CN106318280A - Multicomponent adhesive - Google Patents
Multicomponent adhesive Download PDFInfo
- Publication number
- CN106318280A CN106318280A CN201510377847.6A CN201510377847A CN106318280A CN 106318280 A CN106318280 A CN 106318280A CN 201510377847 A CN201510377847 A CN 201510377847A CN 106318280 A CN106318280 A CN 106318280A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- polyvinyl alcohol
- oleic acid
- polyamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of hot-melt adhesives and particularly relates to a multicomponent adhesive. The multicomponent adhesive contains the following components in parts by mass: 20-30 parts of polyvinyl alcohol, 10-15 parts of oleic acid, 30-40 parts of acrylic resin, 10-15 parts of polyamide imide, 5-12 parts of methoxyphenol, 15-20 parts of ethylene-vinyl acetate copolymer, 4-10 parts of poly(alkyl acrylate) and 10-20 parts of polyamine epihalohydrin resin. After adopting the formula, the multicomponent adhesive disclosed by the invention can be used for adhering a wide range of different matrixes which may be flexible or replaceable rigid; the components of the multicomponent adhesive disclosed by the invention are all environmentally friendly, so that the environment protection effect is good; and the production cost is low, so that the energy consumption is lowered.
Description
Technical field
The present invention relates to hotmelt technical field, particularly a kind of multi-component adhesive.
Background technology
Binding agent is one of most important auxiliary material, applies extremely wide in package handling.Binding agent is tool
Sticking material, can link together the material that two kinds separate by its viscosity.
Hotmelt is in general anhydrous and solvent-free binding agent, and these binding agents are at room temperature
Solid and they be to be applied in molten form in parts to be bonded or substrate, and after the coupling
Naturally place, solidify after cooling.These hot melts have good cohesive force to flexible substrate, and permit
Thin polymer film and the most flawless bonding of very wide range of substrate are permitted.But, in addition,
Some thermosol bodies are had to keep viscosity the most enduringly and can bond.Using moderate pressure
In the case of, these thermosol bodies are bonded to essentially all of substrate immediately, and are referred to as pressure-sensitive
Binding agent.
Summary of the invention
The technical issues that need to address of the present invention are to provide the hotmelt of a kind of environmental protection and low cost.
For solving above-mentioned technical problem, a kind of multi-component adhesive of the present invention according to mass fraction meter include with
Lower component: polyvinyl alcohol 20-30 part, oleic acid 10-15 part, acrylic resin 30-40 part, polyamide acyl
Imines 10-15 part, methoxyphenol 5-12 part, vinyl-vinyl acetate copolymer 15-20 part, poly-alkane
Base acrylate 4-10 part, polyamine epihalohydrines resin 10-20 part.
Further, include following components according to mass fraction meter: polyvinyl alcohol 20 parts, oleic acid 10 parts, third
Olefin(e) acid resin 30 parts, polyamidoimide 10 parts, methoxyphenol 5 parts, ethylene-vinyl acetate c
Thing 15 parts, polyalkyl acrylate 4 parts, polyamine epihalohydrines resin 10 parts.
Further, include following components according to mass fraction meter: polyvinyl alcohol 30 parts, oleic acid 15 parts, third
Olefin(e) acid resin 40 parts, polyamidoimide 15 parts, methoxyphenol 12 parts, ethane-acetic acid ethyenyl ester is common
Polymers 20 parts, polyalkyl acrylate 10 parts, polyamine epihalohydrines resin 20 parts.
Further, include following components according to mass fraction meter: polyvinyl alcohol 22 parts, oleic acid 11 parts, third
Olefin(e) acid resin 33 parts, polyamidoimide 12 parts, methoxyphenol 7 parts, ethylene-vinyl acetate c
Thing 16 parts, polyalkyl acrylate 6 parts, polyamine epihalohydrines resin 13 parts.
Further, include following components according to mass fraction meter: polyvinyl alcohol 26 parts, oleic acid 13 parts, third
Olefin(e) acid resin 36 parts, polyamidoimide 14 parts, methoxyphenol 9 parts, ethylene-vinyl acetate c
Thing 18 parts, polyalkyl acrylate 8 parts, polyamine epihalohydrines resin 15 parts.
After using above-mentioned formula, the multi-component adhesive of the present invention can be used to bond the different substrates of wide scope,
It can be flexible or alternative rigidity；Multi-component adhesive composition all environmental protection of the present invention, protection ring
Border is effective, and production cost is low, reduces energy resource consumption.
Detailed description of the invention
A kind of multi-component adhesive of the present invention includes following components according to mass fraction meter: polyvinyl alcohol 20-30
Part, oleic acid 10-15 part, acrylic resin 30-40 part, polyamidoimide 10-15 part, methoxybenzene
Phenol 5-12 part, vinyl-vinyl acetate copolymer 15-20 part, polyalkyl acrylate 4-10 part, polyamine
Epihalolhydrin resins 10-20 part.
Embodiment one:
Following components is included: polyvinyl alcohol 20 parts, oleic acid 10 parts, acrylic resin 30 according to mass fraction meter
Part, polyamidoimide 10 parts, methoxyphenol 5 parts, vinyl-vinyl acetate copolymer 15 parts, poly-
Alkyl acrylate 4 parts, polyamine epihalohydrines resin 10 parts.
Embodiment two:
Following components is included: polyvinyl alcohol 30 parts, oleic acid 15 parts, acrylic resin 40 according to mass fraction meter
Part, polyamidoimide 15 parts, methoxyphenol 12 parts, vinyl-vinyl acetate copolymer 20 parts,
Polyalkyl acrylate 10 parts, polyamine epihalohydrines resin 20 parts.
Embodiment three:
Following components is included: polyvinyl alcohol 22 parts, oleic acid 11 parts, acrylic resin 33 according to mass fraction meter
Part, polyamidoimide 12 parts, methoxyphenol 7 parts, vinyl-vinyl acetate copolymer 16 parts, poly-
Alkyl acrylate 6 parts, polyamine epihalohydrines resin 13 parts.
Embodiment four:
Following components is included: polyvinyl alcohol 26 parts, oleic acid 13 parts, acrylic resin 36 according to mass fraction meter
Part, polyamidoimide 14 parts, methoxyphenol 9 parts, vinyl-vinyl acetate copolymer 18 parts, poly-
Alkyl acrylate 8 parts, polyamine epihalohydrines resin 15 parts.
Although the foregoing describing the detailed description of the invention of the present invention, but those skilled in the art should managing
Solving, these are merely illustrative of, and present embodiment can be made various changes or modifications, without departing from sending out
Bright principle and essence, protection scope of the present invention is only limited by the claims that follow.
Claims (5)
1. a multi-component adhesive, it is characterised in that include following components according to mass fraction meter: polyvinyl alcohol
20-30 part, oleic acid 10-15 part, acrylic resin 30-40 part, polyamidoimide 10-15 part, methoxy
Base phenol 5-12 part, vinyl-vinyl acetate copolymer 15-20 part, polyalkyl acrylate 4-10 part,
Polyamine epihalohydrines resin 10-20 part.
2. according to a kind of multi-component adhesive described in claim 1, it is characterised in that according to mass fraction meter bag
Include following components: polyvinyl alcohol 20 parts, oleic acid 10 parts, acrylic resin 30 parts, polyamidoimide 10
Part, methoxyphenol 5 parts, vinyl-vinyl acetate copolymer 15 parts, polyalkyl acrylate 4 parts,
Polyamine epihalohydrines resin 10 parts.
3. according to a kind of multi-component adhesive described in claim 1, it is characterised in that according to mass fraction meter bag
Include following components: polyvinyl alcohol 30 parts, oleic acid 15 parts, acrylic resin 40 parts, polyamidoimide 15
Part, methoxyphenol 12 parts, vinyl-vinyl acetate copolymer 20 parts, polyalkyl acrylate 10 parts,
Polyamine epihalohydrines resin 20 parts.
4. according to a kind of multi-component adhesive described in claim 1, it is characterised in that according to mass fraction meter bag
Include following components: polyvinyl alcohol 22 parts, oleic acid 11 parts, acrylic resin 33 parts, polyamidoimide 12
Part, methoxyphenol 7 parts, vinyl-vinyl acetate copolymer 16 parts, polyalkyl acrylate 6 parts,
Polyamine epihalohydrines resin 13 parts.
5. according to a kind of multi-component adhesive described in claim 1, it is characterised in that according to mass fraction meter bag
Include following components: polyvinyl alcohol 26 parts, oleic acid 13 parts, acrylic resin 36 parts, polyamidoimide 14
Part, methoxyphenol 9 parts, vinyl-vinyl acetate copolymer 18 parts, polyalkyl acrylate 8 parts,
Polyamine epihalohydrines resin 15 parts.