CN106366687A - Material for making high-strength door pocket and preparation method of material - Google Patents
Material for making high-strength door pocket and preparation method of material Download PDFInfo
- Publication number
- CN106366687A CN106366687A CN201610981245.6A CN201610981245A CN106366687A CN 106366687 A CN106366687 A CN 106366687A CN 201610981245 A CN201610981245 A CN 201610981245A CN 106366687 A CN106366687 A CN 106366687A
- Authority
- CN
- China
- Prior art keywords
- door pocket
- high intensity
- making
- powder
- intensity door
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a material for making a high-strength door pocket and a preparation method of the material. The material is prepared from, by mass, 60-70 parts of calcium powder, 40-45 parts of wood powder, 30-35 parts of polyvinyl chloride, 10-15 parts of polypropylene, 1-2 parts of aramid fibers, 0.4-0.6 part of a stabilizer, 0.8-1.2 parts of a coloring agent, 0.2-0.4 part of castor oil and 0.6-0.7 part of a flame retardant. According to the material for making the high-strength door pocket and the preparation method of the material, the material can effectively improve the strength property of the domestic door pocket, improves the strength of the door pocket and ensures the quality of the door pocket.
Description
Technical field
The present invention relates to building material field, more particularly, to a kind of material for making high intensity door pocket and its preparation side
Method.
Background technology
Wood plastic composite is a kind of new structure material having very much market potential, one of its primary raw material wood powder or chaff powder
It is a kind of a large amount of farm-forestry crop leftover pieces, and the macromolecule polymeric material being combined therewith typically has the industrial material of extensive use
Material, therefore, the primary raw material of Wood plastic composite is cheap, and cheap for both, abundance material is bonded in
New composite can be produced together.
But, with social development, the requirement more and more higher to material for the people, there is intensity relatively in existing plastic-wood material
Low it is impossible to meet now society high-strength material demand.
Content of the invention
In view of this, the invention provides a kind of material for making high intensity door pocket and preparation method thereof, this material
The strength character of domestic door pocket can be effectively improved, improve the intensity of door pocket, ensure the quality of door pocket.
A kind of material for making high intensity door pocket and preparation method thereof, this material is included by mass component:
Preferably, this material is included by mass component:
Preferably, this material is included by mass component:
Preferably, described coloring agent is fluorescent whitening agent.
Preferably, described stabilizer is solid calcium zinc stabilizer.
Preferably, described fire retardant is APP.
Preferably, described calcium powder is precipitated calcium carbonate.
Preferably, described wood powder cuts bits powder for trees.
Preferably, described trees cutting bits powder is 20-60 mesh.
A kind of preparation method of the material for making high intensity door pocket, the method includes:
Prepared by premix material: wood powder is added in high mixer, with 1,500 1800 revs/min of high-speed stirred 9 minutes, wood powder
Humid control, below 0.5%, is then respectively adding each component of above-mentioned remaining, carries out batch mixing, and batch mixing is by above-mentioned batch mixing by mixing
The hot mixing system discharging of material machine, to cold mixing system, is cooled to 57 DEG C, obtains premix material；
Prepared by semi-finished product pelletize pellet: by premix material through parallel double-screw extruder extruding pelletization, technological temperature is set in
200 210 DEG C, to be used as semi-finished product pelletize pellet etc.；
Prepared by extrusion molding: the particle after extruding pelletization is added to extrusion molding in conical double-screw, technological temperature sets
It is scheduled on 190 200 DEG C, is extruded by door pocket mould, that is, obtain the plastic-wood material door pocket of high intensity.
A kind of material for making high intensity door pocket of the present invention and preparation method thereof, this material can be effectively improved house
With the strength character of door pocket, improve the intensity of door pocket, ensure the quality of door pocket.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is a part of embodiment of the present invention, rather than whole embodiments.Based on the enforcement in the present invention
Example, the every other embodiment that those of ordinary skill in the art are obtained under the premise of not making creative work, broadly fall into
The scope of protection of the invention.
It should be appreciated that when using in this specification and in the appended claims, term " inclusion " and "comprising" indicate
The presence of described feature, entirety, step, operation, element and/or assembly, but it is not precluded from one or more of the other feature, whole
Body, step, operation, the presence of element, assembly and/or its set or interpolation.
It will be further appreciated that, used in description of the invention and appended claims, term "and/or" is
Refer to any combinations of one or more of the associated item listed and be possible to combine, and include these combinations.
Embodiment 1
By weight, being grouped of a kind of material for making high intensity door pocket of the present embodiment and preparation method thereof
Part is as follows:
Embodiment 2
By weight, being grouped of a kind of material for making high intensity door pocket of the present embodiment and preparation method thereof
Part is as follows:
Embodiment 3
By weight, being grouped of a kind of material for making high intensity door pocket of the present embodiment and preparation method thereof
Part is as follows:
Embodiment 4
By weight, being grouped of a kind of material for making high intensity door pocket of the present embodiment and preparation method thereof
Part is as follows:
Embodiment 5
By weight, being grouped of a kind of material for making high intensity door pocket of the present embodiment and preparation method thereof
Part is as follows:
Wherein, wood powder cuts bits for trees, is smashed, and its particle diameter is 20-60 mesh.
A kind of preparation method of the material for making high intensity door pocket, the method includes: 1. premix material preparation: by wood powder
Be added in high mixer, with 1,500 1800 revs/min of high-speed stirred 9 minutes, wood powder humid control below 0.5%, then
It is separately added into each component of above-mentioned remaining, carries out batch mixing, batch mixing is by above-mentioned batch mixing by batch mixer hot mixing system discharging to cold mixed system
System, is cooled to 57 DEG C, obtains premix material；2. semi-finished product pelletize pellet preparation: premix material is extruded through parallel double-screw extruder
Pelletize, technological temperature is set in 200 210 DEG C, to be used as semi-finished product pelletize pellet etc.；3. extrusion molding preparation: will squeeze
Go out the particle after pelletize and be added to extrusion molding in conical double-screw, technological temperature is set in 190 200 DEG C, by door pocket mould
Tool extrusion, that is, obtain the plastic-wood material door pocket of high intensity.
Step in present invention method can carry out order according to actual needs and adjust, merges and delete.
It is more than to provided by the present invention, the invention has the benefit that for the material making high intensity door pocket, being somebody's turn to do
Material can be effectively improved the strength character of domestic door pocket, improves the intensity of door pocket, has ensured the quality of door pocket.
It is described in detail herein, apply specific case and the principle of the present invention and embodiment are explained
State, above example is only intended to help and understands the method for the present invention and its core concept；General skill simultaneously for this area
Art personnel, according to the thought of the present invention, all will change in specific embodiments and applications, in sum, this
Description should not be construed as limitation of the present invention.
Those skilled in the art can be understood that, for convenience and simplicity of description, the system of foregoing description
With the specific work process of unit, may be referred to the corresponding process in preceding method embodiment, will not be described here.
Claims (10)
1. a kind of material for making high intensity door pocket is it is characterised in that described material is included by mass component:
2. be used for as claimed in claim 1 making the material of high intensity door pocket it is characterised in that: described material is by quality group subpackage
Include:
3. be used for as claimed in claim 1 making the material of high intensity door pocket it is characterised in that: described material is by quality group subpackage
Include:
4. be used for as claimed in claim 1 making the material of high intensity door pocket it is characterised in that: described coloring agent is fluorescent brightening
Agent.
5. be used for as claimed in claim 1 making the material of high intensity door pocket it is characterised in that: described stabilizer is solid calcium zinc
Stabilizer.
6. be used for as claimed in claim 1 making the material of high intensity door pocket it is characterised in that: described fire retardant is polyphosphoric acid
Ammonium.
7. be used for as claimed in claim 1 making the material of high intensity door pocket it is characterised in that: described calcium powder is lightweight carbonic acid
Calcium.
8. be used for as claimed in claim 1 making the material of high intensity door pocket it is characterised in that: described wood powder is that trees cutting is considered to be worth doing
Powder.
9. be used for as claimed in claim 9 making the material of high intensity door pocket it is characterised in that: described trees cutting bits powder is
20-60 mesh.
10. it is used for making the preparation method of the material of high intensity door pocket it is characterised in that the method as described in claim 1-9
Including:
Prepared by premix material: wood powder is added in high mixer, with 1,500 1800 revs/min of high-speed stirred 9 minutes, wood powder humidity
Control below 0.5%, be then respectively adding each component of above-mentioned remaining, carry out batch mixing, batch mixing is by above-mentioned batch mixing by batch mixer
Hot mixing system discharging, to cold mixing system, is cooled to 57 DEG C, obtains premix material；
Prepared by semi-finished product pelletize pellet: by premix material through parallel double-screw extruder extruding pelletization, technological temperature is set in 200
210 DEG C, to be used as semi-finished product pelletize pellet etc.；
Prepared by extrusion molding: the particle after extruding pelletization is added to extrusion molding in conical double-screw, technological temperature is set in
190 200 DEG C, extruded by door pocket mould, that is, obtain the plastic-wood material door pocket of high intensity.