaming retarding door panel and preparation method thereof of the present embodiment Component is as follows:
Embodiment 4
By weight, a kind of composition for making the plastic-wood material of inflaming retarding door panel and preparation method thereof of the present embodiment Component is as follows:
Embodiment 5
By weight, a kind of composition for making the plastic-wood material of inflaming retarding door panel and preparation method thereof of the present embodiment Component is as follows:
A kind of preparation method of the plastic-wood material for making inflaming retarding door panel, method includes: 1. premix material preparation: by wood powder Be added in high mixer, with 1,200 1400 revs/min of high-speed stirred 10 minutes, wood powder humid control below 0.5%, then It is separately added into each component of above-mentioned remaining, carries out batch mixing, batch mixing is by above-mentioned batch mixing by batch mixer hot mixing system discharging to cold mixed system System, is cooled to 60 DEG C, obtains premix material;2. semi-finished product pelletize pellet preparation: premix material is extruded through parallel double-screw extruder Pelletize, technological temperature is set in 170 190 DEG C, to be used as semi-finished product pelletize pellet etc.;3. extrusion molding preparation: will squeeze Go out the particle after pelletize and be added to extrusion molding in conical double-screw, technological temperature is set in 205 210 DEG C, by door-plate mould Tool extrusion, that is, obtain flame-resistant plastic-wood material door-plate.
Step in present invention method can carry out order according to actual needs and adjust, merges and delete.
It is more than to provided by the present invention, the invention has the benefit that the door-plate being made using this plastic-wood material, have Have excellent fire resistance, improve door-plate service life while, increased safety.
It is described in detail herein, apply specific case and the principle of the present invention and embodiment are explained State, above example is only intended to help and understands the method for the present invention and its core concept;General skill simultaneously for this area Art personnel, according to the thought of the present invention, all will change in specific embodiments and applications, in sum, this Description should not be construed as limitation of the present invention.
Those skilled in the art can be understood that, for convenience and simplicity of description, the system of foregoing description With the specific work process of unit, may be referred to the corresponding process in preceding method embodiment, will not be described here.

Claims (10)

1. a kind of plastic-wood material for making inflaming retarding door panel is it is characterised in that described plastic-wood material is included by mass component:
2. the as claimed in claim 2 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described paraffin is 1.5-2 Part.
3. the as claimed in claim 1 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described filler is sulphuric acid Barium.
4. the as claimed in claim 4 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described barium sulfate is 42- 44 parts.
5. the as claimed in claim 1 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described stabilizer is organic Antimony stabilizer.
6. the as claimed in claim 6 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described organic antimony stabilizer For 2.2-2.8 part.
7. the as claimed in claim 1 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described plasticizer is adjacent benzene Dicarboxylate.
8. the as claimed in claim 8 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described phthalic acid two Ethyl ester is 1-1.2 part.
9. the as claimed in claim 1 plastic-wood material being used for making inflaming retarding door panel it is characterised in that: described fire retardant is hydrogen-oxygen Change at least one in magnesium and aluminium hydroxide.
10. the preparation method of the described plastic-wood material for making inflaming retarding door panel as arbitrary in claim 1-9, its feature exists In method includes:
Prepared by premix material: wood powder is added in high mixer, with 1,200 1400 revs/min of high-speed stirred 10 minutes, wood powder is wet Degree controls below 0.5%, is then respectively adding each component of above-mentioned remaining, carries out batch mixing, batch mixing is by above-mentioned batch mixing by batch mixing Machine hot mixing system discharging, to cold mixing system, is cooled to 60 DEG C, obtains premix material;
Prepared by semi-finished product pelletize pellet: by premix material through parallel double-screw extruder extruding pelletization, technological temperature is set in 170 190 DEG C, to be used as semi-finished product pelletize pellet etc.;
Prepared by extrusion molding: the particle after extruding pelletization is added to extrusion molding in conical double-screw, technological temperature is set in 205 210 DEG C, extruded by door-plate mould, that is, obtain flame-resistant plastic-wood material door-plate.
CN201610981244.1A 2016-11-08 2016-11-08 Plastic wood material for manufacturing flame retardant door plank and preparation method of plastic wood Pending CN106366686A (en)