CN106336184A - Power quick paste material for outdoor face bricks - Google Patents
Power quick paste material for outdoor face bricks Download PDFInfo
- Publication number
- CN106336184A CN106336184A CN201610694147.4A CN201610694147A CN106336184A CN 106336184 A CN106336184 A CN 106336184A CN 201610694147 A CN201610694147 A CN 201610694147A CN 106336184 A CN106336184 A CN 106336184A
- Authority
- CN
- China
- Prior art keywords
- outdoor face
- king
- face brick
- strength rapid
- rapid pasting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a power quick paste material for outdoor face bricks. The power quick paste material contains the following raw materials (by weight): 20-60 parts of low-alkalinity sulphoaluminate cement, 10-30 parts of sulphoaluminate cement, 0.1-0.4 part of a polycarboxylate superplasticizer, 0.4-1.0 part of a colorant, 0.05-0.2 part of a high-quality high-molecular retarding material, 0.1-0.5 part of redispersible emulsion powder, 30-60 parts of refined quartz sand, 0.02-0.06 part of a dry powder defoamer and 0.02-0.06 part of anti-crack fiber. The power quick paste material for outdoor face bricks is time-saving and labor-saving, prevents secondary face brick breakage, and has advantages of superstrong bonding, no toxicity and environment protection.
Description
Technical field
Present invention relates particularly to a kind of outdoor face brick strength Rapid pasting king's material.
Background technology
For the non-maneuver being used for the urban roads such as densely populated market, supermarket, hotel, bank, hospital, cell in the past
Track, crossing floor tile damage revamping and the outdoor surface brick adherence material that researchs and develops, its deficiency existing and defect include:
Adhesive property, strength character be not high；Setting time, clearance overlong time and because fluidity not causes application property bad, study carefully
Nothing more than limited by raw material and technical recipe is left to be desired and improves, these factors directly affects material pulp layer and base to its reason
The bonding of surface layer and the performance of combination property, lead to unreal, cracking, the hollowing of pulp layer, come off, and make top layer floor tile easily be subject to outer masterpiece
With rupturing, the phenomenon such as damaged, spring or losing fangle.For the quick reparation of road surface local defect, domestic also do not have not very
Good countermeasure, whether dry-laid method or wet-laid process, not only technique is relatively simple for conventional cement-based material local route repair technology, open
Put traffic time length and repair that interface adhesion is poor, repair efficiency is very undesirable, and these local defects are repaiied according to whole plate
Recovering technology, not only repairs long in time limit, particularly can cause secondary breakage quickly, need to repair again, very uneconomical.
Content of the invention
For overcoming the problems of the prior art, the invention provides a kind of time and labour saving, preventing secondary face brick damaged, superpower
Bonding, the outdoor face brick strength rapid mass of asepsis environment-protecting.
The technology of employing and method in order to solve the problems, such as the above-mentioned present invention are as follows:
A kind of outdoor face brick strength Rapid pasting king's material, including the raw material of following weight portion: low-alkalinity sulphoaluminate
Cement 20-60 part, sulphate aluminium cement 10-30 part, high-efficiency water-reducing agent of poly-carboxylic acid 0.1-0.4 part, colouring agent 0.4-1.0 part, excellent
Matter macromolecular sustained gel material 0.05-0.2 part, redispersible latex powder 0.1-0.5 part, purity quartzite 30-60 part, dry powder disappear
Infusion 0.02-0.06 part and anti-crack fiber 0.02-0.06 part.
Further, the macromolecular sustained gel material of described high-quality is sodium gluconate or trisodium citrate.
Further, described colouring agent is iron oxide or zinc oxide.
Further, described redispersible latex powder is ethene or acetate ethylene copolymer.
Further, described dry powder defoamer is liquid hydrocarbon or polyethylene glycol.
Further, described anti-crack fiber is polypropylene.
The invention has the benefit that for the adhesive property increasing product, with the addition of suitable organic in production technology
Adhesive, can be after moist part evaporation, and polymer particle passes through coalescence, forms one layer of polymeric film, plays good glue
Connect effect, improve the flexibility of product, deformability, bending strength, mar proof, tough rigid, cohesive force and density and guarantor
Outlet capacity and good application property；For guaranteeing to have enough engineering times and good application property, in product, mix appropriate gathering
The macromolecular sustained gel material of carboxylic acid high efficiency water reducing agent, high-quality and dry powder defoamer, have reached preferable Construction State.
Brief description
Fig. 1 is a kind of process chart of outdoor face brick strength Rapid pasting king's material of the present invention.
Specific embodiment
With reference to embodiment, the present invention is described in further detail with accompanying drawing, but they are not to skill of the present invention
The restriction of art scheme, based on present invention teach that any conversion of being made, all falls within protection scope of the present invention.
Embodiment 1
A kind of outdoor face brick strength Rapid pasting king's material, including the raw material of following weight portion: low-alkalinity sulphoaluminate
20 parts of cement, 10 parts of sulphate aluminium cement, 0.1 part of high-efficiency water-reducing agent of poly-carboxylic acid, 0.4 part of iron oxide, 0.2 part of sodium gluconate,
0.1 part of ethene, 69 parts of purity quartzite, 0.1 part of liquid hydrocarbon, 0.1 part of polypropylene.
Refering to shown in Fig. 1, two kinds of main materials are first fully stirred in the airtight stirring storehouse of drying by the weight according to above-mentioned raw materials
Mix uniformly, mixing time is 15 minutes, be subsequently adding and add auxiliary agent to be again stirring for 10 minutes after auxiliary material stirs 10 minutes, you can
To sample.Add the water of 20 number amounts of total amount during construction, and fully stir to uniformly no luming, there is the slurry of certain fluidity
Material, then pours slurry in mould into and shakeouts, and places face brick and strikes reality.
Wherein, main material be low-alkalinity sulphoaluminate cement and sulphate aluminium cement, auxiliary material be iron oxide, sodium gluconate,
Ethene, purity quartzite and polypropylene, auxiliary agent is high-efficiency water-reducing agent of poly-carboxylic acid and liquid hydrocarbon.
Embodiment 2
A kind of outdoor face brick strength Rapid pasting king's material, including the raw material of following weight portion: low-alkalinity sulphoaluminate
58 parts of cement, 20 parts of sulphate aluminium cement, 0.4 part of high-efficiency water-reducing agent of poly-carboxylic acid, 1.0 parts of zinc oxide, 0.1 part of trisodium citrate,
0.4 part of acetate ethylene copolymer, 20 parts of purity quartzite, 0.06 part of polyethylene glycol, 0.04 part of polypropylene.
Refering to shown in Fig. 1, two kinds of main materials are first fully stirred in the airtight stirring storehouse of drying by the weight according to above-mentioned raw materials
Mix uniformly, mixing time is 10 minutes, be subsequently adding and add auxiliary agent to be again stirring for 15 minutes after auxiliary material stirs 10 minutes, you can
To sample.Add the water of 18 number amounts of total amount during construction, and fully stir to uniformly no luming, there is the slurry of certain fluidity
Material, then pours slurry in mould into and shakeouts, and places face brick and strikes reality.
Wherein, main material be low-alkalinity sulphoaluminate cement and sulphate aluminium cement, auxiliary material be zinc oxide, trisodium citrate,
Acetate ethylene copolymer, purity quartzite and polypropylene, auxiliary agent is high-efficiency water-reducing agent of poly-carboxylic acid and polyethylene glycol.
Embodiment 3
A kind of outdoor face brick strength Rapid pasting king's material, including the raw material of following weight portion: low-alkalinity sulphoaluminate
40 parts of cement, sulphate aluminium cement 18.3,0.4 part of high-efficiency water-reducing agent of poly-carboxylic acid, 0.7 part of iron oxide, 0.06 part of trisodium citrate,
0.3 part of ethene, 40 parts of purity quartzite, 0.04 part of polyethylene glycol, 0.2 part of polypropylene.
Refering to shown in Fig. 1, two kinds of main materials are first fully stirred in the airtight stirring storehouse of drying by the weight according to above-mentioned raw materials
Mix uniformly, mixing time is 10 minutes, be subsequently adding and add auxiliary agent to be again stirring for 15 minutes after auxiliary material stirs 5 minutes, you can
To sample.Add the water of 19 number amounts of total amount during construction, and fully stir to uniformly no luming, there is the slurry of certain fluidity
Material, then pours slurry in mould into and shakeouts, and places face brick and strikes reality.
Wherein, main material be low-alkalinity sulphoaluminate cement and sulphate aluminium cement, auxiliary material be iron oxide, trisodium citrate,
Ethene, purity quartzite and polypropylene, auxiliary agent is high-efficiency water-reducing agent of poly-carboxylic acid and polyethylene glycol.
Experimental example
Experimental technique: to the outdoor face brick made by embodiments of the invention 1-3 with strength Rapid pasting king's material with now
Some outdoors face brick adhesives is compared experiment.
As can be seen here, the outdoor face brick of present invention strength Rapid pasting king's material is compared to existing outdoor face brick bonding
Material substantially has faster final set speed and higher resistance to compression, anti-folding, adhesion strength.
The invention has the benefit that for the adhesive property increasing product, with the addition of in production technology suitable can be again
Dispersed latex powder, can be after moist part evaporation, and polymer particle passes through coalescence, forms one layer of polymeric film, plays very
Good cementation, improves the flexibility of product, deformability, bending strength, mar proof, tough rigid, bonding force and density
And water holding capacity and good application property；For guaranteeing to have enough engineering times and good application property, mix suitable in product
The high-efficiency water-reducing agent of poly-carboxylic acid of amount, the macromolecular sustained gel material of high-quality and dry powder defoamer, have reached preferable Construction State.
The above, the only specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, and any
The change or replacement expected without creative work, all should be included within the scope of the present invention, therefore, the present invention's
Protection domain should be defined by the protection domain that claims are limited.
Claims (6)
1. a kind of outdoor face brick with strength Rapid pasting king's material it is characterised in that include following weight portion raw material: low alkalinity
Sulphate aluminium cement 20-60 part, sulphate aluminium cement 10-30 part, high-efficiency water-reducing agent of poly-carboxylic acid 0.1-0.4 part, colouring agent 0.4-
1.0 parts, high-quality macromolecular sustained gel material 0.05-0.2 part, redispersible latex powder 0.1-0.5 part, purity quartzite 30-60
Part, dry powder defoamer 0.02-0.06 part and anti-crack fiber 0.02-0.06 part.
2. as claimed in claim 1 outdoor face brick with strength Rapid pasting king's material it is characterised in that: described high-quality macromolecule
Retarded adhesive material is sodium gluconate or trisodium citrate.
3. as claimed in claim 1 outdoor face brick strength Rapid pasting king's material it is characterised in that: described colouring agent be oxygen
Change iron or zinc oxide.
4. as claimed in claim 1 outdoor face brick with strength Rapid pasting king's material it is characterised in that: described redispersible
Latex powder is ethene or acetate ethylene copolymer.
5. as claimed in claim 1 outdoor face brick with strength Rapid pasting king's material it is characterised in that: described dry powder defoamer
For liquid hydrocarbon or polyethylene glycol.
6. as claimed in claim 1 outdoor face brick strength Rapid pasting king's material it is characterised in that: described anti-crack fiber is
Polypropylene.