CN104277333A - Low-temperature-resistant and flame-retardant modified geogrid and preparation method thereof - Google Patents
Low-temperature-resistant and flame-retardant modified geogrid and preparation method thereof Download PDFInfo
- Publication number
- CN104277333A CN104277333A CN201410575584.5A CN201410575584A CN104277333A CN 104277333 A CN104277333 A CN 104277333A CN 201410575584 A CN201410575584 A CN 201410575584A CN 104277333 A CN104277333 A CN 104277333A
- Authority
- CN
- China
- Prior art keywords
- parts
- geogrid
- carbon black
- temperature
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a low-temperature-resistant and flame-retardant modified geogrid prepared by processing the following raw materials in parts by weight: 40-50 parts of PP, 20-30 parts of EVA, 30-40 parts of MLLDPE, 10-20 parts of POE, 10-15 parts of maleic anhydride grafted PE, 1-2 parts of SEBS, 3-5 parts of decabromodiphenyl ethane, 0.2-0.5 part of 2,6-ditert-butyl-4-methyl phenol, 5-10 parts of calcium carbonate and 5-8 parts of modified carbon black master batches. The preparation method of the low-temperature-resistant and flame-retardant modified geogrid comprises the steps of mixing all the materials in the formula, and extruding to obtain a melt; forming a plate from the melt by using a three-roll calendar; punching the plate by using a punching machine; and stretching after heating the pore plate to obtain the geogrid. The raw materials in the formula are modified, so that the geogrid which is resistant to low temperature, good in flame retardance as well as high in strength and toughness is obtained.
Description
technical field
The present invention relates to the manufacture of geo-grid, be specifically related to a kind of low temperature resistant flame retardant modified geogrid and preparation method.
Background technology
Along with the development of geosynthetics industry, increasing geo-grid product has pushed market to, and the main competition of geo-grid is exactly product performance and Costco Wholesale competition.Because polypropylene geogrid field is extensive with use region, therefore geo-grid is required that it has multiple performance.But only realizing these performances by a kind of polymkeric substance is be difficult to realize, and therefore needs to carry out to geo-grid formula the inexorable trend that modification becomes this industry.Being a kind of general and effective means preparing fiber reinforcement in high performance material, strengthening fiber used and being generally glass fibre, carbon fiber etc.The resin tooth successful obtained by these fiber filled, can make the geo-grid of same size thinner.But after using glass fibre and carbon fiber, the tensile elongation of polymkeric substance has again very large decline, cause geo-grid to stretch very short, product weight per unit area rises, and production cost is increased on the contrary, is unfavorable for the object reaching cost degradation.
In geo-grid, add the fillers such as modified carbon black, acidproof, alkaline-resisting, corrosion-resistant and ageing resistance preferably can be made it have, improve resistance to impact shock and tensile strength.
Summary of the invention
The invention provides a kind of low temperature resistant flame retardant modified geogrid and preparation method.The present invention by the raw-material modification of formula, thus obtain having low temperature resistant, flame retardant properties good, the geo-grid that intensity is high, toughness is large.
Technical scheme that the present invention adopts is as follows:
A kind of low temperature resistant flame retardant modified geogrid, it is characterized in that, obtained by the component Raw material processing of following weight part: PP 40-50, EVA 20-30, MLLDPE 30-40, POE 10-20, maleic anhydride graft PE 10-15, SEBS 1-2, TDE 3-5,2,6-ditertbutylparacresol 0.2-0.5, calcium carbonate 5-10, modified carbon black masterbatch 5-8
The preparation method of described modified carbon black masterbatch: (1) takes polyethylene 30-40, polypropylene 10-20, carbon black 40-50, acrylate 0.2-1.5, zinc oxide 0.1-0.4, irgasfos 168 0.1-0.3, protective agent 0.1-0.3, kerosene 0.5-1.0, flyash 1-3, the pungent decylate 3-5 of Polyglycerine, talcum powder 4-6 by weight; (2) load weighted carbon black, acrylate, zinc oxide are added in stirrer, fully mix at the temperature of 60 DEG C-180 DEG C, obtain mixture A; (3) all the other feed composition such as polyethylene, polypropylene, talcum powder, antioxidant 1010, protective agent, white oil, flyash, the pungent decylate of Polyglycerine are dropped into successively homogenizer high speed and stir 3-5 minute, obtain mixture material B; (4) obtaining blend after being mixed by A and B joins in twin screw extruder, and screw speed is 80-130 rpm, and heating barrel zone temperature 180-200 DEG C melt extrudes, cooling, granulation.
The preparation method of described low temperature resistant flame retardant modified geogrid, is characterized in that, comprise the following steps:
(1) each component raw material is taken by formula rate;
(2) PP taken, MLLDPE, POE, SEBS, maleic anhydride graft PE are added in Banbury mixer, at 140 DEG C of-160 DEG C of melting mixings, obtain mixing materials;
(3) by mixing materials and TDE, 2,6-ditertbutylparacresol, calcium carbonate mix, then send in the loading hopper of tablets press, open tablets press, the rotating speed controlling tablets press is 240-330r/min, control feed cylinder of granulator front portion, middle part, rear portion and head temperature be respectively: 225 ~ 235 DEG C, 220 ~ 225 DEG C, 210 ~ 215 DEG C, 230 ~ 235 DEG C, the material extruded from tablets press through water-cooled, pelletizing, sieve, drying, namely obtain mixing materials A;
(4) after dried mixing materials A being mixed with modified carbon black masterbatch, extruded at lower than 225 DEG C of temperature by forcing machine again, melt is by three-roller calendar sheet forming, sheet material uses mould to carry out punching through stamping machine, orifice plate, through being warmed up to 90 DEG C of-110 DEG C of back draft, namely obtains low temperature resistant flame retardant modified geogrid.
The beneficial effect that the present invention obtains is:
The present invention by the raw-material modification of formula, thus obtain having low temperature resistant, flame retardant properties good, the geo-grid that intensity is high, toughness is large.
Embodiment
Below in conjunction with embodiment, the invention will be further described,
A kind of low temperature resistant flame retardant modified geogrid, obtained by the component Raw material processing of following weight (kg): PP 48, EVA 25, MLLDPE 35, POE 16, maleic anhydride graft PE 13, SEBS 2, TDE 4,2,6-ditertbutylparacresol 0.4, calcium carbonate 7, modified carbon black masterbatch 6
Wherein, the preparation method of modified carbon black masterbatch: (1) by weight (kg) takes polyethylene 35, polypropylene 15, carbon black 45, acrylate 0.8, zinc oxide 0.3, irgasfos 168 0.2, protective agent 0.2, kerosene 0.6, flyash 2, the pungent decylate 4 of Polyglycerine, talcum powder 5; (2) load weighted carbon black, acrylate, zinc oxide are added in stirrer, fully mix at the temperature of 60 DEG C-180 DEG C, obtain mixture A; (3) all the other feed composition such as polyethylene, polypropylene, talcum powder, antioxidant 1010, protective agent, white oil, flyash, the pungent decylate of Polyglycerine are dropped into successively homogenizer high speed and stir 3-5 minute, obtain mixture material B; (4) obtaining blend after being mixed by A and B joins in twin screw extruder, and screw speed is 80-130 rpm, and heating barrel zone temperature 180-200 DEG C melt extrudes, cooling, granulation.
The preparation method of low temperature resistant flame retardant modified geogrid, comprises the following steps:
(1) each component raw material is taken by formula rate;
(2) PP taken, MLLDPE, POE, SEBS, maleic anhydride graft PE are added in Banbury mixer, at 140 DEG C of-160 DEG C of melting mixings, obtain mixing materials;
(3) by mixing materials and TDE, 2,6-ditertbutylparacresol, calcium carbonate mix, then send in the loading hopper of tablets press, open tablets press, the rotating speed controlling tablets press is 240-330r/min, control feed cylinder of granulator front portion, middle part, rear portion and head temperature be respectively: 225 ~ 235 DEG C, 220 ~ 225 DEG C, 210 ~ 215 DEG C, 230 ~ 235 DEG C, the material extruded from tablets press through water-cooled, pelletizing, sieve, drying, namely obtain mixing materials A;
(4) after dried mixing materials A being mixed with modified carbon black masterbatch, extruded at lower than 225 DEG C of temperature by forcing machine again, melt is by three-roller calendar sheet forming, sheet material uses mould to carry out punching through stamping machine, orifice plate, through being warmed up to 90 DEG C of-110 DEG C of back draft, namely obtains low temperature resistant flame retardant modified geogrid.
The Performance Detection value of geo-grid different size of the present invention is as following table:
Claims (2)
1. a low temperature resistant flame retardant modified geogrid, it is characterized in that, obtained by the component Raw material processing of following weight part: PP 40-50, EVA 20-30, MLLDPE 30-40, POE 10-20, maleic anhydride graft PE 10-15, SEBS 1-2, TDE 3-5,2,6-ditertbutylparacresol 0.2-0.5, calcium carbonate 5-10, modified carbon black masterbatch 5-8
The preparation method of described modified carbon black masterbatch: (1) takes polyethylene 30-40, polypropylene 10-20, carbon black 40-50, acrylate 0.2-1.5, zinc oxide 0.1-0.4, irgasfos 168 0.1-0.3, protective agent 0.1-0.3, kerosene 0.5-1.0, flyash 1-3, the pungent decylate 3-5 of Polyglycerine, talcum powder 4-6 by weight; (2) load weighted carbon black, acrylate, zinc oxide are added in stirrer, fully mix at the temperature of 60 DEG C-180 DEG C, obtain mixture A; (3) all the other feed composition such as polyethylene, polypropylene, talcum powder, antioxidant 1010, protective agent, white oil, flyash, the pungent decylate of Polyglycerine are dropped into successively homogenizer high speed and stir 3-5 minute, obtain mixture material B; (4) obtaining blend after being mixed by A and B joins in twin screw extruder, and screw speed is 80-130 rpm, and heating barrel zone temperature 180-200 DEG C melt extrudes, cooling, granulation.
2. the preparation method of low temperature resistant flame retardant modified geogrid according to claim 1, is characterized in that, comprise the following steps:
(1) each component raw material is taken by formula rate;
(2) PP taken, MLLDPE, POE, SEBS, maleic anhydride graft PE are added in Banbury mixer, at 140 DEG C of-160 DEG C of melting mixings, obtain mixing materials;
(3) by mixing materials and TDE, 2,6-ditertbutylparacresol, calcium carbonate mix, then send in the loading hopper of tablets press, open tablets press, the rotating speed controlling tablets press is 240-330r/min, control feed cylinder of granulator front portion, middle part, rear portion and head temperature be respectively: 225 ~ 235 DEG C, 220 ~ 225 DEG C, 210 ~ 215 DEG C, 230 ~ 235 DEG C, the material extruded from tablets press through water-cooled, pelletizing, sieve, drying, namely obtain mixing materials A;
(4) after dried mixing materials A being mixed with modified carbon black masterbatch, extruded at lower than 225 DEG C of temperature by forcing machine again, melt is by three-roller calendar sheet forming, sheet material uses mould to carry out punching through stamping machine, orifice plate, through being warmed up to 90 DEG C of-110 DEG C of back draft, namely obtains low temperature resistant flame retardant modified geogrid.