CN106280826A - A kind of art opalescent lacquers and preparation method thereof - Google Patents
A kind of art opalescent lacquers and preparation method thereof Download PDFInfo
- Publication number
- CN106280826A CN106280826A CN201610781522.9A CN201610781522A CN106280826A CN 106280826 A CN106280826 A CN 106280826A CN 201610781522 A CN201610781522 A CN 201610781522A CN 106280826 A CN106280826 A CN 106280826A
- Authority
- CN
- China
- Prior art keywords
- slurry
- base paint
- thickening agent
- preparation
- opalescent lacquers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to coating applied technical field, be specifically related to a kind of art opalescent lacquers and preparation method thereof.Described opalescent lacquers is prepared from by base paint and slurry, and described base paint and slurry mix according to weight portion 1:1；Described preparation method comprises the steps: A) prepare base paint; cellulose is stirring evenly and then adding into emulsion, water, antibacterial, defoamer, antifreeze, the first thickening agent, coalescents, suspension, PH regulator, the second thickening agent and wetting agent, it is ensured that base paint is uniformly dispersed；B) prepare slurry, pearl essence is uniformly dispersed in water, use thickening agent regulation viscosity, then add cosolvent, dispersant, defoamer and thickening agent, complete the preparation of slurry；C) then base paint and slurry being mixed, component is according to the ratio mix homogeneously of 1:1, and regulates to appropriate viscosity.
Description
Technical field
The present invention relates to coating applied technical field, be specifically related to a kind of art opalescent lacquers and preparation method thereof.
Background technology
Opalescent lacquers, it replaces aluminum shot with Muscovitum.Added with the Muscovitum face scribbling titanium dioxide and ferrum oxide in its paint base
Material.After light is mapped on mica particles, the first upper titanium dioxide of band and the color of ferrum oxide, in mica particles, then there is complexity
Refraction and interference.Meanwhile, Muscovitum itself also has a kind of color special, that have transparent feel.So, the light reflected,
Just have a kind of as pearlescent flash of light.
But, opalescent lacquers of the prior art, mostly exist abnormal smells from the patient compared with big, harmful substance is many, the soft degree of gloss not,
Texture is unintelligible.
Summary of the invention
In order to effectively solve the problems referred to above, the present invention provides a kind of art opalescent lacquers and preparation method thereof.
Technical scheme is specific as follows: a kind of art opalescent lacquers, described opalescent lacquers is prepared by base paint and slurry
Forming, described base paint and slurry mix according to weight portion 1:1.
Further, described base paint is by following raw material group layer:
Further, described slurry is by following raw material group layer:
The preparation method of a kind of art opalescent lacquers, for preparing above-mentioned artistic opalescent lacquers, it is characterised in that include as follows
Step:
A) prepare base paint, cellulose is stirring evenly and then adding into emulsion, water, antibacterial, defoamer, antifreeze, first
Thickening agent, coalescents, suspension, PH regulator, the second thickening agent and wetting agent, it is ensured that base paint is uniformly dispersed；
B) prepare slurry, pearl essence is uniformly dispersed in water, use thickening agent regulation viscosity, then add cosolvent, divide
Powder, defoamer and thickening agent, complete the preparation of slurry；
C) then base paint and slurry being mixed, component is according to the ratio mix homogeneously of 1:1, and regulates to appropriate viscosity and be
Can.
The invention have the benefit that
1, cellulose, PU thickening agent, suspension, the synergism of HASE thickening agent, imparts art opalescent lacquers excellence
Workability and storge quality, it is ensured that pearl essence is stability in system；
2, ensure that the dispersed of pearl essence by the adjustment of production technology；
3, by the adjustment of construction technology, it is provided that multiple indoor decorative effect attractive in appearance.
Detailed description of the invention
In order to make the purpose of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, to the present invention
It is explained in further detail.Should be appreciated that specific embodiment described herein is used only for explaining the present invention, be not used to
Limit the present invention.
On the contrary, the present invention contain any be defined by the claims the replacement done in the spirit and scope of the present invention, repair
Change, equivalent method and scheme.Further, in order to make the public that the present invention to be had a better understanding, thin to the present invention below
During joint describes, detailed describe some specific detail sections.There is no these detail sections for a person skilled in the art
Description can also understand the present invention completely.
One embodiment of the present of invention provides a kind of art opalescent lacquers, and described opalescent lacquers is by base paint and slurry preparation
Becoming, described base paint and slurry mix according to weight portion 1:1.
Described base paint is by following raw material group layer:
Described cellulose is that hydroxyethyl cellulose, methylcellulose, carboxymethyl cellulose, ethyl cellulose or hydroxypropyl are fine
Dimension element therein one or more；Described emulsion is pure silicon acrylic emulsion；Described antibacterial be in prior art coating apply in
Relatively conventional that there is fungus and mildew resistance function, can be such as n-octyl Kazon, but be not limited to only n-octyl Kazon；Institute
Stating defoamer is mineral oil antifoam agent；Described antifreeze is alcohols antifreeze；Described first thickening agent is methylcellulose, carboxylic first
Cellulose derivative, starch derivatives, casein, sodium polyacrylate, polyethylene glycol oxide, the polyvinylpyrrolidines such as base cellulose
Ketone, polyvinyl alcohol, low-molecular polyethylene wax, polyacrylamide therein one or more；Described coalescents is 2,2,4-tri-
Methyl isophthalic acid, 3-pentanediol mono isobutyrate；Described suspending agent is SN suspending agent；Described PH regulator is AMP95；Described second increases
Thick dose is a kind of water-dispersible polyurethane thickening agent；
Described wetting agent is wetting agent conventional in existing coating products technical field.
Described slurry is by following raw material group layer:
Described cosolvent be sodium benzoate, sodium salicylate or acetamide therein one or more；Described defoamer is ore deposit
Thing oil defoamer；Described dispersant is low-molecular-weight wax class dispersant；Described thickening agent is a kind of water-dispersible polyurethane thickening agent
The preparation method of a kind of art opalescent lacquers, for preparing above-mentioned artistic opalescent lacquers, it is characterised in that include as follows
Step:
A) prepare base paint, be sequentially added into after cellulose is stirred emulsion, water, antibacterial, defoamer, antifreeze,
First thickening agent, coalescents, suspension, PH regulator, the second thickening agent and wetting agent, it is ensured that base paint is uniformly dispersed；
In step A) in, the temperature conditions adding the first thickening agent and the second thickening agent is different, is adding the first increasing
The temperature conditions of thick dose is 200-220 DEG C, until adding before the second thickening agent, needs to be always maintained at this temperature, is adding the
The temperature conditions of two thickening agents is 70-80 DEG C, and after adding the second thickening agent, 10min under conditions of keeping 70-80 DEG C, with
After be down to room temperature；Wherein mixing speed can depend on the circumstances；
B) prepare slurry, pearl essence is uniformly dispersed in water, use thickening agent regulation viscosity, then add cosolvent, divide
Powder, defoamer and thickening agent, complete the preparation of slurry；
C) then base paint and slurry being mixed, component is according to the ratio mix homogeneously of 1:1, and regulates to appropriate viscosity and be
Can.
Claims (4)
1. an artistic opalescent lacquers, it is characterised in that described opalescent lacquers is prepared from by base paint and slurry, described base paint and
Slurry mixes according to weight portion 1:1.
A kind of art opalescent lacquers the most according to claim 1, it is characterised in that described base paint is by following raw material group
Layer:
A kind of art opalescent lacquers the most according to claim 2, it is characterised in that described slurry is by following raw material group layer:
4. a preparation method for artistic opalescent lacquers, for preparing the artistic opalescent lacquers that one of the claims 1-3 are described, its
It is characterised by, comprises the steps:
A) prepare base paint, cellulose is stirring evenly and then adding into emulsion, water, antibacterial, defoamer, antifreeze, the first thickening
Agent, coalescents, suspension, PH regulator, the second thickening agent and wetting agent, it is ensured that base paint is uniformly dispersed；
B) prepare slurry, pearl essence be uniformly dispersed in water, use thickening agent regulation viscosity, then add cosolvent, dispersant,
Defoamer and thickening agent, complete the preparation of slurry；
C) then base paint and slurry being mixed, component is according to the ratio mix homogeneously of 1:1, and regulates to appropriate viscosity.