CN106278210A - 一种高致密度熔融石英陶瓷的制备方法 - Google Patents

一种高致密度熔融石英陶瓷的制备方法 Download PDF

Info

Publication number
CN106278210A
CN106278210A CN201610726915.XA CN201610726915A CN106278210A CN 106278210 A CN106278210 A CN 106278210A CN 201610726915 A CN201610726915 A CN 201610726915A CN 106278210 A CN106278210 A CN 106278210A
Authority
CN
China
Prior art keywords
powder
preparation
slip
vitreous silica
fused quartz
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610726915.XA
Other languages
English (en)
Inventor
麦浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bright Cities And Towns Gaoming District Foshan City New Forms Of Energy New Material Industry Innovation Centers
Original Assignee
Bright Cities And Towns Gaoming District Foshan City New Forms Of Energy New Material Industry Innovation Centers
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bright Cities And Towns Gaoming District Foshan City New Forms Of Energy New Material Industry Innovation Centers filed Critical Bright Cities And Towns Gaoming District Foshan City New Forms Of Energy New Material Industry Innovation Centers
Priority to CN201610726915.XA priority Critical patent/CN106278210A/zh
Publication of CN106278210A publication Critical patent/CN106278210A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高致密度熔融石英陶瓷的制备方法，包括：步骤A、将高纯熔融石英粉料进行混合；加入去离子水以及聚乙烯醇、乳酸、碳酸氢三钠制成固含量为75‑80vol%的料浆；B、将40wt%丙烯酰胺水溶液与N,N‑亚甲基双丙烯酰胺混合，搅拌溶解制得预混液；C、将步骤A中的料浆、烧结助剂、步骤B中的预混液进行混合，加入引发剂制成成型料浆；D、将步骤C中制得的成型料浆注入动态注凝成型装置的模具中，振动20‑30min，将坯体与模具一起放置于烘箱中进行固化，固化温度为72‑78℃，固化时间为3‑4h，冷却后打开模具即得所需陶瓷生坯；E、将步骤D中的生坯在高温炉中以1175‑1200℃温度烧制成型，保温时间为2‑3h，即制成所需熔融石英陶瓷。

Description

一种高致密度熔融石英陶瓷的制备方法
技术领域
本发明属于陶瓷材料领域，具体涉及一种高致密度熔融石英陶瓷的制备方法。
背景技术
石英陶瓷是指以石英玻璃或者熔融石英为原料，仅破碎、成型、烧成等一系列陶瓷制作工艺制得的制品，又称为熔融石英陶瓷、石英玻璃陶瓷。熔融石英陶瓷由于拥有优异的热震稳定性、低的热导率和低的热膨胀系数等一系列优良性能，在冶金、玻璃、化工、航天等多个领域得到越来越广泛的应用。熔融石英陶瓷主要具有以下优点：
1）热膨胀系数小。纯的熔融石英陶瓷热膨胀系数（室温条件下）仅为0.54×10-6/℃，与石英玻璃的热膨胀系数相同，具有良好的体积稳定性。因此熔融石英陶瓷具有良好的热震稳定性，可多次用于冷热交换的环境中。
2）熔融石英陶瓷具有良好的化学稳定性，除了氢氟酸以及300℃以上的热浓磷酸对其有侵蚀外，其他的酸碱液对石英陶瓷几乎没有作用。
3）熔融石英陶瓷具有稳定的热导率，随着温度的变化其热导率几乎不变。
4）熔融石英陶瓷的弯曲强度随着温度的升高而增加。
5）熔融石英陶瓷坯体在干燥烧成时收缩率非常小。
除上述优点以外，熔融石英陶瓷还具有好的电性能、核性能以及相转变性能等优点。熔融石英陶瓷虽然具有上述优良的特性，但是与其他结构陶瓷相比，其强度和致密性明显偏低，作为耐火材料使用足够，但是无法作为工业陶瓷使用。如何提升熔融石英陶瓷的致密度，从而提升熔融石英陶瓷的强度和物理性能是熔融石英陶瓷制备工艺的研究重点。
发明内容
传统石英陶瓷的生产过程中，普遍采用的成型工艺是注浆成型法，其次还有离心浇注成型、浇灌成型、蜡注成型、半干法成型、等静压成型等方法。上述这些方法中普遍存在显微结构不均匀、材料可靠性差、制品致密度低、强度低的缺点，而且效率低下、难以适应大批量工业化生产的需要。
本发明中考虑到传统成型工艺远不能满足各领域对熔融石英陶瓷的要求，采用注凝成型技术，将陶瓷粉末颗粒分散于含有有机聚合物和交联剂的熔液中，形成低粘度、高固相体积含量的浓悬浮体（即料浆），然后加入引发剂，将这种料浆注入模型中，在一定的温度条件下，有机聚合物交联形成三维网络状聚合物凝胶，并将陶瓷颗粒原位粘结固化形成坯体。该方法大大提高了陶瓷之间显微结构的均匀性，增加了陶瓷材料的可靠性。
本发明所要解决的技术问题通过以下步骤予以实现：
本发明提供的一种高致密度熔融石英陶瓷的制备方法，包括如下步骤：
A、将高纯熔融石英粉料进行混合，其中熔融石英粉料的粒度分布及所占质量分数为：5-8μm，2-5wt%；8-21μm，6-8wt%；21-58μm，10-20wt%；58-114μm，35-39wt%；114-160μm，18-25wt %；160-175μm，8-15 wt %；将上述高纯熔融石英粉料加入去离子水以及占粉料质量为0.25-0.3%的聚乙烯醇、0.35-0.42%的乳酸、0.1-0.2%碳酸氢三钠制成固含量为75-80vol%的料浆；
进一步优选原料，步骤A中的熔融石英粉料的纯度大于99.99wt%。
熔融石英粉料的选择直接关系着料浆的质量，料浆的性能则取决于液相和固相的性能以及液固两相的相互作用。熔融石英粉料的粒径分布很大一部分程度上决定了料浆中固相颗粒的状态，粉料颗粒的分散性则很大程度上取决于颗粒表面化学组成及吸附状态。制备料浆的主要目的是制备出组分均匀分布、稳定性好且流动性好的能够满足成形及坯体性能要求的料浆。
当熔融石英粉体颗粒的粒径小于20μm时，粉体颗粒会与水作用形成溶胶，适量溶胶的存在能够增加料浆的塑性，而过量的溶胶存在则会使料浆的粘度变大，触变性变强，加大浇注步骤中的难度。故本发明中，将熔融石英粉料粒度分为6个不同的范围，控制每个范围所占的质量百分数，即控制了料浆中形成的溶胶的量和料浆固体颗粒之间的作用及分布。聚乙烯醇和乳酸的加入可以使SiO2粉体颗粒的表面张力降低，润湿性提高，从而改善料浆的流动性。酒石酸可吸附于SiO2粉体颗粒表面，减弱体系内离子之间的吸引力，提升排斥力位能，使高固相料浆中含有足够的自由水，从而保持料浆具有良好的流动性。聚乙烯醇、乳酸、碳酸氢三钠作为分散剂和pH调节剂配合使用，控制其添加量能够有效改善SiO2粉体颗粒表面的润湿性，提升料浆的稳定性。
再进一步地，步骤A中的熔融石英粉料中还可添加占其质量百分比为0.35-0.65%的Si3N4粉体，所述加入的Si3N4粉体粒径为40-60μm。熔融石英粉体中加入Si3N4粉体可提升整体石英陶瓷的强度，在实际应用过程中发现，采用添加占SiO2粉体颗粒质量百分比为0.35-0.65%的50-80μm的Si3N4粉体最佳。
再进一步地，步骤A中的熔融石英粉料中还可添加占其质量百分比为0.35-0.65%的二氧化硅气凝胶粉体。所述二氧化硅气凝胶比表面积为400-500m2/g，密度为65kg/m3。二氧化硅气凝胶具有大的比表面积和高的孔隙率，在料浆中具有良好的分散性和悬浮性，能够有效调节料浆的黏度和触变性能，适量添加可促进料浆均匀分散和增强其流动性。
B、将40wt%丙烯酰胺水溶液与N,N-亚甲基双丙烯酰胺以质量比21.2-25:1进行混合，搅拌溶解制得预混液；
进一步优选，步骤B中40wt%丙烯酰胺水溶液与N,N-亚甲基双丙烯酰胺的质量比为22-23:1。
C、将步骤A中的料浆、烧结助剂、步骤B中的预混液以质量比为38-42:1:2-4进行混合，以450-800r/min转速下分散30-60min，然后加入占预混液质量1.5-4%的过硫酸铵，搅拌均匀后得到成型料浆；
本发明中采用的注凝成型技术中选择使用丙烯酰胺及N,N-亚甲基双丙烯酰胺的预混液作为液体介质，采用过硫酸铵作为引发剂，在成型的过程中利用丙烯酰胺的聚合反应完成料浆的固化。丙烯酰胺的聚合反应过程为：首先引发剂分解，形成初级自由基，初级自由基与单体加成，生成单体自由基，单体自由基不断与单体分子结合，形成链自由基，上述反应不断进行，生成聚丙烯酰胺长链聚合物，最终完成单体的聚合反应。料浆通过丙烯酰胺的聚合反应完成固化成型，成型的坯体以聚丙烯酰胺的网络结构为骨架，石英粉料颗粒与聚合物凝胶通过吸附作用形成具有一定强度和韧性的坯体。
进一步优选，步骤C中的烧结助剂为氧化铝粉体、氧化锆粉体、碳化锆粉体、氮化硼粉体中的一种。所述烧结助剂粉体粒度为20-30μm。
D、将步骤C中制得的成型料浆注入动态注凝成型装置的模具中，振动20-30min，将坯体与模具一起放置于烘箱中进行固化，固化温度为72-78℃，固化时间为3-4h，冷却后打开模具即得所需陶瓷生坯。
E、将步骤D中的生坯在高温炉中以1175-1200℃温度烧制成型，保温时间为2-3h，即制成所需熔融石英陶瓷。
进一步地，步骤E中烧制成型步骤具体为：以3-5℃/min由室温升至900℃，保温10min后，再以6-8℃/min升至1175-1200℃，保温后随炉冷却。
熔融石英陶瓷收到方石英析晶的影响，烧制成型的温度不宜超过1300℃，本发明中的熔融石英陶瓷烧结在900℃时开始，然后通过快速升温至所需烧结温度，可在最大程度上控制烧制成型的收缩率。添加适量的烧结助剂有助于进一步提高注凝成型制品的烧结程度和致密程度。
本发明具有如下有益效果：
1、本发明提供的一种熔融石英陶瓷的制备方法采用注凝成型技术，将陶瓷粉末颗粒分散于含有有机聚合物和交联剂的溶液中，形成低粘度、高固相体积含量的浓悬浮体（即料浆），然后加入引发剂，将这种料浆注入模型中，在一定的温度条件下，有机聚合物交联形成三维网络状聚合物凝胶，并将陶瓷颗粒原位粘结固化形成坯体。该方法大大提高了陶瓷之间显微结构的均匀性，增加了陶瓷材料的可靠性。
2、本发明中提供的制备方法制备出的熔融石英陶瓷制品致密度高、强度好，能够作为工业陶瓷使用。
3、本发明中提供的熔融石英陶瓷的制备方法工艺简单易行，无需额外的加工设备，可进行大规模工业化生产。
具体实施方式
下面通过实施例对本发明的内容进行进一步的描述。
实施例1
1、熔融石英成型料浆的制备
实施例中原料采用纯度大于99.99wt%的熔融石英粉料。
将高纯熔融石英粉料按照以下粒度分布及所占质量百分数进行混合：5-8μm，5wt%；8-21μm，8wt%；21-58μm，15wt%；58-114μm，36wt%；114-160μm，21 wt %；160-175μm，15wt %。将上述高纯熔融石英粉料加入去离子水以及占粉料质量为0.26%的聚乙烯醇、0.38%的乳酸、0.2%碳酸氢三钠制成固含量为80vol%的料浆。
将40wt%丙烯酰胺水溶液与N,N-亚甲基双丙烯酰胺以质量比23:1进行混合，搅拌溶解制得预混液。
将上述制得的料浆、氧化锆粉、预混液以质量比40:1:4进行混合，在750r/min转速下分散60min，然后加入占预混液质量3.5%的过硫酸铵，搅拌均匀后得到成型料浆。其中氧化锆粉粉体粒度为25μm。
2、生坯及烧成
将成型料浆注入动态注凝成型装置的模具中，振动30min，将坯体与模具一起放置于烘箱中进行固化，固化温度为75℃，固化时间为4h，冷却后打开模具即得所需陶瓷生坯。
将生坯在高温炉中以1185℃条件下烧制成型，保温2h，随炉冷却后得到所需熔融石英陶瓷。烧制成型步骤具体为：以3℃/min由室温升至900℃，保温10min后，再以8℃/min升至1185℃，保温后随炉冷却。
实施例2
本实施例中工艺条件及原料与实施例1保持一致，不同点在于：在熔融石英粉料中添加占其质量百分为为0.55%的Si3N4粉体，且Si3N4粉体粒径为45μm。
实施例3
本实施例中工艺条件及原料与实施例1保持一致，不同点在于：在熔融石英粉料中添加占其质量百分为为0.5%的二氧化硅气凝胶微粉，二氧化硅气凝胶比表面积为450m2/g，密度为65kg/m3。
实施例4
本实施例中工艺条件及原料与实施例1保持一致，不同点在于：烧结助剂采用粒度为25μm的氧化铝粉体。
实施例5
本实施例中工艺条件及原料与实施例1保持一致，不同点在于：烧结助剂采用粒度为25μm的碳化锆粉体。
实施例6
本实施例中工艺条件及原料与实施例1保持一致，不同点在于：烧结助剂采用粒度为25μm的氮化硼粉体。
实施例1-6中所制得的熔融石英陶瓷制品表面光滑平整无任何表面凸起（一般为由析晶引起的缺陷）、致密度高。实施例2中的熔融石英陶瓷制品强度最佳，实施例3中的熔融石英陶瓷制品致密度最佳，实施例4-6中的熔融石英陶瓷制品与实施例1中制得的熔融石英陶瓷制品无显著区别。
最后需要说明的是，以上实施例仅用以说明本发明实施例的技术方案而非对其进行限制，尽管参照较佳实施例对本发明实施例进行了详细的说明，本领域的普通技术人员应当理解依然可以对本发明实施例的技术方案进行修改或者等同替换，而这些修改或者等同替换亦不能使修改后的技术方案脱离本发明实施例技术方案的范围。

Claims (10)

1.一种高致密度熔融石英陶瓷的制备方法，其特征在于包括如下步骤：
A、将高纯熔融石英粉料进行混合，其中熔融石英粉料的粒度分布及所占质量分数为：5-8μm，2-5wt%；8-21μm，6-8wt%；21-58μm，10-20wt%；58-114μm，35-39wt%；114-160μm，18-25wt %；160-175μm，8-15 wt %；将上述高纯熔融石英粉料加入去离子水以及占粉料质量为0.25-0.3%的聚乙烯醇、0.35-0.42%的乳酸、0.1-0.2%碳酸氢三钠制成固含量为75-80vol%的料浆；
B、将40wt%丙烯酰胺水溶液与N,N-亚甲基双丙烯酰胺以质量比21.2-25:1进行混合，搅拌溶解制得预混液；
C、将步骤A中的料浆、烧结助剂、步骤B中的预混液以质量比为38-42:1:2-4进行混合，以450-800r/min转速下分散30-60min，然后加入占预混液质量1.5-4%的过硫酸铵，搅拌均匀后得到成型料浆；
D、将步骤C中制得的成型料浆注入动态注凝成型装置的模具中，振动20-30min，将坯体与模具一起放置于烘箱中进行固化，固化温度为72-78℃，固化时间为3-4h，冷却后打开模具即得所需陶瓷生坯；
E、将步骤D中的生坯在高温炉中以1175-1200℃温度烧制成型，保温时间为2-3h，即制成所需熔融石英陶瓷。
2.如权利要求1所述的制备方法，其特征在于：步骤A中的熔融石英粉料的纯度大于99.99wt%。
3.如权利要求1所述的制备方法，其特征在于：步骤A中的熔融石英粉料中还可添加占其质量百分比为0.35-0.65%的Si3N4粉体。
4.如权利要求1所述的制备方法，其特征在于：所述加入的Si3N4粉体粒径为40-60μm。
5.如权利要求1所述的制备方法，其特征在于：步骤A中的熔融石英粉料中还可添加占其质量百分比为0.35-0.65%的二氧化硅气凝胶粉体。
6.如权利要求5所述的制备方法，其特征在于：所述二氧化硅气凝胶比表面积为400-500m2/g，密度为65kg/m3。
7.如权利要求1所述的制备方法，其特征在于：步骤B中40wt%丙烯酰胺水溶液与N,N-亚甲基双丙烯酰胺的质量比为22-23:1。
8.如权利要求1所述的制备方法，其特征在于：步骤C中的烧结助剂为氧化铝粉体、氧化锆粉体、碳化锆粉体、氮化硼粉体中的一种。
9.如权利要求8所述的制备方法，其特征在于：所述烧结助剂粉体粒度为20-30μm。
10.如权利要求1所述的制备方法，其特征在于：步骤E中烧制成型步骤具体为：以3-5℃/min由室温升至900℃，保温10min后，再以6-8℃/min升至1175-1200℃，保温后随炉冷却。
CN201610726915.XA 2016-08-26 2016-08-26 一种高致密度熔融石英陶瓷的制备方法 Pending CN106278210A (zh)