CN106188971A - A kind of plastic sheeting and preparation method thereof - Google Patents

A kind of plastic sheeting and preparation method thereof Download PDF

Info

Publication number
CN106188971A
CN106188971A CN201610654659.8A CN201610654659A CN106188971A CN 106188971 A CN106188971 A CN 106188971A CN 201610654659 A CN201610654659 A CN 201610654659A CN 106188971 A CN106188971 A CN 106188971A
Authority
CN
China
Prior art keywords
parts
plastic sheeting
raw material
weight
tissuemat
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610654659.8A
Other languages
Chinese (zh)
Inventor
焦国平
齐继业
方兴旺
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Songtai Packing Material Co Ltd
Original Assignee
Anhui Songtai Packing Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Songtai Packing Material Co Ltd filed Critical Anhui Songtai Packing Material Co Ltd
Priority to CN201610654659.8A priority Critical patent/CN106188971A/en
Publication of CN106188971A publication Critical patent/CN106188971A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of plastic sheeting and preparation method thereof, described plastic sheeting is made up of the raw material of following parts by weight: polrvinyl chloride 40 70 parts, acrylic resin 40 60 parts, Tissuemat E 8 13 parts, Pulvis Talci 10 18 parts, organic montmorillonite 59 parts, polyvinyl alcohol 30 50 parts, 8 16 parts of titanium phosphate sodium, polyacrylamide 12 24 parts, cumyl peroxide 1.5 3 parts, antioxidant 13 parts, calcium carbonate 8 13 parts, silane coupler 0.3 0.7 parts, dioctyl phthalate 8 13 parts, light stabilizer 13 parts, glyceryl tristearate 37 parts, styrene acrylonitrile copolymer 1.5 5 parts, plasticizer 0.8 1.8 parts.Compared with prior art, in the present invention, the tensile strength of plastic sheeting is high and preparation technology is simple.

Description

A kind of plastic sheeting and preparation method thereof
Technical field
The invention belongs to thin film materials art, particularly to a kind of plastic sheeting and preparation method thereof.
Background technology
Plastic sheeting is mainly used in packaging and is used as coating layer.Plastics package and plastic packet product are commercially shared Share increasing, particularly composite plastic flexible package, have been widely used for the fields such as food, medicine, chemical industry, wherein Maximum with packaging for foodstuff proportion again, such as beverage packaging, quick frozen food packaging, cooking food packaging, fast food packaging Deng, these products all bring great convenience to people's life.But the tensile strength of existing plastic sheeting is the most poor, it is difficult to full Foot people's life and demand of industrial production.
Summary of the invention
It is an object of the invention to provide a kind of plastic sheeting and preparation method thereof, this plastic sheeting have tensile strength high, The advantages such as preparation technology is simple.
For achieving the above object, the present invention provides following technical scheme:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 40-70 part, acrylic resin 40- 60 parts, Tissuemat E 8-13 part, Pulvis Talci 10-18 part, organic montmorillonite 5-9 part, polyvinyl alcohol 30-50 part, titanium phosphate sodium 8-16 part, polyacrylamide 12-24 part, cumyl peroxide 1.5-3 part, antioxidant 1-3 part, calcium carbonate 8-13 part, silane Coupling agent 0.3-0.7 part, dioctyl phthalate 8-13 part, light stabilizer 1-3 part, glyceryl tristearate 3-7 part, benzene second Alkene-acrylonitrile copolymer 1.5-5 part, plasticizer 0.8-1.8 part.
Preferably, described plastic sheeting is made up of the raw material of following parts by weight: polrvinyl chloride 52 parts, acrylic resin 45 Part, Tissuemat E 9 parts, Pulvis Talci 12 parts, organic montmorillonite 7 parts, polyvinyl alcohol 42 parts, 10 parts of titanium phosphate sodium, polyacrylamide 18 parts, cumyl peroxide 2.2 parts, antioxidant 1.2 parts, calcium carbonate 9 parts, silane coupler 0.5 part, phthalic acid two Monooctyl ester 9 parts, light stabilizer 1 part, glyceryl tristearate 4 parts, SAN 2.5 parts, plasticizer 1.2 parts.
Preferably, described plastic sheeting is made up of the raw material of following parts by weight: polrvinyl chloride 45 parts, acrylic resin 54 Part, Tissuemat E 11 parts, Pulvis Talci 10 parts, organic montmorillonite 6 parts, polyvinyl alcohol 38 parts, 10 parts of titanium phosphate sodium, polyacrylamide 20 parts, cumyl peroxide 3 parts, antioxidant 2 parts, calcium carbonate 10 parts, silane coupler 0.5 part, phthalic acid two is pungent Ester 10 parts, light stabilizer 1.6 parts, glyceryl tristearate 4.8 parts, SAN 2.6 parts, plasticizer 1 part.
Preferably, described plastic sheeting is made up of the raw material of following parts by weight: polrvinyl chloride 62 parts, acrylic resin 50 Part, Tissuemat E 8 parts, Pulvis Talci 16 parts, organic montmorillonite 8 parts, polyvinyl alcohol 35 parts, 13 parts of titanium phosphate sodium, polyacrylamide 15 parts, cumyl peroxide 2 parts, antioxidant 1.3 parts, calcium carbonate 11 parts, silane coupler 0.6 part, phthalic acid two Monooctyl ester 10 parts, light stabilizer 1.4 parts, glyceryl tristearate 5.5 parts, SAN 2.8 parts, plasticizer 1.3 Part.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Compared with prior art, the invention has the beneficial effects as follows:
In the present invention, the preparation technology of plastic sheeting is simple, low raw-material cost, and its have excellent mechanical property, Heat stability is high and water-tolerant, thus makes it have broader practice field, preferably meet people's daily life with And commercial production needs.
Detailed description of the invention
Describe technical scheme in detail below in conjunction with embodiment, but protection domain is not limited thereto.
Embodiment one:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 42 parts, acrylic resin 45 parts, Tissuemat E 9 parts, Pulvis Talci 12 parts, organic montmorillonite 7 parts, polyvinyl alcohol 48 parts, 10 parts of titanium phosphate sodium, polyacrylamide 22 Part, cumyl peroxide 1.6 parts, antioxidant 1.4 parts, calcium carbonate 11 parts, silane coupler 0.45 part, phthalic acid two Monooctyl ester 9 parts, light stabilizer 1.3 parts, glyceryl tristearate 5.6 parts, SAN 3.7 parts, plasticizer 1 part.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Embodiment two:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 52 parts, acrylic resin 45 parts, Tissuemat E 9 parts, Pulvis Talci 12 parts, organic montmorillonite 7 parts, polyvinyl alcohol 42 parts, 10 parts of titanium phosphate sodium, polyacrylamide 18 Part, cumyl peroxide 2.2 parts, antioxidant 1.2 parts, calcium carbonate 9 parts, silane coupler 0.5 part, phthalic acid two is pungent Ester 9 parts, light stabilizer 1 part, glyceryl tristearate 4 parts, SAN 2.5 parts, plasticizer 1.2 parts.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Embodiment three:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 45 parts, acrylic resin 54 parts, Tissuemat E 11 parts, Pulvis Talci 10 parts, organic montmorillonite 6 parts, polyvinyl alcohol 38 parts, 10 parts of titanium phosphate sodium, polyacrylamide 20 Part, cumyl peroxide 3 parts, antioxidant 2 parts, calcium carbonate 10 parts, silane coupler 0.5 part, dioctyl phthalate 10 parts, light stabilizer 1.6 parts, glyceryl tristearate 4.8 parts, SAN 2.6 parts, plasticizer 1 part.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Embodiment four:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 62 parts, acrylic resin 50 parts, Tissuemat E 8 parts, Pulvis Talci 16 parts, organic montmorillonite 8 parts, polyvinyl alcohol 35 parts, 13 parts of titanium phosphate sodium, polyacrylamide 15 Part, cumyl peroxide 2 parts, antioxidant 1.3 parts, calcium carbonate 11 parts, silane coupler 0.6 part, phthalic acid two is pungent Ester 10 parts, light stabilizer 1.4 parts, glyceryl tristearate 5.5 parts, SAN 2.8 parts, plasticizer 1.3 Part.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Embodiment five:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 60 parts, acrylic resin 50 parts, Tissuemat E 10 parts, Pulvis Talci 10 parts, organic montmorillonite 8 parts, polyvinyl alcohol 35 parts, 10 parts of titanium phosphate sodium, polyacrylamide 18 Part, cumyl peroxide 1.7 parts, antioxidant 2 parts, calcium carbonate 9 parts, silane coupler 0.4 part, dioctyl phthalate 9 parts, light stabilizer 1.4 parts, glyceryl tristearate 4.5 parts, SAN 2.5 parts, plasticizer 1.3 parts.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Embodiment six:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 42 parts, acrylic resin 60 parts, Tissuemat E 12 parts, Pulvis Talci 13 parts, organic montmorillonite 5 parts, polyvinyl alcohol 50 parts, 11 parts of titanium phosphate sodium, polyacrylamide 23 Part, cumyl peroxide 2.2 parts, antioxidant 2.5 parts, calcium carbonate 9 parts, silane coupler 0.4 part, phthalic acid two is pungent Ester 9 parts, light stabilizer 1.8 parts, glyceryl tristearate 7 parts, SAN 5 parts, plasticizer 0.8 part.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Embodiment seven:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 55 parts, acrylic resin 55 parts, Tissuemat E 13 parts, Pulvis Talci 10 parts, organic montmorillonite 9 parts, polyvinyl alcohol 47 parts, 15 parts of titanium phosphate sodium, polyacrylamide 16 Part, cumyl peroxide 2.7 parts, antioxidant 1.4 parts, calcium carbonate 9 parts, silane coupler 0.6 part, phthalic acid two is pungent Ester 11 parts, light stabilizer 3 parts, glyceryl tristearate 4.6 parts, SAN 4 parts, plasticizer 1.5 parts.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Embodiment eight:
A kind of plastic sheeting, it is made up of the raw material of following parts by weight: polrvinyl chloride 62 parts, acrylic resin 48 parts, Tissuemat E 8 parts, Pulvis Talci 13 parts, organic montmorillonite 6.5 parts, polyvinyl alcohol 45 parts, 9 parts of titanium phosphate sodium, polyacrylamide 22 Part, cumyl peroxide 1.6 parts, antioxidant 1.3 parts, calcium carbonate 9 parts, silane coupler 0.6 part, phthalic acid two is pungent Ester 11 parts, light stabilizer 1.8 parts, glyceryl tristearate 6 parts, SAN 3 parts, plasticizer 1.3 parts.
The preparation method of described plastic sheeting, comprises the following steps:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, obtain Raw mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting Product.
Finally illustrating, above example is only in order to illustrate technical scheme and unrestricted, although with reference to relatively The present invention has been described in detail by good embodiment, it will be understood by those within the art that, can be to the skill of the present invention Art scheme is modified or equivalent, and without deviating from objective and the scope of the technical program, it all should be contained in the present invention Right in the middle of.

Claims (5)

1. a plastic sheeting, it is characterised in that be made up of the raw material of following parts by weight: polrvinyl chloride 40-70 part, polypropylene Resin 40-60 part, Tissuemat E 8-13 part, Pulvis Talci 10-18 part, organic montmorillonite 5-9 part, polyvinyl alcohol 30-50 part, phosphorus Acid titanium sodium 8-16 part, polyacrylamide 12-24 part, cumyl peroxide 1.5-3 part, antioxidant 1-3 part, calcium carbonate 8-13 Part, silane coupler 0.3-0.7 part, dioctyl phthalate 8-13 part, light stabilizer 1-3 part, glyceryl tristearate 3-7 Part, SAN 1.5-5 part, plasticizer 0.8-1.8 part.
A kind of plastic sheeting the most according to claim 1, it is characterised in that be made up of the raw material of following parts by weight: poly- 52 parts of vinyl chloride, acrylic resin 45 parts, Tissuemat E 9 parts, Pulvis Talci 12 parts, organic montmorillonite 7 parts, polyvinyl alcohol 42 Part, 10 parts of titanium phosphate sodium, polyacrylamide 18 parts, cumyl peroxide 2.2 parts, antioxidant 1.2 parts, calcium carbonate 9 parts, silane Coupling agent 0.5 part, dioctyl phthalate 9 parts, light stabilizer 1 part, glyceryl tristearate 4 parts, styrene-acrylonitrile is common Polymers 2.5 parts, plasticizer 1.2 parts.
A kind of plastic sheeting the most according to claim 1, it is characterised in that be made up of the raw material of following parts by weight: poly- 45 parts of vinyl chloride, acrylic resin 54 parts, Tissuemat E 11 parts, Pulvis Talci 10 parts, organic montmorillonite 6 parts, polyvinyl alcohol 38 Part, 10 parts of titanium phosphate sodium, polyacrylamide 20 parts, cumyl peroxide 3 parts, antioxidant 2 parts, calcium carbonate 10 parts, silane is even Connection agent 0.5 part, dioctyl phthalate 10 parts, light stabilizer 1.6 parts, glyceryl tristearate 4.8 parts, styrene-propene Lonitrile copolymer 2.6 parts, plasticizer 1 part.
A kind of plastic sheeting the most according to claim 1, it is characterised in that be made up of the raw material of following parts by weight: poly- 62 parts of vinyl chloride, acrylic resin 50 parts, Tissuemat E 8 parts, Pulvis Talci 16 parts, organic montmorillonite 8 parts, polyvinyl alcohol 35 Part, 13 parts of titanium phosphate sodium, polyacrylamide 15 parts, cumyl peroxide 2 parts, antioxidant 1.3 parts, calcium carbonate 11 parts, silane Coupling agent 0.6 part, dioctyl phthalate 10 parts, light stabilizer 1.4 parts, glyceryl tristearate 5.5 parts, styrene-the third Alkene lonitrile copolymer 2.8 parts, plasticizer 1.3 parts.
5. according to the preparation method of the plastic sheeting according to any one of claim 1-4, it is characterised in that include following step Rapid:
(1) each raw material components is weighed according to ratio of weight and number；
(2) by off-the-shelf each raw material components addition mixing roll in step (1) being sufficiently stirred for and uniformly mixing, raw material is obtained Mixture；
(3) raw mixture in step (2) is added in extruder, extruded, cooling, obtain plastic sheeting finished product.
CN201610654659.8A 2016-08-11 2016-08-11 A kind of plastic sheeting and preparation method thereof Pending CN106188971A (en)