CN107603016A - A kind of high-temperature flame-retardant plastic film and preparation method thereof - Google Patents
A kind of high-temperature flame-retardant plastic film and preparation method thereof Download PDFInfo
- Publication number
- CN107603016A CN107603016A CN201710904530.2A CN201710904530A CN107603016A CN 107603016 A CN107603016 A CN 107603016A CN 201710904530 A CN201710904530 A CN 201710904530A CN 107603016 A CN107603016 A CN 107603016A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic film
- raw material
- temperature flame
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-temperature flame-retardant plastic film and preparation method thereof, the high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:25 35 parts of butyl propionate, 50 65 parts of acrylic resin, 20 35 parts of ethyl-para-hydroxybenzoate, 10 20 parts of polyketone resin, 5 10 parts of cumyl peroxide, 12 18 parts of Phenoxyethanol, 26 parts of fire retardant, 36 parts of phosphorous acid lipid stabilizer, 25 parts of magnesium stearate, 39 parts of Tissuemat E, 3 12 parts of lagoriolite, 37 parts of diatomite, 5 parts of silica 1,27 parts of oleamide, 10 25 parts of polyoxyethylene carboxylate, 28 parts of calcium monohydrogen phosphate, 22 33 parts of PLA.High-temperature flame-retardant plastic film in the present invention has good heat-resisting quantity, anti-flammability, can better meet requirement.
Description
Technical field
The invention belongs to thin film materials art, more particularly to a kind of high-temperature flame-retardant plastic film and preparation method thereof.
Background technology
Plastic sheeting can be used for packaging, coating layer, and in recent years, plastics package and plastic packet product are commercially shared
Share it is increasing, particularly composite plastic flexible package, have been widely used for the fields such as food, medicine, chemical industry, wherein
It is again maximum with packaging for foodstuff proportion, such as beverage packaging, quick-frozen food packaging, cooking food packaging, fast food packaging
All brought great convenience Deng, these products to people's life.However, existing plastic sheeting generally existing resistance to elevated temperatures
And fire resistance is poor, while toughness is also required to further improve, thus makes its application field and application by great
Limitation.
The content of the invention
It is an object of the invention to provide a kind of high-temperature flame-retardant plastic film and preparation method thereof, the plastic sheeting has excellent
Good heat-resisting quantity and anti-flammability.
To achieve the above object, the present invention provides following technical scheme:
A kind of high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:Butyl propionate 25-35 parts, polypropylene
Resin 50-65 parts, ethyl-para-hydroxybenzoate 20-35 parts, polyketone resin 10-20 parts, cumyl peroxide 5-10 parts, benzene oxygen
Ethanol 12-18 parts, fire retardant 2-6 parts, phosphorous acid lipid stabilizer 3-6 parts, magnesium stearate 2-5 parts, Tissuemat E 3-9 parts, silicon
Sour aluminium sodium 3-12 parts, diatomite 3-7 parts, -5 parts of silica 1, oleamide 2-7 parts, polyoxyethylene carboxylate 10-25 parts,
Calcium monohydrogen phosphate 2-8 parts, PLA 22-33 parts.
Preferably, described high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:27 parts of butyl propionate,
60 parts of acrylic resin, 25 parts of ethyl-para-hydroxybenzoate, 14 parts of polyketone resin, 8 parts of cumyl peroxide, Phenoxyethanol 16
Part, 3 parts of fire retardant, 4 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 5 parts of Tissuemat E, 10 parts of lagoriolite, diatomite 5
Part, 3 parts of silica, 5 parts of oleamide, 16 parts of polyoxyethylene carboxylate, 6 parts of calcium monohydrogen phosphate, 30 parts of PLA.
Preferably, described high-temperature flame-retardant plastic film is prepared from the following raw materials in parts by weight:30 parts of butyl propionate,
52 parts of acrylic resin, 28 parts of ethyl-para-hydroxybenzoate, 13 parts of polyketone resin, 7 parts of cumyl peroxide, Phenoxyethanol 12
Part, 2 parts of fire retardant, 5 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 8 parts of Tissuemat E, 6 parts of lagoriolite, diatomite 3
Part, 2 parts of silica, 6 parts of oleamide, 17 parts of polyoxyethylene carboxylate, 3 parts of calcium monohydrogen phosphate, 24 parts of PLA.
Preferably, described high-temperature flame-retardant plastic film is prepared from the following raw materials in parts by weight:35 parts of butyl propionate,
55 parts of acrylic resin, 33 parts of ethyl-para-hydroxybenzoate, 18 parts of polyketone resin, 8 parts of cumyl peroxide, Phenoxyethanol 14
Part, 3 parts of fire retardant, 6 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 7 parts of Tissuemat E, 9 parts of lagoriolite, diatomite 4
Part, 3 parts of silica, 3 parts of oleamide, 25 parts of polyoxyethylene carboxylate, 5 parts of calcium monohydrogen phosphate, 22 parts of PLA.
The preparation method of described high-temperature flame-retardant plastic film, comprises the following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed is
270-285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) by step (2) raw mixture add extruder in, extrusion forming, cooling, obtain plastic sheeting into
Product.
Compared with prior art, the beneficial effects of the invention are as follows:
Plastic sheeting in the present invention is mainly added with butyl propionate, ethyl-para-hydroxybenzoate, polyketone resin, fire-retardant
The raw materials such as agent, phosphorous acid lipid stabilizer, lagoriolite, silica, the plastics are made by rational proportion between each raw material components
Film has the advantages that heat-resisting quantity, fire resistance are good, greatly improves its using effect.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited thereto.
Embodiment one:
A kind of high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:26 parts of butyl propionate, polypropylene tree
57 parts of fat, 33 parts of ethyl-para-hydroxybenzoate, 17 parts of polyketone resin, 7 parts of cumyl peroxide, 14 parts of Phenoxyethanol are fire-retardant
3 parts of agent, 6 parts of phosphorous acid lipid stabilizer, 5 parts of magnesium stearate, 4 parts of Tissuemat E, 8 parts of lagoriolite, 4 parts of diatomite, dioxy
3 parts of SiClx, 6 parts of oleamide, 15 parts of polyoxyethylene carboxylate, 6 parts of calcium monohydrogen phosphate, 30 parts of PLA.
The preparation method of described high-temperature flame-retardant plastic film, comprises the following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed is
270-285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) by step (2) raw mixture add extruder in, extrusion forming, cooling, obtain plastic sheeting into
Product.
Embodiment two:
A kind of high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:27 parts of butyl propionate, polypropylene tree
60 parts of fat, 25 parts of ethyl-para-hydroxybenzoate, 14 parts of polyketone resin, 8 parts of cumyl peroxide, 16 parts of Phenoxyethanol are fire-retardant
3 parts of agent, 4 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 5 parts of Tissuemat E, 10 parts of lagoriolite, 5 parts of diatomite, dioxy
3 parts of SiClx, 5 parts of oleamide, 16 parts of polyoxyethylene carboxylate, 6 parts of calcium monohydrogen phosphate, 30 parts of PLA.
The preparation method of described high-temperature flame-retardant plastic film, comprises the following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed is
270-285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) by step (2) raw mixture add extruder in, extrusion forming, cooling, obtain plastic sheeting into
Product.
Embodiment three:
A kind of high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:30 parts of butyl propionate, polypropylene tree
52 parts of fat, 28 parts of ethyl-para-hydroxybenzoate, 13 parts of polyketone resin, 7 parts of cumyl peroxide, 12 parts of Phenoxyethanol are fire-retardant
2 parts of agent, 5 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 8 parts of Tissuemat E, 6 parts of lagoriolite, 3 parts of diatomite, dioxy
2 parts of SiClx, 6 parts of oleamide, 17 parts of polyoxyethylene carboxylate, 3 parts of calcium monohydrogen phosphate, 24 parts of PLA.
The preparation method of described high-temperature flame-retardant plastic film, comprises the following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed is
270-285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) by step (2) raw mixture add extruder in, extrusion forming, cooling, obtain plastic sheeting into
Product.
Example IV:
A kind of high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:35 parts of butyl propionate, polypropylene tree
55 parts of fat, 33 parts of ethyl-para-hydroxybenzoate, 18 parts of polyketone resin, 8 parts of cumyl peroxide, 14 parts of Phenoxyethanol are fire-retardant
3 parts of agent, 6 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 7 parts of Tissuemat E, 9 parts of lagoriolite, 4 parts of diatomite, dioxy
3 parts of SiClx, 3 parts of oleamide, 25 parts of polyoxyethylene carboxylate, 5 parts of calcium monohydrogen phosphate, 22 parts of PLA.
The preparation method of described high-temperature flame-retardant plastic film, comprises the following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed is
270-285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) by step (2) raw mixture add extruder in, extrusion forming, cooling, obtain plastic sheeting into
Product.
Embodiment five:
A kind of high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:25 parts of butyl propionate, polypropylene tree
50 parts of fat, 20 parts of ethyl-para-hydroxybenzoate, 10 parts of polyketone resin, 5 parts of cumyl peroxide, 12 parts of Phenoxyethanol are fire-retardant
2 parts of agent, 3 parts of phosphorous acid lipid stabilizer, 2 parts of magnesium stearate, 3 parts of Tissuemat E, 3 parts of lagoriolite, 3 parts of diatomite, dioxy
1 part of SiClx, 2 parts of oleamide, 10 parts of polyoxyethylene carboxylate, 2 parts of calcium monohydrogen phosphate, 22 parts of PLA.
The preparation method of described high-temperature flame-retardant plastic film, comprises the following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed is
270-285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) by step (2) raw mixture add extruder in, extrusion forming, cooling, obtain plastic sheeting into
Product.
Embodiment six:
A kind of high-temperature flame-retardant plastic film is made up of the raw material of following parts by weight:35 parts of butyl propionate, polypropylene tree
65 parts of fat, 35 parts of ethyl-para-hydroxybenzoate, 20 parts of polyketone resin, 10 parts of cumyl peroxide, 18 parts of Phenoxyethanol are fire-retardant
6 parts of agent, 6 parts of phosphorous acid lipid stabilizer, 5 parts of magnesium stearate, 9 parts of Tissuemat E, 12 parts of lagoriolite, 7 parts of diatomite, dioxy
5 parts of SiClx, 7 parts of oleamide, 25 parts of polyoxyethylene carboxylate, 8 parts of calcium monohydrogen phosphate, 33 parts of PLA.
The preparation method of described high-temperature flame-retardant plastic film, comprises the following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed is
270-285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) by step (2) raw mixture add extruder in, extrusion forming, cooling, obtain plastic sheeting into
Product.
Finally illustrate, the above embodiments are merely illustrative of the technical solutions of the present invention and it is unrestricted, although with reference to compared with
The present invention is described in detail good embodiment, it will be understood by those within the art that, can be to the skill of the present invention
Art scheme is modified or equivalent substitution, and without departing from the objective and scope of the technical program, it all should cover in the present invention
Right among.
Claims (5)
1. a kind of high-temperature flame-retardant plastic film, it is characterised in that be made up of the raw material of following parts by weight:Butyl propionate 25-
35 parts, acrylic resin 50-65 parts, ethyl-para-hydroxybenzoate 20-35 parts, polyketone resin 10-20 parts, cumyl peroxide
5-10 parts, Phenoxyethanol 12-18 parts, fire retardant 2-6 parts, phosphorous acid lipid stabilizer 3-6 parts, magnesium stearate 2-5 parts, polyethylene
Wax 3-9 parts, lagoriolite 3-12 parts, diatomite 3-7 parts, -5 parts of silica 1, oleamide 2-7 parts, aliphatic acid polyethenoxy
Ester 10-25 parts, calcium monohydrogen phosphate 2-8 parts, PLA 22-33 parts.
2. high-temperature flame-retardant plastic film according to claim 1, it is characterised in that by the raw material group of following parts by weight
Into:27 parts of butyl propionate, 60 parts of acrylic resin, 25 parts of ethyl-para-hydroxybenzoate, 14 parts of polyketone resin, peroxidating diisopropyl
8 parts of benzene, 16 parts of Phenoxyethanol, 3 parts of fire retardant, 4 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 5 parts of Tissuemat E, silicic acid
10 parts of aluminium sodium, 5 parts of diatomite, 3 parts of silica, 5 parts of oleamide, 16 parts of polyoxyethylene carboxylate, 6 parts of calcium monohydrogen phosphate,
30 parts of PLA.
3. high-temperature flame-retardant plastic film according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into:30 parts of butyl propionate, 52 parts of acrylic resin, 28 parts of ethyl-para-hydroxybenzoate, 13 parts of polyketone resin, peroxidating diisopropyl
7 parts of benzene, 12 parts of Phenoxyethanol, 2 parts of fire retardant, 5 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 8 parts of Tissuemat E, silicic acid
6 parts of aluminium sodium, 3 parts of diatomite, 2 parts of silica, 6 parts of oleamide, 17 parts of polyoxyethylene carboxylate, 3 parts of calcium monohydrogen phosphate, gather
24 parts of lactic acid.
4. high-temperature flame-retardant plastic film according to claim 1, it is characterised in that by the raw material system of following parts by weight
Into:35 parts of butyl propionate, 55 parts of acrylic resin, 33 parts of ethyl-para-hydroxybenzoate, 18 parts of polyketone resin, peroxidating diisopropyl
8 parts of benzene, 14 parts of Phenoxyethanol, 3 parts of fire retardant, 6 parts of phosphorous acid lipid stabilizer, 3 parts of magnesium stearate, 7 parts of Tissuemat E, silicic acid
9 parts of aluminium sodium, 4 parts of diatomite, 3 parts of silica, 3 parts of oleamide, 25 parts of polyoxyethylene carboxylate, 5 parts of calcium monohydrogen phosphate, gather
22 parts of lactic acid.
5. the preparation method of the high-temperature flame-retardant plastic film according to any one of claim 1-4, it is characterised in that bag
Include following steps:
(1) each raw material components are weighed according to ratio of weight and number;
(2) each raw material components being ready in step (1) are added in kneading machine and stirred, mixing speed 270-
285 revs/min, mixing time is 16-22 minutes, and temperature control is 80-85 DEG C, obtains raw mixture;
(3) raw mixture in step (2) is added in extruder, extrusion forming, cooling, obtains plastic sheeting finished product.