CN106319964A - 碳纤维水刺非织造布及其制备方法和用途 - Google Patents
碳纤维水刺非织造布及其制备方法和用途 Download PDFInfo
- Publication number
- CN106319964A CN106319964A CN201510323947.0A CN201510323947A CN106319964A CN 106319964 A CN106319964 A CN 106319964A CN 201510323947 A CN201510323947 A CN 201510323947A CN 106319964 A CN106319964 A CN 106319964A
- Authority
- CN
- China
- Prior art keywords
- carbon fiber
- ammonium chloride
- chloride solution
- trimethyl ammonium
- macromolecular compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种碳纤维水刺非织造布的制备方法，它包括以下步骤：将水刺非织造布原料静置于温度为50至100℃的甲基丙烯酰氧乙基三甲基氯化铵溶液中；在该甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂，以使甲基丙烯酰氧乙基三甲基氯化铵溶液聚合成高分子化合物，从而将高分子化合物通过其羧基嫁接到非织造布的表面。一种碳纤维水刺非织造布，它包括在水刺非织造布的表面通过高分子化合物的羧基嫁接有高分子化合物，该高分子化合物由在甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂形成。本发明采用上述方法、结构和用途，该种碳纤维水刺非织造布具有较好的吸附力。
Description
技术领域
本发明涉及一种纺织领域，尤其涉及一种碳纤维水刺非织造布及其制备方法和用途。
背景技术
纤维非织造布，又称纤维无纺布，是一种不需要纺纱织布而形成的织物，只是将纺织短纤维或者长丝进行定向或随机排列，形成纤网结构，然后采用机械、热粘或化学等方法加固而成。它直接利用高聚物切片、短纤维或长丝通过各种纤网成形方法和固结技术形成的具有柔软、透气和平面结构的新型纤维制品。
我国国家标准GB/T 5709——1997《纺织品 非织造布 术语》对非织造布的定义是：定向或随机排列的纤维，通过摩擦、抱合、或粘合，或者这些方法的组合而相互结合制成的片状物、纤网或絮垫，不包括纸、机织物、针织物、簇绒织物以及湿法缩绒的毡制品。简单的讲就是： 它不是由一根一根的纱线交织、编结在一起的，而是将纤维直接通过物理的方法粘合在一起的，所以，当你拿到你衣服里的粘称时，就会发现，是抽不出一根根的线头的。非织造布突破了传统的纺织原理，并具有工艺流程短、生产速度快，产量高、成本低、用途广、原料来源多等特点。
但是在现有技术中，纤维非织造布的吸附能力较差，作为一种清洁材料的效果较差。
发明内容
为了克服现有技术的上述缺陷，本发明所要解决的技术问题是提供一种碳纤维水刺非织造布及其制备方法和用途，其能解决上述问题中的任一种。
为达到上述目的，本发明的技术方案是：
一种碳纤维水刺非织造布的制备方法，它包括以下步骤：
将水刺非织造布原料静置于温度为50至100℃的甲基丙烯酰氧乙基三甲基氯化铵溶液中；
在该甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂，以使甲基丙烯酰氧乙基三甲基氯化铵溶液聚合成高分子化合物，从而将高分子化合物通过其羧基嫁接到非织造布的表面。
优选地，它包括以下步骤：甲基丙烯酰氧乙基三甲基氯化铵溶液的温度为80摄氏度。
优选地，它包括：所述自由基引发剂可以为Cl2、Br2、过氧化环己酮、过氧化二苯甲酰、叔丁基过氧化氢中的一种或几种。
优选地，它还包括：在该甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂后，静置半小时，以使高分子化合物通过羧基充分嫁接到水刺非织造物的表面。
本发明还公开了一种碳纤维水刺非织造布，其特征在于，它包括在水刺非织造布的表面通过高分子化合物的羧基嫁接有高分子化合物，该高分子化合物由在甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂形成。
本发明还公开了一种如上述的碳纤维水刺非织造布的用途，其用于吸附色素或重金属化合物。
本发明采用上述方法、结构和用途，该种碳纤维水刺非织造布具有较好的吸附力。
具体实施方式
在此描述的本发明的具体实施方式，仅用于解释本发明的目的，而不能以任何方式理解成是对本发明的限制。在本发明的教导下，技术人员可以构想基于本发明的任意可能的变形，这些都应被视为属于本发明的范围。
一种碳纤维水刺非织造布的制备方法，它包括以下步骤：
将水刺非织造布原料或水刺无纺布（植物粘胶级或者纯棉）静置于温度为50至100℃的甲基丙烯酰氧乙基三甲基氯化铵溶液中；利用植物纤维亲水功能，很容易将DMC溶液完全浸入纤维内部。时间约10分钟后添加自由基引发剂将DMC固着在植物粘胶级或者纯棉上，再静置30分钟左右即可水洗烘干。
在该甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂，以使甲基丙烯酰氧乙基三甲基氯化铵溶液聚合成高分子化合物，从而将高分子化合物通过其羧基嫁接到非织造布的表面。
其中，甲基丙烯酰氧乙基三甲基氯化铵又称DMC。DMC溶于水，不溶于酯、酮及烃。可用自由基引发剂进行溶液聚合，悬浮液聚合和乳液聚合可与其它单体均聚或共聚，由此给聚合物引入季铵盐基团，因而有极强的极性和对阴离子性物质的亲合性。DMC为中性盐，CH2=C(CH3)COOCH2CH2N
(CH3)3Cl。含有不饱和双键，在50-80度温度下在引发剂条件引发下能聚合成高分子化合物C6H14ClNO 2,3-环氧丙基三甲基氯化铵。
优选地，它包括以下步骤：甲基丙烯酰氧乙基三甲基氯化铵溶液的温度为80摄氏度。
优选地，它包括：所述自由基引发剂可以为Cl2、Br2、过氧化环己酮、过氧化二苯甲酰、叔丁基过氧化氢中的一种或几种。
优选地，它还包括：在该甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂后，静置半小时，在本实施方式中静置0.5个小时，以使高分子化合物通过羧基充分嫁接到水刺非织造物的表面。
本发明还公开了一种碳纤维水刺非织造布，它包括在水刺非织造布的表面通过高分子化合物的羧基嫁接有高分子化合物，该高分子化合物由在甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂形成。
本发明还公开了一种如上述的碳纤维水刺非织造布的用途，其用于吸附色素或重金属化合物。
本发明采用上述方法、结构和用途，该种碳纤维水刺非织造布具有较好的吸附力。经过试验证明，将同等质量体积的本申请中的碳纤维水刺非织造布和普通吸湿纤维分别放入滴了红墨水的蒸馏水中，本申请中的碳纤维水刺非织造布在5分钟内即可将水还原至干净透明，普通吸湿纤维则无法将红墨水吸收干净。
本说明书中的各个实施例均采用递进的方式描述，每个实施例重点说明的都是与其他实施例的不同之处，各个实施例之间相同相似的部分互相参见即可。
上述实施例只为说明本发明的技术构思及特点，其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施，并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰，都应涵盖在本发明的保护范围之内。
Claims (6)
1.一种碳纤维水刺非织造布的制备方法，其特征在于，它包括以下步骤：
将水刺非织造布原料静置于温度为50至100℃的甲基丙烯酰氧乙基三甲基氯化铵溶液中；
在该甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂，以使甲基丙烯酰氧乙基三甲基氯化铵溶液聚合成高分子化合物，从而将高分子化合物通过其羧基嫁接到非织造布的表面。
2.根据权利要求1所述的碳纤维水刺非织造布的制备方法，其特征在于，它包括以下步骤：甲基丙烯酰氧乙基三甲基氯化铵溶液的温度为80摄氏度。
3.根据权利要求1所述的碳纤维水刺非织造布的制备方法，其特征在于，它包括：所述自由基引发剂可以为Cl2、Br2、过氧化环己酮、过氧化二苯甲酰、叔丁基过氧化氢中的一种或几种。
4.根据权利要求1所述的碳纤维水刺非织造布的制备方法，其特征在于，它还包括：在该甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂后，静置0.1至1小时，以使高分子化合物通过羧基充分嫁接到水刺非织造物的表面。
5.一种碳纤维水刺非织造布，其特征在于，它包括在水刺非织造布的表面通过高分子化合物的羧基嫁接有高分子化合物，该高分子化合物由在甲基丙烯酰氧乙基三甲基氯化铵溶液加入自由基引发剂形成。
6.一种如权利要求5的碳纤维水刺非织造布的用途，其用于吸附色素或重金属化合物。