CN106243948A - Separating zipper - Google Patents
Separating zipper Download PDFInfo
- Publication number
- CN106243948A CN106243948A CN201610788875.1A CN201610788875A CN106243948A CN 106243948 A CN106243948 A CN 106243948A CN 201610788875 A CN201610788875 A CN 201610788875A CN 106243948 A CN106243948 A CN 106243948A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight portion
- parts
- protective paint
- chain belt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of separating zipper, its metal tooth surface is covered with protective paint, protective paint is made by the steps: 1) 1～2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc, 1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin is put into successively in 25 parts by weight of deionized water, stirs；2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portion DC11s, 1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums are put into the most successively, continue stirring, to being sufficiently mixed uniformly, prepare protective paint.Separating zipper of the present invention, its metal tooth surface-coated has protective paint, can ensure slide fastener life-time service.
Description
Technical field
The present invention relates to a kind of separating zipper.
Background technology
Existing slide fastener, wear-resisting, the antioxidation of its metal tooth, antirust, decay resistance have much room for improvement, and affect the length of slide fastener
Phase uses.
Summary of the invention
It is an object of the invention to provide a kind of separating zipper, its metal tooth is coated with protective paint, makes metallic bond toilet article
There are wear-resisting, antioxidation, antirust, the decay resistance of excellence, thus ensure slide fastener energy life-time service.
For achieving the above object, the technical scheme is that a kind of separating zipper of design, including chain belt, this chain belt is longitudinally
Edge is provided with chain tooth, and this metal tooth surface is covered with protective paint, and described protective paint is made by the steps:
1) by 1～2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro
Zinc, 1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
Preferably, separating zipper, including chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered with
Protective paint, described protective paint is made by the steps:
1) by 1 weight portion three ester in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc,
1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
Preferably, separating zipper, including chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered with
Protective paint, described protective paint is made by the steps:
1) by 2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc,
1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
Preferably, separating zipper, including chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered with
Protective paint, described protective paint is made by the steps:
1) by 1.2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro
Zinc, 1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
Advantages of the present invention and having the beneficial effects that: providing a kind of separating zipper, its metal tooth is coated with protective paint, makes
Metal tooth has wear-resisting, antioxidation, antirust, the decay resistance of excellence, thus ensures slide fastener energy life-time service.
Performance and the purposes of " protective paint " are determined by its component and proportioning, and the different component meeting in " protective paint "
Influencing each other, component and proportioning thereof can determine the final performance of " protective paint ", as the most mutually coordinated in fruit component and proportioning thereof, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, and the when of serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
Paint " optimal component and proportioning so that multiple components combine, mutually coordinated and produce forward comprehensive effect.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.Following example are only used for more
Add and clearly demonstrate technical scheme, and can not limit the scope of the invention with this.
The technical scheme that the present invention is embodied as is:
Embodiment 1
Separating zipper, including chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered with protective paint,
Described protective paint is made by the steps:
1) by 1～2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro
Zinc, 1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
Embodiment 2
Separating zipper, including chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered with protective paint,
Described protective paint is made by the steps:
1) by 1 weight portion three ester in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc,
1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
Embodiment 3
Separating zipper, including chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered with protective paint,
Described protective paint is made by the steps:
1) by 2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc,
1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
Embodiment 4
Separating zipper, including chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered with protective paint,
Described protective paint is made by the steps:
1) by 1.2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro
Zinc, 1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions are put into the most successively
DC11,1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring,
To being sufficiently mixed uniformly, prepare protective paint.
The separating zipper of the various embodiments described above, its metal tooth is coated with protective paint, makes metal tooth have the resistance to of excellence
Mill, antioxidation, antirust, decay resistance, thus ensure slide fastener energy life-time service.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvements and modifications, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. separating zipper, it is characterised in that include chain belt, this chain belt longitudinal edge is provided with chain tooth, and this metal tooth surface is covered
Protective paint, described protective paint is had to be made by the steps:
1) by 1～2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc,
1.5 weight portion carboxymethyl celluloses, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions 11 are put into the most successively
Carbon dicarboxylic acid, 1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring, to filling
Divide mix homogeneously, prepare protective paint.
Separating zipper the most according to claim 1, it is characterised in that include chain belt, this chain belt longitudinal edge is provided with chain tooth,
This metal tooth surface is covered with protective paint, and described protective paint is made by the steps:
1) by 1 weight portion three ester in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc, 1.5 weights
Amount part carboxymethyl cellulose, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions 11 are put into the most successively
Carbon dicarboxylic acid, 1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring, to filling
Divide mix homogeneously, prepare protective paint.
Separating zipper the most according to claim 1, it is characterised in that include chain belt, this chain belt longitudinal edge is provided with chain tooth,
This metal tooth surface is covered with protective paint, and described protective paint is made by the steps:
1) by 2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc, 1.5 weights
Amount part carboxymethyl cellulose, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions 11 are put into the most successively
Carbon dicarboxylic acid, 1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring, to filling
Divide mix homogeneously, prepare protective paint.
Separating zipper the most according to claim 1, it is characterised in that include chain belt, this chain belt longitudinal edge is provided with chain tooth,
This metal tooth surface is covered with protective paint, and described protective paint is made by the steps:
1) by 1.2 weight portion three esters in the last of the ten Heavenly stems, 1.5 weight portion 2-Sulfosuccinic acid Diisooctyl sodium, 0.5 parts by weight of phosphoric acid dihydro zinc, 1.5
Weight portion carboxymethyl cellulose, 15 weight portion alkyd resin put in 25 parts by weight of deionized water successively, stir；
2) 0.4 parts by weight epoxy resin coated ammonium polyphosphate, 2.6 parts by weight acetic acid butyl esters, 2.1 weight portions 11 are put into the most successively
Carbon dicarboxylic acid, 1.7 weight portion ATMPs, 1.1 weight portion chloro distearyl dimethyl ammoniums, continue stirring, to filling
Divide mix homogeneously, prepare protective paint.