CN106280591A - A kind of thick coated type steel structure fire-proof paint and preparation method thereof - Google Patents
A kind of thick coated type steel structure fire-proof paint and preparation method thereof Download PDFInfo
- Publication number
- CN106280591A CN106280591A CN201610634144.1A CN201610634144A CN106280591A CN 106280591 A CN106280591 A CN 106280591A CN 201610634144 A CN201610634144 A CN 201610634144A CN 106280591 A CN106280591 A CN 106280591A
- Authority
- CN
- China
- Prior art keywords
- coating
- weight portion
- portland cement
- steel structure
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to technical field of coatings, be specifically related to the fireproof coating of a kind of thick coated type steel structure, this coating is compound adhesive by 42.5R portland cement and Macrogol 2000, using alumina silicate fibre inorganic material as crack resistence thermal insulating filling;This thicker fireproof coating is a kind of low cost, excellent performance, easy construction, good endurance; there is the novel environment friendly coating of broad development prospect; this product has bond strength, water-tolerant, resistance to acids and bases is good, safety non-toxic, the amount of being fuming are few, cracking resistance and the thick coated type steel structure fire-proof paint that crack resistence is good, fire protecting performance is excellent, can be widely applied to the flame-proof finishing protection of indoor and outdoor steel construction.
Description
Technical field
The present invention relates to technical field of coatings, be specifically related to a kind of thick coated type steel structure fire-proof paint and preparation method thereof.
Background technology
High-rise and building the framework great majority of modernization use steel construction, although the steel as supporting member have
Have intensity high, from advantages such as heavy and light, load-bearing capacity is big, anti-seismic performance good, easy construction, pollution-free, reusable edibles, but, its
Heat conductivity is big [52W/ (m K)], once runs into fire, and in 10-15min, its temperature can rise to 700 DEG C, considerably beyond
The critical temperature (540 DEG C) of self, now, loses hold because the yield strength of steel drastically drops to about the 40% of normal-temperature
Load power, can cause building to collapse.At present, China's many employings fire-resistant coating for steel structure carries out coating protection to it.For high level
The support column of civil buildings, general industry and civil buildings support the post of multilamellar, large-span steel Factory Building, petrochemical industry work
Journeys etc., the many employing fire endurance thick matter fire-resistant coating for steel structures more than more than 2.5h are protected.But thickness of the prior art
The fireproof coating of formed steel construction, although fire endurance more than 3 hours, coating layer thickness about 25mm, but owing to coating layer thickness is thick,
The phenomenon such as the most cracking, hollowing in work progress.Simultaneously in work progress, inevitably damage paint film, in order to
Prevent phenomenon and the use longevity of fireproof coating such as the most cracking in work progress, the hollowing of thicker fire-resistant coating for steel structure
Life, improves fireproof coating function and is very important.
Summary of the invention
For these reasons, applicant by studying for many years, obtain with 42.5R portland cement and Macrogol 2000 be
Compound adhesive, using alumina silicate fibre inorganic material as the fire-resistant coating for steel structure of the thick coated type of crack resistence thermal insulating filling, should
Thicker fireproof coating is a kind of low cost, excellent performance, easy construction, good endurance, has the Novel ring of broad development prospect
Friendly coating, this product has bond strength, water-tolerant, resistance to acids and bases is good, safety non-toxic, the amount of being fuming are few, cracking resistance and crack resistence
Property good, thick coated type steel structure fire-proof paint that fire protecting performance is excellent, the flame-proof finishing that can be widely applied to indoor and outdoor steel construction is protected
Protect.
The present invention is achieved through the following technical solutions.
The fireproof coating of a kind of thick coated type steel structure, this coating is multiple by 42.5R portland cement and Macrogol 2000
Close adhesive, using alumina silicate fibre inorganic material as crack resistence thermal insulating filling.
This coating is prepared from than raw material by following weight: 42.5R portland cement 25.0-35.0 weight portion, expansion trematodiasis
Stone 35-45 weight portion, cenosphere 5.0-8.0 weight portion, length 1-3mm alumina silicate fibre 0.3-1.0 weight portion, coal ash powder
5.0-8.0 weight portion, Macrogol 2000 1.0-2.5 weight portion, hydroxypropyl methyl cellulose 0.1-0.2 weight portion, meerschaum
Powder 4.0-6.0 weight portion, coating additive 4-5 weight portion.
This preparation method for coating is:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into
Alumina silicate fibre, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock,
Mix homogeneously, obtains coating.
The present invention has a following useful technique effect:
(1) thicker fireproof coating of the present invention is a kind of low cost, excellent performance, easy construction, good endurance, has extensively
The novel environment friendly coating of development prospect.
(2) thicker fireproof coating of the present invention is to have that bond strength, water-tolerant, resistance to acids and bases be good, safety non-toxic, be fuming
Amount is less, cracking resistance is good with crack resistence, fire protecting performance is excellent, can be widely applied to the flame-proof finishing protection of indoor and outdoor steel construction.
Coating additive of the present invention is purchased from Lian Biao Science and Technology Ltd. of Shenzhen, is the auxiliary agent of thicker fire-resistant coating for steel structure,
Its product batch number is 20160405.
Detailed description of the invention
Test 1
The impact of Macrogol 2000 consumption
Table 1 coating raw material
Preparation method for coating is as follows with technological process:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into
Alumina silicate fibre, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock,
Mix homogeneously, obtains coating.
In table 1 formula under conditions of ceteris paribus, the different amounts of Macrogol 2000 is to thick coated type steel structure
The impact of fire-proof corrosive-resistant paint performance is shown in Table 2.
Table 2 Macrogol 2000 and the impact on fire-proof corrosive-resistant paint performance of the alumina silicate fibre consumption
Conclusion (of pressure testing): as shown in Table 2, along with the increase of Macrogol 2000 consumption in formula, the bond strength of coating, anti-
Compressive Strength, resistance to water, cold-hot cyclicity and resistance to acids and bases improve the most accordingly, and especially bond strength and resistance to water improves aobvious
Writing, wherein test 4 groups and test 5 groups, properties is attained by or more than set quota in GB14907-2002 standard.
Preparation embodiment
Although embodiment of the invention below is described, but the invention is not limited in above-mentioned specific embodiment party
Case and application, following specific embodiments the most schematic, guiding rather than restrictive.This area
Those of ordinary skill under the enlightenment of this specification and in the case of the scope protected without departing from the claims in the present invention,
Can be to make a variety of forms, these belong to the row of present invention protection.
The present invention has a following useful technique effect:
(1) thicker fireproof coating of the present invention is a kind of low cost, excellent performance, easy construction, good endurance, has extensively
The novel environment friendly coating of development prospect;
(2) thicker fireproof coating of the present invention is to have that bond strength, water-tolerant, resistance to acids and bases be good, safety non-toxic, be fuming
Amount is less, cracking resistance is good with crack resistence, fire protecting performance is excellent, can be widely applied to the flame-proof finishing protection of indoor and outdoor steel construction.
Embodiment 1
Table 3 proportioning raw materials
Preparation method for coating is as follows with technological process:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into
Alumina silicate fibre, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock,
Mix homogeneously, obtains coating.
Embodiment 2
Table 4 proportioning raw materials
Sequence | Raw material title | kg |
1 | Portland cement 42.5R | 28 |
2 | Expanded vermiculite | 38 |
3 | Cenosphere | 5.5 |
4 | Alumina silicate fibre (length 1-3mm) | 0.5 |
5 | Coal ash powder | 6.5 |
6 | Macrogol 2000 | 1.4 |
7 | Hydroxypropyl methyl cellulose | 0.12 |
8 | Sepiolite powder | 4.5 |
9 | Coating additive | 4.5 |
Preparation method for coating is as follows with technological process:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into
Alumina silicate fibre, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock,
Mix homogeneously, obtains coating.
Embodiment 3
Table 5 proportioning raw materials
Sequence | Raw material title | kg |
1 | Portland cement 42.5R | 30 |
2 | Expanded vermiculite | 30 |
3 | Cenosphere | 6 |
4 | Alumina silicate fibre (length 1-3mm) | 0.7 |
5 | Coal ash powder | 7.0 |
6 | Macrogol 2000 | 1.8 |
7 | Hydroxypropyl methyl cellulose | 0.14 |
8 | Sepiolite powder | 5.0 |
9 | Coating additive | 4.5 |
Preparation method for coating is as follows with technological process:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into
Alumina silicate fibre, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock,
Mix homogeneously, obtains coating.
Embodiment 4
Table 6 proportioning raw materials
Sequence | Raw material title | kg |
1 | Portland cement 42.5R | 32 |
2 | Expanded vermiculite | 42 |
3 | Cenosphere | 7 |
4 | Alumina silicate fibre (length 1-3mm) | 0.8 |
5 | Coal ash powder | 7.4 |
6 | Macrogol 2000 | 2.2 |
7 | Hydroxypropyl methyl cellulose | 0.18 |
8 | Sepiolite powder | 5.5 |
9 | Coating additive | 4.5 |
Preparation method for coating is as follows with technological process:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into
Alumina silicate fibre, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock,
Mix homogeneously, obtains coating.
Embodiment 5
Table 7 proportioning raw materials
Sequence | Raw material title | kg |
1 | Portland cement 42.5R | 35 |
2 | Expanded vermiculite | 45 |
3 | Cenosphere | 8 |
4 | Alumina silicate fibre (length 1-3mm) | 1.0 |
5 | Coal ash powder | 8 |
6 | Macrogol 2000 | 2.5 |
7 | Hydroxypropyl methyl cellulose | 0.2 |
8 | Sepiolite powder | 6 |
9 | Coating additive | 5.0 |
Preparation method for coating is as follows with technological process:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into
Alumina silicate fibre, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock,
Mix homogeneously, obtains coating.
Application test:
Add suitable quantity of water stirring at low speed form slurry during by embodiment 3 coating application, spray or be applied in five steel basic units, construction
Shi Jiashui part by weight is: coating: water=1.0:1.2.Product is by country's fixed fire extinguishing system and fireproof construction quality surveillance inspection
Center of testing, by GB14907-2002 standard detection, the results are shown in Table 8.
Coating property index test of the present invention
The performance indications of table 8 embodiment 3 thick coated type steel structure fire-proof paint
Result and discussion: thick coated type steel structure fire-proof paint is usually non-expansion type coating.Simple by inorganic binder structure
Become thick-layered fire coating, also exist bond strength relatively low (being typically only 0.1MPa), resistance to water is poor, coating is hard and crisp,
It is easily generated the defects such as crackle, with Macrogol 2000, inorganic binder is modified, form compound adhesive system, be prepared as
Thick matter fireproof coating, is remarkably improved its bond strength, comprcssive strength, waterproof impervious characteristic, pliable and tough crack resistance, cold-hot circulation
Property, fire endurance value etc..
Raw material of the present invention is provided by following producer.
Table 9 is tested and embodiment raw material producer
Claims (3)
1. the fireproof coating of a thicker steel construction, it is characterised in that this coating is by 42.5R portland cement and Polyethylene Glycol
2000 is compound adhesive, using alumina silicate fibre inorganic material as crack resistence thermal insulating filling.
The fireproof coating of a kind of thicker steel construction the most according to claim 1, this coating by following weight than raw material system
For forming: 42.5R portland cement 25.0-35.0 weight portion, expanded vermiculite 35-45 weight portion, cenosphere 5.0-8.0 weight
Part, length 1-3mm alumina silicate fibre 0.3-1.0 weight portion, coal ash powder 5.0-8.0 weight portion, Macrogol 2000 1.0-2.5
Weight portion, hydroxypropyl methyl cellulose 0.1-0.2 weight portion, sepiolite powder 4.0-6.0 weight portion, coating additive 4-5 weight portion.
The fireproof coating of described a kind of thicker steel construction the most according to claim 2, this preparation method for coating is:
(1) sieve 1-3mm by expanded vermiculite, screens out coarse granule;
(2) by 42.5R portland cement, coal ash powder, sepiolite powder, addition dry powder blender, stirring is gradually added into silicic acid
Aluminum fiber, after inorfil is uniformly dispersed, adds coating additive, is eventually adding cenosphere and surplus stock, mixing
Uniformly, coating is obtained.