CN106336841A - Modified epoxide resin adhesive with high strength and preparing method thereof - Google Patents
Modified epoxide resin adhesive with high strength and preparing method thereof Download PDFInfo
- Publication number
- CN106336841A CN106336841A CN201610732213.2A CN201610732213A CN106336841A CN 106336841 A CN106336841 A CN 106336841A CN 201610732213 A CN201610732213 A CN 201610732213A CN 106336841 A CN106336841 A CN 106336841A
- Authority
- CN
- China
- Prior art keywords
- parts
- butadiene rubber
- acrylonitrile butadiene
- latex
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a modified epoxide resin adhesive with high strength and a preparing method thereof. The modified epoxide resin adhesive is prepared from, by weight, 80-100 parts of epoxide resin, 3-21 parts of carboxylic acrylonitrile butadiene rubber latex, 1.1-7.7 parts of polyacrylate latex, 5-10 parts of quartz powder, 1.1-1.5 parts of aluminium silicate, 2-3 parts of anti-settling agent, 1-3 parts of aminopropyltriethoxysilan; the ratio of carboxylic acrylonitrile butadiene rubber latex to polyacrylate latex is 2.7:1; the modified epoxide resin adhesive with high strength has good properties of ablation resistance, acid and alkali resistance, moisture absorption and thermal stability, aging resistance, anti-shearing force, high insulation and high sealing, and in terms of electrical insulation property, due to quartz powder added in the formula, and the product after solidification has stronger insulation property and ablation resistance property.
Description
Technical field
The present invention relates to epoxy resin adhesive technical field, the modified epoxy adhesive of particularly a kind of high intensity
And preparation method thereof.
Background technology
The metal through strict surface treatment for the current high-performance modified epoxy resin adhesive bonding and nonmetallic all have
Good adhesive strength and endurance quality, but bonding is without the strict metal being surface-treated and nonmetallic, not only adhesive strength
Low, and endurance quality is poor.Such as conventional high-performance epoxy resin adhesive modification e51 epoxy resin is matrix resin,
The adhesive of 200# polyamide curing agent preparation, has good bonding intensity and endurance quality, and bonding phosphoric acid is processed
Ly2cz aluminum alloy surface, normal temperature shear strength can reach 37mpa, 55 degree of rh98-100% hydrothermal agings 1000 hours and 90 degree
The adhesive property that shear strength after aging 300 hours for the salt fog is compared under normal temperature also increases, excellent in durability, but bonding
The aluminium alloy that sand papering is processed, even without the section of the sheet material being deliberately surface-treated, normal temperature shear strength only has
19.23mpa, the 55 degree of rh98-100% hydrothermal agings 1000 hours and 90 degree of salt fogs shear strength after aging 300 hours is almost
Zero.Domestic temporarily still do not have a kind of adhesive good for having without the strict metal being surface-treated or nonmetallic surface or section
Good adhesive strength and endurance quality.
Content of the invention
It is an object of the invention to provide modified epoxy adhesive of a kind of high intensity and preparation method thereof.
The technical solution realizing the object of the invention is: a kind of modified epoxy adhesive of high intensity and its preparation
Method, described modified epoxy adhesive press mass fraction by 80~100 parts epoxy resin, 3~21 parts of carboxyl butyronitrile glue
Breast, 1.1~7.7 parts of polyacrylic ester latexs, 5~10 parts of silica flour, 1.1~1.5 parts of alumina silicate, 2-3 part anti-settling agent, 1~3 part
Gamma-aminopropyl-triethoxy-silane is made;And described carboxylic acrylonitrile butadiene rubber latex is 2.7 with the mass ratio of polyacrylic ester latex:
1;
The preparation method of described modified epoxy adhesive comprises the steps:
(a) by after carboxylic acrylonitrile butadiene rubber latex breakdown of emulsion, dry for standby;
(b) by after polyacrylic ester latex breakdown of emulsion, dry for standby;
C () carboxylic acrylonitrile butadiene rubber latex after step (a) is added in epoxy resin, react 2h under conditions of temperature is 120 DEG C,
Sequentially add the polyacrylic ester latex after step (b) and gamma-aminopropyl-triethoxy-silane, the condition being 120 DEG C in temperature
Lower reaction 1h, obtaining is the epoxy resin of thick liquid under normal temperature;
D () sequentially adds anti-settling agent, alumina silicate and silica flour in the epoxy resin of thick liquid, after stirring 40min, obtain final product height
The modified epoxy adhesive of intensity.
The present invention compared with prior art, its remarkable advantage: the present invention have resistance to ablation, anti-soda acid, moisture absorption heat endurance,
Ageing-resistant, anti-shearing force, height insulate, the excellent properties of high sealing, can be effectively ensured in the metal without strict surface treatment
Or nonmetallic surface or section have good bonding intensity and endurance quality, in terms of electrical insulation properties, add due in formula
Added with silica flour, the product after present invention solidification has higher insulating properties and ablation resistance.
Below the present invention is described in further detail.
Specific embodiment
Modified epoxy adhesive of a kind of high intensity and preparation method thereof, described modified epoxy adhesive presses matter
The epoxy resin of 90 parts of number of amount, 16.2 parts of carboxylic acrylonitrile butadiene rubber latexs, 6 parts of polyacrylic ester latexs, 7 parts of silica flours, 1.3 parts of silicic acid
Aluminium, 2.5 portions of anti-settling agents, 35 parts of polyamide curing agents and 1.1 parts of gamma-aminopropyl-triethoxy-silanes are made;And described carboxyl
NBR latex is 2.7:1 with the mass ratio of polyacrylic ester latex;
The preparation method of described modified epoxy adhesive comprises the steps:
(a) by after carboxylic acrylonitrile butadiene rubber latex breakdown of emulsion, dry for standby;
(b) by after polyacrylic ester latex breakdown of emulsion, dry for standby;
C () carboxylic acrylonitrile butadiene rubber latex after step (a) is added in epoxy resin, react 2h under conditions of temperature is 120 DEG C,
Sequentially add the polyacrylic ester latex after step (b) and gamma-aminopropyl-triethoxy-silane, the condition being 120 DEG C in temperature
Lower reaction 1h, obtaining is the epoxy resin of thick liquid under normal temperature;
D () sequentially adds anti-settling agent, alumina silicate and silica flour in the epoxy resin of thick liquid, after stirring 40min, obtain final product height
The modified epoxy adhesive of intensity.
The present invention has resistance to ablation, anti-soda acid, moisture absorption heat endurance, ageing-resistant, anti-shearing force, high insulation, high sealing
Excellent properties, can be effectively ensured that to have good bonding in the metal without strict surface treatment or nonmetallic surface or section strong
Degree and endurance quality, by the modified epoxy adhesive of the formula in embodiment and the high intensity of preparation method preparation, lead to
Cross 200# polyamide as the product after curing agent solidification, through adding after curing agent solidification with ordinary epoxy resin adhesive
Data Comparison Analysis, show that present invention shearing force intensity at normal temperatures is 23.02mpa, damp and hot at 55 degree 98~100%
Shearing force intensity after aging 1000 hours is 22.48mpa, shears force intensity and be after aging 300 hours of 90 degree salt fogs
22.35mpa, has more structurally sound mechanics gluing performance than product after the solidification of market ordinary epoxy resin adhesive;Electric
Insulating properties aspect, is added with silica flour due in formula, and the product after present invention solidification has higher insulating properties and resistance to
Ablation property.
In addition to the above embodiments, other not described embodiments also should be within protection scope of the present invention.Herein
Described specific embodiment is only explanation for example to present invention spirit, and those skilled in the art are permissible
Described specific embodiment is made with various modifications or supplements or substituted using similar mode, but without departing from this
Invention spirit or surmount scope defined in appended claims.Although illustrating through specific term herein,
It is not excluded for the possibility using other terms, be used for the purpose of easily describing and explaining the basis of the present invention using these terms
Matter, it is all contrary with spirit of the present invention for being construed as any additional restriction.
Claims (1)
1. modified epoxy adhesive of a kind of high intensity and preparation method thereof is it is characterised in that described modified epoxy
Adhesive press mass fraction by 80~100 parts epoxy resin, 3~21 parts of carboxylic acrylonitrile butadiene rubber latexs, 1.1~7.7 parts of polyacrylic acid
Ester gum breast, 5~10 parts of silica flours, 1.1~1.5 parts of alumina silicate, 2-3 part anti-settling agent, 1~3 part of gamma-aminopropyl-triethoxy-silane
Make;And described carboxylic acrylonitrile butadiene rubber latex is 2.7:1 with the mass ratio of polyacrylic ester latex;
The preparation method of described modified epoxy adhesive comprises the steps:
(a) by after carboxylic acrylonitrile butadiene rubber latex breakdown of emulsion, dry for standby;
(b) by after polyacrylic ester latex breakdown of emulsion, dry for standby;
C () carboxylic acrylonitrile butadiene rubber latex after step (a) is added in epoxy resin, react 2h under conditions of temperature is 120 DEG C,
Sequentially add the polyacrylic ester latex after step (b) and gamma-aminopropyl-triethoxy-silane, the condition being 120 DEG C in temperature
Lower reaction 1h, obtaining is the epoxy resin of thick liquid under normal temperature;
D () sequentially adds anti-settling agent, alumina silicate and silica flour in the epoxy resin of thick liquid, after stirring 40min, obtain final product height
The modified epoxy adhesive of intensity.