CN106238657B - 一种螺旋桨轴锻造工艺 - Google Patents
一种螺旋桨轴锻造工艺 Download PDFInfo
- Publication number
- CN106238657B CN106238657B CN201610706817.XA CN201610706817A CN106238657B CN 106238657 B CN106238657 B CN 106238657B CN 201610706817 A CN201610706817 A CN 201610706817A CN 106238657 B CN106238657 B CN 106238657B
- Authority
- CN
- China
- Prior art keywords
- heated
- circular arc
- swage block
- temperature
- hours
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种螺旋桨轴锻造工艺，其特征在于：包括如下步骤：1)、第一火将坯料的钢锭加热温度至1100~1220℃，保温6~8小时，压钳口，倒棱，去锭底；2)、第二火对1)步获得的坯材进行再次加热，加热至1220~1250℃，保温16小时，采用圆弧齿状上凸下凹型砧镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1100~1220℃，采用圆弧齿状上凸下凹型砧镦粗，拔长至规定尺寸，切边；4)、热处理：加热至600±10°C保温7~9小时，空冷至300°C，加热至500±10°C，空冷。该工艺生产的产品内部变形均匀，易于成形，锻件内部质量好，提高了锻件的使用寿命。
Description
技术领域
本发明属于锻造技术领域，尤其涉及一种螺旋桨轴锻造工艺。
背景技术
螺旋桨轴属于船用锻件，随着世界船舶工业的迅速发展，船用锻件规格越来越大，技术要求越来越高，生产难度越来越大，大型钢锭中存在非金属夹杂物、气体、偏析、中心带粗晶、空洞和疏松等缺陷，大型锻件质量控制的核心问题是压实空洞性缺陷改变偏析以及防止表面开裂。
发明内容
本发明的目的为了解决上述技术问题，提供一种螺旋桨轴锻造工艺，该工艺使锻坯心部和次表层金属同时获得较大的变形量，等效应变的分布更加均匀，易于成形压实，克服了内部变形不均匀和偏析的缺陷。其技术方案如下：一种螺旋桨轴锻造工艺，其特征在于：包括如下步骤：1)、第一火将坯材的钢锭加热温度至1100～1220℃，保温6～8小时，压钳口，倒棱，去锭底；2)、第二火对1)步获得的坯材进行再次加热，加热至1220～1250℃，保温16小时，采用圆弧齿状上凸下凹型砧镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1100～1220℃，采用圆弧齿状上凸下凹型砧镦粗，拔长至规定尺寸，切边；4)、热处理：加热至600±10℃保温7～9小时，空冷至300℃，加热至500±10℃，空冷.；所述圆弧齿状上凸下凹型砧，包括上型砧和下型砧，上型砧为两侧锥面凸起到中间设置成凸出的两个以上相等半径的圆弧凸面，且相邻圆弧凸面之间由圆弧曲面光滑过渡，下型砧为V型锥面凹陷至中间设置成凸出的两个以上相等半径的圆弧凸面，相邻的圆弧凸面之间由圆弧曲面光滑过渡，所述圆弧凸面与V型锥面之间也由圆弧曲面光滑过渡，所述两侧锥面夹角和V型锥面夹角相等都为α，α可在135°～155°范围之内变化。
与现有技术相比，本发明的优点是：内部变形均匀，易于成形，锻件内部质量好，提高了锻件的使用寿命。
具体实施方式
实施例一
一种螺旋桨轴锻造工艺，其特征在于：包括如下步骤：1)、第一火将坯材的钢锭加热温度至1100℃，保温6小时，压钳口，倒棱，去锭底；2)、第二火对1)步获得的坯材进行再次加热，加热至1220℃，保温16小时，采用圆弧齿状上凸下凹型砧镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1100℃，采用圆弧齿状上凸下凹型砧镦粗，拔长至规定尺寸，切边；4)、热处理：加热至590℃保温7小时，空冷至300℃，加热至490℃，空冷.；所述圆弧齿状上凸下凹型砧，包括上型砧和下型砧，上型砧为两侧锥面凸起到中间设置成凸出的两个以上相等半径的圆弧凸面，且相邻圆弧凸面之间由圆弧曲面光滑过渡，下型砧为V型锥面凹陷至中间设置成凸出的两个以上相等半径的圆弧凸面，相邻的圆弧凸面之间由圆弧曲面光滑过渡，所述圆弧凸面与V型锥面之间也由圆弧曲面光滑过渡，所述两侧锥面夹角和V型锥面夹角相等都为α，α为135°。
实施例二
一种螺旋桨轴锻造工艺，其特征在于：包括如下步骤：1)、第一火将坯材的钢锭加热温度至1110℃，保温7小时，压钳口，倒棱，去锭底；2)、第二火对1)步获得的坯材进行再次加热，加热至1230℃，保温16小时，采用圆弧齿状上凸下凹型砧镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1110℃，采用圆弧齿状上凸下凹型砧镦粗，拔长至规定尺寸，切边；4)、热处理：加热至600℃保温8小时，空冷至300℃，加热至500℃，空冷.；所述圆弧齿状上凸下凹型砧，包括上型砧和下型砧，上型砧为两侧锥面凸起到中间设置成凸出的两个以上相等半径的圆弧凸面，且相邻圆弧凸面之间由圆弧曲面光滑过渡，下型砧为V型锥面凹陷至中间设置成凸出的两个以上相等半径的圆弧凸面，相邻的圆弧凸面之间由圆弧曲面光滑过渡，所述圆弧凸面与V型锥面之间也由圆弧曲面光滑过渡，所述两侧锥面夹角和V型锥面夹角相等都为α，α为145°。
实施例三
一种螺旋桨轴锻造工艺，其特征在于：包括如下步骤：1)、第一火将坯材的钢锭加热温度至1220℃，保温8小时，压钳口，倒棱，去锭底；2)、第二火对1)步获得的坯材进行再次加热，加热至1250℃，保温16小时，采用圆弧齿状上凸下凹型砧镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1220℃，采用圆弧齿状上凸下凹型砧镦粗，拔长至规定尺寸，切边；4)、热处理：加热至610℃保温9小时，空冷至300℃，加热至510℃，空冷.；所述圆弧齿状上凸下凹型砧，包括上型砧和下型砧，上型砧为两侧锥面凸起到中间设置成凸出的两个以上相等半径的圆弧凸面，且相邻圆弧凸面之间由圆弧曲面光滑过渡，下型砧为V型锥面凹陷至中间设置成凸出的两个以上相等半径的圆弧凸面，相邻的圆弧凸面之间由圆弧曲面光滑过渡，所述圆弧凸面与V型锥面之间也由圆弧曲面光滑过渡，所述两侧锥面夹角和V型锥面夹角相等都为α，α为155°。
Claims (1)
1.一种螺旋桨轴锻造工艺，其特征在于：包括如下步骤：1)、第一火将坯材的钢锭加热温度至1100～1220℃，保温6～8小时，压钳口，倒棱，去锭底；2)、第二火对1)步获得的坯材进行再次加热，加热至1220～1250℃，保温16小时，采用圆弧齿状上凸下凹型砧镦粗，拔长；3)、第三火对2)步获得的坯材进行再次加热，加热至1100～1220℃，采用圆弧齿状上凸下凹型砧镦粗，拔长至规定尺寸，切边；4)、热处理：加热至600±10℃保温7～9小时，空冷至300℃，加热至500±10℃，空冷；所述圆弧齿状上凸下凹型砧，包括上型砧和下型砧，上型砧为两侧锥面凸起到中间设置成凸出的两个以上相等半径的圆弧凸面，且相邻圆弧凸面之间由圆弧曲面光滑过渡，下型砧为V型锥面凹陷至中间设置成凸出的两个以上相等半径的圆弧凸面，相邻的圆弧凸面之间由圆弧曲面光滑过渡，所述圆弧凸面与V型锥面之间也由圆弧曲面光滑过渡，所述两侧锥面夹角和V型锥面夹角相等都为α，α可在135°～155°范围之内变化。