CN106520012A - Soybean protein adhesive reinforcing agent special for wood and wood-based panels and preparation method thereof - Google Patents
Soybean protein adhesive reinforcing agent special for wood and wood-based panels and preparation method thereof Download PDFInfo
- Publication number
- CN106520012A CN106520012A CN201611155877.3A CN201611155877A CN106520012A CN 106520012 A CN106520012 A CN 106520012A CN 201611155877 A CN201611155877 A CN 201611155877A CN 106520012 A CN106520012 A CN 106520012A
- Authority
- CN
- China
- Prior art keywords
- wood
- reinforcing agent
- parts
- soybean protein
- protein adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a soybean protein adhesive reinforcing agent special for wood and wood-based panels and a preparation method thereof. The soybean protein adhesive reinforcing agent is prepared from, by weight, 0.2-15.0 parts of calcium sulfate and 0.1-5.0 parts of graphene. 0.2-15.0 parts of calcium sulfate and 0.1-5.0 parts of graphene are mixed to be uniform and added when a soybean protein adhesive is prepared. The soybean protein adhesive reinforcing agent is used for manufacturing the wood-based panel, the bonding strength of the manufactured wood-based panel is remarkably improved, and the bonding strength of plywood is 0.7-1.3 MPa before the reinforcing agent is added and is 1.4-1.8 MPa after the reinforcing agent is added.
Description
Technical field
The present invention relates to a kind of adhesive reinforcing agent, more particularly to a kind of timber and wood-based plate specialized soybean protein adhesive
Reinforcing agent and preparation method thereof.
Background technology
At present, in building board production process, be first applying glue to be carried out with soybean albumen adhesive, then form through hot pressing.This
Artificial board formaldehyde release can be solved, the root problem of human body is poisoned.But, the shortcoming of soybean albumen adhesive is：Make
Difference of the bonding strength of wood-based plate than phenolic resin glue.
The content of the invention
The purpose of the present invention：A kind of timber and wood-based plate specialized soybean protein adhesive reinforcing agent and its preparation side are provided
Method, can play potentiation to soybean albumen adhesive, be allowed to adhesive property raising.
To achieve these goals, the technical scheme is that：
A kind of timber and wood-based plate specialized soybean protein adhesive reinforcing agent, are made up of following portions by weight raw material：Calcium sulfate
0.2-15.0 parts and Graphene 0.1-5.0 parts.
Above-mentioned timber and wood-based plate specialized soybean protein adhesive reinforcing agent, wherein, described calcium sulfate is 0.2 part,
Described Graphene is 0.1 part.
Above-mentioned timber and wood-based plate specialized soybean protein adhesive reinforcing agent, wherein, described calcium sulfate is 15 parts, institute
The Graphene stated is 5 parts.
The preparation method of a kind of timber and wood-based plate specialized soybean protein adhesive reinforcing agent, described calcium sulfate 0.2-
15.0 parts and Graphene 0.1-5.0 parts uniformly mix, and add when soybean albumen adhesive is prepared.
For manufacturing wood-based plate, the wood-based plate bonding strength made is significantly improved the present invention, the glue before this reinforcing agent is added
The bonding strength of plywood is 0.7-1.3 MPa, is 1.4-1.8 MPa after adding this reinforcing agent.
Specific embodiment
A kind of timber and wood-based plate specialized soybean protein adhesive reinforcing agent, are made up of following portions by weight raw material：Sulphuric acid
Calcium 0.2-15.0 parts and Graphene 0.1-5.0 parts.
Described calcium sulfate is 0.2 part, and described Graphene is 0.1 part.
Described calcium sulfate is 15 parts, and described Graphene is 5 parts.
A kind of preparation method of timber and wood-based plate specialized soybean protein adhesive reinforcing agent：Described calcium sulfate 0.2-
15.0 parts and Graphene 0.1-5.0 parts uniformly mix, and add when soybean albumen adhesive is prepared.
Embodiment one：
0.2 part of calcium sulfate, 0.1 part of Graphene.Preparation technology is：By above-mentioned formula by calcium sulfate, Graphene mix homogeneously；Prepare
Add during soybean albumen adhesive.
Embodiment two：
15.0 parts of calcium sulfate, 5 parts of Graphene.Preparation technology is：By above-mentioned formula by calcium sulfate, Graphene mix homogeneously；Prepare
Add during soybean albumen adhesive.
In sum, for manufacturing wood-based plate, the wood-based plate bonding strength made is significantly improved the present invention, is adding this enhancing
Before agent, the bonding strength of plywood is 0.7-1.3 MPa, is 1.4-1.8 MPa after adding this reinforcing agent.
The preferred embodiments of the present invention are the foregoing is only, the scope of the claims of the present invention, every utilization is not thereby limited
The equivalent structure transformation made by present specification, or directly or indirectly with the technology neck for being attached to other Related products
Domain, is included within the scope of the present invention.
Claims (4)
1. a kind of timber and wood-based plate specialized soybean protein adhesive reinforcing agent, it is characterised in that：By following portions by weight raw material
Make：Calcium sulfate 0.2-15.0 parts and Graphene 0.1-5.0 parts.
2. timber according to claim 1 and wood-based plate specialized soybean protein adhesive reinforcing agent, it is characterised in that：It is described
Calcium sulfate be 0.2 part, described Graphene is 0.1 part.
3. timber according to claim 1 and wood-based plate specialized soybean protein adhesive reinforcing agent, it is characterised in that：It is described
Calcium sulfate be 15 parts, described Graphene is 5 parts.
4. a kind of timber being applied to described in claim 1-3 any one and wood-based plate specialized soybean protein adhesive reinforcing agent
Preparation method, it is characterised in that：Described calcium sulfate 0.2-15.0 parts and Graphene 0.1-5.0 parts uniformly mix, and in system
Add during standby soybean albumen adhesive.