CN107572882A - A kind of preparation method of environmental type constructional ornamental material - Google Patents
A kind of preparation method of environmental type constructional ornamental material Download PDFInfo
- Publication number
- CN107572882A CN107572882A CN201710869937.6A CN201710869937A CN107572882A CN 107572882 A CN107572882 A CN 107572882A CN 201710869937 A CN201710869937 A CN 201710869937A CN 107572882 A CN107572882 A CN 107572882A
- Authority
- CN
- China
- Prior art keywords
- parts
- tealeaves
- lavender
- preparation
- constructional ornamental
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of preparation method of environmental type constructional ornamental material, the constructional ornamental material is made up of the component of following parts by weight:10 20 parts of quartz sand, 8 16 parts of atlapulgite, 12 18 parts of attapulgite, 10 18 parts of melamine resin, 48 parts of begonia wood chip, 15 parts of acticarbon, 15 parts of lavender, 8 16 parts of isocyanates, 15 parts of tealeaves, 26 parts of 6 12 parts of silicate fiber cotton, 12 24 parts of calcium carbonate, 8 12 parts of rubber powder and two mercaptan.The advantage of the invention is that:Environmental type constructional ornamental material of the present invention, the effect of antimildew and antibacterial is permanent, is effectively improved IAQ, improves safety coefficient, green, pollution-free;And lavender and tealeaves are added in formula, moreover it is possible to give out natural scent, tranquilization and refreshment is played a part of to human body, so as to ensure the health of human body, there is provided the Easy Living Envi-ronment of a safety and comfort.
Description
Technical field
The present invention relates to environment-friendly building materials field, more particularly to a kind of environmental type construction and decoration material
The preparation method of material.
Background technology
The event that finishing pollution damages to caused by human body happens occasionally, and presents and increase trend, therefore, expert advice people
When carrying out interior decoration, must have environmental consciousness, prevent the air pollution caused by finishing by every possible means.But modern times dress
Composite board, binder and paint are used in repairing in large quantities, these are all the main dirts of the poison gases such as formaldehyde, toluene, dimethylbenzene
Dye source.Because the maximum source of poison gas is exactly binder, and most of building materials have the composition of bonding, each as in the market
The Lauxite using formaldehyde as main component is used to be used as binder in kind particieboard, medium density fibre board (MDF), glued board.These
The harm of poison gas is all very big, have every year exceed 100,000 people just die from house ornamentation pollution, cause very big loss.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of preparation method of environmental type constructional ornamental material, with solution
Certainly above-mentioned technical problem.
In order to solve the above technical problems, the technical scheme is that:A kind of system of environmental type constructional ornamental material
Preparation Method, its innovative point are:The constructional ornamental material is made up of the component of following parts by weight:Quartz sand 10-20 parts, it is living
Property carclazyte 8-16 parts, attapulgite 12-18 parts, melamine resin 10-18 parts, begonia wood chip 4-8 parts, activated carbon inhale
Attached dose of 1-5 part, lavender 1-5 parts, isocyanates 8-16 parts, tealeaves 1-5 parts, silicate fiber cotton 6-12 parts, calcium carbonate 12-24
Part, rubber powder 8-12 parts and two mercaptan 2-6 parts;The preparation method comprises the following steps:
(1)By above-mentioned parts by weight by quartz sand, atlapulgite, attapulgite, melamine resin, begonia wood chip, work
Property carbon adsorbent, lavender, isocyanates, tealeaves, silicate fiber cotton, calcium carbonate, rubber powder and two mercaptan, launch and arrive batch mixing
Uniformly mixed in machine, then delivered to mixing material in steam heater;
(2)Mixing material is heated to 80~120 DEG C by steam heater, is then sent in extruder;
(3)Mixing material after heating is squeezed into by block structure by extruder, processing is then dried, building dress is made
Repair material.
Further, the constructional ornamental material is made up of the component of following parts by weight:Quartz sand 14-16 parts, activity
Carclazyte 11-13 parts, attapulgite 14-16 parts, melamine resin 12-16 parts, begonia wood chip 5-7 parts, activated carbon are inhaled
Attached dose of 2-4 part, lavender 2-4 parts, isocyanates 11-13 parts, tealeaves 2-4 parts, silicate fiber cotton 8-10 parts, calcium carbonate 16-20
Part, rubber powder 9-11 parts and two mercaptan 3-5 parts.
Further, the constructional ornamental material is made up of the component of following parts by weight:15 parts of quartz sand, atlapulgite
12 parts, 15 parts of attapulgite, 14 parts of melamine resin, 6 parts of begonia wood chip, 3 parts of acticarbon, lavender 3
4 parts of part, 12 parts of isocyanates, 3 parts of tealeaves, 9 parts of silicate fiber cotton, 18 parts of calcium carbonate, 10 parts of rubber powder and two mercaptan.
The advantage of the invention is that:Environmental type constructional ornamental material of the present invention, the effect of antimildew and antibacterial is permanent, effectively
Improve IAQ, improve safety coefficient, it is green, it is pollution-free;And lavender and tealeaves are added in formula, also
Natural scent can be given out, tranquilization and refreshment is played a part of to human body, so as to ensure the health of human body, there is provided one
The Easy Living Envi-ronment of safety and comfort.
Embodiment
The following examples can make professional and technical personnel that the present invention be more fully understood, but therefore not send out this
It is bright to be limited among described scope of embodiments.
Embodiment 1
The preparation method of the present embodiment environmental type constructional ornamental material, the constructional ornamental material are by following parts by weight
Component forms:10 parts of quartz sand, 8 parts of atlapulgite, 12 parts of attapulgite, 10 parts of melamine resin, begonia wood chip 4
Part, 1 part of acticarbon, 1 part of lavender, 8 parts of isocyanates, 1 part of tealeaves, 6 parts of silicate fiber cotton, 12 parts of calcium carbonate, rubber
2 parts of 8 parts of rubber powder and two mercaptan;The preparation method comprises the following steps:
(1)By above-mentioned parts by weight by quartz sand, atlapulgite, attapulgite, melamine resin, begonia wood chip, work
Property carbon adsorbent, lavender, isocyanates, tealeaves, silicate fiber cotton, calcium carbonate, rubber powder and two mercaptan, launch and arrive batch mixing
Uniformly mixed in machine, then delivered to mixing material in steam heater;
(2)Mixing material is heated to 80~120 DEG C by steam heater, is then sent in extruder;
(3)Mixing material after heating is squeezed into by block structure by extruder, processing is then dried, building dress is made
Repair material.
Embodiment 2
The preparation method of the present embodiment environmental type constructional ornamental material, the constructional ornamental material are by following parts by weight
Component forms:20 parts of quartz sand, 16 parts of atlapulgite, 18 parts of attapulgite, 18 parts of melamine resin, begonia wood chip
8 parts, 5 parts of acticarbon, 5 parts of lavender, 16 parts of isocyanates, 5 parts of tealeaves, 12 parts of silicate fiber cotton, 24 parts of calcium carbonate,
6 parts of 12 parts of rubber powder and two mercaptan;The preparation method comprises the following steps:
(1)By above-mentioned parts by weight by quartz sand, atlapulgite, attapulgite, melamine resin, begonia wood chip, work
Property carbon adsorbent, lavender, isocyanates, tealeaves, silicate fiber cotton, calcium carbonate, rubber powder and two mercaptan, launch and arrive batch mixing
Uniformly mixed in machine, then delivered to mixing material in steam heater;
(2)Mixing material is heated to 80~120 DEG C by steam heater, is then sent in extruder;
(3)Mixing material after heating is squeezed into by block structure by extruder, processing is then dried, building dress is made
Repair material.
Embodiment 3
The preparation method of the present embodiment environmental type constructional ornamental material, the constructional ornamental material are by following parts by weight
Component forms:14 parts of quartz sand, 11 parts of atlapulgite, 14 parts of attapulgite, 12 parts of melamine resin, begonia wood chip
5 parts, 2 parts of acticarbon, 2 parts of lavender, 11 parts of isocyanates, 2 parts of tealeaves, 8 parts of silicate fiber cotton, 16 parts of calcium carbonate,
3 parts of 9 parts of rubber powder and two mercaptan;The preparation method comprises the following steps:
(1)By above-mentioned parts by weight by quartz sand, atlapulgite, attapulgite, melamine resin, begonia wood chip, work
Property carbon adsorbent, lavender, isocyanates, tealeaves, silicate fiber cotton, calcium carbonate, rubber powder and two mercaptan, launch and arrive batch mixing
Uniformly mixed in machine, then delivered to mixing material in steam heater;
(2)Mixing material is heated to 80~120 DEG C by steam heater, is then sent in extruder;
(3)Mixing material after heating is squeezed into by block structure by extruder, processing is then dried, building dress is made
Repair material.
Embodiment 4
The preparation method of the present embodiment environmental type constructional ornamental material, the constructional ornamental material are by following parts by weight
Component forms:16 parts of quartz sand, 13 parts of atlapulgite, 16 parts of attapulgite, 16 parts of melamine resin, begonia wood chip
7 parts, 4 parts of acticarbon, 4 parts of lavender, 13 parts of isocyanates, 4 parts of tealeaves, 10 parts of silicate fiber cotton, 20 parts of calcium carbonate,
5 parts of 11 parts of rubber powder and two mercaptan;The preparation method comprises the following steps:
(1)By above-mentioned parts by weight by quartz sand, atlapulgite, attapulgite, melamine resin, begonia wood chip, work
Property carbon adsorbent, lavender, isocyanates, tealeaves, silicate fiber cotton, calcium carbonate, rubber powder and two mercaptan, launch and arrive batch mixing
Uniformly mixed in machine, then delivered to mixing material in steam heater;
(2)Mixing material is heated to 80~120 DEG C by steam heater, is then sent in extruder;
(3)Mixing material after heating is squeezed into by block structure by extruder, processing is then dried, building dress is made
Repair material.
Embodiment 5
The preparation method of the present embodiment environmental type constructional ornamental material, the constructional ornamental material are by following parts by weight
Component forms:15 parts of quartz sand, 12 parts of atlapulgite, 15 parts of attapulgite, 14 parts of melamine resin, begonia wood chip
6 parts, 3 parts of acticarbon, 3 parts of lavender, 12 parts of isocyanates, 3 parts of tealeaves, 9 parts of silicate fiber cotton, 18 parts of calcium carbonate,
4 parts of 10 parts of rubber powder and two mercaptan;The preparation method comprises the following steps:
(1)By above-mentioned parts by weight by quartz sand, atlapulgite, attapulgite, melamine resin, begonia wood chip, work
Property carbon adsorbent, lavender, isocyanates, tealeaves, silicate fiber cotton, calcium carbonate, rubber powder and two mercaptan, launch and arrive batch mixing
Uniformly mixed in machine, then delivered to mixing material in steam heater;
(2)Mixing material is heated to 80~120 DEG C by steam heater, is then sent in extruder;
(3)Mixing material after heating is squeezed into by block structure by extruder, processing is then dried, building dress is made
Repair material.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The skill of the industry
For art personnel it should be appreciated that the present invention is not limited to the above embodiments, described in above-described embodiment and specification is explanation
The principle of the present invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these
Changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and
Its equivalent thereof.
Claims (3)
- A kind of 1. preparation method of environmental type constructional ornamental material, it is characterised in that:The constructional ornamental material be by with The component composition of lower parts by weight:Quartz sand 10-20 parts, atlapulgite 8-16 parts, attapulgite 12-18 parts, melamino-formaldehyde Resin 10-18 parts, begonia wood chip 4-8 parts, acticarbon 1-5 parts, lavender 1-5 parts, isocyanates 8-16 parts, tealeaves 1-5 parts, silicate fiber cotton 6-12 parts, calcium carbonate 12-24 parts, rubber powder 8-12 parts and two mercaptan 2-6 parts;The preparation method bag Include following steps:(1)By above-mentioned parts by weight by quartz sand, atlapulgite, attapulgite, melamine resin, begonia wood chip, work Property carbon adsorbent, lavender, isocyanates, tealeaves, silicate fiber cotton, calcium carbonate, rubber powder and two mercaptan, launch and arrive batch mixing Uniformly mixed in machine, then delivered to mixing material in steam heater;(2)Mixing material is heated to 80~120 DEG C by steam heater, is then sent in extruder;(3)Mixing material after heating is squeezed into by block structure by extruder, processing is then dried, building dress is made Repair material.
- 2. the preparation method of environmental type constructional ornamental material according to claim 1, it is characterised in that:The building Finishing material is made up of the component of following parts by weight:Quartz sand 14-16 parts, atlapulgite 11-13 parts, attapulgite 14-16 Part, melamine resin 12-16 parts, begonia wood chip 5-7 parts, acticarbon 2-4 parts, lavender 2-4 parts, isocyanide Acid esters 11-13 parts, tealeaves 2-4 parts, silicate fiber cotton 8-10 parts, calcium carbonate 16-20 parts, rubber powder 9-11 parts and two mercaptan 3-5 Part.
- 3. the preparation method of environmental type constructional ornamental material according to claim 1, it is characterised in that:The building Finishing material is made up of the component of following parts by weight:15 parts of quartz sand, 12 parts of atlapulgite, 15 parts of attapulgite, melamine 14 parts of amine-formaldehyde resins, 6 parts of begonia wood chip, 3 parts of acticarbon, 3 parts of lavender, 12 parts of isocyanates, 3 parts of tealeaves, 4 parts of 9 parts of silicate fiber cotton, 18 parts of calcium carbonate, 10 parts of rubber powder and two mercaptan.