CN106189176A - 热可塑性聚氨酯弹性体复合材料发泡组成物 - Google Patents

热可塑性聚氨酯弹性体复合材料发泡组成物 Download PDF

Info

Publication number
CN106189176A
CN106189176A CN201510220633.8A CN201510220633A CN106189176A CN 106189176 A CN106189176 A CN 106189176A CN 201510220633 A CN201510220633 A CN 201510220633A CN 106189176 A CN106189176 A CN 106189176A
Authority
CN
China
Prior art keywords
thermoplastic polyurethane
foaming
elastic composite
polyurethane elastic
peroxide
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510220633.8A
Other languages
English (en)
Inventor
吴俊雄
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yifeng Mstar Technology Ltd
Original Assignee
Yifeng Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yifeng Mstar Technology Ltd filed Critical Yifeng Mstar Technology Ltd
Priority to CN201510220633.8A priority Critical patent/CN106189176A/zh
Publication of CN106189176A publication Critical patent/CN106189176A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种热可塑性聚氨酯弹性体复合材料发泡组成物，其主要包含有：一热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer)；一发泡剂群，该发泡剂群为4,4-氧代双苯磺酰肼(P,P-Oxybis Benzene Sulfonyl Hydrazide)及微胶囊发泡剂(micro-capsule blowing agent)；一高分子材料；一相容剂；一过氧化物架桥剂；将该热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer)、该发泡剂群、该高分子材料、相容剂及该过氧化物架桥剂进行熔融、混合、造粒或出片处理后，即可作为发泡用的材料。

Description

热可塑性聚氨酯弹性体复合材料发泡组成物
技术领域
本发明涉及一种发泡材料，特别涉及一种热可塑性聚氨酯弹性体复合材料发泡组成物。
背景技术
按，现有塑胶或弹性体发泡工艺，如乙烯－醋酸乙烯共聚合物(ethylene-vinylacetate copolymer，简称EVA)、聚烯烃弹性体(polyolefin elastomer)与苯乙烯系弹性体(Styrenic elastomer)的过氧化物架桥发泡制程及其相关产品已相当成熟，对于经过多年发展的发泡材料工业来说已经没有明显的突破。
惟，由于热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer，简称TPU)材料的化学结构中，缺乏可以用过氧化物进行架桥的官能基，因此无法用来制造模压发泡材料，包括模内与模外发泡。
发明内容
有鉴于此，为改善先前技术中，习知无法以热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer，简称TPU)作为发泡材料的问题；缘此，本发明乃提供一种热可塑性聚氨酯弹性体复合材料发泡组成物，其主要包含有：
一热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer)，25-75重量份；
一发泡剂群，该发泡剂群为4,4-氧代双苯磺酰肼(P,P-Oxybis BenzeneSulfonyl Hydrazide)及微胶囊发泡剂(micro-capsule blowing agent)，1-15重量份；
一高分子材料，25-75重量份；
一相容剂，3-10重量份；
一过氧化物架桥剂，0.1-1重量份；
将该热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer)、该发泡剂群、该高分子材料、相容剂及该过气化物架桥剂进行熔融、混合、造粒或出片处理后，即可作为发泡用的材料。
本发明的热可塑性聚氨酯弹性体复合材料发泡组成物，其中优选，该高分子材料为苯乙烯－丁二烯－苯乙烯(SBS)及其充油(oil-extended)复合材。该充油复合材是苯乙烯－乙烯/丁烯－苯乙烯与白蜡油浸泡后获得。
本发明的热可塑性聚氨酯弹性体复合材料发泡组成物，其中优选，该高分子材料为苯乙烯－乙烯/丁烯－苯乙烯(SEBS)及其充油(oil-extended)复合材。该充油复合材是苯乙烯－乙烯/丁烯－苯乙烯与白蜡油浸泡后获得。
本发明的热可塑性聚氨酯弹性体复合材料发泡组成物，其中优选，该过氧化物架桥剂为二异丙苯基过氧化物(Dicumyl peroxide)。
本发明的热可塑性聚氨酯弹性体复合材料发泡组成物，其中优选，该过氧化物架桥剂为2,5-二甲基-2,5-二(叔丁基过氧基)己烷(2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane)。
本发明的热可塑性聚氨酯弹性体复合材料发泡组成物，其中优选，该过氧化物架桥剂为1,4-双叔丁基过氧异丙基苯(Di-(tert-butyl peroxy-isopropyl)benzene)。
本发明的热可塑性聚氨酯弹性体复合材料发泡组成物，其中优选，该相容剂为酸酐接枝(anhydride-grafting)或其共聚物(anhydride copolymer)中之任一种。优选马来酸酐接枝聚乙烯或苯乙烯-马来酸酐共聚物。
附图说明
图1为本发明制造步骤流程示意图。
具体实施方式
为使贵审查委员能对本发明的特征与其特点有更进一步的了解与认同，兹列举以下较佳的实施例并配合说明书附图说明如下：
请参阅图1，其为本发明一较佳实施例所提供的一种热可塑性聚氨酯弹性体复合材料发泡组成物，主要包含有：
一热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer，简称TPU)，用量是25-75重量份，如可以是30、40、50、70份等25-75重量份之间任意的数值。
一发泡剂群，该发泡剂群为4,4-氧代双苯磺酰肼(P,P-Oxybis Benzene SulfonylHydrazide)，简称OBSH发泡剂及微胶囊发泡剂(micro-capsule blowing agent)。用量是1-15重量份，如可以是2、5、10、12份等1-15重量份之间任意的数值。
一高分子材料，该高分子材料可为苯乙烯－丁二烯－苯乙烯(SBS)、苯乙烯－乙烯/丁烯－苯乙烯(SEBS)及其充油(oil-extended)复合材(苯乙烯－乙烯/丁烯－苯乙烯与白蜡油浸泡后获得)中的任一种。该高分子材料的用量是25-75重量份，如可以是30、40、50、70份等25-75重量份之间任意的数值。
一相容剂，该相容剂为酸酐接枝(anhydride-grafting)或其共聚物(anhydridecopolymer)中的任一种。该相容剂可以是马来酸酐与聚乙烯接枝或与苯乙烯共聚得到，相容剂为现有产品，可通过购买得到。该相容剂的含量为3-10重量份，如可以是4份、6份、8份等3-10重量份之间任意的数值。
一过氧化物架桥剂，该过氧化物架桥剂可为二异丙苯基过氧化物(Dicumylperoxide)、2,5-二甲基-2,5-二(叔丁基过氧基)己烷(2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane)、1,4-双叔丁基过氧异丙基苯(Di-(tert-butyl peroxy-isopropyl)benzene)等中的任一种。该过氧化物架桥剂的含量为0.1-1重量份，如可以是0.2份、0.5份、0.8份等0.1-1重量份之间任意的数值。
是以，上述即为本发明较佳实施例的热可塑性聚氨酯弹性体复合材料发泡组成物，其再将制成方式及使用方式介绍如下：
首先，将该热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer，简称TPU)搭配上述适当比例的发泡剂群及高分子材料、相容剂及过氧化物架桥剂，放入密练机(Kneader)或万马力机(Banbury mixer)，在100℃至140℃间进行高温融合，混练均匀后随即放入单螺杆造粒机(single-screw extruder)造成粒子，或是放入双滚轮出片机(two-roll mill)出片后备用。
接着，将上述的粒子或片材称重后，放入已经设定好温度的模压机(hot-pressedmolding machine)内的模具中，经加温(150℃至170℃)热压、发泡，冷却后即完成发泡。
藉此，本发明所提供热可塑性聚氨酯弹性体复合材料发泡组成物，其所选用的发泡剂群及过氧化物架桥剂的分解温度范围不会对热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer，简称TPU)造成劣化的影响。
另外，本发明以热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer，简称TPU)为主要基材，再与高分子材料熔融共混后，经适当的相容化(compatibilization)处理后，并添入发泡剂群及过氧化物架桥剂后，便可得到可进行发泡的热可塑性聚氨酯弹性体复合材料发泡组成物。
以上所揭，仅为本发明所提供的较佳实施例而已，并非用以限制本发明的实施范围，凡本技术领域内的相关技艺者根据本创作所为的均等变化，皆应属本发明所涵盖之范围。

Claims (7)

1.一种热可塑性聚氨酯弹性体复合材料发泡组成物，其主要包含有：
一热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer)，25-75重量份；
一发泡剂群，该发泡剂群为4,4-氧代双苯磺酰肼(P,P-Oxybis Benzene SulfonylHydrazide)及微胶囊发泡剂(micro-capsule blowing agent)，1-15重量份；
一高分子材料，25-75重量份；
一相容剂，3-10重量份；
一过氧化物架桥剂，0.1-1重量份。
将该热可塑性聚氨酯弹性体(thermoplastic polyurethane elastomer)、该发泡剂群、该高分子材料、相容剂及该过氧化物架桥剂进行熔融、混合、造粒或出片处理后，即可作为发泡用的材料。
2.依据权利要求1所述的热可塑性聚氨酯弹性体复合材料发泡组成物，其中，该高分子材料为苯乙烯－丁二烯－苯乙烯(SBS)及其充油(oil-extended)复合材。
3.依据权利要求1所述的热可塑性聚氨酯弹性体复合材料发泡组成物，其中，该高分子材料为苯乙烯－乙烯/丁烯－苯乙烯(SEBS)及其充油(oil-extended)复合材。
4.依据权利要求1所述的热可塑性聚氨酯弹性体复合材料发泡组成物，其中，该过氧化物架桥剂为二异丙苯基过氧化物(Dicumyl peroxide)。
5.依据权利要求1所述的热可塑性聚氨酯弹性体复合材料发泡组成物，其中，该过氧化物架桥剂为2,5-二甲基-2,5-二(叔丁基过氧基)己烷(2,5-Dimethyl-2,5-di(tert-butylperoxy)hexane)。
6.依据权利要求1所述的热可塑性聚氨酯弹性体复合材料发泡组成物，其中，该过氧化物架桥剂为1,4-双叔丁基过氧异丙基苯(Di-(tert-butylperoxy-isopropyl)benzene)。
7.依据权利要求1所述的热可塑性聚氨酯弹性体复合材料发泡组成物，其中，该相容剂为酸酐接枝(anhydride-grafting)或其共聚物(anhydride copolymer)中的任一种。
CN201510220633.8A 2015-05-04 2015-05-04 热可塑性聚氨酯弹性体复合材料发泡组成物 Pending CN106189176A (zh)