CN106220069A - A kind of environment-friendly type finishing material and preparation method - Google Patents
A kind of environment-friendly type finishing material and preparation method Download PDFInfo
- Publication number
- CN106220069A CN106220069A CN201610637232.7A CN201610637232A CN106220069A CN 106220069 A CN106220069 A CN 106220069A CN 201610637232 A CN201610637232 A CN 201610637232A CN 106220069 A CN106220069 A CN 106220069A
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly type
- finishing material
- type finishing
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of environment-friendly type finishing material and preparation method, environment-friendly type finishing material is by major ingredient, aggregate, filler, auxiliary agent and additive composition, wherein major ingredient is by redispersable latex powder, cellulose, lignin, polypropylene fibre forms, aggregate is by cement, ash calcium, Gypsum Fibrosum powder forms, filler is with triple superphosphate, fine particle calcium carbonate, kieselguhr, Pulvis Talci forms, auxiliary agent is by starch ether, bentonite, Kaolin, medical stone powder, titanium dioxide and noble metal catalyst composition, additive is made up of pigment and antifungus agent, material prepared by the present invention has stronger adsorptivity and ion exchangeable, compared with mill run, it is greatly improved its absorption harmful substance and catalytic decomposition ability, have the effects such as fungus and mildew resistance concurrently simultaneously.
Description
Technical field
The present invention relates to building material field, be specifically related to a kind of environment-friendly type finishing material and preparation method.
Background technology
Along with the development in epoch, the public place finishing such as household, school, market, hotel is more and more, occurs finishing therewith
A large amount of releases of the harmful gas of material, work and life to people brings puzzlement greatly, healthy to people
Being negatively affected, to this end, some environment-friendly type finishing materials just receive the favor of consumers in general, environmental protection finishing material does not contains
Evil chemical substance, does not fire except having, sound insulation, in addition to the feature such as waterproof, lightweight and heat insulation, also has dehumidifying, deodorization, clean room
Interior air etc. act on, but existing product need to improve at aspects such as moisture absorption, bacteria mildew-proof, harmful substance decomposition.
Summary of the invention
The problem existed for prior art, the invention provides that a kind of preparation technology is simple, formula design science is reasonable
Environment friendly decorative material and preparation method, obtained product has preferable combination property.
A kind of environment-friendly type finishing material and preparation method, wherein environment-friendly type finishing material by following components according to part by weight
Composition: redispersable latex powder: 1-3 part, cellulose: 0.3-0.8 part, lignin: 0.2-0.5 part, polypropylene fibre: 0.1-
0.5 part, cement: 50-60 part, ash calcium: 2-5 part, Gypsum Fibrosum powder: 0.3-0.5 part, triple superphosphate: 20-25 part, fine particle calcium carbonate: 5-10 part, Talcum
Powder: 3-5 part, kieselguhr: 25-40 part, starch ether: 0.05-0.15 part, bentonite: 3-5 part, Kaolin: 0.1-0.5 part, wheat meal
Stone powder: 0.1-0.3 part, titanium dioxide: 0.3-0.5 part, pigment: 0.3-0.5 part, antifungus agent: 0.1-0.5 part, precious metal catalyst
Agent: 0.2-0.5 part.
A kind of environment-friendly type finishing material and preparation method, main preparation process is as follows:
(1) it is first according to part by weight and weighs environment-friendly type finishing material major ingredient, aggregate, filler, auxiliary agent and additive each component unit
Element, is individually positioned in dustless hermetic container；
(2) by redispersable latex powder, cellulose, lignin, polypropylene fibre, cement, ash calcium, Gypsum Fibrosum powder, triple superphosphate, fine particle calcium carbonate,
Kieselguhr and Pulvis Talci add blender and are sufficiently stirred for, and mixing time is 10-30 minute；
(3) starch ether, bentonite, Kaolin, medical stone powder, titanium dioxide, noble metal catalyst and antifungus agent are added stirring
Machine carries out reverse agitating function, and mixing time is 10-30 minute；
(4) in blender, add pigment, judge according to the uniformity of stirring, forward stirring 10-20 minute, reverse agitating function 10-
20 minutes, blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30-60 DEG C dry 5-30 hour, will use after drying
Polyethylene packaging bag carries out subpackage, packs.
Detailed description of the invention
Embodiment 1
A kind of environment-friendly type finishing material and preparation method, wherein environment-friendly type finishing material by following components according to part by weight group
Become: redispersable latex powder: 1 part, cellulose: 0.3 part, lignin: 0.2 part, polypropylene fibre: 0.1 part, cement: 50 parts, ash
Calcium: 2 parts, Gypsum Fibrosum powder: 0.3 part, triple superphosphate: 20 parts, fine particle calcium carbonate: 5 parts, Pulvis Talci: 3 parts, kieselguhr: 25 parts, starch ether: 0.05 part,
Bentonite: 3 parts, Kaolin: 0.1 part, medical stone powder: 0.1 part, titanium dioxide: 0.3 part, pigment: 0.3 part, antifungus agent: 0.1
Part, noble metal catalyst: 0.2 part.
A kind of environment-friendly type finishing material and preparation method, main preparation process is as follows:
(1) it is first according to part by weight and weighs environment-friendly type finishing material major ingredient, aggregate, filler, auxiliary agent and additive each component unit
Element, is individually positioned in dustless hermetic container；
(2) by redispersable latex powder, cellulose, lignin, polypropylene fibre, cement, ash calcium, Gypsum Fibrosum powder, triple superphosphate, fine particle calcium carbonate,
Kieselguhr and Pulvis Talci add blender and are sufficiently stirred for, and mixing time is 10 minutes；
(3) starch ether, bentonite, Kaolin, medical stone powder, titanium dioxide, noble metal catalyst and antifungus agent are added stirring
Machine carries out reverse agitating function, and mixing time is 10 minutes；
(4) in blender, add pigment, judge according to the uniformity of stirring, forward stirring 10 minutes, reverse agitating function 10 minutes,
Blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30 DEG C are dried 5 hours, will use polyethylene after drying
Packaging bag carries out subpackage, packs.
Embodiment 2
A kind of environment-friendly type finishing material and preparation method, wherein environment-friendly type finishing material by following components according to part by weight group
Become: redispersable latex powder: 3 parts, cellulose: 0.8 part, lignin: 0.5 part, polypropylene fibre: 0.5 part, cement: 60 parts, ash
Calcium: 5 parts, Gypsum Fibrosum powder: 0.5 part, triple superphosphate: 25 parts, fine particle calcium carbonate: 10 parts, Pulvis Talci: 5 parts, kieselguhr: 40 parts, starch ether: 0.15 part,
Bentonite: 5 parts, Kaolin: 0.5 part, medical stone powder: 0.3 part, titanium dioxide: 0.5 part, pigment: 0.5 part, antifungus agent: 0.5
Part, noble metal catalyst: 0.5 part.
A kind of environment-friendly type finishing material and preparation method, main preparation process is as follows:
(1) it is first according to part by weight and weighs environment-friendly type finishing material major ingredient, aggregate, filler, auxiliary agent and additive each component unit
Element, is individually positioned in dustless hermetic container；
(2) by redispersable latex powder, cellulose, lignin, polypropylene fibre, cement, ash calcium, Gypsum Fibrosum powder, triple superphosphate, fine particle calcium carbonate,
Kieselguhr and Pulvis Talci add blender and are sufficiently stirred for, and mixing time is 10 minutes；
(3) starch ether, bentonite, Kaolin, medical stone powder, titanium dioxide, noble metal catalyst and antifungus agent are added stirring
Machine carries out reverse agitating function, and mixing time is 30 minutes；
(4) in blender, add pigment, judge according to the uniformity of stirring, forward stirring 20 minutes, reverse agitating function 20 minutes,
Blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30 DEG C are dried 30 hours, will use polyethylene after drying
Packaging bag carries out subpackage, packs.
Embodiment 3
A kind of environment-friendly type finishing material and preparation method, wherein environment-friendly type finishing material by following components according to part by weight group
Become: redispersable latex powder: 1 part, cellulose: 0.8 part, lignin: 0.2 part, polypropylene fibre: 0.3 part, cement: 55 parts, ash
Calcium: 2 parts, Gypsum Fibrosum powder: 0.3 part, triple superphosphate: 20 parts, fine particle calcium carbonate: 5 parts, Pulvis Talci: 3 parts, kieselguhr: 29 parts, starch ether: 0.05 part,
Bentonite: 3 parts, Kaolin: 0.1 part, medical stone powder: 0.1 part, titanium dioxide: 0.5 part, pigment: 0.3 part, antifungus agent: 0.3
Part, noble metal catalyst: 0.3 part.
A kind of environment-friendly type finishing material and preparation method, main preparation process is as follows:
(1) it is first according to part by weight and weighs environment-friendly type finishing material major ingredient, aggregate, filler, auxiliary agent and additive each component unit
Element, is individually positioned in dustless hermetic container；
(2) by redispersable latex powder, cellulose, lignin, polypropylene fibre, cement, ash calcium, Gypsum Fibrosum powder, triple superphosphate, fine particle calcium carbonate,
Kieselguhr and Pulvis Talci add blender and are sufficiently stirred for, and mixing time is 10 minutes；
(3) starch ether, bentonite, Kaolin, medical stone powder, titanium dioxide, noble metal catalyst and antifungus agent are added stirring
Machine carries out reverse agitating function, and mixing time is 30 minutes；
(4) in blender, add pigment, judge according to the uniformity of stirring, forward stirring 20 minutes, reverse agitating function 10 minutes,
Blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30 DEG C are dried 5 hours, will use polyethylene after drying
Packaging bag carries out subpackage, packs.
Claims (2)
1. an environment-friendly type finishing material and preparation method, it is characterised in that environment-friendly type finishing material by following components according to weight
Amount ratio forms: redispersable latex powder: 1-3 part, cellulose: 0.3-0.8 part, lignin: 0.2-0.5 part, polypropylene fibre:
0.1-0.5 part, cement: 50-60 part, ash calcium: 2-5 part, Gypsum Fibrosum powder: 0.3-0.5 part, triple superphosphate: 20-25 part, fine particle calcium carbonate: 5-10 part,
Pulvis Talci: 3-5 part, kieselguhr: 25-40 part, starch ether: 0.05-0.15 part, bentonite: 3-5 part, Kaolin: 0.1-0.5 part,
Medical stone powder: 0.1-0.3 part, titanium dioxide: 0.3-0.5 part, pigment: 0.3-0.5 part, antifungus agent: 0.1-0.5 part, noble metal
Catalyst: 0.2-0.5 part.
A kind of environment-friendly type finishing material the most according to claim 1 and preparation method, it is characterised in that main preparation process
As follows:
(1) it is first according to part by weight and weighs environment-friendly type finishing material major ingredient, aggregate, filler, auxiliary agent and additive each component unit
Element, is individually positioned in dustless hermetic container；
(2) by redispersable latex powder, cellulose, lignin, polypropylene fibre, cement, ash calcium, Gypsum Fibrosum powder, triple superphosphate, fine particle calcium carbonate,
Kieselguhr and Pulvis Talci add blender and are sufficiently stirred for, and mixing time is 10-30 minute；
(3) starch ether, bentonite, Kaolin, medical stone powder, titanium dioxide, noble metal catalyst and antifungus agent are added stirring
Machine carries out reverse agitating function, and mixing time is 10-30 minute；
(4) in blender, add pigment, judge according to the uniformity of stirring, forward stirring 10-20 minute, reverse agitating function 10-
20 minutes, blender can be closed；
(5) material after stirring is inserted drying baker and is dried, and 30-60 DEG C dry 5-30 hour, will use after drying
Polyethylene packaging bag carries out subpackage, packs.